A technique for the rapid assessment of wood surface degradation during weathering
1987 - IRG/WP 2281
Radiate pine (Pinus radiata D. Don) sapwood samples taken from four trees were converted into thin strips 100 x 10 x 0.085 (85 µm) mm³, (longitudinal x radial x tangential) in size and exposed in preweighed hatches to the weather inclined at 45° facing equatorially for 10, 20, 40, 60, 80 and 100 days. Significant (P < 0.001) weight losses occurred with time over the exposure period. Differen...
P D Evans, D Abbott, S Thein
Field Liners™ prevent creosote migration from transmission poles to soil during service
1996 - IRG/WP 96-40067
A full scale trial utilised 150 12m Eucalyptus grandis transmission poles treated with standard retentions of creosote according to SABS Method 457. One hundred poles had Field Liners™ applied while 50 did not. The 150 poles were used to complete an electricity transmission line in Southern KwaZulu-Natal. After 18 months service, incremental cores were taken from 15 cm below the ground lines of ...
M R Behr, G D Shelver, A A W Baecker
Characterization of checks and cracks on the surface of weathered wood
2000 - IRG/WP 00-40153
The surface roughness of unweathered and untreated pine; unweathered copper chromium arsenate type C (CCA) - treated pine; weathered CCA-treated pine; and weathered CCA-plus-water-repellent (WR) - treated pine was evaluated by a stylus tracing method. Surface roughness parameters Ra, Rz, Rmax, Rk, Rpk, and Rvk were measured. Ra, Rpk, and Rvk were the most appropriate parameters for describing modi...
D P Kamdem, Jun Zhang
Durability of exterior natural wood finishes in Brazil
1985 - IRG/WP 3343
Wood finishes systems were evaluated in natural weathering conditions during 5 (five) years, over "Parana-pine" (Araucaria angustifolia). Test samples results show that: - Semitransparent wood preservative stains, based on polimerized linseed oil, provided very good protection to the wood, compared with the one based on alkyd varnish; - Solid color wood preservative stains provided good durability...
D R Macedo
Disodium octaborate tetrahydrate, alone and in conjunction with a selected isolate of Trichoderma viride, reduces decay of fresh felled pine independent of the effect of weathering
1994 - IRG/WP 94-10054
Unpeeled billets of Corsican pine were treated with the following: 5% aqueous disodium octaborate tetrahydrate (DOT) solution; 5% DOT solution with an isolate of Trichoderma viride with a low susceptibility to borate; the Trichoderma viride isolate alone. Half of the billets in each treatment group were also placed in large-diameter plastic pipes to protect the billets from the weather. All three ...
M W Schoeman, D J Dickinson, J F Webber
Wharf-borer a threat to stored archaeological timbers
1992 - IRG/WP 92-1560
Increased interest in marine archaeology has occured in recent years. Stored waterlogged archaeological timbers have been shown to be degraded by physical and microbial agents. In recent years a new threat has been highlighted, namely the wharf-borer Nacerdes melanura (L.). The objective of this paper is to outline studies of the morphology, biology, life-history and carbohydrate digestion by this...
A J Pitman, E B G Jones, A M Jones, M Rule
Black Stain of Western red-cedar by Aureobasidium pullulans and its Relationship with Tropolone Depletion
2005 - IRG/WP 05-10564
Western red-cedar is valued for its natural durability conferred by fungicidal tropolone chemicals. However, weathered surfaces of WRC products are still susceptible to ‘black stain’ caused by fungi such as Aureobasidium pullulans. The effect of weathering on the tropolone content of heartwood was characterized and correlated with the ability of this fungal species to colonize the same weather...
R Chedgy, R Daniels, P I Morris, C Breuil
Rapid loss of lignin at wood surfaces during natural weathering
1992 - IRG/WP 92-2390
Thin veneers of radiata pine (Pinus radiata D. Don) were exposed to natural weathering over a period of 30 days. Incident UV radiation was monitored at the test site. FTIR internal reflectance spectroscopy was used to study the chemical changes taking place at the veneer surface during weathering. Spectra obtained show that after only 3 days exposure there was substantial delignification at veneer...
P D Evans, K J Schmalzl, A J Michell
Permanence of permethrin and bifenthrin in framing timbers subjected to hazard class 3 exposure
2005 - IRG/WP 05-30383
End-sealed Pinus radiata specimens measuring 235 x 90 x 35 mm were treated using a modified Lowry schedule with permethrin or bifenthrin in white spirit to Hazard Class 2 (H2) retentions. After conditioning, the specimens were exposed at 45o on north facing racks near Melbourne (Australia). Samples of the specimens were taken before installation, and after three and six months exposure. Analyses o...
A C Hunt, D G Humphrey, R Wearne, L J Cookson
Assessment of residual retentions in creosote treated Scots pine (Pinus sylvestris) poles after 45 years ground contact service in the Lemstervaart in the Dutch polder
1994 - IRG/WP 94-50022
In a project funded by the Water State Authorities (RWS) and the Noordoostpolder Water Board, the residual retentions in ten creosote treated Scots pine (Pinus sylvestris) poles were examined after 45 years ground contact service along a canal (Lemstervaart) in the Dutch Noordoostpolder. The Lemstervaart location was selected due to the fact that the poles involved had been originally treated and ...
P Esser, W L D Suitela, A J Pendlebury, H Visscher
Losses of preservatives from treated wood during service. Results from a questionnaire
1994 - IRG/WP 94-50031
From environmental as well as from performance point of view it is of interest to know how much of the preservatives in treated wood that is leached out or evaporated from the wood during service. Many laboratory studies are carried out on leaching from small samples in distilled water or water with different pH. These studies give a good picture of the relative leaching from wood treated with dif...
M-L Edlund
A methodology for the life-cycle assessment of treated timber products
1993 - IRG/WP 93-50001-01
Using case studies of CCA-treated motorway fenceposts and creosote-treated electricity transmission poles, the paper suggests an approach to evaluation of the overall environmental impact of treated timber products, utilising the emerging systems analysis method of life-cycle assessment (LCA). The development and application of LCA methodologies to date is reviewed and the key features identified....
S R Smith, R J Murphy, D J Dickinson
Water-based silicones on wood
1997 - IRG/WP 97-30144
Five waterbased silicones commonly used on masonry where tested as water repellents for wood. The Water Repellent Effectiveness was determined by swellometer-tests and by measuring the water uptake of samples after 24 hours complete immersion and by immersion in a water level of 4 mm for 24 hours. The different methods are compared and discussed. Artificial and natural weathering was performed to ...
D Lukowsky, R D Peek, A O Rapp
Blue stain in service on wood surface coatings. Part 1: The nutritional requirements of Aureobasidium pullulans
1992 - IRG/WP 92-1556
The nutritional requirements of Aureobasidium pullulans was examined with regard to nutrient sources that are potentially available in fresh and weathered wood. The study was designed to determine how far wood cell wall components need to be broken down during weathering before they provide a useful nutrient source for Aureobasidium pullulans. Various carbon sources were tested, with eight differe...
P R Sharpe, D J Dickinson
Modification of wood by graft treatment
2003 - IRG/WP 03-40257
New water-repellent systems for wood are needed to improve the weathering characteristics. This study found that treatment of wood with chemical grafting systems imparted substantial water repellency. Different direct oxidative grafting systems were examined. Specifically, KMnO4, Fe(NH4)(SO4)2·12H2O, Fe2(SO4)3·5H2O, and (NH4)2Ce(NO3)6 were used as initiators and styrene as the monomer. All the...
M M Morshed, D D Nicholas, C Pittman Jr, T Schultz
Evaluation of outdoor weathering performance of modified wood
2004 - IRG/WP 04-20296
Interlace treated, oil treated, silicon treated as well as untreated Scots pine samples have been exposed outdoors. For evaluating the samples on their long term performance an internal standard had been developed. Parameters to be determined were the uptake of liquid water (submersion test), weight variation during exposure, crack performance, surface roughness and colour change.
This paper disc...
Y Schulte, S Donath, A Krause, H Militz
An environmental aspect relating to leachability of CCA from hardwood and softwood poles in Bangladesh
2001 - IRG/WP 01-50167
Leachability of CCA and the service performance of 8 softwood and 5 heartwood poles in service after 5 to 17 years in Bangladesh have been studied. The study included determination of retention of CCA-C in outer 6 mm zones at groundline (GL) and above groundline (AGL) along with the observation of decay and conditions of soils. The mean leaching of CCA-C derived from retention differential at GL a...
A K Lahiry
A rearing procedure for the house longhorn beetle Hylotrupes bajulus L
1973 - IRG/WP 228
The technique practised at the Princes Risborough Laboratory for culturing Hylotrupes bajulus is described. It is modified from methods previously suggested by German workers. A protein and vitamin enriched wood diet to accelerate larval growth is employed and larvae are subsequently given a period of cool storage to induce pupation. Adults are confined in groups with prepared surfaces for egg lay...
R W Berry
Assessing the importance of degradation mechanisms on the loss of effectiveness of wood preservatives
2000 - IRG/WP 00-20193
Accelerated ageing systems developed for application to samples in the laboratory prior to biological tests, should reflect those natural deterioration processes that are likely to occur in the hazard classes defined in EN 335-1. Losses through evaporation or the effects of leaching have been recognised, however their importance, relative to other mechanisms has not been quantified. Degradation me...
E D Suttie, R J Orsler, T Dearling
Diffusion modeling of inorganic wood preservative leaching in service
2005 - IRG/WP 05-50224-5
To evaluate the potential environmental and health implications of leaching of inorganic wood preservatives in service under different conditions, there is a need for a predictive model that provides estimates of the rate and extent of leaching over a wide range of product dimensions and exposure conditions. In this paper, we show that the leaching behavior of inorganic preservative components fr...
L Waldron, P A Cooper, Y T Ung
Remedial treatment of creosoted railway sleepers of redwood by selective application of boric acid
1980 - IRG/WP 3134
An ideal preservative for remedial treatment must primarily be characterized by two requirements. First, it must have an ability to diffuse and distribut evenly into the wood and secondly, it must be fixed properly so that it does not leach out too fast. However, these two characteristics conflict with each other, and the choice of preservative must of necessity be a compromise. Wood preservatives...
C Bechgaard, L Borup, B Henningsson, J Jermer
Artificial weathering exposure as an alternative for standard ageing according to EN 84 (leaching) and EN 73 (evaporation)
2002 - IRG/WP 02-20254
In order to verify potential weaknesses of wood preservatives fungal tests are carried out after ageing of wood preservative treated test blocks. The European standard EN 599 as a framework for efficacy assessment of wood preservatives includes the use of two ageing methods prior to fungal testing, namely a leaching method (EN 84) and an evaporation method (EN 73). The European research project "F...
J Van Acker, M Grinda, D J Dickinson
Dutch national environmental policy strategy (NMP): Implications throughout the life cycle of treated timber and for the Dutch preservation industry
1993 - IRG/WP 93-50001-31
All overview of relevant environmental legislation and instruments for control is given for each stage of the life cycle of treated timber. Recent policy in the Netherlands has been focused around the "National Environmental Policy Strategy", in which a general policy with regard to reduction of pollution to the air, soil and water is described. The principle is one of an "Integrated Chain of Cont...
P Esser, D A Lewis, A J Pendlebury
Screening of modified linseed oils on their applicability in wood protection
2004 - IRG/WP 04-30346
In this study modified linseed oils, rape oil and three waxes were screened on their efficacy as wood protecting agents. By testing all products when impregnated with high retentions in Scots Pine sapwood on water repellence qualities, additionally an accelerated weathering test, drying quality, accelerated brown rot and blue stain test, an indication is formed of the capability of these products ...
A Treu, J Lückers, H Militz
In search of excellence - A necessary challenge
1990 - IRG/WP 3567
Consumerism and environmentalism are gaining much influence. At national and E.C.-level the policy conducted is based on prevention of pollution through "sound" wood preservatives. Supposing that "environmental friendly" products do not exist it is understood that "sound" products have least effect on the environment during their whole life cycle. In the past only the effectiveness was paramount, ...
G Rustenburg