Your search resulted in 278 documents. Displaying 25 entries per page.
Experiments in accelerated ageing
1984 - IRG/WP 2223
Experiments using a vacuum oven to accelerate the evaporative loss of g-HCH from treated wood blocks have indicated that the method described in this paper has the potential to reproduce in a relatively short time the distributions and loadings of the insecticide that are found during natural ageing. By contrast, the wind tunnel removed the volatile material in a way not found in natural ageing an...
R J Orsler, M W S Stone
Utilization of coconut timber from north Sulawesi, Indonesia. Part 2: Treatability
1994 - IRG/WP 94-40025
Under tropical conditions coconut wood is quickly degraded by mold and blue stain fungi. Low density wood in ground contact is commonly decomposed by wood destroying fungi within a period of only a few months, higher density wood from the outer stem regions within 24 to 30 months (MOSTEIRO, CASIN, SERIBAN 1976; McQUIRE 1975). Moreover, according to McQUIRE (1975) green wood of lower density is hig...
R-D Peek
Fixation of CCA preservatives in cocos-, oil- and rattan-palm
1986 - IRG/WP 3371
In previous tests with jubaea-palm almost no fixation of a CCA-preservative Type B could be achieved, consequently, further leaching tests were carried out with samples of 1 cocos-, 1 oil- and 2 rattan-palms from Malaysia. A good fixation of chromium and copper took place in cocos-palm after 4 weeks storage at 28°C. Nevertheless the fixation was slower than in pine-wood and demanded an elevated t...
H Willeitner, K Brandt
In-house accelerated method for testing decay resistance of treated wood
2004 - IRG/WP 04-20286
Fungicidal compounds often change their effectiveness when they are incorporated into candidate formulations. For this reason fungistatic effectiveness needs to be re-evaluated as many times as the formula has been modified for better performance. To avoid multiple expenses, in-house fungistatic tests are essential. Our goal was to develop in-house usable, simple but reliable and reproductive proc...
N Vidovic
Oxidation of wood components during CCA-C fixation
1993 - IRG/WP 93-30024
Pre-extracted radial sections of southern yellow pine sapwood were treated with CCA-C and analyzed by X-ray photoelectron spectroscopy (XPS). The ratio of C1 (carbon bonded to carbon and/or hydrogen) to C2 (carbon bonded to one oxygen) in XPS Cls spectra was taken as a measure of the progress of oxidation of wood components during CCA fixation. This ratio was 0.82 before CCA treatment and increase...
M Kaldas, P A Cooper
Rapid fixation of Chromated Copper Arsenate (CCA) wood preservatives by microwave treatment
2000 - IRG/WP 00-40184
Rapid microwave heating of freshly chromated copper arsenate (CCA) treated timber indicates that rapid preservative fixation is possible within approximately 40 seconds. The leaching of CCA was evaluated using simulated rainfall. Cost analyses indicates that microwave fixation using an on-line conveyor belt fixation process with an output of 4m3/hour using a microwave power supply of 230 kW costs ...
G Torgovnikov, P Vinden, E Mapanda, P R S Cobham
Some practical implications from recent research on the fixation of CCA preservatives
1975 - IRG/WP 358
The mechanism of fixation of CCA preservatives is briefly described. If the temperature is increased during the primary fixation period, the formation of intermediate fixation compounds is less extensive. The length of the primary fixation period is of practical interest. It is determined by preservative composition and concentration, temperature and wood species. Diagrams are given for Pinus sylv...
S-E Dahlgren
Moderate temperature fixation of CCA-C
1989 - IRG/WP 3522
Several Canadian treating plants are using moderate temperature (40-60C°) fixation chambers to reduce drippage and leaching from fresh CCA treated wood. In this study, chromium reduction and surface leaching properties of CCA-C treated red pine (Pinus resinosa) pole sections were monitored during exposure to temperatures of 50-60C° and 90-100% RH conditions. Chromium-VI concentration in the abso...
P A Cooper, Y T Ung
Studies of the mechanism of chromated-copper preservative. Fixation using electron spin resonance
1992 - IRG/WP 92-3701
Two softwoods and one hardwood species were treated with chromium trioxide, copper sulphate, chromated-copper wood preservative (CCA). The treated wood samples were analyzed during fixation by electron spin resonance (ESR). ESR spectra indicated that more than one Cr(V) species was generated from Cr(VI) soon after CCA treatment. The Cr(V) signal became strong within increased several hours followe...
K Yamamoto, J N R Ruddick
The accelerated L-joint test method for determination of the out of ground natural durability
1998 - IRG/WP 98-20146
The accelerated L-joint test incorporates a moistening device and uses a close end water trap in an open joint connection with a laminated tenon member consisting of the perishable reference wood species scots pine sapwood and beech.
After one year of exposure it is possible to show a distinct identification of natural durability classes 4 and 5 against the more durable wood species. Both weight ...
J Van Acker, C Brauwers, M Stevens
The performance of chlorothalonil after 4.5 years in the accelerated field simulator
1994 - IRG/WP 94-30041
The decay resistance of chlorothalonil in oil was examined in an accelerated field simulator (AFS). Pinus radiata D. Don and Eucalyptus regnans F. Muell. sapwood stakes were treated, placed in soil in the AFS, and monitored over 4.5 years. CCA type C treated stakes were included for comparison. Water and toluene treated control stakes were heavily decayed after 1-2.5 years. Oil treated controls, t...
L J Cookson
Industrial fixation systems: key factors, limitations and optimisation through the use of computer simulation modelling. Discussion paper
1994 - IRG/WP 94-40026
This paper briefly describes four fixation operative in the Netherlands, namely: circulating and non-circulating steam fixation cylinders, steam fixation chambers and controlled climate rooms. The general limitations of industrial practice are reviewed against the background of established fixation theory. The controlling variables, both material and process-related, for fixation processing are sp...
A J Pendlebury, M Riepen, M J Boonstra, W Gard
Stability, performance and distribution of propiconazole (R 49362) in acceleratedly aged wood
1991 - IRG/WP 3647
The permanency of propiconazole (R 49362 - WOCOSENÔ technical - Janssen Pharmaceutica) in wood was examined in an 18 month storage test, an evaporative ageing study (EN 73), a volatilization stress experiment, and water-leaching studies (EN 84). The biological efficacy against two brown rot fungi: Coniophora puteana BAM Ebw. 15 and Gloeophyllum trabeum BAM Ebw. 109 was assessed according to the E...
A R Valcke, M Stevens
Accelerated weathering test for the evaluation of wood preservative efficacy
2003 - IRG/WP 03-20262
Wood samples treated with ammonium copper quat (ACQ-1900 and ACQ-2200), Chromated copper arsenate (CCA), Tanalith E 3491 and Wolmanit CX-8 have been studied in accelerated weathering experiments.
The weathering experiment was performed by cycles of 2 hours UV-light irradiation followed by water spray for 18 minutes. The changes on the surface of the weathered samples were characterized by FTIR Sp...
A Temiz, M Eikenes, Ü C Yildiz, F G Evans, B Jacobsen
Differences and their causes of CCA and CCB efficacay among some softwoods and hardwoods
1991 - IRG/WP 3656
Wood blocks from two softwoods and two tropical hardwoods species treated with different concentrations of CCA, CCB, and combinations of CrO3, CuS04, H3BO3 were subjected to the decay by brown rot fungus, Tyromyces palustris. CCA maintained good effect both in softwoods and hardwoods, while CCB and the other combinations lost their effectiveness after leaching. Chemicals leached from CCA treated w...
K Yamamoto, M Rokova
Effect of compression wood on leaching of chromium, copper, and arsenic from CCA-C treated red pine (Pinus resinosa Ait.)
2000 - IRG/WP 00-30232
In this study, the effect of compression wood formation on the release rate of chromium, copper, and arsenic elements from red pine (Pinus resinosa Ait) was investigated. Wood blocks from red pine containing compression and normal wood portions were treated with a 1.0% CCA-C solution and were then allowed to fix at 23 ± ??2°C (74 ± 4°F) for 0, 6, 24, 48, 96, 192, and 336 hours. After each fixa...
S N Kartal, S T Lebow
Copper based water-borne preservatives: Copper adsorption in relation to performance against soft rot
1987 - IRG/WP 3452
As part of a fundamental study concerned with the performance of copper based water-borne preservatives the adsorption of copper from aqueous solutions by 4 hardwood and 1 softwood species has been studied. Experiments were conducted to determine the influence of solution pH, solution concentration and solution temperature. The results obtained were consistent with an acid form ion-exchange mechan...
P M S Rennie, S M Gray, D J Dickinson
A diffusion and reaction model for the leaching of Cr-VI from unfixed CCA-treated wood
2001 - IRG/WP 01-50169
A physical model applicable to the leaching of any substance undergoing a first-order fixation reaction with wood is presented. Using this model and a laboratory leaching experiment with small wood samples immersed in water, the radial and tangential diffusion coefficients and the reaction rate constants of Cr-VI in unfixed CCA-treated red pine (Pinus resinosa Ait.) are measured. Reaction rate con...
L Waldron, P A Cooper
Bibliography on the use of boron compounds for the preservation of wood
1973 - IRG/WP 315
This bibliography is based on an earlier literature survey prepared by J. Thornton and Wm. E. Bruce (O.E.C.D. Document No. 27/DAS/CSI/M/91) which was enlarged and revised for a meeting in Paris in October 1968 (Document 27/DAS/CSI/M554) by Professor W. Bavendamm of Reinbek. The latter (1968) document with its 166 references has now been extended and brought up to date. Acknowledgments are due to B...
R Cockcroft, J F Levy
Comments on leaching in view of accelerated testing
1977 - IRG/WP 294
We developed an accelerated test for leaching at elevated temperatures (75-85°C). This test was used for the examination of 11 preservative formulations containing Cu, Zn and As. The data obtained from these experiments were compared with data on some formulations tested by ASTM standard leaching test. The method consists in making a large surface to volume ratio of wood from a treated block by c...
J Rak
Investigation of CCA fixation in wood by sequential extraction. I Determination of CCA component fixation and preliminary extraction results
2002 - IRG/WP 02-50188
The fixation of CCA-C preservative was investigated in sapwood of red pine (Pinus resinosa Ait.), trembling aspen (Populus tremuloides Michx.) and red maple (Populus tremuloides Michx.) at target retentions of 4.0, 6.4, 9.6 and 30.0 kg/m3. Treated wood sawdust was water extracted at close time intervals during the fixation and analyzed for the contents of unfixed hexavalent chromium, total Cr, Cu ...
S Radivojevic, P A Cooper
Possible durability transfer from durable to non durable wood species. The study case of teak wood
2001 - IRG/WP 01-10392
Teakwood is well known for its excellent natural durability, mostly due to its high proportion of extracts. Amongst these extracts, quinones, and more precisely some naphtoquinones (such as lapachol) and anthraquinones (such as tectoquinone) appear to play a crucial role in the resistance to wood decay organisms. At a laboratory scale, sawdust from malaysian teak heartwood has been extracted under...
M-F Thévenon, C Roussel, J-P Haluk
Remediation of environmental impacts related to inorganic wood preservative chemicals using in-situ geochemical fixation
2001 - IRG/WP 01-50166-17
Use of the inorganic wood preservative chemical chromated copper arsenate (CCA) has resulted in several documented cases of soil and ground water contamination at wood treatment plants due to spills or releases of the treatment chemical. The most significant impact from releases of CCA to the environment is related to hexavalent chromium contamination of ground water. This is due to the relative s...
R M Thomasser, J V Rouse
Standard and accelerated testing of boron-additive wood protection systems
2005 - IRG/WP 05-30381
The main objective of this research was to determine the effectiveness of boron-additive protection systems for above ground applications by means of field testing. The two field test procedures used are based on the L-joint test described in the European standard EN 330. For the first set up the boron treated timber was coated in accordance with the standard EN 330 system. The second set up is ba...
A Mohareb, J Van Acker, M Stevens
Co-operative studies on determining toxic values against wood-destroying basidiomycetes: Progress report to April 1990
1990 - IRG/WP 2357
This document reports progress on the co-operative study between nine laboratories, set up following the proposals contained in Document IPG/WP/2316 (1988). Results have been received from eight laboratories. Toxic values data have been established successfully for the test fungus Coniophora puteana with soil, malt agar and vermiculite methods and with the test fungi Gloeophyllum trabeum and Poria...
J K Carey, A F Bravery