Water-Borne Copper Naphthenate: An Emerging Wood Preservative
2002 - IRG/WP 02-30280
Waterborne copper naphthenate (WB Cu-N) was used to treat southern yellow pine (Pinus spp) and red maple (Acer rubrum) stakes. The treated stakes were exposed in test sites located in Florida, Michigan and Mississippi for 3 to 6 years. Copper Chromium Arsenate (CCA),
Ammoniacal Copper Quat (ACQ) and Oil-borne Copper Naphthenate (OB Cu-N) were also used to treat some stakes for comparison. Results...
P Nzokou, D P Kamdem, M H Freeman
Durability of heat-treated wood
1999 - IRG/WP 99-40145
Heat-treated wood from the French process were laboratory tested against decay using agar block test and a modified soil block test. Water absorption, bending strength, lignin content and acid number were also determined to evaluate the effect of heat treatment. Heat treated samples exhibit a higher lignin content and a lower acid number compared to untreated control indicating the degradation of ...
D P Kamdem, A Pizzi, R Guyonnet, A Jermannaud
Effect of water repellents on leaching of CCA from treated fence and deck units - An update
1997 - IRG/WP 97-50086
In an earlier study, it was shown that CCA leaching losses could be reduced over an accelerated leaching and short term natural weathering exposures by post treatment application of a commercial water repellent. In this report, the effects of this coating and two commercial CCA solution water repellent additives are evaluated after two years of natural weathering. Wood boards were pressure treated...
P A Cooper, Y T Ung, R M Vicar
The effect of water storage on the cell-structure of Sitka spruce (Picea sitchensis) with reference to its permeability and preservation
1970 - IRG/WP III 3A
Commercial treatment trials with full sized transmission poles have shown that water storage considerably improves the permeability of Sitka and Norway spruce. These results were confirmed by laboratory measurements which showed that in the sapwood of ponded Sitka spruce there is a vast improvement in permeability in all three grain directions. Heartwood permeability does not seem to be affected t...
J A Dunleavy, A J McQuire
Susceptibility of painted wood to discolouring fungi - influence of binder, solvent and surfactant
1992 - IRG/WP 92-3714
Previous studies have shown that the basic composition of paints, without fungicide addition, can significantly contribute to the varying microbial susceptibility of painted wood. Previously, non-weathered water-borne acrylic paints applied to wood without a primer were shown to be more susceptible to mould attack than solvent-borne alkyd paints. The present study was initiated to reveal if this d...
J Bjurman, C Herder
Performance of different treatments and finishes on wood out of ground contact. Preliminary results
1984 - IRG/WP 2221
Pinus and Eucalyptus L-joints treated with CCA, a water dispersable PCP and untreated ones were painted according to seven different finish's schedules and exposed at two sites in State of Sao Paulo. After ten months of exposure, it was possible to verify that preservative treatment improve the performance of both wood and finish. It was also possible to observe that wood substrate, prese...
S Milano
Effect of soil type and moisture content on soft rot testin
1986 - IRG/WP 2270
Several soils of different types were tested at a range of moisture contents for their suitability for use in a soil burial soft rot test. Their effectiveness was assessed by weight loss in CCA treated and untreated beech and birch outerwood. A horticultural loam (John Innes No. 2) was the most appropriare soil in terms of amount of weight loss caused, tolerance to changes in soil moisture content...
S M Gray
Effect of climate, species, preservative concentration and water repellent on leaching from CCA-treated lumber exposed above ground
2001 - IRG/WP 01-50178
Few studies have examined leaching of chromated copper arsenate (CCA) from treated wood in above ground exposures due to the assumption that leaching is less severe compared to wood in continuous contact with soil or water. However, a significant portion of CCA treated wood is used for above ground applications, exposing considerable volumes of the preservative to precipitation and potential leach...
J L Taylor, P A Cooper
Water-borne DNBP wood preservatives - Preparation and performance
1987 - IRG/WP 3407
Three waterborne wide-spectrum ground-contact DNBP (2-sec-butyl-4,6-dinitrophenol) wood preservative formulations and their performance are presented. Two are double-treatment formulations in which insolubilization and precipitation of the preservative is attained by salt formation or by formation of a water insoluble Cu/NH3/DNBP complex of formula [DNBP]2 [Cu(NH3)2]2 the clarified structure of wh...
W E Conradie, A Pizzi
The fate of salt preservatives in facility yard soils and decontamination of soils and drainage waters
1993 - IRG/WP 93-50001-25
Extensive studies during the past 10 to 15 years revealed that noticeable amounts of preservative components may be released in the environment by dripping off or by rain prior to fixation unless adequate precautions are taken. Therefore, soil and groundwater contamination especially from chromium-VI compounds but also from other inorganic and organic constituents exist in impregnation plants, pos...
R-D Peek, H Klipp, K Brandt
Difference of CCA efficacy among coniferous wood species
1990 - IRG/WP 3601
Wood blocks of Cryptomeria japonica, Tsuga heterophylla, and Pinus radiata successively extracted with n-hexane, ether, and methanol were treated with various concentrations of CCA type 3, which were subjected to the decay by Tyromyces palustris. The weight loss were different among species and kinds of extraction. Cryptomeria japonica treated with CCA had higher fungal resistance than Tsuga heter...
K Yamamoto, M Inoue
Wood surface pretreatments with metal tannates
1989 - IRG/WP 3552
The sequential application of aqueous solutions of tannins derived from radiata pine bark and water-soluble metal salts was examined as a means of improving the water repellency of wood surfaces. Nine metal salts were screened in combination with tannin solutions and, based on water repellency of pretreated filter paper, four were selected for further study. The two-step application of tannin solu...
D V Plackett, D R Cronshaw
Comparative natural resistance of eighty-two timber species to damage by marine borers at Goa (India)
1996 - IRG/WP 96-10139
Natural bioresistance of eighty-two species of Indian timbers to attack by marine wood-borers has been presented based on data collected from test panels exposed in Goa waters (west coast of India) for periods ranging from five to thirteen months. All the timber species, except Artocarpus gomeziana and Pterocarpus santalinus, were completely destroyed within a short period of three to six months. ...
L N Santhakumaran
Water-based silicones on wood
1997 - IRG/WP 97-30144
Five waterbased silicones commonly used on masonry where tested as water repellents for wood. The Water Repellent Effectiveness was determined by swellometer-tests and by measuring the water uptake of samples after 24 hours complete immersion and by immersion in a water level of 4 mm for 24 hours. The different methods are compared and discussed. Artificial and natural weathering was performed to ...
D Lukowsky, R D Peek, A O Rapp
IRG/COIPM INTERNATIONAL MARINE TEST - to determine the effect of timber substrate on the effectiveness of water-borne salt preservatives in sea-water. Progress Report 3: Report of first inspection of samples at Lae, Papua New Guinea
1978 - IRG/WP 446
Samples for the international marine test were placed on frames numbered I to VII. Frames numbered VII of both CCA and CCB trials are being stored dry in the laboratory at F.P.R. & D.C. Frames I to VI of both trials were suspended in the sea at Lae Harbour (Morobe Province, Papua New Guinea) on 6th December 1977. The first inspection of the CCA trial was carried out on 8th June 1978, at which ...
S M Cragg, C R Levy
Preservative treatment of Gollah cane (Daemonorops jenkinsiana) by soaking method
2001 - IRG/WP 01-40197
The feasibility of preservative treatment of gollah cane (Daemonorops jenkinsiana (Griff.) Mart.) by soaking method was tested in the present study. Cane samples of 1m, 2m and 3m long were soaked with 10% borax and boric acid solution. The study revealed that adequate dry salt retention (DSR) in the above samples could be obtained in 3 days, 4 days and 5 days of soaking, respectively. Within these...
M Younus-uzzaman, K Akhter, M H Chowdhury
An appraisal of the vertical distribution of attack of untreated and treated wood by warm water sphaeromatids at some tropical sites - A discussion paper
1986 - IRG/WP 4124
Examples of the vertical distribution of burrows of warm water sphaeromatids relative to tide levels and mud line from sites in India, Papua New Guinea and tropical Australia are discussed in detail. These data show clearly that these animals concentrate their attack of resistant natural wood or resistant treated wood in the tidal zone, particularly around Mean Sea Level. Supportive evidence from ...
J E Barnacle, L J Cookson, C N McEvoy
The effect of rate of pressure application on preservative uptake along and across the grain of fir (Abies bornmulleriana Mattf.) at different ramp and constant pressure times
2004 - IRG/WP 04-20292
This study was particularly design to determine the preservative uptake at different ramp (rate of increase in pressure) and constant pressure times on longitudinal, tangential and radial penetrations of fir (Abies bornmulleriana Mattf.) which grown indigeneously in Turkey. The samples of 2 cm cubes of kiln-dried wood (nominated to 12% moisture content) were treated at different ramp times varied ...
I Usta
A field trial of water repellents as anti-sapstain treatment additives
1987 - IRG/WP 3417
The assessment of water repellents as anti-sapstain treatment additives has been included in a recent FRI research programme investigating improved surface protection of New Zealand Pinus radiata. Laboratory work has shown variation in water repellent effectiveness with chemical type and subsequently a field trial was established to examine the performance of selected water repellent/anti-sapstain...
J A Drysdale, D V Plackett
Water repellency of wood treated with alkylammonium compounds and chromated copper arsenate
2000 - IRG/WP 00-30231
The comparative water sorption properties of southern pine treated with CCA and several alkylammonium compounds was evaluated for freshly treated wood and for wood after exposure in a fungus cellar. It was found that CCA imparts considerable water repellency to wood which is reduced somewhat after exposure to wet soil. With the exception of a long chain (C20 -C22) compound, the alkylammonium compo...
D D Nicholas, A Kabir, A D Williams, A F Preston
Comparative field performance of CCA and CCA-water repellent treated Southern pine lumber
1995 - IRG/WP 95-30089
This paper describes the field performance of end-matched southern pine boards treated with either CCA type C or CCA type C containing an emulsion water repellent (WR) additive. Boards were either kiln or air-dried after treatment, constructed into decks, and exposed for over 3 years at Harrisburg, NC. During this exposure, matched boards were monitored for internal moisture content, cupping at mi...
A R Zahora
Detection of methanogenic bacteria in mining timber
1988 - IRG/WP 1352
Methane explosions in gold mines have been attributed to spontaneous ignition of methane/air mixtures. Biogenesis of methane in the heartwood of diseased trees has been shown, but never in timber in service. Studies were therefore undertaken to establish whether methanogens were present in wooden pit props. Core samples were removed by Pressler increment borer from props in disused areas 2,600 m d...
L D Abraham, K Westlake, R I Mackie, J F Putterill, A A W Baecker.
Interactions between water-borne preservatives and emulsion additives that influence the water repellency of wood
1991 - IRG/WP 2374
Incorporation of non-polar additives into water-borne treatments through of emulsion technology can greatly improve the physical characteristics of wood in service. Of specific interest with these emulsions is their effectiveness in reducing the rate of wood swelling. We have observed that the presence or absence of preservatives can often significantly influence the resultant effectiveness of the...
A R Zahora
Occurrence of wood-boring pholads in Kochi harbour waters (south-west coast of India)
1992 - IRG/WP 92-4175
The paper reports the occurrence of four species of wood-boring pholads (Pholadidae: Martesiinae), namely Martesia (Martesia) striata (Linnaeus), Martesia (Martesia) fragilis Verrill and Bush. Martesia (Particoma) nairi Turner and Santhakumaran and Lignopholas fluminalis (Blanford), in the Kochi back-waters, south-west coast of India. Of these Martesia nairi and Lignopholas fluminalis are now reco...
L N Santhakumaran, M V Rao
Influences of the hydro-thermal treatment on physical properties of beech wood (Fagus orientalis)
2005 - IRG/WP 05-40303
Influences of the hydro-thermal treatment on physical properties of beech wood were studied. Wood specimens (2×2×2cm) were treated in two steps. At first step, samples were treated at 160,180 & 200ºC for 4, 5 & 6 hours. At second step, treated samples were cured based on their first step treatment temperatures (160,180 & 200ºC) for 16 hours. The treated samples were soaked in water...
B Mohebby, I Sanaei