Natural durability of fifty species of Indian timber in Goa waters against marine wood-borers
1989 - IRG/WP 4150
Results of the investigations on the natural durabilitv of fifty species of Indian timber, based on data collected bv exposing test panels at Betim near Panaji (Goa) continuously for a period of 11 months are presented. The study revealed that none of the timber species tested has any natural resistance at this locality and all the panels were completely destroyed within 11 months. Details on the ...
L N Santhakumaran, S Udaya Bhaskar, J C Jain
Microbial fouling of 10-40% naphthalene in creosote treated and untreated wooden pilings in the marine environment - A progress report
1980 - IRG/WP 455
In June 1978, Document No: IRG/WP/442 entitled 'Microbial Biofouling of 10-40% Naphthalene in Creosote Treated and Untreated Wooden Pilings in the Marine Environment" was released to the IRG members as a report on the early results of a long term (about 5 years) study of whether the naphthalene content of creosote was importart in protecting wood pilings in the marine environment from bor...
R R Colwell, A J Emery
Performance of preservative-treated timber against biodeterioration in Indian waters
1984 - IRG/WP 4106
Results on the investigation on the durability of panels of 32 timber species, pressure-treated with various preservatives and exposed along the Indian coast for varying periods upto a maximum of 15 years, are summarised. Panels of even non-durable timber gave excellent results against biodeterioration after treatment. Their life was comparable to that of treated durable timber. The preservative t...
L N Santhakumaran, J C Jain, M C Tewari
Decay resistance of densified ammonia-plasticized stems of oil palm (Elaeis guineensis)
1991 - IRG/WP 3673
When wafers of oil palm stems (Elaeis guineensis) were plasticized with 28% aqueous ammonia and immediately compressed mechanically, the treated material, gained 73% in basic density (average basic density, 0.695 g/cm³), and was highly resistant to decay by wood rot basidiomycetes. Compared with the control specimens (density, 0.403 g/cm³), resistance to decay of the densified specimens by Corio...
A H H Wong, M P Koh
The evaluation of non-rubber extractives from the guayule plant (Parthenium argentatum Gray) for pesticidal worth
1986 - IRG/WP 4125
The resin obtained from the guayule plant (Parthenium argentatum Gray) of the southwestern United States is a potentially imporant domestic source of natural rubber, however only about 20 percent of the extractives from the plant produce this material. An effort is underway to find marketable uses for the remaining non-rubber extractives, and the Naval Research Laboratory is evaluating this resin ...
J D Bultman, R H Beal, C A Bailey, W W Schloman
NIR spectroscopy for rapid estimation of decay resistance
2004 - IRG/WP 04-20294
In Scandinavia Scots pine (Pinus sylvestris L.) is an important commercial tree species. Its heartwood has traditionally been used in constructions exposed to risk of decay. In a laboratory experiment Scots pine wood specimens sampled from inner heartwood, outer heartwood and sapwood were exposed to the brown rot fungus Poria placenta. In general outer heartwood was more resistant than inner heart...
P O Flæte, E Ystrøm Haartveit
Laboratory evaluation of termite resistance of five lesser-known Malaysian hardwoods used for roof and ceiling construction
2001 - IRG/WP 01-10398
The general laboratory procedure of AWPA E1-97 was used to evaluate the termite resistance of 5 lesser- known species (LKT) of Malaysian hardwoods: Kekatong (Cynometra sp.), Kelat (Eugenia spp.), Mempening (Lithocarpus spp.), Perah (Elateriospermum tapos) and Pauh Kijang (Irvingia malayana) against the subterranean termite Coptotermes curvignathus over 28 days. Kempas (Koompassia malaccensis) and ...
A A H Wong, Kee Suan Cheok, J K Grace
Biological resistance of wood treated with waterbased resins and drying oils in a mini-block test
1998 - IRG/WP 98-40107
In recent years it was found that the resistance of wood against fungal degradation could be increased by impregnation with an etherificated melamine formaldehyde resin. Using this resin as a reference, a waterbased fatty acid modificated alkyd-resin and two drying-oils were assessed for their biological performance in a mini-block laboratory test. Although drying-oils, like linseed-oil, are often...
M Sailer, A O Rapp, R-D Peek
Wharf-borer a threat to stored archaeological timbers
1992 - IRG/WP 92-1560
Increased interest in marine archaeology has occured in recent years. Stored waterlogged archaeological timbers have been shown to be degraded by physical and microbial agents. In recent years a new threat has been highlighted, namely the wharf-borer Nacerdes melanura (L.). The objective of this paper is to outline studies of the morphology, biology, life-history and carbohydrate digestion by this...
A J Pitman, E B G Jones, A M Jones, M Rule
Timber deterioration and its prevention in marine environment
2005 - IRG/WP 05-10559
Wood-borer activity is an established fact in Mumbai harbour that leads to severe deterioration of timber. In order to prevent the deterioration caused by wood borers three resin preservatives containing Zinc borate, Organo-copper polymer (4 wt% Cu) and Organo-Tin polymer Copoly(TBTM-MMA) were used for timber treatment. Test panels were treated using standard method and the...
B S Swami, M Udhayakumar, P Kumar, A B Samui
Decay resistance of Platanus acerifolia wood against White Rot Fungi (Coriolus versicolor)
2002 - IRG/WP 02-10431
Degradation of the lignocellulose complex in wood varies on the microorganism causing decay and chemical composition of wood. The weight loss of Platanus acerifolia wood after decay by white rot fungus (Coriolus versicolor) for period 16 weeks were evaluated according to European standard EN 113 and beech wood as a control. The samples were collected in October 2000 from Nantes, France. The aim of...
M Irmouli, O Duchelier, N Ayadi, B Charrier
Marine trials with water-borne salts and organotin compound
1986 - IRG/WP 4128
Pinus sylvestris blocks treated with water-borne salts (CCA, CCB, CCF) and organotin compounds (TBTO, TBTCl) were submerged in the sea at Follonica station. The results obtained after 12 years of immersion are presented. The samples treated with CCA, CCB and CCF at the lowest concentration (2%) were destroyed after 7-9 years and the samples treated with CCB and CCF at the highest concentrations (4...
A Gambetta, E Orlandi
IRG/COIPM INTERNATIONAL MARINE TEST - to determine the effect of timber substrate on the effectiveness of water-borne salt preservatives in sea-water. Progress Report 18. Report of seventh inspection (72 months) in Australia
1984 - IRG/WP 4108
This report includes the results for the 72 month inspection of the IRG/COIPM International Marine Test installed in Sydney Harbour. Although, overall, attack by teredinid and limnorid borers have been most commonly encountered in test specimens at this site, slight attack, mainly by sphaeromatids, has recently been initiated on some hitherto unattacked treated Alstonia scholaris and Pinus sylvest...
L J Cookson, J E Barnacle
Is laboratory testing of decay resistance questionable as a single criterion for natural durability?
1996 - IRG/WP 96-20096
In a laboratory test set up over 20 hardwood species were evaluated according to the European Standard EN 350-1 including Basidiomycete and soft rot testing. Half of the species used were of a known natural durability. The Basidiomycete testing was carried out using Coriolus versicolor, Gloeophyllum trabeum and Coniophora puteana in a malt agar test similar to EN 113. From this test it was not pos...
J Van Acker, M Stevens, T Van Cauwenberghe, T Seynaeve
Surface accumulation of copper on CCA-impregnated Pinus patula stakes during marine preservative trials in the southern hemisphere
1992 - IRG/WP 92-4181
Pinus patula stakes treated with CCA to target retentions of 30 kg/m³ salts were exposed to sea water in marine and estuarine ecosystems off the coast of Southern Africa for two years. Samples were then analysed for copper and arsenic. Analysis of samples from the marine ecosystem showed (IRG/WP/4167) that arsenic was longitudinally and transversely leached from the wood, whereas the copper was r...
G D Shelver, C D McQuaid, M Tarin, A A W Baecker
Screening techniques for potential wood preservative chemicals. Proceedings of a special seminar held in association with the 10th Annual Meeting of the IRG, Peebles 1978. Report No 136, 1979
1980 - IRG/WP 2138
This paper continues following issues:
I. SCREENING INSECTICIDES
1) R W Berry (BRE/PRL, UK): Screen testing of insecticides for use in remedial wood preservatives.
2) D J Cross (FRI, New Zealand): Rapid screening of contact insecticides for use on forest products.
3) C R Coggins; A Forsyth; A E Glaser (Rentokil, UK): Experience in the use of indicative screening techniques for termiticides.
...
Anonymous
Proposing innovative technologies in the control of dry-wood insects
1985 - IRG/WP 1262
This paper discusses the social-economic problems involved in the biological evaluation of dry-wood insects with particular reference to Nigeria. It also discusses prospects of applying non-conventional methods of control against such insects, integrating these with the conventional preservatives as a control strategy. This discussion follows attempts made to identify the major dry-wood insects in...
M O Akanbi
New boron-based biocides for the protection of wood
2002 - IRG/WP 02-30283
Boric acid and other simple inorganic oxides of boron are amongst the oldest wood preservatives currently in use. Their relatively low toxicity and broad-spectrum activity are just some of their desirable characteristics. The primary disadvantage associated with conventional boron-based preservatives is their lack of permanence in exposed applications. A collaborative project between CSIRO and the...
D G Humphrey, P J Duggan, E M Tyndall, J M Carr, L J Cookson
The relationship between the electrical resistance and fixation of water-borne CCA salts and pressure-treated wood
1991 - IRG/WP 3657
Two investigations at 22°C and 30°C have been carried out. The electrical resistance in the treated wood and chemical analyses of the remaining amount of unfixed copper, chromium and arsenic were investigated. Samples impregnated with water were used as references. To hold the samples moist during the investigation, each sample was wrapped in a polyethylene plastic foil immediately after impregn...
F G Evans, B Nossen
Sphaeroma terebrans Bate: A note on distribution and preservative tolerance in Florida coastal waters
1987 - IRG/WP 4135
Treated test panels were installed in January 1984 in a Florida estuary where Sphaeroma terebrans had severely damaged pilings treated with copper chromate arsenate (CCA). Test treatments were CCA at three retentions, coal-tar creosote at three retentions, creosote with chlorpyrifos, dual treatment with CCA and creosote, and three types of chemical modification of the wood test panels. We describe...
B R Johnson, E D Estevez, S A Rice
The Protection of Wood with Oxy-aluminium Compounds
2002 - IRG/WP 02-30286
Wood inorganic composites (WICs) containing aluminium compounds were developed and tested in relation to some essential requirements of preservative treated wood. Four different oxy-aluminium treatments were developed and identified according to the final insoluble compounds formed (sodium aluminate, aluminium hydroxide, magnesium aluminate and aluminium borate) in wood. Vacuum impregnation or dou...
F A Ximenes, P D Evans
The comparative resistance to fungi of the wood munika (Pinus heldreichii Christ.), fir (Abies alba Mill.) and spruce (Picea excelsa Poir.) compared with Pinus sylvestris L. and some physical and mechanical characteristics of munika
1981 - IRG/WP 1129
The munika (Pinus heldreichii Christ.) is situated primarily in the Balkans, and partially in the south of the Apenine peninsula. As an endemic species, with a very little annual increment, it has not been used enough as a timber for mechanical conversion up till now, although the oldest trees can grow to 27 m in height, with a diameter at breast height of about 60 cm. According to data of many Ba...
M Petrovic, M Miric
Soil-bed decay resistance evaluation of strandboards treated with preservative at different points of the manufacture process after 18 months exposure
2002 - IRG/WP 02-40230
Strandboards were treated with a copper-boron water-based preservative at different points of manufacture process namely, green strand diffusion, vacuum, spray application in the resin blender and post manufacture heat and cold quench.
Preservative was applied to achieve five different retentions (0, 1.5, 3, 6, 12 kg m-3). The modulus of rupture and modulus of elasticity were assessed before expo...
G J Goroyias, M D C Hale
Performance of Paraserianthus falcataria treated with ACZA, ACQ, CC or CCA and exposed in Krishnapatnam harbour, India
2005 - IRG/WP 05-30382
Paraserianthus falcataria (=Albizia falcataria) treated to two retentions with ammoniacal copper zinc arsenate (ACZA), ammoniacal copper quaternary (ACQ), ammoniacal copper citrate (CC) and chromated copper arsenate (CCA) was assessed over 34 months in a tropical marine waters at Krishnapatnam harbour on the east coast of India. ACZA treatment showed comparatively better resistance than CCA, ACQ a...
B Tarakanadha, K S Rao, J J Morrell
Relative tolerance of CCA by larvae and adults of the common shipworm, Bankia gouldi
1992 - IRG/WP 92-4174
Southern pine sapwood "2 x 4´s" were created by bolting together four panels 13 mm thick by 89 mm wide by 457 mm long. The two outer laminates were untreated and the two inner laminates were each treated to different CCA retentions, ranging from 8.0 to 43.2 kg/m³. Test specimens were exposed from May to October in a tributary of the Chesapeake Bay. Larvae were unable to settle on and burrow into...
B R Johnson