The resistance of wood coated with different solvent-borne paints against colonisation by decay fungi
2009 - IRG/WP 09-40468
This paper examines different solvent-borne paints characteristics and their decay resistance when applied on pine wood surface. It was determined by the standard ENV 839 procedure. The part of samples were subjected to accelerated ageing according to the EN 84 standard. The discussed commercial paint systems were typical stains or penetrating oil-based products, with or without biocides....
B Mazela, P Hochmańska
Performance if internal remedial treatments to arrest fungal attack in poles and large timbers
2018 - IRG/WP 18-40834
Internal remedial treatments have been used to arrest internal fungal attack in utility poles and other large timbers. Water diffusible systems and volatile fumigants have both been used for this purpose. While both work, it is important to understand the performance attributes of each system. This paper reviews the literature on both systems and makes recommendations for future research....
J J Morrell
Effect of permeability and extractives on the decay rate of southern pine sapwood in above grund exposure
2005 - IRG/WP 05-20310
The effects of wood permeability and hydrophilic and hydrophobic extractives on the decay rate of southern pine sapwood in above ground exposure were investigated. Permeability was determined by water sorption measurements, and the effect of extractives was studied by pre-extracting the test samples prior to outdoor exposure using water to extract hydrophilic extractives or sequential methanol/cy...
D D Nicholas, T Schultz, L Sites, D Buckner
The Relationship of Fiber Cell Wall Ultrastructure to Soft Rot Decay in Kempas (Koompassia malaccensis) Heartwoo
2004 - IRG/WP 04-10541
The ultrastructure of fiber walls in kempas (koompassia malaccensis) heartwood was examined in relation to soft rot cavity formation. The fibers consisted of middle lamella and thick secondary wall. The secondary wall was differentiated in to a S1 layer, and a unique multi-lamellar S2 layer. Two distinct forms of lamellae were recognisable, one type being considerably thicker than the other. They ...
A P Singh, A H H Wong, Yoon Soo Kim, Seung-Gon Wi
The use of TCMTB in applications other than sapstain prevention: A review
1990 - IRG/WP 3606
The efficacy of TCMTB against staining fungi and surface moulds has been thoroughly investigated during the last decade. As a result, the chemical is used as an alternative to the chlorinated phenols in various parts of the world for the preservation of freshly sawn timber. Less known are the data obtained against brown rot, white rot and soft rot fungi. The termite repellent and bactericidal prop...
R Van der Eynde
Isolation and identification of bacteria from degraded wood - A progress report
1986 - IRG/WP 192
During attempts to isolate tunnelling bacteria in pure culture, physical separation from other bacteria was successfully achieved by the use of cellophane. Cellophane was used in liquid cultures as a substrate for tunnelling bacteria that were present in a mixture with other bacteria. By tunnelling into cellophane, TB were physically removed from contaminating bacteria which could then be removed ...
J A Drysdale, P J Ruland, J A Butcher
Effect of mineral wools on growth and decay capacities of Serpula lacrymans and some other brown-rot fungi
1991 - IRG/WP 1481
The influence of stone wool and glass wool on growth and decay capacities of Serpula lacrymans and some other brown-rot fungi was studied. Mass losses of pine wood caused by Serpula lacrymans and Gloeophyllum trabeum were increased when stone wool was present. Glass wool had no influence on mass losses. Coniophora puteana, Serpula lacrymans and Gloeophyllum trabeum grew into stone wool and destroy...
L Paajanen, A-C Ritschkoff
The use of pyrethroids against Limnoria spp
1981 - IRG/WP 473
Synthetic pyrethroid insecticides discovered in the last fifteen years have been developed as crop sprays and used in aerosol formulations for the control of household pests. High toxicity to a wide range of arthropod pests, combined with reasonably low mammalian toxicity, confers an advantage over many other control agents. Some of the more recent pyrethroids are photostable and display residual ...
D Rutherford, R C Reay, M G Ford
Bifenthrin, a new insecticide for the control of termites and wood-boring insects
1995 - IRG/WP 95-30076
Bifenthrin, a new insecticidal compound Bifenthrin has been extensively tested, to determine its potential use to control termites and other wood destroying insects. Bifenthrin is effective at extreme low rates which can minimize human and environmental exposure to the product. Results of tests carried out by several research institutes and by FMC in different countries will be presented. The phys...
G Rustenburg
N-tritylmorpholine as a potential marine wood protectant against teredinids and pholads - A preliminary evaluation
1983 - IRG/WP 497
The molluscicide, N-tritylmorpholine, is effective in eradicating certain fresh water snails, the intermediate hosts in the transmission of schistosomiasis in man. This preliminary study shows that N-tritylmorpholine is also active against wood-boring marine mollusks. Fine sapwood impregnated with this morpholino compound was not damaged by teredinids or pholads while exposed at two marine sites i...
J D Bultman, K K Parrish
Comparison between the Hylotrupes bajulus strains of different European laboratories
1980 - IRG/WP 1118
In several European countries, wood preservatives of the same formulation are subjected for the quality label to particular tests according to standards established by the CEN. The different laboratories which carry out these tests have had their cultures for many years. The insects are kept in optimal nutritional and climatic conditions and have always mated amongst themselves. On the one hand, e...
M-M Serment
Long term performance of CCA preservatives in ground contact
2000 - IRG/WP 00-30223
Copper-chrome-arsenate (CCA) preservatives have been use extensively in New Zealand since the mid-1950s for a wide range of ground contact uses, radiata pine being the main species treated. They have been the subject of a comprehensive field testing programme in up to five sites in New Zealand, the earliest tests being established in 1955. Main factors affecting performance have been formulation t...
M E Hedley, D R Page, B E Patterson
Preliminary screening of diffusion formulations for the control of soft rot
1978 - IRG/WP 2104
We have an urgent need in Australia to develop in situ remedial treatments for the present population of in-service transmission poles. For various reasons we have opted for formulations which can be applied as bandage treatments and thus we are primarily concerned with assaying diffusable toxicants. Two basic approaches have been made: an assay of the formulation's toxicity; and a combin...
H Greaves
Biodegradation of acetylated southern pine and aspen composition boards
1994 - IRG/WP 94-40020
This objective of this study was to investigate the influence of the acetylation treated wood fiber, Phenol-formaldehyde resin content level, two wood fiber species, three fungi species on the dimensional stability and decay resistence of high density composition boards. A standard ASTM method was used to evaluate weight loss and thickness change. The linear shrinkage and expansion of each species...
P Chow, T Harp, R Meimban, J A Youngquist, R M Powell
Positive dosage response of CCA in hardwood power poles to soft rot indicated from New South Wales soft rot survey dat
1983 - IRG/WP 3233
Experience and observation have shown that retentions of less than 16 kg/m³ in the sapwood of individual hardwood poles are unlikely to delay its deterioration sufficiently to ensure an economic performance in some instances. The higher retentions of current practice should do so subject to adequate inspection and maintenance. Increases in retentions requirements up to 35 kg/m³ more or less, dep...
A J Witheridge
Preservative performance of copper naphthenate (SANPRESER-OGR) in brush treatment of timber
1991 - IRG/WP 3663
Preservative efficacy of copper naphthenate (SANPRESER-OGR) was evaluated in the laboartory and field trials when timber was treated by brushing. Results of field trial indicated that service life of the brush-treated timber could be approximately 10 years or longer under ground contact conditions, although life span was slightly varied with timber species and test sites. After four years&apos...
Y Sugai, K Hamada, M Kitada, K Tomoi
Mapping soft rot decay distribution using image analysis
1993 - IRG/WP 93-20011
Image analysis has been shown to be a useful technique for the assessment of soft rot decay caused by Chaetomium globosum in birch and bamboo (Wickens and Murphy, 1992). The technique can permit assessment of decay in individual or small groups of cells and this has been used to undertake soft rot decay mapping in thin sections of bamboo. Assessments were made of the extent of soft rot decay with ...
P J Wickens, R J Murphy, G F M Watts
Co-operative field trial. Background notes and questionnaire for field sites
1992 - IRG/WP 92-3733
The first co-operative field trial was designed to study the occurrence of soft-rot in CCA treated hardwoods. Generally speaking very similar results were obtained from the different field sites. In the early part of the trial considerable variability was evident with regard to the rate and type of attack which occurred in the untreated material. With the CCA treated timber the type of decay was p...
D J Dickinson
Acetylation of lignocellulosic materials
1989 - IRG/WP 3516
A simplified procedure for the acetylation of lignocellulosic materials has been developed. The acetylation is done with a limited amount of liquid acetic anhydride without the addition of a catalyst or an organic co-solvent. Dimensional stability and biological resistance are both much improved by the acetylation. Equilibrium moisture content in acetylated material is considerably lower than in u...
P Larsson, A-M Tillman
The use of plastic meshes in soft rot monoculture testing
1990 - IRG/WP 2353
Plastic meshes were introduced between the wood blocks and agar medium in a miniaturised soft rot monoculture test in order to minimise transfer of the preservative from the wood and mineral salts from the agar. Although several different sizes and types of mesh were used and the blocks were wetted up to an appropriate moisture content for soft rot attack the amount of decay was substantially redu...
S M Gray
Inhibition of wood decay and termite damage by calcium precipitation
1996 - IRG/WP 96-30111
Fungal decay of wood in service, especially brown rot, results in billions of dollars (US) of losses annually. Recent environmental restrictions, both U.S. and international, are limiting or eliminating the use of broad spectrum biocides for wood preservation, primarily due to problems with disposal. In order to design new, environmentally benign methods for control of wood decay fungi, it is esse...
F Green III, T A Kuster, L Ferge, T L Highley
The effect of high temperature and long pressing time on the dimensional stability and decay resistance of OSB
2002 - IRG/WP 02-40237
The exterior use of OSB is restricted because when it is exposed to wet conditions swelling, loss of internal bond strength (IB) and decay occur. In this study an alternative process of pressing which results in the production of dimensionally stable and a more decay resistant strandboard was investigated. Boards were pressed at elevated temperatures for prolonged pressing cycles and their physi...
G J Goroyias, M D C Hale
Effects of artificial UV weathering and soft rot decay on heat treated wood
2005 - IRG/WP 05-40302
Oil and inert gas oven heat treated pine wood strips 100 µm thick were mildly heat treated (200°C, 30 mins linseed oil, 120 mins oven). Following treatment, specimens were exposed to UV weathering (300 hours) and decay by the soft rot fungus, Chaetomium globosum. The effects of each treatment were assessed by zero span tensile testing, microscopy and by FTIR.
Tensile testing of heat treated s...
M D C Hale, S C Ghosh, M J Spear
Effects of a formaldehyde and sulphur dioxide treatment on decay and mechanical properties of aspen waferboard
1983 - IRG/WP 3242
Aspen wafers were sequentially treated under vacuum with formaldehyde and sulfur dioxide gas and pressed into waferboard bonded with powdered phenol formaldehyde resin. Decay resistance and strength properties were determined before and after simulated weathering. The water resistance of the phenol bonding system was lost in board made from the gas-treated wafers. This white rot fungus Coriolus ve...
E L Schmidt
Examining environmental conditions and the biodeterioration of historic waterlogged wood: the Kolding Cog
2002 - IRG/WP 02-10441
Survival of waterlogged wood from thousands and in rare cases millions of years presents scientists with a unique opportunity to examine wood specimens which, due to select properties of the wood itself and/or the depositional environment, have not been completely degraded. This paper discusses the biodeterioration of a submerged shipwreck buried in Kolding Fjord, Denmark for the past 1000 years....
B A Jordan, D J Gregory, E L Schmidt