Soft Rot Determines Service Life of L-joints with Low Borate Loading
2008 - IRG/WP 08-30470
As part of a research program on the potential use of borates by the Canadian wood products industry, Forintek set up an L-joint test of untreated and borate-diffusion treated hem-fir (western
hemlock and amabilis fir) in 1990. The treated material had a low initial retention of only 0.2% boric acid equivalent and analysis after 5 years revealed no detectable borate close to the tenon. Nev...
P I Morris, J Wang, J K Ingram
Penetration Depth of Borates in Historic Wooden Structures in Virginia City Montana
2008 - IRG/WP 08-30475
Virginia City, Montana contains some of the best preserved examples of gold boom construction in the United States. Unfortunately, even the dry climate and fortuitous lack of fire have not prevented decay from claiming parts of the historic fabric. This project aims to determine if borates should be integrated into the preservation plan of the Montana Heritage Commission. Solutions of disodium ...
A A Turner
Finite Element Modelling of the Checking of Wood Exposed to Accelerated Weathering
2010 - IRG/WP 10-20459
The surface checking that develops when wood is exposed to the weather reduces the visual appeal of treated wood products and can reduce the effectiveness of preservative treatments. There is strong interest in developing solutions to this problem and also a growing realization that such solutions may evolve from a deeper understanding of the mechanisms responsible for surface checking. In this pa...
S G Ribarits, P D Evans
Influence addition of boron compounds to adhesives on the bonding quality and fungicidal properties of glued wood
2010 - IRG/WP 10-40497
Wood is one of the most important construction materials. However, users of wood face two issues: limited dimensions and insufficient durability. These issues have been overcome with the development of bonding and wood preservation. The preservation of glued wood is elucidated in this paper. Through the addition of boric acid to adhesives, we tried to improve the fungicidal properties of glued woo...
M Humar, B Lesar, A Ugovsek, M Kariz, P Kralj, M Šernek
Riverbed Construction Technology using Thinned Timbers for Carbon Dioxide Sink in Korea
2010 - IRG/WP 10-50271
The Climatic Change Convention is a big burden in limiting the energy usage like the blood of economy. The certification standard about the carbon storage of timbers after harvesting them is expected to be an important role in setting the goal for future reduction of the green house gas(CO2). The extension of a timber's life span through its preservation is one of technologies for carbon sink...
Dong-heub Lee, Won-Joung Hwang
Ambient-temperature borate dip-diffusion treatment of green railroad crossties
2011 - IRG/WP 11-40556
In the USA, borates are increasingly being applied prior to air seasoning and creosote treatment of railroad ties (railway sleepers). Borates are typically applied to green ties by vacuum pressure application at 1 to 10% disodium octaborate tetrahydrate (DOT) concentration or by traditional dip-diffusion treatments at elevated temperatures. Higher temperatures are used to maintain the 30 to 50% so...
Jae-Woo Kim, A M Taylor, C Köse
Performance of boron diffused wood products used indoors for 144 months in Bangladesh
2012 - IRG/WP 12-30581
In this service performance study of boron diffused hardwoods, boron in the form of boric acid (H3BO3) was applied separately through paste and through wet cloth. The born diffused woods were kept indoors for 144-months in Bangladesh to ascertain the performance of treated wood against wood destroying insects. The new easy application processes of cost effectual boric acid have been found effectiv...
A K Lahiry, T Lahiry
Mold Control for Treated Lumber in Block-Stack Storage Conditions
2012 - IRG/WP 12-30588
The mold development and control for freshly treated and block-stacked wood have been evaluated using a green house mold testing method. The results for the mold resistance of several commonly used water boron preservative treatment systems, such as ACQ, Copper Azole, and borates with and without inclusion of mold inhibitors are presented. The data suggest that the different preservative treatme...
L Jin, P Walcheski, A Preston
Migration of copper from copper naphthenate treated Douglas-fir poles during storage
2014 - IRG/WP 14-50302
Preservative migration from treated wood products has raised concerns among regulators, especially when the biocides move into surface waters. In most cases, chemical levels are well below the acceptable minimum level, but can become a concern if large quantities of treated wood are stored in one location. One such case would be a location where utility poles are stored for use in emergency repai...
C S Love, C M Freitag, J J Morrell
Some comments on durability testing of WPC according to EN 15534-1
2015 - IRG/WP 15-40695
The standard EN 15534-1 (2014) gives advice for broad characterization of WPC materials and products. It contains instructions for test procedures concerning different properties e.g. mechanical properties, thermal properties, as well as durability.
In this paper some WPC materials from the market were tested for their resistance against brown rot. Furthermore, the water uptake and bending prope...
S Bollmus, A Gellerich, H Militz
Steam accelerated borate diffusion: Optimizing dry tie treatment
2015 - IRG/WP 15-40713
A small laboratory study was carried out which demonstrated that dry wood dip treated in a high concentration borate solution could not be subsequently treated properly with oil borne copper naphthenate unless it was subsequently steam treated to accelerate borate penetration into the wood and re-dry the wood beforehand. A larger study with commercial sized cross ties (railway sleepers) was carri...
J-W Kim, J D Lloyd
Effect of the Storage Time of Logs in Anti-Stain Treatment Effectiveness
2016 - IRG/WP 16-30683
Storage of green lumber, for 7 months, operationally treated with anti-stain products, depending on the storage time of the logs (10, 20 and 30 days) post harvesting allows to affirm that with increasing storage time of the logs, occurs a progressive increase in intensity, severity and types of fungi present in the logs. It is further noted, a significant increase in the percentage of sawn lumber ...
M A Peredo, C Barria
Fabrication and characterization of MicroPCMs filled wood-plastic composites: Effects of polyethylene glycol on melamine–formaldehyde shell material
2016 - IRG/WP 16-40728
Microencapsulated phase change materials (MicroPCMs) containing dodecanol were fabricated using melamine-formaldehyde (MF) or polyethylene glycol 200 modified melamine-formaldehyde (PMF) resin as the shell materials by in situ polymerization. Wood flour/high-density polyethylene (WF/HDPE) composites with MF shell MicroPCMs (MF-MicroPCMs) or PMF shell MicroPCMs (PMF-MicroPCMs) were prepared, respec...
Xi Guo, Jinzhen Cao
Decontamination of sludges, liquids and soils polluted by “class 1, 2 & 3a” and “temporary” wood treatment products from dipping tanks
2016 - IRG/WP 16-50315
Wood is one of the most widely used building materials as it is easy to find and process. As an organic material, time leads to a degradation of its substance, and even more so when it is exposed to pathogens such as fungi, bacteria and insects. In order to try and inhibit this phenomenon, several preservation treatments have been developed and applied thanks to the production of chemical biocides...
A Zaremski, E Wozniak, S Maman, C Zaremski, S Morel
Life cycle assessment of creosote treated wood and tall oil treated wood with focus on end-of-life
2016 - IRG/WP 16-50320
The use of creosote for protecting wood products in heavy-duty application outdoors has been common for many years, but stricter regulations have limited creosote’s use. Life cycle assessments (LCA) have shown that in some applications alternatives to creosote treated products do not have less environmental impacts. Searching for alternatives to creosote, tall-oil-based preservatives have been ...
L G F Tellnes, U Hundhausen
Durability of energy efficient wooden buildings: a building physical point of view
2017 - IRG/WP 17-40812
The drive for more energy efficient and sustainable buildings resulted in an increased popularity of wooden buildings, even in countries with a masonry tradition. Often guidelines and prescriptions then are copied from other countries. Different climatic boundary conditions and tradition of finishing, though, do require different moisture tolerance criteria. This is clearly the case for water vapo...
S Roels, J Langmans
Boron dual-treatments for Douglas-fir utility poles: Tracking boron migration over time
2019 - IRG/WP 19-30739
The potential for using boron pressure-treatment prior to over-treatment with conventional, heavy-duty wood preservatives to limit internal decay in-service was investigated in two field tests on Douglas-fir utility poles. Pole sections were pressure-treated with disodium octaborate tetrahydrate (DOT) and then over-treated with either pentachlorophenol or copper naphthenate in oil. Alternatively, ...
J Cappellazzi, M J Konkler, J J Morrell
Wood Protection Through Diffusion: Dimensional Stabilisation with Amine Oxides
2019 - IRG/WP 19-30747
Wood is a phenomenal construction material. In addition to its great physical properties and its beautiful appearance, it possesses many environmental-friendly virtues like the sequestration of carbon dioxide. It is however subject to dimension changes when submitted to fluctuating moistures levels, which can lead to warps, cracks and the peeling of paints. Many water repellents can slow down the ...
S Pepin, P Blanchet, V Landry
Limiting Polysaccharide Motion Protects Wood From Decay
2020 - IRG/WP 20-40890
It is well known that chemical modifications to improve decay resistance also reduce the equilibrium moisture content (EMC) of wood. The mechanism of this action, however, has been the subject of much debate. Several groups have suggested that decay resistance is a result of lower diffusion rates of fungal degradation agents through the wood cell wall. A recent paper explained the fundamental prin...
C G Hunt, S L Zelinka, J E Jakes
Application of suberin fatty acids extracted from birch bark for wood coating
2021 - IRG/WP 21-40914
It is well known that chemical modifications to improve decay resistance also reduce the equilibrium moisture content (EMC) of wood. The mechanism of this action, however, has been the subject of much debate. Several groups have suggested that decay resistance is a result of lower diffusion rates of fungal degradation agents through the wood cell wall. A recent paper explained the fundamental prin...
A Kumar, Risto Korpinen, Veikko Möttönen
Significance of the thermal design and the sorption isotherm shape in hygroscopic wood moisture dynamics and service life
2022 - IRG/WP 22-20682
Moisture dynamics are considered important for predicting the service performance of wood in exterior applications. Above a critical moisture content, water acts a softener on the structural polymer matrix of the wood cell wall, enabling the necessary diffusion of molecular species involved in the fungal degradation mechanism of wood. Water may enter solid wood in either liquid form or in vapor fo...
W Willems
Preservative Treatment of CLT: An Example at Shimojishima Airport
2019 - IRG/WP 19-30748
Cross laminated timber (CLT) is a relatively new construction method that allows multi-storey construction using solid wood instead of concrete or steel. It is a method favoured by progressive architects and recognized for its much lower environmental footprint. Wood is an excellent construction material and is a long-term carbon sink that also performs well in the event of earthquakes and fire....
J Lloyd, N Yamashita, A Taylor
Premature adhesion failure of exterior wood coatings – The influence of substrate temperature at coating application and moisture accumulation during storage
2022 - IRG/WP 22-40937
The present study aimed at extending the knowledge about premature coating failures of industrially finished wood cladding. Two potential factors were studied: the influence of substrate temperature at coating application and moisture accumulation during storage on the adhesion of waterborne coating systems. In the first experiment, 4 batches of wood specimens were submitted to 4 different tempera...
U Hundhausen
Manipulation of the hierarchical wood structure for extended carbon storage in the built environment
2023 - IRG/WP 23-50381
The sustainable processing of trees into construction materials can act as carbon storage. Carbon storage in durable sustainable wooden construction material has cumulative effects and net gain in storage in the built environment that can be offset by net losses in forest carbon by cutting the tree. Carbon storage for an extended period plays an important role in the mitigation of CO2 emissions an...
T Singh, A Arpanaei, D Elustondo, Q Fu
Developing thermal-energy storage systems based on Kraft lignin-glyoxal and organic phase-change material modified wood
2024 - IRG/WP 24-30810
This study investigated the use of modified wood as a thermal-energy storage material through the integration of paraffin-based phase-change materials (PCMs). The objective was to evaluate the influence of Kraft lignin-glyoxal prepolymer on the properties of wood modified with PCMs. The implementation of the modified wood involved preparing PCM emulsions, synthesizing lignin-glyoxal prepolymer, an...
C-F Lin, O Karlsson, D Jones, D Sandberg