Copper Coating on Wood: a New Way of Protecting Wood
2013 - IRG/WP 13-30617
Thermal spray metal coating technology was used to apply a thin layer of copper on the surfaces of a number of wood species. The adhesion of metal coating to mahogany, oak, soft maple, spruce, white pine and medium density fibreboard (MDF) was evaluated by pull off adhesion test. The resistance of copper coated wood samples to mildew were assessed in the lab. Also, the decay resitance and water re...
M Nejad, R Shafaghi, L Pershin, J Mostaghimi, P Cooper
The effects of impregnation with secondary metabolite extracted from Ipe on durability of Japanese cedar and beech wood
2013 - IRG/WP 13-30618
Ipe wood is known for its high durability; it has been widely used in exterior structures that are exposed to the weather. In this paper, to increase the durability of less durable wood, Japanese cedar and beech specimens were impregnated with a secondary metabolite from Ipe. In a previous study, secondary metabolites extracted by a Soxhlet extraction method showed antifungal properties. Therefore...
T Iida, R Konuma, K Kawarada
Preparation of Copper Rosinate Emulsion and Its Resistance against Wood Decay Fungi
2013 - IRG/WP 13-30619
A leaching-resistant water-borne copper preservative was prepared by means of the following three steps: (1) Gum rosin was saponified with potassium hydroxide. (2) The soap reacted with copper sulfate to form copper rosinate. (3) The copper rosinate was emulsified with a mixture of Tween 20 and Span 80. Poplar (Populus ussuriensis) wood was impregnated with 0.5%, 1.0%, 1.5%, or 2.0% of the copper ...
Mingxin Zhang, Shujun Li, Qian Wang, Bo Li, Qiong Wu
Effect of Nano and Micronized Particles as Wood Preservatives for Termite Control
2013 - IRG/WP 13-30620
Subterranean termites are a major factor in the biodegradation of wood constructor products. In this study the efficacy of wood treated with micronized copper, zinc oxide and their mixture was compared to that of wood treated with soluble amine copper oxide with subterranean termites in a laboratory test. All of the formulations tested were effective in controlling wood degradation by the termites...
M Akhtari, D Nicholas, A Rowlen, M Arefkhani
Effect of biodiesel on Performance of Isothiazolone
2013 - IRG/WP 13-30625
Biodiesel has a number of attractive properties, including the ability to readily solubilize a number of biocides and a tendency to reduce odors associated with other solvents such as petroleum-based diesel. Biodiesels, however, have also been implicated in reduced performance of some, but not all preservatives. It is important to assess the effects of biodiesel on each biocide. Soil block tests ...
Cheng Hua-Kang, L Jin, C Freitag, J J Morrell
Curing kinetics of nano cupric oxide (CuO) modified PF resin as wood adhesive: Effect of surfactant
2013 - IRG/WP 13-40620
The effect of nano cupric oxide (CuO) in combination with surfactants on the curing kinetics of phenol formaldehyde (PF) resin, as well as the bonding strength of plywood prepared using the modified resin were investigated in this study using dynamic and isothermal differential scanning calorimetry (DSC). The result showed that the incorporation of nano CuO along with alkane surfactant made in the...
Wei Gao, Guanben Du
Hygroscopicity of wood after polyethylene glycol (PEG) impregnation and/or heat treatment
2013 - IRG/WP 13-40623
The hygroscopicity of wood after polyethylene glycol (PEG) impregnation and/or heat treatment was investigated by testing the water uptake, equilibrium moisture content (EMC) at various relative humidity levels, and contact angle of the poplar wood surface. The results showed that: (1) At the first moment, the heat treatment at temperatures lower than 160 ℃ did not reduce the water uptake be...
Weiyue Xu Yuan Zhu, Jinzhen Cao
Utilization of TG-DSC to study thermal degradation of beech and silver fir
2013 - IRG/WP 13-40628
Thermal treatment of wood is, besides other wood modification system, used to improve the decay resistance and dimensional stability. However, the chemical changes that are caused by treatment process are still difficult to quantify, characterize and control. Previous studies have shown that thermodesorption coupled to GC-MS is an attractive tool to characterize and quantify products formed during...
K Candelier, A Treu, J Dibdiakova, E Larnøy, A Petrissans, S Dumarçay, M Pétrissans, P Gérardin
Study of UV resistance and natural weathering of coatings on chemically modified wood
2013 - IRG/WP 13-40629
In this study, UV resistance and weathering performance of rubberwood (Hevea brasiliensis) and radiata pine (Pinus radiata) modified with benzoyl chloride and acetic anhydride was studied. Performance of polyurethane based wood coatings on modified wood was also evaluated. Unmodified and chemically modified specimens were exposed to accelerated and natural weathering. Modified and unmodified woo...
K K Pandey, K Srinivas
Field performance of wood impregnated with siloxanes using supercritical carbon dioxide
2013 - IRG/WP 13-40632
This paper presents preliminary results from a 13-month field test containing pine sapwood samples (Pinus sylvestris) impregnated with a mixture of siloxane and organic biocides using supercritical carbon dioxide as carrier. Samples were exposed above ground at a Danish field test site using matched non-treated sapwood controls for every treated sample. All samples were painted before exposure. Pi...
A Kjellow, F Imsgard, J Fernandes, R Wagner, J Delis
Effect of electron beam irradiation on the fire retardant penetration into wood
2013 - IRG/WP 13-40642
Electron beam processing which can fast and easy change the nature of the material has received considerable attention recently. Studies using electron beam has been conducted in various fields and it has been applied in many industrial sectors. Electron beam has higher energy than other electromagnetic waves. It has excellent object permeability. It affects degradation of intermolecular cross-lin...
Dong won Son, Jong Sin Lee, Mee Ran Kang, Sang Bum Park
COST Action FP0904 – Increasing the Understanding of Thermo-Hydro-Mechanical Wood Behaviour and Processing
2013 - IRG/WP 13-40646
The polymeric components of wood and its porous structure allow its properties to be modified under the combined effects of temperature, moisture and mechanical action – so-called Thermo-Hydro-Mechanical (THM) treatments. Various types of processing techniques, including high temperature steam with or without an applied mechanical force, can be utilised to enhance wood properties, to produce eco...
D Jones, P Navi
Durability of alternatives to CCA-treated wood - Results from field tests after 11 years exposure
2013 - IRG/WP 13-30633
The present study was initiated as a consequence of restrictions against the use of CCA-type
wood preservatives in Sweden in the 1990s. New copper-based formulations were introduced on
the market and to some extent, also alternatives to preservative-treated wood, such as thermally
and chemically modified and linseed oil treated wood as well as heartwood of non-tropical
naturally durable wood s...
P Larsson Brelid, M-L Edlund
Effect of Nano and Micronized Particles as Wood Preservatives for Termite Control
2013 - IRG/WP 13-30620
Subterranean termites are a major factor in the biodegradation of wood constructor products.
In this study the efficacy of wood treated with micronized copper, zinc oxide and their
mixture was compared to that of wood treated with soluble amine copper oxide with
subterranean termites in a laboratory test. All of the formulations tested were effective in
controlling wood degradation by the term...
M Akhtari, D Nicholas, A Rowlen, M Arefkhani
Effect of Nano-silver and Nano-copper and Nano-zinc oxide on Paulownia wood exposed to white-rot fungus
2013 - IRG/WP 13-30635
Paulownia is known as a fast growing tree and it can be used in several applications. The present study investigated the effect of Nano-silver and Nano-copper and Nano- zinc oxide on resistance of Paulowina (Paulownia fortunei) wood against the white rot fungus (Coriolus versicolor). Wood specimens with a dry density of 0.37g/cm3 were impregnated with a 400 ppm aqueous suspension of micronized na...
M Akhtari, M Ganjipour
Protein extraction from wood decay fungus Postia placenta
2014 - IRG/WP 14-10827
Wood decay fungi (often distinguished as white rot and brown rot) belonging to the basidiomycetes, are common inhabitants of forest litter, where they play an important role in carbon cycling. Brown rot fungi are perhaps the most important organism involved in the degradation of wood products, and of considerable economic importance. Brown rotted wood loses strength very early because of the rapid...
A Pilgård, P Arnold, K Richter
The Chelator Mediated Fenton System in the Brown Rot Fungi: Details of the Mechanism, and Reasons Why it has Been Ineffective as a Biomimetic Treatment in some Biomass Applications – a Review
2014 - IRG/WP 14-10828
The chelator-mediated Fenton (CMF) reaction requires the action of two types of chelating compounds. The first chelator, oxalate, solubilizes and then sequesters iron, and the second chelator reduces iron. Iron reduction must be controlled near the fungal hyphae to prevent damaging Fenton chemistry from occurring in that location. Similarly, iron reduction must be promoted within the wood/plant ce...
B S Goodell, M Nakamura, J Jellison
Resistance to Decay Fungi of Scots Pine Impregnated with Natural and Chemical Preservatives
2014 - IRG/WP 14-30650
In this study, heart-wood and sap-wood specimens of the Scots pine which is naturally grown in Turkey were treated with natural (valex) and some chemical preservatives such as CCA - C (Copper / Chrome / Arsenic), CBA - A (Copper / Boron / Azole). The wood protective efficacies of these preservatives were investigated by means of fungi decay test (EN 113).
As a result of the study it was found t...
S Yildiz, U B Şimşek
Chemistry of copper preservative treated wood
2014 - IRG/WP 14-30651
The reaction chemistry of micronized copper wood preservatives is fundamentally different from any previous inorganic preservative system. In order to study the chemistry, analytical procedures had to be developed which allowed the determination of the total copper as well as the copper which reacted with the wood forming copper-wood complexes. With the success of this approach it also became poss...
Wei Xue, P Kennepohl, J N R Ruddick
Visualization of gold/silver nanostars in wood by surface enhanced Raman spectroscopy
2014 - IRG/WP 14-30653
Nanotechnology is a fast growing up-to-date technology and ventures expeditiously in the wood preservative market. However, there is still a huge lack of understanding about the interaction and incorporation of nanoparticles (NSs) in wood. Surface-enhanced Raman scattering (SERS) offers unique advantages as an analytical tool with a high selectivity and sensitivity without matrix interference. Her...
C Geers, L Rodríguez-Lorenzo, M Placencia Peña, P Brodard, T Volkmer, B Rothen-Rutishauser, A Petri-Fink
Thermal durability and biodegradation of tannin lignin adhesives
2014 - IRG/WP 14-40657
Mimosa tannins and lignosulfonates were used in wood adhesives formulation to substitute resins based on formaldehyde. Mimosa tannins were mixed with either glyoxalated sodium lignosulfonates or glyoxalated ammonium lignosulfonates. The ratios of mimosa tannins and sodium lignosulfonates varied from 20% tannins to 60% tannins. The thermal durability of the adhesives were analysed by thermogravimet...
L Chupin, B Charrier, A Pizzi, F Charrier
Full-scale impregnation of wood with siloxane using supercritical carbon dioxide
2014 - IRG/WP 14-40659
Full-scale impregnation of wood with siloxane was carried out using supercritical carbon dioxide as solvent. A batch of 3530 kg of Scots pine sapwood was impregnated to a retention of approximately 1.3% siloxane. The treatment also consisted of a simultaneous impregnation with organic biocides. The performance of the wood was evaluated in terms of capillary water uptake according to a modified EN ...
A Kjellow, F Imsgard, J Fernandes, R Wagner, J Delis
Termite resistance of wood modified with short- and long-chain siloxanes
2014 - IRG/WP 14-40660
Scots pine (Pinus sylvestris L.) sapwood specimens modified with short- and long-chain amino-functional siloxane emulsions were exposed to subterranean termites (Reticulitermes flavipes Kollar). Laboratory choice and no-choice tests following the standard EN 117 (2013) were conducted for 8 weeks in order to evaluate the influence of these silicon-based compounds on the termite resistance of treate...
P Gascón-Garrido, M-F Thévenon, H Militz, C Mai
The effect of UV irradiation on some technological properties of different polyurethane varnishes coated plywood panels from veneers dried at different temperatures
2014 - IRG/WP 14-40661
In this study, the effect of UV irradiation on some technological properties of three different polyurethane varnishes coated plywood panels produced from Scots pine (Pinus sylvestris L.) and Maritime pine (Pinus pinaster L.) veneers manuactured and dried at different temperatures was studied. Accordingly, 32°C log peeling temperature and three different veneer drying temperatures (110, 140 and ...
Ö Özgenç, C Demirkir, Ü C Yildiz, G Çolakoğlu
Effect of Nano-Wollastonite on Water Absorption in Particleboard
2014 - IRG/WP 14-40662
Effects of wollastonite nanofibers on physical properties of particleboard were studied. Nano-wollastonite (NW) was applied at 5, 10, 15, and 20 g/kg, based on the dry weight of wood-chips, and compared with control specimens. Two application methods of NW were used: surface application (SA), and internal application (IA). Density was kept constant at 0.68 g/cm3 for all treatments. Tests were carr...
S Karimi, H Reza Taghiyari, A Karimi, P M Tahir, J Abdul Halip