Investigation of CCA fixation in wood by sequential extraction. I Determination of CCA component fixation and preliminary extraction results
2002 - IRG/WP 02-50188
The fixation of CCA-C preservative was investigated in sapwood of red pine (Pinus resinosa Ait.), trembling aspen (Populus tremuloides Michx.) and red maple (Populus tremuloides Michx.) at target retentions of 4.0, 6.4, 9.6 and 30.0 kg/m3. Treated wood sawdust was water extracted at close time intervals during the fixation and analyzed for the contents of unfixed hexavalent chromium, total Cr, Cu ...
S Radivojevic, P A Cooper
Effect of treatment process on performance of copper-chrome-arsenate. Part 1: Fungus cellar tests
1995 - IRG/WP 95-40045
Pinus radiata sapwood stakes 20 x 20 x 400 mm³ were treated with CCA Type C using a range of concentrations and three treatment processes; Bethell, Lowry and Rueping. Preservative retention was determined by chemical analysis of treated material. Following fixation, fungus cellar stakelets, 5 x 10 x 180 mm³ were cut from treated material and after leaching were exposed in unsterile soil beds in ...
M E Hedley, J Anderson, J B Foster, B E Patterson
Possible durability transfer from durable to non durable wood species. The study case of teak wood
2001 - IRG/WP 01-10392
Teakwood is well known for its excellent natural durability, mostly due to its high proportion of extracts. Amongst these extracts, quinones, and more precisely some naphtoquinones (such as lapachol) and anthraquinones (such as tectoquinone) appear to play a crucial role in the resistance to wood decay organisms. At a laboratory scale, sawdust from malaysian teak heartwood has been extracted under...
M-F Thévenon, C Roussel, J-P Haluk
Comparison of the anti-fungal efficacy of Cobra with drill perforation on oscillating pressure treated spruce transmission poles -Laboratory test
1988 - IRG/WP 3469
A laboratory method for measuring the depth of penetration of the fungicidal concentrations effective against basidiomycetes (brown rot) was developed. The tests on CCB oscillating pressure treated spruce transmission poles have shown that the depth of salt penetration can be increased by about 10 mm by a drill perforation before the impregnation. An even better penetration is reached, however, if...
E Graf, B Zgraggen
Remediation of environmental impacts related to inorganic wood preservative chemicals using in-situ geochemical fixation
2001 - IRG/WP 01-50166-17
Use of the inorganic wood preservative chemical chromated copper arsenate (CCA) has resulted in several documented cases of soil and ground water contamination at wood treatment plants due to spills or releases of the treatment chemical. The most significant impact from releases of CCA to the environment is related to hexavalent chromium contamination of ground water. This is due to the relative s...
R M Thomasser, J V Rouse
Standard and accelerated testing of boron-additive wood protection systems
2005 - IRG/WP 05-30381
The main objective of this research was to determine the effectiveness of boron-additive protection systems for above ground applications by means of field testing. The two field test procedures used are based on the L-joint test described in the European standard EN 330. For the first set up the boron treated timber was coated in accordance with the standard EN 330 system. The second set up is ba...
A Mohareb, J Van Acker, M Stevens
Co-operative studies on determining toxic values against wood-destroying basidiomycetes: Progress report to April 1990
1990 - IRG/WP 2357
This document reports progress on the co-operative study between nine laboratories, set up following the proposals contained in Document IPG/WP/2316 (1988). Results have been received from eight laboratories. Toxic values data have been established successfully for the test fungus Coniophora puteana with soil, malt agar and vermiculite methods and with the test fungi Gloeophyllum trabeum and Poria...
J K Carey, A F Bravery
Evaluation of the protective means of some wood preservatives by means of accelerated tests
1973 - IRG/WP 232
In site conditions of the eastern site in the forest-steppe part of the Krasnovarsk region, the relative effectiveness of a series of wood preservatives was obtained by means of field tests. To obtain a more accurate evaluation of the protective qualities of these accelerated tests were carried out in laboratory conditions. In 9 boxes filled with non-sterile soil taken from the site, 72 samples of...
I A Petrenko
Borates as wood preserving compounds: The status of research in the United States
1989 - IRG/WP 3542
This paper describes the extensive, on-going cooperative research effort among government and university research laboratories and industry to fully evaluate the potential for borates as wood preservatives in the United States. Research is discussed in terms of laboratory evaluations, field testing and mill trials, pilot plant pressure treatment studies, and remedial treatments. Future research pl...
H M Barnes, T L Amburgey, L H Williams, J J Morrell
A new concept for the evaluation of wood durability for out of ground contact using accelerated L-joint testing
1997 - IRG/WP 97-20123
Since the wood preservation sector is developing in favour of defining exactly the utilization of wood products and preservation techniques as a function of the envisaged hazard class, more in particular the hazard classes 3 and 4 (EN 350) there is obviously a need for a test method evaluating natural durability for out of ground contact applications. Based on the L-joint test as described in the ...
J Van Acker, M Stevens
A study of the rate of fixation of various chromium-containing preservatives
1991 - IRG/WP 3653
Denmark, and Scandinavia in general, has perhaps the widest range of approved industrial wood preservative types in the world. As an aid in setting realistic fixation periods, work was undertaken to investigate the rate of fixation of chromium in CCA salt, CCA oxide, CCP, CCB, CC and CCF formulations at summer and winter temperatures. The rate of fixation measured in terms of the concentration of ...
L B Sheard
Five years field test results for CCA and ACQ preservatives fixed in different climates
1999 - IRG/WP 99-30208
During assessment of the ground contact stakes in the Norwegian test field, we have found that very often the first visual rot attack is in the zone of the stakes were the stakes have been in contact with each other during the fixation. These parts are usually light green, caused by the lack of light during fixation, compared to the rest of the stake surface, which has a darker colour. To investig...
F G Evans
Accelerated testing for out of ground contact using natural biological preconditioning
1996 - IRG/WP 96-20088
Small blocks made of Scots pine sapwood were treated, buried in vermiculite and exposed to natural microbial colonisation during outdoor exposure prior to laboratory decay testing. Periodic microbial isolations, moisture content, permeability and weight loss tests were also conducted. Bacteria and moulds colonised the vermiculite and miniblocks well. Aureobasidium pullulans was common on TnBTO tre...
S Molnar, D J Dickinson, R J Murphy
Investigation of temperature effect on fixation of Celcure preservative (ACC) in Hornbeam (Carpinus betulus I)
2003 - IRG/WP 03-30304
In this research, the fixation speed of Celcure 2 % (ACC) preservative salt, under temperature of 30 ºC, 40 ºC and 50 ºC on intact wood specimens of hornbeam was investigated. For this purpose, blocks of wood with 2Í 2 Í2 cm dimensions of hornbeam were prepared and saturated with 2% ACC concentration by full-cell process. The specimens were put in three incubators at the above-mentioned temperatures. For measuring the percentage of fixation through time, the specimens were extracted by using hydraulic pressure equipment, under 70 Mpa pressure. The PH of extraction was measured with the method of Diphenyl Carbazid and by using spectrophotometer. This measurement was done continuously and the amount of 6-valence chromium concentration present in the extract was compared with the amount of chromium concentration in the primary solution and then the percentage of fixation was calculated.
The results showed that the decrease in 6-valence chromium is accompanied with increase of PH, this due to absorption of positive hydrogen ion by 6-valence chromium for reduction to 3-valence chromium and also ion –exchange of active components with wood during the primary phase of fixation. Also, the time necessary for reaching complete fixation in intact wood in the fixation temperature conditions of 30, 40, 50 ºC were 98, 52, 24 hours, respectively. In general, the results showed that temperature has effective role accelerating of fixation process.
R Imani, R E Majdar, A Karimi
Exterior wood stains
1979 - IRG/WP 3136
The use of semi-transparent exterior wood stains has grown remarkably since their development during the 1960s. This can be partly attributed to their offering a break with tradition at a time when it was being recognised that changes in the quality of timber and how it was used demanded different methods of exterior wood finishing. Information is already available on the characteristics and uses ...
E R Miller
Accelerated anti-termite laboratory tests, simulation of field conditions and assessment of results for service life
1994 - IRG/WP 94-20034
Termites are one of the most serious biodegrading agents in the tropics. Though some species of termites occur in the warmer temperate regions, only a few species can withstand the rigours of colder regions. Testing of termite resistance of material is done either by field tests or by accelerated laboratory tests. Field tests, though realistic to assess service life, are elaborate, take a long tim...
P K Sen-Sarma
Termite durability of sugi (Cryptomeria japonica) heartwood kiln-dried under high-temperature process in relation to wood extractives
2005 - IRG/WP 05-10547
Termite durability of sugi heartwood samples kiln-dried under a high-temperature process were evaluated by using Reticulitermes speratus (Kolbe) as a test termite sp. The n-hexane extractives of these samples were analysed by a GC technique. The less termite durability was shown on the wood samples dried under the high-temperature process, in comparison with that of the air-dried samples. No GC-p...
S Shibutani, E Obataya, K Hanata, S Doi
Investigation of copper fixation in timber by sodium nitrit
1992 - IRG/WP 92-3707
Solutions containing mixtures of water soluble copper salts and sodium nitrite have been shown to be capable of producing leach resistant copper treatments when impregnated into timber. A rapid leaching trial showed that copper fixation levels of 85-90% were possible which compared well with the fixation level obtained with conventional hexavelant chromium containing systems in the same test regim...
C Waldie, J A Cornfield
Microdistribution of water-borne preservatives in blue gum treated by full-cell process
1990 - IRG/WP 3617
The present work deals with the study of the microdistribution of copper, chrome and arsenic elements in Eucalyptus globulus Labill. sapwood, treated with a CCA water-borne preservative by full-cell process, with the help of scanning electron microscopy together with energy dispersion X-ray analysis technique. The work shows that the retention of CCA elements is high in vessels and vasicentric par...
D De Sousa Castro Reimão, J M Palacios
Gaseous preservative treatment of wood
1990 - IRG/WP 3631
A recent development in processing wood with a gaseous preservative means that dry, treated wood can be produced in under 30 hours with the benefits of product diversification, faster stock turnover and the ability to respond to short term demand. About 400,000 m³ of wood are treated each year in New Zealand with boron salts to protect from borer infestation. Traditionally this treatment is effec...
R Burton, A J Bergervoet, K Nasheri, P Vinden, D R Page
Differential retention and leaching of CCA (C) in sapwood and heartwood of Kenyan-grown blue gum (Eucalyptus saligna) and black wattle (Acacia mearnsii)
2005 - IRG/WP 05-30371
Retention and leaching of CCA(C) in small samples of sapwood and heartwood of Kenyan-grown blue gum (Eucalyptus saligna) and black wattle (Acacia mearnsii) were tested under laboratory conditions. Clear samples (100mm x 30mm x 40mm) were removed from the sapwood and heartwood of sampled defect-free and sound plantation trees of the two species. These were separately air-dried to 15% MC, end-seal...
R Venkatasamy
Environmental characterisation of retification process by-products (liquid and gaseous wastes)
2005 - IRG/WP 05-50224-10
In order to reduce environmental risks during the service life of the treated wood and to find new alternative developments on the durability of wood, some research and technology development have been made on thermal treatment. The retification process is one of these processes. The retification process induces chemical modification of the lignin and cellulosic components and modifies the intrins...
G Labat, E Bucket, S Legay, C Yriex, P Marchal, E Raphalen, M Vernois, R Guyonnet, H Besset, E Fredon), G Vilarem, L Rigal, C Raynaud
Wood preservatives treatment of black spruce
1997 - IRG/WP 97-40092
A representative sample of black spruce logs from Central Newfoundland was harvested and processed to dressed 2"x4" lumber. Over 400 pieces of lumber were then incised and treated with ACQ preservative in a semi-industrial retort. 9 charges of 20 samples were used to determine treating parameters and 11 charges of 20 pieces were treated using the optimized process. This material was inspected by a...
A R Zahora, J P Hösli
Chemically modified tannin and tannin-copper complexes as preservatives for wood
2001 - IRG/WP 01-30271
The efficacy of Mimosa tannin, chemically modified tannin, and tannin-copper complexes as wood preservatives was studied. When the tannin-ammonia-CuCl2 solutions were impregnated into wood specimens in a one-step procedure, a large quantity of the tannin-copper complex was fixed in the specimens. Little of the complex was leached from specimens by a weathering treatment, and these specimens showed...
H Yamaguchi
The movement of iron into field test stakes
1987 - IRG/WP 2284
Failed and sacrificial stakes recovered from the Westham Island field test site were examined for their iron content. Varying amounts were recorded, which were greatest in the failed stakes. The possible role of the iron taken up by the below ground portion of the stakes, in accelerating the decay process and/or the preservative leaching is under investigation. The reaction of the iron with the ch...
J N R Ruddick, P I Morris