Evidence for actinomycete degradation of wood cell walls
1990 - IRG/WP 1444
Several unique patterns of degradation occurring in wood cell walls have been observed in wooden stakes inserted in unsterile soil in the laboratory. Some of the patterns have also been observed in coniferous wood taken from forest floors. All the observed attack types occur within wood cell walls, mainly within the S2 layer. Attack is characterised by channels of varying diameter or small fusifor...
T Nilsson, G F Daniel, S L Bardage
The influence of staining fungi on the decay resistance of wood treated with alkylammonium compounds
1984 - IRG/WP 3308
Although found to be very effective in laboratory tests, alkylammonium compounds (AAC's) have failed to perform as well in field stake tests. Examination of leachability showed that this was not the cause. The present study investigated the possibility that staining fungi, (which have been observed to rapidly infect the field stakes), degrade the AAC wood preservative. Soil-blocks were tr...
J N R Ruddick
Wood and filter paper degradation, phenol oxidase and one-electron oxidation activities by the white rot fungus Ceriporiopsis subvermispora
2003 - IRG/WP 03-10486
The activities of one-electron oxidation and phenol oxidase during incubation of cultures of the white-rot basidiomycete Ceriporiopsis subvermispora containing either glucose or wood were periodically measured. Further, the degradation activities against wood and filter paper were examined during the course of cultivation. Weight losses of Japanese beech wood and Japanese cedar wood after 12 wee...
H Tanaka, S Itakura, A Enoki
Chemical and biological investigations of double-vacuum treated windows after 5 years in service
1983 - IRG/WP 3219
In 1980 The Swedish Wood Preservation Institute initiated an investigation to study the degradation of TBTO and possible fungal attack in double-vacuum treated window joinery in service during 5 years. A hospital in Gothenburg was chosen that was built during 1969 to 1976. Both untreated and double-vacuum treated windows of Pinus sylvestris were used. A brown alkyl oil type paint (Nordsjö system ...
J Jermer, M-L Edlund, B Henningsson, W Hintze, S V Ohlsson
Immunolocalization of extracellular metabolites from Poria placenta
1988 - IRG/WP 1361
Polyclonal antisera produced to Poria placenta extracellular metabolites was used in immuno-fluoresence microscopy and immuno-gold TEM studies. In the fluorescence work, labelling of Poria placenta hyphae in wet fixed wood material was observed but not in infected wood which was oven dried prior to sectioning and immunolabelling. TEM studies provided better resolution, with gold labelling detected...
B Goodell, G F Daniel, J Jellison, T Nilsson
Degradation of polycyclic aromatic hydrocarbons by laccase
1998 - IRG/WP 98-10267
The degradation of polycyclic aromatic hydrocarbons (PAH) by laccase was investigated. Laccase catalyzed oxidation of phenanthrene, solubilized in the surfactant Tween 20, exhibited an absolute requirement for the mediator compound 1-hydroxybenzotriazole. When Tween 80 was used as the solubilizing agent, the oxidation rates were more than six times higher as compared to Tween 20. Using the thiobar...
S Böhmer, E Srebotnik, K Messner
Field study: Wood degradation pattern in buildings and utility poles in tropical climates of Nigeria
1992 - IRG/WP 92-1521
The paper is the result of five years field study of wood degradation patterns in three ecological forest zones (Guinea Savannah, Tropical rain forest and mangrove forest zones, respectively). It involved 800 residential buildings and 700 electric overhead transmission poles. The methodology used was a modified Eslyn (6) test. A high rate of Ascomycetes and Basidiomycetes attack especially on the ...
E O Onuorah
Fungal detoxification of organotin biocides
1985 - IRG/WP 1258
The ability of a range of wood decaying fungi to inactivate bis(tri-n-butyltin) oxide (TnBTO) in the extracellular growth medium, in stationary liquid culture was determined. A distinction between the ability to tolerate the fungicide and to inactivate it was made: the white-rot organism Coriolus versicolor being the most efficient inactivator. In an attempt to determine the extracellular agents r...
P S Belford, D J Dickinson
Genetic Engineering in tree breeding
1998 - IRG/WP 98-10294
The genetic improvement of forest trees by classical breeding is a slow process in comparison with that of annual crops. Tree breeding however is of great importance and has led to trees with better growth characteristics and better disease resistance. An important wood characteristic which has been neglected in breeding programs is wood durability. The durability of the wood will determine for wh...
J Van Doorsselaere, H Beeckman, M Van Montagu, W Boerjan
Comments on soft rot attack in timbers treated with CCA preservatives: A document for discussion
1982 - IRG/WP 1167
This paper is not based on any particular results but rather on several observations of soft-rot during many years of studies, and on a review of the existing literature. The short time available has unfortunately not permitted a detailed review of the literature. Data and knowledge of important facts are lacking for several aspects of soft-rot attack and for reactions occurring in the wood as a r...
T Nilsson
The relationship between preservative type and surface degrade in Pinus radiata
1980 - IRG/WP 3158
Samples of Pinus radiata D. Don were impregnated with one of two preservative types, a copper chrome arsenic salt and a light organic solvent preservative. The panels were exposed to the weather for 4-5 years at a site near Sydney, Australia. Macroscopic and microscopic examinations showed different rates and patterns of weathering between the samples treated with each preservative and an untreate...
R S Johnstone, R K Bamber
Surface characteristics of wood treated with various AAC, ACQ and CCA formulations after weathering
1991 - IRG/WP 2369
Wood samples treated with various alkylammonium compounds (AACs) as well as ammoniacal copper quat (ACQ) and chromated copper arsenate (CCA) have been studied in accelerated weathering experiments. Microscopic examination of the surfaces of these samples after exposure in a weatherometer revealed several different changes. Samples treated with didecyldimethyl ammonium chloride (DDAC) show consider...
L Jin, K J Archer, A F Preston
The involvement of extracellular substances for the generation of hydroxyl radical during wood degradation by white-rot fungi
1997 - IRG/WP 97-10218
The activities of one-electron oxidation, hydroxyl radical generation, and phenol oxidase during the incubation of cultures of four white-rot fungi containing either glucose or wood were periodically measured. Further, their degradation activities against wood were examined during the course of cultivation. The generation of hydroxyl radical was correlated to the activity of wood degradation and i...
H Tanaka, S Itakura, A Enoki
Persistence and residual activity of organophosphorus termiticides in soil and prevention against the degradation of chlorpyrifos
1991 - IRG/WP 1518
The persistence and the residual activity of four comercial organophosphorous termiticides, Chlorpyrifos, Fenitrothion, Tetrachlorvinphos, Pyridaphenthion, in soil were studied under laboratory conditions. The persistence and the residual activity of four organophosphorous termiticides in two types of soil decreased with the lapse of time. These termiticides were mostly degraded by microorganisms ...
T Iijima, M Tanaka, M Higaki
Biological degradation resistance of wood acetylated with thioacetic acid
1983 - IRG/WP 3223
Chemically, modification of wood is being considered as an alternative to conventional preservation by toxic chemicals. Acetylated wood has been reported to be quite resistant to most biodegrading organisms at weight percent gains (WPG) around 15-19. The conventional acetylation techniques with acethic anhyrdride result in generation of acetic acid. However, acetylation with thioacetic acid overco...
S Kumar, S C Agarwal
Chemical and biological investigations of double-vacuum treated windows after 7½ years in service
1985 - IRG/WP 3339
Earlier investigations of double-vacuum treated windows after five years in service have shown that tributyltin oxide (TBTO) degrades to di- and monobutyltin compounds and that the resistance of the wood against decay decreases. An investigation 2.5 years later of the same windows shows that the degradation of TBTO proceeds fast. After 7.5 years in service only 15-35% of the remaining organotin co...
M-L Edlund, J Jermer, B Henningsson, W Hintze
FTIR characterization of copper ethanolamine - wood interaction
1999 - IRG/WP 99-20154
The interaction of copper ethanolamine (Cu-EA) and wood components was studied by using Fourier transform infrared spectroscopy (FTIR). In Cu-EA treated wood, significant reduction was noticed on the band attributed to carbonyl vibration from carboxylic groups at 1735±5 cm-1 and an increase in band intensity was obtained from carbonyl in carboxylate at 1595±5 cm-1. The same observation was made ...
Jun Zhang, D P Kamdem
Screening of fungal strains for wood extractive degradation
1998 - IRG/WP 98-10254
Fungal strains were screened for their ability to degrade apolar extractives in wood from scots pine. The degradation of total wood extractives by 91 different strains was monitored in stationary batch assays incubated for 6 weeks. The results obtained show that the ability of wood-inhabiting fungi to utilize wood extractives varied greatly, even for different isolates of the same species. Fungal ...
J Dorado, M J Martinez-Inigo, T A van Beek, F W Claassen, J B P A Wijnberg, R Sierra-Alvarez
The examination of preservative-treated radiata pine using electron spin resonance spectroscopy
1987 - IRG/WP 3423
Electron spin resonance spectroscopy (ESR) may be used to characterise the molecular environment of chemical species containing unpaired electrons. These species include free radicals, bi-radicals, point defects in solids, localised crystal imperfections and many transition metal ions. ESR has previously been applied to the examination of wood weathering or wood pyrolysis and now FRI and Massey Un...
D V Plackett, E W Ainscough, A M Brodie
Microscopic FT-IR depth profiling study of photo-induced degradation in wood
2001 - IRG/WP 01-20229
FT-IR microspectroscopy was used to monitor the changes in the chemical composition at various depths from the photo-irradiated surface of sugi (Cryptomeria japonica D. Don) sapwood. The radially cut wood face was exposed to artificial solar radiation from a xenon light source at 375 Wm-2 (in a 300 - 700 nm spectral range) for up to 600 h. The IR depth profiling spectra showed that the artificial ...
Y Kataoka, M Kiguchi.
Surface protection of wood with titanium, zirconium and manganese compounds
2005 - IRG/WP 05-30376
Thin radiata pine veneers were treated with a range of titanium, zirconium and manganese compounds and exposed to natural weathering. Veneer weight and tensile strength losses were used to assess the protective efficacy of the compounds. The oxidative manganese compounds potassium permanganate and manganic acetate restricted both weight and tensile strength loss of treated wood veneers during weat...
K J Schmalzl, P D Evans
Bacterial degradation of wood cell wall: A review of degradation patterns
1990 - IRG/WP 1460
Information from bacterial degradation studies of 60's and 70's was reviewed by Nilsson in 1982. The application of electron microscopy to this area in recent years has provided much useful information and has eliminated earlier scepticism among workers about the ability of bacteria to degrade lignified wood cell walls. Studies using transmission electron microscopy together with...
A P Singh, J A Butcher
Micromorphological and chemical changes of archaeological woods from wrecked ship's timbers
1987 - IRG/WP 4136
Micromorphological and chemical alterations of sea-waterlogged woods obtained from the ship-wrecked materials which had been submerged in Yellow Sea for over 700 years were investigated. The woods were deteriorated in varying degrees by marine organisms depending on species and parts of the woods. Under the light and scanning electron microscope the morphological characteristics of deteriorated wo...
Y S Kim
The degradation of wood surfaces by dilute acids
1985 - IRG/WP 3326
Thin radial/longitudinal sections(~100 µ) of Corsican Pine (Pinus nigra) and Lime (Tilia vulgaris), were exposed to Sulphuric, Sulphurous, nitric, acetic, and formic acid at 40°C in the pH range 2-6. After about 3 months exposure to Sulphuric, nitric, acetic and formic acid at pH 2.0 Pine lost some 20-25% of its tensile strength. Losses in tensile strength due to sulphurous acid were greater bei...
P D Evans, W B Banks
FTIR studies on the weathering of didecyldimethylammonium compound (DDAC) treated wood
1993 - IRG/WP 93-30013
Wood treated with alkylammonium compounds (AACs), such as DDAC, weathered more rapidly than untreated wood. In order to examine the influence of DDAC treatment of wood on its weathering, treated and untreated microtomed sections of southern yellow pine earlywood of various thicknesses, were prepared and weathered for approximately one month. The changes in these samples were monitored using FTIR. ...
R Liu, J N R Ruddick