Utilization of coconut timber from north Sulawesi, Indonesia. Part 2: Treatability
1994 - IRG/WP 94-40025
Under tropical conditions coconut wood is quickly degraded by mold and blue stain fungi. Low density wood in ground contact is commonly decomposed by wood destroying fungi within a period of only a few months, higher density wood from the outer stem regions within 24 to 30 months (MOSTEIRO, CASIN, SERIBAN 1976; McQUIRE 1975). Moreover, according to McQUIRE (1975) green wood of lower density is hig...
R-D Peek
Fixation of CCA preservatives in cocos-, oil- and rattan-palm
1986 - IRG/WP 3371
In previous tests with jubaea-palm almost no fixation of a CCA-preservative Type B could be achieved, consequently, further leaching tests were carried out with samples of 1 cocos-, 1 oil- and 2 rattan-palms from Malaysia. A good fixation of chromium and copper took place in cocos-palm after 4 weeks storage at 28°C. Nevertheless the fixation was slower than in pine-wood and demanded an elevated t...
H Willeitner, K Brandt
Practical experiments with Boracol 10 Rh used as a fungicide in the repair process after attack by the dry rot fungus (Serpula lacrymans)
1987 - IRG/WP 3458
The test is carried out in an old house in Nyhavn, Copenhagen. The roof and the walls close to were heavily attacked by dry rot fungus (Serpula lacrymans) because damage to the zinc covering the frontspice were letting in water to the wood and wall construction. An attack by the dry rot fungus is more complicated to repair compared with other wood destroying fungi because beside the damage on wood...
J Bech-Andersen
In-house accelerated method for testing decay resistance of treated wood
2004 - IRG/WP 04-20286
Fungicidal compounds often change their effectiveness when they are incorporated into candidate formulations. For this reason fungistatic effectiveness needs to be re-evaluated as many times as the formula has been modified for better performance. To avoid multiple expenses, in-house fungistatic tests are essential. Our goal was to develop in-house usable, simple but reliable and reproductive proc...
N Vidovic
Oxidation of wood components during CCA-C fixation
1993 - IRG/WP 93-30024
Pre-extracted radial sections of southern yellow pine sapwood were treated with CCA-C and analyzed by X-ray photoelectron spectroscopy (XPS). The ratio of C1 (carbon bonded to carbon and/or hydrogen) to C2 (carbon bonded to one oxygen) in XPS Cls spectra was taken as a measure of the progress of oxidation of wood components during CCA fixation. This ratio was 0.82 before CCA treatment and increase...
M Kaldas, P A Cooper
Rapid fixation of Chromated Copper Arsenate (CCA) wood preservatives by microwave treatment
2000 - IRG/WP 00-40184
Rapid microwave heating of freshly chromated copper arsenate (CCA) treated timber indicates that rapid preservative fixation is possible within approximately 40 seconds. The leaching of CCA was evaluated using simulated rainfall. Cost analyses indicates that microwave fixation using an on-line conveyor belt fixation process with an output of 4m3/hour using a microwave power supply of 230 kW costs ...
G Torgovnikov, P Vinden, E Mapanda, P R S Cobham
Some practical implications from recent research on the fixation of CCA preservatives
1975 - IRG/WP 358
The mechanism of fixation of CCA preservatives is briefly described. If the temperature is increased during the primary fixation period, the formation of intermediate fixation compounds is less extensive. The length of the primary fixation period is of practical interest. It is determined by preservative composition and concentration, temperature and wood species. Diagrams are given for Pinus sylv...
S-E Dahlgren
Moderate temperature fixation of CCA-C
1989 - IRG/WP 3522
Several Canadian treating plants are using moderate temperature (40-60C°) fixation chambers to reduce drippage and leaching from fresh CCA treated wood. In this study, chromium reduction and surface leaching properties of CCA-C treated red pine (Pinus resinosa) pole sections were monitored during exposure to temperatures of 50-60C° and 90-100% RH conditions. Chromium-VI concentration in the abso...
P A Cooper, Y T Ung
Step-wise pressure process for reducing surface roughness in Japanese cedar timber
2003 - IRG/WP 03-40256
Sixteen dried sawn-timber (10.5 x 10.5 x 360 cm) were cut into half. The half of them was treated by step-wise pressure process with 2.5 MPa maximum, and the other half was treated by conventional pressure process with 2.5 MPa maximum. Average DDAC preservative absorption was 461 kg/m3 in the former and 525 kg/m3 in the later. Surface roughness was expressed as the profile element height of collap...
K Yamamoto, M Nozoki
Service Life Prediction of Wood Claddings by in-situ Measurement of Wood Moisture Content
2004 - IRG/WP 04-20304
The Danish Technological Institute is in co-operation with industry partners running a project aiming at predicting the service life of different wood protecting systems.
The project focuses on examining the moisture reducing effect of different wood claddings and the ability to maintain the appearance of the surfaces, when the wood is used in service class 3.
A façade construction is exposed t...
B Lindegaard, N Morsing
Gaseous boron treatments of wood and wood products
1992 - IRG/WP 92-3691
Treatment of wood and wood products by gaseous organoborates has now been under study for about 5 years. This technique has potential for boron treatment of a wide range of substrates from solid wood through to wood composite materials such as particleboard or wet and dry formed fibreboards. The vapour treatment technique is proving to be very flexible in that it can be adapted to integrate into a...
A J Bergervoet, R Burton, K Nasheri, D R Page, P Vinden
Studies of the mechanism of chromated-copper preservative. Fixation using electron spin resonance
1992 - IRG/WP 92-3701
Two softwoods and one hardwood species were treated with chromium trioxide, copper sulphate, chromated-copper wood preservative (CCA). The treated wood samples were analyzed during fixation by electron spin resonance (ESR). ESR spectra indicated that more than one Cr(V) species was generated from Cr(VI) soon after CCA treatment. The Cr(V) signal became strong within increased several hours followe...
K Yamamoto, J N R Ruddick
The accelerated L-joint test method for determination of the out of ground natural durability
1998 - IRG/WP 98-20146
The accelerated L-joint test incorporates a moistening device and uses a close end water trap in an open joint connection with a laminated tenon member consisting of the perishable reference wood species scots pine sapwood and beech.
After one year of exposure it is possible to show a distinct identification of natural durability classes 4 and 5 against the more durable wood species. Both weight ...
J Van Acker, C Brauwers, M Stevens
Development process of a new anti-sapstain formulation and its present status with the relevant problems
2001 - IRG/WP 01-30257
An anti-sapstain formulation, which contains 2-(thiocyanomethylthio)benzothiazol (TCMTB) and methylene-bis-thiocyanate (MBT) as active ingredients, was developed by a technical agreement with Buckman Laboratories (Memphis, TN, USA) as an alternative to chlorinated phenols for the Japanese market. The formulation was commercialized as BAM 12 years ago. As anti-sapstain treatment is commonly conduct...
K Nobashi, Y Nomura, K Tsunoda
Estimation of the impregnation degree of pine wood by the distribution analysis of active ions concentration in the cross-section
1999 - IRG/WP 99-20174
Samples in the form of pine wood rollers of diversified moisture content of ca. 50, 28 and 12% were impregnated with a water solution of the mixture type CCB with the use of the full-cell process. Moisture content was determined in individual layers from the girth to the pith. In the same way the concentrations of copper and chromium ions with the use of the spectrophotometric method and recalcula...
K Lutomski, B Mazela
The performance of chlorothalonil after 4.5 years in the accelerated field simulator
1994 - IRG/WP 94-30041
The decay resistance of chlorothalonil in oil was examined in an accelerated field simulator (AFS). Pinus radiata D. Don and Eucalyptus regnans F. Muell. sapwood stakes were treated, placed in soil in the AFS, and monitored over 4.5 years. CCA type C treated stakes were included for comparison. Water and toluene treated control stakes were heavily decayed after 1-2.5 years. Oil treated controls, t...
L J Cookson
Industrial fixation systems: key factors, limitations and optimisation through the use of computer simulation modelling. Discussion paper
1994 - IRG/WP 94-40026
This paper briefly describes four fixation operative in the Netherlands, namely: circulating and non-circulating steam fixation cylinders, steam fixation chambers and controlled climate rooms. The general limitations of industrial practice are reviewed against the background of established fixation theory. The controlling variables, both material and process-related, for fixation processing are sp...
A J Pendlebury, M Riepen, M J Boonstra, W Gard
Stability, performance and distribution of propiconazole (R 49362) in acceleratedly aged wood
1991 - IRG/WP 3647
The permanency of propiconazole (R 49362 - WOCOSENÔ technical - Janssen Pharmaceutica) in wood was examined in an 18 month storage test, an evaporative ageing study (EN 73), a volatilization stress experiment, and water-leaching studies (EN 84). The biological efficacy against two brown rot fungi: Coniophora puteana BAM Ebw. 15 and Gloeophyllum trabeum BAM Ebw. 109 was assessed according to the E...
A R Valcke, M Stevens
Accelerated weathering test for the evaluation of wood preservative efficacy
2003 - IRG/WP 03-20262
Wood samples treated with ammonium copper quat (ACQ-1900 and ACQ-2200), Chromated copper arsenate (CCA), Tanalith E 3491 and Wolmanit CX-8 have been studied in accelerated weathering experiments.
The weathering experiment was performed by cycles of 2 hours UV-light irradiation followed by water spray for 18 minutes. The changes on the surface of the weathered samples were characterized by FTIR Sp...
A Temiz, M Eikenes, Ü C Yildiz, F G Evans, B Jacobsen
Differences and their causes of CCA and CCB efficacay among some softwoods and hardwoods
1991 - IRG/WP 3656
Wood blocks from two softwoods and two tropical hardwoods species treated with different concentrations of CCA, CCB, and combinations of CrO3, CuS04, H3BO3 were subjected to the decay by brown rot fungus, Tyromyces palustris. CCA maintained good effect both in softwoods and hardwoods, while CCB and the other combinations lost their effectiveness after leaching. Chemicals leached from CCA treated w...
K Yamamoto, M Rokova
Effect of compression wood on leaching of chromium, copper, and arsenic from CCA-C treated red pine (Pinus resinosa Ait.)
2000 - IRG/WP 00-30232
In this study, the effect of compression wood formation on the release rate of chromium, copper, and arsenic elements from red pine (Pinus resinosa Ait) was investigated. Wood blocks from red pine containing compression and normal wood portions were treated with a 1.0% CCA-C solution and were then allowed to fix at 23 ± ??2°C (74 ± 4°F) for 0, 6, 24, 48, 96, 192, and 336 hours. After each fixa...
S N Kartal, S T Lebow
Copper based water-borne preservatives: Copper adsorption in relation to performance against soft rot
1987 - IRG/WP 3452
As part of a fundamental study concerned with the performance of copper based water-borne preservatives the adsorption of copper from aqueous solutions by 4 hardwood and 1 softwood species has been studied. Experiments were conducted to determine the influence of solution pH, solution concentration and solution temperature. The results obtained were consistent with an acid form ion-exchange mechan...
P M S Rennie, S M Gray, D J Dickinson
A diffusion and reaction model for the leaching of Cr-VI from unfixed CCA-treated wood
2001 - IRG/WP 01-50169
A physical model applicable to the leaching of any substance undergoing a first-order fixation reaction with wood is presented. Using this model and a laboratory leaching experiment with small wood samples immersed in water, the radial and tangential diffusion coefficients and the reaction rate constants of Cr-VI in unfixed CCA-treated red pine (Pinus resinosa Ait.) are measured. Reaction rate con...
L Waldron, P A Cooper
Bibliography on the use of boron compounds for the preservation of wood
1973 - IRG/WP 315
This bibliography is based on an earlier literature survey prepared by J. Thornton and Wm. E. Bruce (O.E.C.D. Document No. 27/DAS/CSI/M/91) which was enlarged and revised for a meeting in Paris in October 1968 (Document 27/DAS/CSI/M554) by Professor W. Bavendamm of Reinbek. The latter (1968) document with its 166 references has now been extended and brought up to date. Acknowledgments are due to B...
R Cockcroft, J F Levy
Comments on leaching in view of accelerated testing
1977 - IRG/WP 294
We developed an accelerated test for leaching at elevated temperatures (75-85°C). This test was used for the examination of 11 preservative formulations containing Cu, Zn and As. The data obtained from these experiments were compared with data on some formulations tested by ASTM standard leaching test. The method consists in making a large surface to volume ratio of wood from a treated block by c...
J Rak