Physical and Mechanical Properties of Hydrothermally Modified Mulberry (Morus alba L.) Wood
2009 - IRG/WP 09-40481
This research was carried out to investigate influences of hydrothermal modification on physical and mechanical properties of mulberry wood that is used for musical instruments in Iran. Samples of mulberry wood were cut into size of 20x20x360 mm and placed in a water filled stainless steel cylinder and treated at temperatures of 100, 120 and 140ºC for 1 and 5 hours. Treated samples were subjected...
A Talaei, K Yaghoobi
Non-destructive evaluation of termite and decay damaged to timber-in- service
2010 - IRG/WP 10-20451
A leading joint research project was financed by the ARC, engaging some of the leading Universities in Australia, to look at field techniques to determine if timber-in-service is infested with termites and decay fungi after which microwave technology will be employed to eliminate the termites and/or decay in-situ. The next step will be to quantify the damage caused on the sectional dimensions of t...
C Adam, B M Ahmed Shiday, G Brodie
The kinetics of catalytic acetylation of Pinus radiata (D. Don) using conventional and microwave heating
2010 - IRG/WP 10-40485
This study outlines the effect of catalyst and microwave heating on the degree of acetylation in radiata pine. Samples of radiata pine sapwood were impregnated with potassium acetate (KAc) dissolved in two different solvents (water and methanol). Impregnated samples were dried and subjected to acetic anhydride loading followed by conventional and microwave heating. The degree of acetylation was ev...
A Kumar Sethy, P Vinden, G Torgovnikov, S Przewloka
Hydrothermal modification for upgrading the durability properties of soft deciduous wood
2010 - IRG/WP 10-40494
To extend the application potentialities of soft deciduous wood, upgrading the durability properties, hydrothermal modification (HTM) of aspen alder and birch wood was investigated. The treatment was conducted in a multifunctional laboratory device WTT. In the previous cases it has been found that the treatment at 160oC improves the durability insufficiently. The modification at 180oC ensured a hi...
B Andersons, I Andersone, V Biziks, I Irbe, J Chirkova, E Sansonetti, J Grinins, H Militz
Wet and dry adhesion of coatings on modified and unmodified wood: comparison of the pull-off test and the cross-cut test
2010 - IRG/WP 10-40524
The objective of this paper is to study the influence of several types of modification (acetylation, furfurylation, thermal modification) on coatings adhesion and to compare two methods of assessing the adhesion: the cross-cut test and the pull-off test both tested in dry and wet conditions. The study also investigates the effect of other parameters of the wood substrates on adhesion like the ring...
L Podgorski, G Grüll, M Truskaller, J D Lanvin, V Georges, S Bollmus
Bioresistance of Poplar Wood Compressed by Combined-Hydro-Thermo-Mechanical Wood Modification (CHTM) Process
2010 - IRG/WP 10-40532
Bioresistance of treated Poplar wood by CHTM process (Combined-Hydro-Thermo-Mechanical Wood Modification) was studied in the current research work. Resistance against brown rot fungus Gloeophyllum trabeum as well as the soft rot decay was the main concern of this work. Poplar wood blocks were hydrothermally treated at temperatures of 120,150 and 180°C for holding time of 0, 30 and 90 min. afterwa...
L Khademi-Bami, B Mohebby
Microwave-Assisted Organic Acids Extraction of Chromate Copper Arsenate (CCA)-Treated Southern Pine
2010 - IRG/WP 10-50267
The extraction effects of acid concentration, reaction time and temperature in a microwave reactor on recovery of CCA-treated wood were evaluated. Extraction of copper, chromium, and arsenic metals from chromated copper arsenate (CCA)-treated southern pine wood samples with two different organic acids (i.e., acetic acid and oxalic acid) was investigated using a microwave reactor. Oxalic acid was e...
Bin Yu, Chung Y Hse, T F Shupe
Multilayer hot-press drying and chemical modifying of poplar wood with urea-formaldehyde prepolymer
2011 - IRG/WP 10-40539
The objective of this study was to determine the technology of chemical modifying and multilayer hot-press drying on poplar wood. The chemicals were impregnated into cell lumen space by pulse-dipping machine to improve the dimension stability and mechanical property of timber. The timbers were compressed and dried by the multilayer hot-press drying to increase the density of timber. Results indica...
Guofeng Wu, Yifei Jiang, Sheng Yao, Junwen
Molecular investigation of Postia placenta growing in modified wood
2011 - IRG/WP 11-10756
Brown rot is the most common and destructive type of fungal decay for wood in service. These fungi depolymerize preferentially the structural carbohydrates, cellulose and hemicellulose in the cell wall leaving oxidized lignin behind. Modified wood can provide protection against a variety of wood deteriorating organisms, including decay fungi. However, there is still little known about the mode of ...
B Schmöllerl, G Alfredsen, C G Fossdal, M Westin, A Steitz
Comparative investigations between thermal and microwave assisted digestion as a novel tool for the chemical analysis of inorganic wood preservative components
2011 - IRG/WP 11-20461
The correct chemical impregnation of wood requires an internal as well as external quality control of the treated wood. The active is located in a solid matrix, therefore it is often difficult to analyse such material since most analytical procedures are based on liquid systems. Because of this quite a number of methods – like extraction or thermal digestion - were developed in order to transfer...
H Ahl, J Fromm, E Melcher
Effects of Heat-Treatment in Hot Water and Steam Mediums on Gas Permeability of Beech Wood
2011 - IRG/WP 11-40557
Heat-treatment, as a major method of wood modification, improving dimensional stability, and natural durability, has been studied greatly from different aspects. The effect of heat-treatment on gas permeability, as an important physical property of wood, in two different mediums of hot water and steam, as well as in two buffers of 7 and 8, is the main topic of the present study. Hydrothermal treat...
H Reza Taghiyari, A Talaei, A Karimi
Wet and dry adhesion of coatings on modified and unmodified wood: influence of 18 months of natural weathering on the pull-off test and cross-cut test results
2011 - IRG/WP 11-40569
The objective of this paper is to study the influence of several types of modification (acetylation, furfurylation, heat treatment) on coatings adhesion after 18 months of natural weathering according to EN 927-3 in Vienna (Austria).
The paper compares two methods for assessing the adhesion: the cross-cut test (EN ISO 2409) which is the conventional method used and recommended in EN 927-3 and th...
L Podgorski, G Grüll, M Truskaller, J D Lanvin, S Bollmus
Preliminary laboratory bioassay to evaluate engineered Fibre-boards against subterranean termites C. acinaciformis (Isoptera: Rhinotermitidae)
2012 - IRG/WP 12-10768
In Australia, laboratory bioassays with subterranean termites typically contain groups of workers and soldiers in a substrate of moist mound material. This termite substrate may affect termite consumption, and the test materials create a favorable termite condition for the test. The main purpose of this test is to examine the effect of a melamine formaldehyde treatment of wood panels to evaluate t...
B M Ahmed (Shiday), H Militz, B Ozarska, I Ali, L Kloeser
Effects of oil types and treatment temperature on the properties of wood subjected to thermal modification in oil medium
2012 - IRG/WP 12-40574
The effect of the use of oil as a medium of heat transfer during thermal modification of different species of wood has been widely investigated with different results accruing with regards to the various end-use properties of the materials. However very little have been done on the effect of oil types as well as its interaction with treatment temperature on the resultant properties of the material...
L Awoyemi, M M Apetogbor, A A Oteng-Amoako
The resistance of thermo and thermo-oil modified black poplar wood (Populus nigra L.) to Basidiomycetes fungi
2012 - IRG/WP 12-40585
The share of area taken by poplar tree species in Poland account for 2.0% of the area of state forests, 4.8% of national parks and for 2.3% in the privately-owned forests. It is shown and expected an increase in the share of poplar stands connected with plantation of fast growing trees. The poplar wood is not resistant to Basidiomycetes fungi, easy attacked by insects and in consequence is regarde...
A Fojutowski, A Kropacz, A Noskowiak
Corrosion of fasteners in heat-treated wood – progress report after nine years’ exposure outdoors
2012 - IRG/WP 12-40601
The corrosion of common fastener materials now in use - mild steel, zinc-coated steel, aluminium and Sanbond Z-coated steel – has been evaluated after nine years’ exposure outdoors in untreated and heat-treated (thermally modified) spruce (Picea abies). Spruce from south-western Sweden was used. The heat-treatment was carried out in Finland by Stora-Enso Oy according to the ThermoWood process ...
J Jermer, B-L Andersson
Improvement of the biological performance and dimensional stability of two tropical woods by thermal modification
2012 - IRG/WP 12-40605
Pink cedar wood and rubberwood were thermally modified at 230°C in air for 4 h or for 8 h, and then subjected to bending, compression and hardness tests to evaluate the effect of the treatment on these mechanical properties. The biological performance of the modified wood was also determined, according to EN113, and the dimensional stability measured by means of the anti-swelling efficiency. The ...
M M González-Peña
Microwave Treatment of Frozen Wood Packaging Material
2012 - IRG/WP 12-40609
As part of the wood packaging material (WPM) regulation in international trade, the dielectric heating (DH) is soon to be included in ISPM15 (IPPC 2009) as an approved phytosanitary treatment. It has been considered that when using dielectric radiation (i.e. microwaves or radio-frequencies), reaching 60°C or more throughout the entire profile of the wood during at least 60s (i.e. 60°C/60s) ensur...
J-M Henin, A Bauduin, V Leemans, M Leyman, B Jourez, J Hébert
Performance testing of DMDHEU-modified wood in Australia
2013 - IRG/WP 13-30613
Chemical wood modification with dimethyloldihydroxy-ethyleneurea (DMDHEU) or its derivatives has been researched for many years and shown to be applicable to improve certain wood properties to both solid lumber and wood-based composites. Earlier research proved a high biological resistance of DMDHEU-modified wood against biological degradation in laboratory and field tests in Europe. Due to the ve...
H Militz, J Norton
Decay resistance of thermally modified Scots pine after 6 years’ exposure above ground
2013 - IRG/WP 13-40624
In the present study the performance of boards treated by ThermoWood process were studied above ground and the results given are based on a “modified” horizontal double- layer test. The base layer of boards was in direct contact with ground and the conditions were much harder than in the standard method. After six years’ exposure clear differences were found between untreated Scots pine and ...
H Viitanen, S Metsä-Kortelainen, A Nurmi, S Jämsä
Study of UV resistance and natural weathering of coatings on chemically modified wood
2013 - IRG/WP 13-40629
In this study, UV resistance and weathering performance of rubberwood (Hevea brasiliensis) and radiata pine (Pinus radiata) modified with benzoyl chloride and acetic anhydride was studied. Performance of polyurethane based wood coatings on modified wood was also evaluated. Unmodified and chemically modified specimens were exposed to accelerated and natural weathering. Modified and unmodified woo...
K K Pandey, K Srinivas
Characterization of wood modification prepared by in situ polymerization with pre-polymer and the mechanism of modification
2013 - IRG/WP 13-40633
Chemical modification of wood is a potential way to obtain high quality wood. In this study, the fast-growing poplar was impregnated with modifier using a pulse-dipping machine by in situ polymerization. Fungal decay analysis, mechanical properties and dimension stability of the natural and modified woods were investigated. The wood samples were also characterized by X-ray diffraction (XRD) Therma...
Qian Lang, Zeng Bi, Junwen Pu
Combined effects of thermal modification and ACQ-D impregnation on properties of southern yellow pine wood
2013 - IRG/WP 13-40637
In this study, samples of southern yellow pine sapwood were first thermally modified and then treated by the alkaline copper quat-type D (ACQ-D) wood preservative. Two heating temperature (180℃ and 220℃) and two concentrations of ACQ-D solution (0.9% and 1.35%) were used in the experiments. The combined effects of thermal modification and ACQ-D on leaching performance, mechanical prope...
Wang Wang, Yuan Zhu, Jinzhen Cao
Effect of bio-resin from cashew nut shell liquid (CNSL) on decay resistance properties of wood
2013 - IRG/WP 13-40649
This study assesses the decay resistance properties of bio-resin modified wood against decay fungi of the Basidiomycota according to the EN 113 protocol. A bio-resin system was developed by ozonolysis process from cashew nut shell liquid (CNSL), a naturally occurring mixture of phenolics. Small wood blocks from sapwood of Scots pine (Pinus sylvestris), Obeche (Triplochiton scleroxylon) and Gmelina...
M Ashaduzzaman, M D Hale, V Tverezovskiy, G A Ormondroyd
Protein extraction from wood decay fungus Postia placenta
2014 - IRG/WP 14-10827
Wood decay fungi (often distinguished as white rot and brown rot) belonging to the basidiomycetes, are common inhabitants of forest litter, where they play an important role in carbon cycling. Brown rot fungi are perhaps the most important organism involved in the degradation of wood products, and of considerable economic importance. Brown rotted wood loses strength very early because of the rapid...
A Pilgård, P Arnold, K Richter