Assessment of losses of wood preservatives from treated wood by leaching into the environment
1993 - IRG/WP 93-50001-13
Wood preservative chemicals may be lost from treated timber by leaching into water or soil. The degree to which this might occur and its effect on the environment is difficult to assess quantitatively due to the absence of appropriate test methods. This paper describes work to assess test methodology capable of allowing the rates of loss of wood preservative from treated timber to be quantified. T...
R J Orsler, G E Holland
Some observations on causes of failure of preservative treated natural round transmission poles in Nigeria
1977 - IRG/WP 291
Treated natural round transmission poles in Nigeria have been discovered to be attacked underground as early as two years after planting. Termites and rot fungi attack the inner tissues and leave a pattern characteristic for the species of the pole. Tectona grandis, Nauclea diderrichii and Wide Pore pine, the major species for transmission poles in Nigeria show these attacks. A form of termite shi...
M A Odeyinde
Observations on the failure of anti-sapstain treated timber under non-drying conditions
1990 - IRG/WP 1437
A range of bacteria and yeasts were isolated from antisapstain treated timber and fresh sawdust. Solution samples containing 100 ppm of TCMTB in a nutrient medium were inoculated with these organisms and incubated at 25°C for 5 days. The levels of TCMTB remaining in solution were determined by HPLC analysis after this time. Results indicated high losses of active ingredient for a range of organis...
G R Williams
Comparison of decay rates of preservative-treated stakes in field and fungus cellar tests
1980 - IRG/WP 2135
With the exception of acid-copper-chromate, zinc-chrome-arsenate, and sodium pentachlorophenoxide, the relative performance of preservatives in the fungus cellar was similar to that in the field....
M E Hedley
A comparison of the effectiveness of a vacuum oven and a wind tunnel in the accelerated ageing of treated wood by evaporation
1989 - IRG/WP 2334
R J Orsler, G E Holland
X-ray analysis of selected anatomical structures in copper/chrome/arsenic treated wood
1973 - IRG/WP 320
Application of analytical electron microscopy to problems in wood preservation has been very limited. Indeed, less than ten workers appear to have published their results using the technique, and of these' only two papers deal with energy dispersion procedures in the scanning electron microscope; the others employ the more familiar wavelength dispersive methods of the electron probe....
H Greaves
Above ground performance of CCA-treated fingerjointed lumbe
1993 - IRG/WP 93-40003
Studs made from short lengths by finger jointing are becoming more commonly used in North America. Recently Forintek has received enquiries about the performance of such material in a treated form. Treated and untreated nominal 2x4 inch² spruce-pine-fir (SPF) studs exposed above ground for 12 years in southwestern British Columbia were evaluated for evidence of decay. Despite shallow preservative...
P I Morris, G E Troughton
Fire resistance of Alder wood treated with some chemicals.
Part II. Effect of Other Chemicals on the Combustion Properties
2002 - IRG/WP 02-40235
Samples from alder wood (Alnus glutinosa (L.) Gaertn. subsp. barbata (C.A.Mey) Yalt.) were impregnated according to ASTM D 1413-88 with boron compounds (boric acid, borax,
sodium perborate), vinyl monomers (styrene, methyl methacrylate), Tanalith-CBC, Phosphoric acid, Vacsol, Immersol, Polyethylene glycole (PEG-400) and their mixed solutions of chemicals in order to determine their combustion pro...
A Temiz, Ü C Yildiz
Leaching of Active Components from Preservative Treated Timber. Stage 1: Semi-Field Testing
2004 - IRG/WP 04-20302
The project is aiming at finding realistic leaching rates from preservative-treated wood in use class 3 (above ground). The project focuses on developing a field trial method for investigating leaching.
Panels are subjected to outdoor exposure under natural weather conditions at a test field at the Danish Technological Institute. The leachate is collected and monitored by chemical analysis of the...
N Morsing, B Lindegaard
Performance of surface-treated hardwoods and softwoods out of ground contact
1990 - IRG/WP 3592
A number of fungicides were tested as brush treatments for protection of southern pine, Douglas-fir, maple, and red oak against decay above ground. Cross-brace and L-joint test units were treated just before assembly and exposed from 3-10 years. Untreated Douglas-fir cross-brace units were not decayed at either the Mississippi or Madison, WI, site. Untreated red oak cross-brace units were not deca...
T L Highley
Reworded resolution
1976 - IRG/WP 145
New evidence has demonstrated that certain timber species are unexpectedly difficult to protect against biological degradation by the use of known preservation systems. Several of these timber species are expected to become of wide commercial use in the future. The issues raised are of such fundamental importance and require so intensive basic research that official bodies should be encouraged to ...
B Henningsson
A laboratory soil-block decay evaluation of plywoods edge-treated with preservatives
1982 - IRG/WP 2174
Preservative-treated plywood used under conditions or severe decay hazard frequently has its original, or cut edges, protected by the application of a field-cut preservative. This study uses a laboratory test method to compare the efficacy of four commercial preservative treatments against two commonly occurring brown-rot fungi. The results are not meant to indicate the service life of such treate...
R S Smith, A Byrne
Biodegradation of creosote/naphthalene-treated wood in the marine environment
1977 - IRG/WP 428
The present study was undertaken to determine the biodegradability of marine grade creosote and selected components, including naphtalene, and to determine the effectiveness of (up to 40%) creosote in protecting wood from microbial attack. Also, the impact(s) of creosote and naphtalene-enriched creosote on the microbial ecology os estuarine environments was examined....
P A Seesman, R R Colwell, A Zachary, A J Emery
Preservative-treated wood as a component in the recovered wood stream in Europe – A quantitative and qualitative review
2004 - IRG/WP 04-50218
Wood preservatives have been used for the protection of timber products in the European market in appreciable quantities for about 100 years. Between the 1960s up to the present day this usage has been particularly noticeable. The aim of this paper is to present quantitative and qualitative data on the volumes of preservative treated wood placed on the market in the UK and Sweden and to evaluate t...
R J Murphy, P Mc Quillan, J Jermer, R-D Peek
Current and future options for managing used preservative-treated wood
1995 - IRG/WP 95-50042
The amount of preservative-treated wood available for disposal will continue to increase exponentially in the next several decades as landfill availability declines. At the same time, recent legal ruling on competitiveness among utilities and disposal of ash has clouded the economic outlook for combustion of treated wood for energy recovery. This report identifies current and future options for ma...
R C De Groot, C Felton
nvestigation of anomalous fixation and leaching of CCA-treated red maple
2004 - IRG/WP 04-30341
The fixation of CCA-C preservative was investigated in red maple sawdust (Acer rubrum L.) at target retentions of 4.0, 6.4, 9.6 and 30.0 kg/m3. The effect of water-soluble extractives on the course of fixation was evaluated comparing the non-extracted with pre-extracted samples treated to 6.4 and 30 kg/m3. Leaching of the CCA components was monitored after complete fixation for all retentions. Fix...
S Radivojevic, P A Cooper
Ultrastructural and TEM-EDAX studies on the degradation of CCA treated radiata pine by tunnelling bacteria
1985 - IRG/WP 1260
An ultrastructural study was carried out on bacterial attacked Pinus radiata stakes treated with a high level (24.7 kg/m³) of Tanalith NCA preservative. The purpose of the investigation was to determine whether the organism possessed intracellular and/or extracellular detoxification mechanisms in order to overcome the high levels of copper, chrome and arsenic present within the wood fibre walls. ...
G F Daniel, T Nilsson
Co-operative Field Experiment: Performance of preservative-treated timber: Report on condition of specimens after seven years installed in New South Wales - Australia
1986 - IRG/WP 3362
R S Johnstone
Surface coatings for impregnated wood
1992 - IRG/WP 92-3684
The use of proper surface coatings enhances the aesthetic and protective properties of impregnated wood. Good results with especially water-borne coatings have been obtained for class-A impregnated L-joints and claddings in field tests started in 1982....
L Kotama
Ecotoxicological risks of anti-sapstain preservatives washed off from treated timber
2000 - IRG/WP 00-50144
A field method for ecotoxicity assessment of rain water wash-off from anti-sapstain treated timber was developed. In the course of this study freshly sawn timber treated with 1.5% Busan 30 L (reference preservative) and a control stack with untreated pine were exposed to weathering. The run-off water was ecotoxicologically tested with organisms from three trophic levels (Vibrio fischeri, Kirchneri...
G Aschacher, R Gründlinger
Use of biossay to determine CCF and CCB preservative retentions in treated Pinus sylvestris
1984 - IRG/WP 2216
The retention of each a copper/chromium/boron and copper/chromium/fluoride preservative in pressure treated pinepoles was tested by bioassay using Aspergillus niger as test fungus. Small samples of 5 mm³ were taken from various depth of the poles and placed on potato-dextrose agar plates. The inhibition of fungal growth depends on the preservative retention in the cubes and corresponds closely to...
J C Moreschi, H Willeitner
Evaluation of wood treated with copper-based preservatives for Cu loss during exposure to heat and copper-tolerant Bacillus licheniformis
1999 - IRG/WP 99-20155
Copper-based wood preservatives need to be effective against exposure to all types of microorganisms. Wood treated with six copper-based preservatives was exposed to 121°C and 20 psi pressure for 15 minutes under standard autoclave conditions and the copper-tolerant bacterium, Bacillus licheniformis CC01, for 10 d at 28°C and 150 rpm. Sixteen to 37 percent of the copper was released from the woo...
D M Crawford, C A Clausen
Short term preconditioning of preservative-treated wood in soil contact in relation to performance in field trials
2000 - IRG/WP 00-20185
The effect of pre-exposure to primary colonising micro-organisms on preservative-treated wood, prior to a basidiomycete decay test, was determined by preconditioning in two soil types. Scots pine EN 113 blocks treated with 3 model systems (a triazole, a copper quaternary compound and a copper boron triazole) were leached according to EN 84 and subjected to 6 weeks and 8 weeks burial in either John...
S Molnar, D J Dickinson
Biological and chemical observation on the early fungal colonization of TBTO treated Swedish redwood stakes
1984 - IRG/WP 3311
Data on the early fungal colonization of Swedish redwood stakes, impregnated with 1% TBT0 / 0.5% dieldrin solution, both by double vacuum impregnation and immersion processes are presented. Results of chemical analyses of wood samples from the outer 1 mm of separate painted and unpainted stakes, exposed over the same twelve month period, are also discussed....
R Hill, A H Chapman, A Samuel, K Manners, G Morton
The performance of glue laminated railway ties after 40 years of service in the main line track
1989 - IRG/WP 2325
Two series of horizontally glue laminated ties made of a softwood body and topped with a hardwood lamination were creosoted and installed in 1947 in a tangent and a curved main line track. The tests are now 40 years old and the excellent condition of the ties of these two series suggest that a service life of 50-60 years can be expected....
J P Hösli, E E Doyle, C P Bird, T Lee