Environmental Impacts of CCA-Treated Wood: A Summary from Seven Years of Study Focusing on the U.S. Florida Environment
2003 - IRG/WP 03-50205
Wood treated with chromated copper arsenate (CCA) was identified in 1995 as the cause of elevated arsenic concentrations within wood fuel used for cogeneration within Florida. Since this time a research team from the University of Miami and University of Florida has evaluated the environmental impacts of CCA-treated wood within the State. Research has focused on two distinct areas: in-service l...
H M Solo-Gabriele, T G Townsend, J D Schert
The influence of UV and IR radiation on leaching of copper and chromium from preservative-treated pine and spruce
1992 - IRG/WP 92-3687
The influence of artifical UV- and IR-radiation on the leaching of copper and chromium components of a CCB-preservative from freshly treated pine and spruce was evaluated. On small pinewood samples it could be shown, that the leaching of copper and chromium can considerabely be reduced by UV-radiation. A Philips HPA lamp type reduced the leaching most effective. IR-radiation lead to higher leachin...
H Militz
Fungal degradation of wood treated with metal-based preservatives. Part 1: Fungal tolerance
1996 - IRG/WP 96-10163
In recent years, concerns have arisen about the leaching of heavy metals from wood treated with chromated copper arsenate (CCA), particularly because of the large amount of CCA treated wood that will be discarded in the coming years. The long term objectives of this work are to determine the fate of copper, chromium and arsenic with the aging and potential decay of CCA-treated wood, and to develop...
B Illman, T L Highley
Use of the enzyme-linked immunoassay (ELISA) and immunocytochemistry to detect soft rot in preservative treated and untreated wood
1990 - IRG/WP 2347
A polyclonal antibody was raised against mycelial extracts from the soft rot fungus Phialophora mutabilis. In ELISA assays, the antibody showed strong reactions with its own antigen and strong to moderate cross reactions with 6 other Phialophora soft rot species. With the exception of Ceratocystis albida, the antibody gave only weak or negative reactions with 11 other mold, blue stain and rot fung...
G F Daniel, T Nilsson
Effects of hard water, sea water and humic acid on the release of CCA components from treated wood
2005 - IRG/WP 05-50228
Leaching medium is an important factor affecting release of preservative components from treated wood because physical and chemical characteristics of medium increase or decrease the solubility of fixed preservative components. This study evaluated the leaching properties of copper, chromium and arsenic elements from chromated copper arsenate (CCA)-treated wood specimens subjected to laboratory le...
S N Kartal, W J Hwang, Y Imamura
Acoustic technique for assessing decay in preservative treated wood
1998 - IRG/WP 98-20138
This study investigated the suitability of vibration techniques to assess the performance of wood preservatives in ground contact. Small stakes (10 x 5 x 100 mm3) of treated and untreated Scots pine sapwood were exposed to decay in lab-scale terrestrial ecosystems. Tests were conducted using three different soils including a garden compost soil, and soils obtained from a test field and a conifer f...
L Machek, M-L Edlund, R Sierra-Alvarez, H Millitz
Correlation between modulus of elasticity, mass losses and FTIR spectra of copper treated decayed wood
2006 - IRG/WP 06-10580
The composition of copper-based preservatives will change from copper-chromium to copper-ethanolamine, due to environmental demands. The most important drawback of copper-impregnated wood is the presence of tolerant fungal organisms that have developed an ability to degrade such preserved wood. In order to elucidate these processes, specimens (0.5×1.0×15 cm) made of Norway spruce (Picea abies) w...
M Humar, B Bucar, F Pohleven
Water analysis in chemicals, wood or chemically treated wood using a new analytical method for selective water detection
2006 - IRG/WP 03-30391
Water or moisture content analysis can be a challenging task in many applications. However, knowing accurately the type of water which can be found in a given sample or product can provide important information about a chemical compound used for wood treatment and especially about the treated wood sample.
Moisture content in wood plays an important role in fungal growth and it needs to be extensi...
R Craciun, D Taylor
Preliminary screening of a boron based wood preservative for biological efficacy (fungicidal) in treated timber
2006 - IRG/WP 06-30396
The resistance of Pinus radiata D.Don sapwood blocks, treated with a boron based preservative, to attack by five wood destroying fungi (Fomitopsis lilacino-gilva, Coniophora olivacea, Gloeophyllum abietinum (boron resistant), Serpula lacrymans and Perenniporia tephropora) was investigated. A phenyl pyrazole termiticide (fipronil) was also incorporated into the formulation to examine if its presen...
S R Przewloka, J A Hann, P Vinden
Paintability and gluability of wood treated with arsenic-free and chromium free preservative treatments
2006 - IRG/WP 06-40342
The objective of this project was to study, in comparison with traditional CCA treatment, the paintability and gluability of wood treated with arsenic-free and chromium-free preservative treatments.
Four formulations, all certified CTB P+, were selected in accordance with their representativeness of the preservative product market: one CCA reference formulation and three chromium and arsenic free...
L Podgorski, G Legrand
The Effect of Wick Action upon Moisture Distribution in Ellagate Treated Pinus radiata Wood
2006 - IRG/WP 06-40328
Sapwood stakes of Pinus radiata D. Don were treated with water-soluble tetraguanidinium, tetracholine and tetrakis-benzyltrimethylammonium ellagates. The effect of these treatments upon moisture distribution was investigated by wick action. Given that chemical reactions within the wood substrate between nutrients and treatment solutions may alter the properties of the wood with regard to moistur...
S R Przewloka, B J Shearer, J A Hann
Furfurylated wood - An alternative to Preservative-treated wood
2006 - IRG/WP 06-40349
Chemically modified wood is currently being marketed as a non-toxic alternative to traditional preservative treated wood (wood impregnated with biocides). Over the last decade the authors have developed modernised processes for wood modified by furfurylation. These new systems do not add metals or halogens to the product, which is important for an environmentally acceptable product. This presentat...
S Lande, M H Schneider, M Westin, J Phillips
Wood decay fungi from New Zealand ‘leaky’ buildings: PCR identification and laboratory decay tests of wood preservative-treated Pinus radiata (Part 1)
2007 - IRG/WP 07-10620
Fungi colonising Pinus radiata D. Don framing timber of ‘leaky’ New Zealand buildings were isolated to produce pure cultures. Mycelia from these cultures on agar media were collected to extract DNA. To identify the fungi to the species level, polymerase chain reaction (PCR) with primer pairs ITS1-F and ITS4 were performed followed by sequencing of the internal transcribed spacer (ITS) region. ...
D Stahlhut, R L Farrell, R Wakeling, M Hedley
Use of Moisture Meters with Treated Wood
2007 - IRG/WP 07-40382
Drying wood treated with waterborne preservatives after treatment to near outdoor EMC conditions improves its physical performance characteristics. This is primarily due to the reduced checking, splitting and warping which can occur when wet wood, particularly if restrained from shrinking by being nailed or otherwise fastened, shrinks in use. Monitoring of the drying process, rate, and end point...
W B Smith, Hwan Myeong Yeo, C Stark, B Morey, C Tascioglu, P Schneider, D Herdman, M Freeman
Influence of ethanolamine on lignin depolymerization and copper leaching from treated Norway spruce and beech wood
2007 - IRG/WP 07-30423
Copper-ethanolamine based wood preservatives are replacing several classical copper-chromium based solutions, due to foreseen ban of chromium. Fixation of copper-ethanolamine based wood preservatives is not as good as fixation of copper-chromium ones. The main object of this manuscript was to prove, that ethanolamine is the prime reason for insufficient fixation of copper-ethanolamine formulations...
M Humar, B Bucar, M Zupancic, D Žlindra, F Pohleven
Tropical In-Ground Durability of CCB-treated Keruing and other Structural Sarawak Timbers after 8 – 10 Years Exposure
2007 - IRG/WP 07-30439
The heartwood of 12 mainly low-durability native timber species of Sarawak [4 Dipterocarpus (Keruing) species, Anisoptera grossivenia (Mersawa kunyit), Canarium apertum (Seladah), Dacryodes incurvata (Seladah laut), Dryobalanops oblongifolia (Kapur kelansau), Mesua macrantha (Mergasing), Podocarpus micropedunculatus (Kayu cina), Shorea compressa (Engkabang langgai), and Pterospermum javanicum (Ba...
A H H Wong, Ling Wang Choon
Effects of sodium hypochlorite on compression strength and copper retention of spruce wood treated with copper azole and alkaline copper quat
2007 - IRG/WP 07-40362
This work investigates the effects of sodium hypochlorite on compression strength values and copper retention ratios of refractory spruce wood (Picea oriental L.) treated with the waterborne preservative Copper Azole, (CBA-A, Tanalith-E 3492) and alkaline copper quat (ACQ-2200). Before the copper azole and alkaline copper quat treatment, the samples were immersed in 500 ml of sodium hypochlorite s...
S Yildiz, E Dizman, A Temiz, Ü C Yildiz
Effect of barriers on moisture content of treated and non-treated utility poles
2007 - IRG/WP 07-40369
The potential for non-biocidal barriers to slow moisture sorption was investigated using butt treated western redcedar poles immersed in either water or moist soil over a 2 year period. Moisture sorption was initially slowed by the barriers, but openings at the bottoms of the barriers eventually allowed moisture to migrate upward. Moisture levels in wrapped poles eventually reached those found in...
C S Love, J J Morrell
The effect of additives on copper losses from alkaline copper treated wood
2007 - IRG/WP 07-50246
The replacement of chromated copper arsenate (CCA) by alkaline copper compounds has heightened awareness of the potential impact of copper losses on aquatic organisms. While there remains a healthy debate concerning the actual risk of copper leaching from wood preservatives into aquatic ecosystems, it is clear that reducing these losses will be necessary to avoid continued regulatory actions aga...
J Mitsuhashi, J J Morrell, L Jin, A F Preston
Evaluating the Process of ACQ-Treated Woods with TGAand CEM Analysis
2007 - IRG/WP 07-20374
To provide an understanding of the fundamental thermal behaviour and the disposal-end products of ACQ-treated woods, this study is comprised of two categories of examination. The first is related to the use of TGA under different thermal decomposition conditions (nitrogen or air, and 5 or 40 oC/min), and the use of EDX to examine certain residual elements of the char. The second applies the CEM ...
Han Chien Lin, Tsang-Chyi Shiah, Jung Ting Tsai
Durability of some alternatives to preservative-treated wood. Progress report 2: Results from field tests after 5 years’exposure
2007 - IRG/WP 07-30442
A number of alternatives to preservative-treated wood have been tested according to EN 252 (stake test) and a specially designed ground-proximity field test, the latter in Sweden as well as in Hawaii, USA. Seven untreated wood species and four alternative wood treatments labelled as environmentally friendly (acetylation, linseed oil, heat treatment, vinyl polymer) were included in the study. Four ...
M-L Edlund, J Jermer
Primary Study on Compressed Preservative-treated Wood (CPW) for Outdoor Applications
2008 - IRG/WP 08-40412
In this study, the compressed wood samples pre-treated with hot water bath or water spraying were immersed in the ammoniacal copper quat –type D (ACQ-D) preservative solution to get compressed preservative-treated wood (CPW). The liquid absorption and the recovery rate of compression deformation of the compressed wood was determined, as well as the surface hardness, the distribution of density a...
Jinzhen Cao, Jia Mao
Formation and Structure of Metal Azole Complexes
2008 - IRG/WP 08-30469
Divalent copper and zinc complexes with metal:azole ratio 1:2 were readily formed at room temperature with the fungicides tebuconazole and propiconazole. The structure of copper and zinc tebuconazole acetate and zinc cis-propiconazole chloride were examined by X-ray crystallography. In copper tebuconazole acetate, the copper atom lies on a crystallographic inversion centre and is coordinated to tw...
P D Evans, K J Schmalzl, C M Forsyth, G D Fallon, S Schmid, B Bendixen, S Heimdal
Effects of acetic acid and nitric acid pre-treatment on copper content of spruce wood treated with CBA-A and CCA
2008 - IRG/WP 08-40406
This work investigates the effects of nitric acid and acetic acid on compression strength values and copper retention contents of refractory spruce wood (Picea oriental L.) treated with the waterborne preservative Copper azole, (CBA-A, Tanalith-E 3492) and copper / chrom / arsenic (CCA). Before the CBA-A and CCA treatment, the samples were immersed in 500 ml of nitric and acetic acid solutions for...
S Yildiz, E Dizman, Ü C Yildiz
Bending Properties of Southern Pine Treated with Micronized Preservative Systems
2008 - IRG/WP 08-40414
This study indicates that treatment of southern pine with micronized copper systems have no
deleterious effect on the residual strength property values. No statistical differences between wood treated with micronized systems and water-treated controls were noted when means were compared using either Tukey’s test or S-N-K mean comparison tests. Using the more discriminating Least Squares anal...
H M Barnes, G B Lindsey, J Hill, M Pompeo, R Hodge