Influences of the hydro-thermal treatment on physical properties of beech wood (Fagus orientalis)
2005 - IRG/WP 05-40303
Influences of the hydro-thermal treatment on physical properties of beech wood were studied. Wood specimens (2×2×2cm) were treated in two steps. At first step, samples were treated at 160,180 & 200ºC for 4, 5 & 6 hours. At second step, treated samples were cured based on their first step treatment temperatures (160,180 & 200ºC) for 16 hours. The treated samples were soaked in water...
B Mohebby, I Sanaei
Microbial decay in an extremely durable Malaysian hardwood Belian (Eusideroxylon zwageri) - an overview
1997 - IRG/WP 97-10216
The heartwood of Belian (Eusideroxylon zwageri) is highly regarded among the naturally durable Malaysian hardwoods, and is therefore a choice timber for soilcontact use in the humid tropics such as untreated telecommunication poles, fence posts and railway sleepers. The high microbial resistance of the wood is evidenced by the mere superficial degradation observed in some pole samples after 20 yea...
A H H Wong, A P Singh
Assessing the importance of degradation mechanisms on the loss of effectiveness of wood preservatives
2000 - IRG/WP 00-20193
Accelerated ageing systems developed for application to samples in the laboratory prior to biological tests, should reflect those natural deterioration processes that are likely to occur in the hazard classes defined in EN 335-1. Losses through evaporation or the effects of leaching have been recognised, however their importance, relative to other mechanisms has not been quantified. Degradation me...
E D Suttie, R J Orsler, T Dearling
Thermal modification of non-durable wood species 2. Improved wood properties of thermal treated wood
1998 - IRG/WP 98-40124
Properties of wood treated in a new heat-treatment process called the PLATO-process have been studied. Several wood species have been treated using this new thermal modification process using a range of process conditions (mainly time and temperature). In this study the characteristics of the treated wood were determined using samples from whole planks treated on pilot plant scale. The modified ch...
B F Tjeerdsma, M J Boonstra, H Militz
Bacterial degradation of Pinus radiata compression wood
1996 - IRG/WP 96-10153
An inspection of twelve year old, CCA-treated Pinus radiata wood from an industrial cooling tower showed extensive surface decay of wood. Electron microscopic examination of decaying compression wood indicated that compression wood cells were attacked exclusively by bacteria, which were of erosion and tunnelling types. As compared to the normal wood, compression wood appeared to be more resistance...
A P Singh, R N Wakeling
Properties of cellulose degraded by the brown rot fungus, Postia placenta
1988 - IRG/WP 1350
To gain further understanding of the nature of the cellulose depolymerizing agent or agents of brown-rot fungi, brown-rotted cellulose was chemically and physically characterized. Various culture conditions, such as low nitrogen and elevated oxygen levels, did not induce degradation of cellulose by Postia placenta in liquid cultures. Therefore, brown-rotted cellulose for analysis was prepared by a...
T L Highley, R E Ibach, T K Kirk
The influence of drying and chemical stress on the lignin degradation in aspen by Phanerochaete chrysosporium
1992 - IRG/WP 92-1573
Wood wafers of Populus tremuloides sapwood were incubated on common media with the white rot fungus Phanaerochaete chrysosporium (wild isolate) and subjected to cyclic drying or chemical agents (low levels of borate or trifluoperazine [a calmodulin antagonist]). After a mass loss of approximately 5.5%, wafers were dried and analyzed for acid-insoluble lignin. Those wafers containing chemical agent...
E L Schmidt, Y-L Lin
Targeted inhibition of wood decay fungi: degradation of cotton cellulose
1999 - IRG/WP 99-10321
Brown-rot decay is responsible for 80% of the damage and replacement of wood in service. For nearly thirty years, researchers have postulated a one-electron oxidase system combining Fe+2 oxalic acid, and H2O2 in the production of hydroxy radicals which ultimately oxidize cellulose in situ. Recently, researchers have been investigating antioxicants, in combination with biocides (Schultz, et al.,199...
F Green III, T A Kuster
Experiments on the degradation of tributyltin oxide: A progress report
1984 - IRG/WP 3287
A variety of experiments designed to assess the chemical and physical factors affecting the degradation of tributyltin oxide in treated timber are described. Simple procedures in which temperature and oxygen availability were increased in the presence of wood and water suggest that the wood itself was of prime importance. Attempts to decrease degradation with antioxidants were unsuccessful but led...
R J Orsler, G E Holland
Deterioration of wood viewed from iron nail
1991 - IRG/WP 2368
Deterioration of nail was graded by a five - rank numerical - rating. The rating of nail moisture content and decay of wood were inspected in a mortal-wall of 34-year-old house. The wood was mostly in decay, when the rating of the nail was above about 4, and the moisture content was above about 20%. Nailed wood specimens kept in several humidity room of 20°C for 4 years showed that the rating of ...
H Imamura
Soft-rot in Tabebuia sp. wood used in water cooling tower:
identification and degradation capacity of the fungi
1998 - IRG/WP 98-10253
Tabebuia sp. (ipe), a native Brazilian wood, is considered of high natural resistance to decaying fungi, and has been used in harsh environments, as cooling towers. Fifty-one fungi, belonging to mitosporic fungi group (Fungi Imperfecti), were isolated from deteriorated Tabebuia sp. wood samples, collected from the mist eliminator and packing of a cooling tower in operation for about 23 years. The ...
S Brazolin, M Tomazello, I H Schoenlein-Crusius
Some practical implications from recent research on the fixation of CCA preservatives
1975 - IRG/WP 358
The mechanism of fixation of CCA preservatives is briefly described. If the temperature is increased during the primary fixation period, the formation of intermediate fixation compounds is less extensive. The length of the primary fixation period is of practical interest. It is determined by preservative composition and concentration, temperature and wood species. Diagrams are given for Pinus sylv...
S-E Dahlgren
Termiticide degradation in Mississippi field tests
1994 - IRG/WP 94-30052
Degradation rates of some currently marketed United States termiticides are currently being studied. Separate quantities of soil were each treated at lowest label rates with termiticide, and placed in trenches along the inside and outside of concrete walls. Composite soil samples, each consisting of four soil cores, were collected after 1, 30, 60, 120, 180, 240, and 365 days, and again at 2 and 3 ...
B M Kard
Application of non-destructive techniques (durometric and ultrasonic) to evaluate the degradation of woods in service by Gloeophyllum trabeum
2001 - IRG/WP 01-20220
In order to establish the degree of degradation of wood used in construction, it is necessary to employ non-destructive methods (ultrasonic, durometric, densitometric). In this study, ultrasonic and Pilodyn durometric techniques have been applied to try to establish parameters of relationship between the values obtained by both, for their immediate application to wood in service. As a method of re...
M T De Troya, L Palaia, A Navarrete, V Galvañ, R Molina, A Guijarro, J Camacho
Ammoniacal wood preservatives for use in non-pressure treatment of spruce and aspen poplar. Part 2
1984 - IRG/WP 3274
A series of thermal diffusion treatments were carried out on unseasoned white spruce (Picea glauca (Moench) Voss) lumber and air dry aspen poplar (Populus tremuloides Michx.) timbers using an ammoniacal copper arsenate wood preservative. Under the specific conditions described, certain charges of lumber met the present Canadian Standards Association Wood Preservation Committee's requireme...
C D Ralph, J K Shields
The quantitative determination of N-cyclohexyl-diazeniumdioxide (HDO) containing compounds in treated wood using TD-GC-MS
2001 - IRG/WP 01-20223
Last year we presented the paper (IRG/WP/00-20201) "Determination of N-cyclohexyl-diazeniumdioxide (HDO) containing compounds in treated wood using GC-MS". Based on the intensive discussion at the meeting, the first experiences made with the calibration of the system for this application will be reported. For the quantitative determination of N-cyclohexyl-diazeniumdioxide in treated wood, milled m...
P Jüngel, J Wittenzellner, E Melcher
Ultrastructure of Prumnopitys ferruginea wood from a buried forest in New Zealand
1991 - IRG/WP 1489
The buried wood of Prumnopitys ferruginea, a New Zealand native tree, was examined by scanning and transmission electron microscopy to investigate the extent to which the wood had deteriorated and the cause of its deterioration. Examinations showed that some deterioration of wood had occurred. Microscopy revealed a decay pattern similar to that produced by cavitation bacteria. Lenticular cavities ...
A P Singh, T Nilsson, G F Daniel
16S rRNA Analysis of the Bacteria Associated with Biocide Degradation
2004 - IRG/WP 04-10543
The bacterially mediated degradation of the new anti-fungal biocide, bethoxazin, was studied in vitro, by means of 16S rRNA PCR-amplification and cloning techniques. Woodblocks impregnated with a subtoxic concentration of bethoxazin were incubated in compost, and the micro-organisms associated with the wood after 6 and 12 weeks was studied. It was found that after 6 weeks the wood contained a la...
D F Wallace, D J Dickinson
Evidence for actinomycete degradation of wood cell walls
1990 - IRG/WP 1444
Several unique patterns of degradation occurring in wood cell walls have been observed in wooden stakes inserted in unsterile soil in the laboratory. Some of the patterns have also been observed in coniferous wood taken from forest floors. All the observed attack types occur within wood cell walls, mainly within the S2 layer. Attack is characterised by channels of varying diameter or small fusifor...
T Nilsson, G F Daniel, S L Bardage
The influence of staining fungi on the decay resistance of wood treated with alkylammonium compounds
1984 - IRG/WP 3308
Although found to be very effective in laboratory tests, alkylammonium compounds (AAC's) have failed to perform as well in field stake tests. Examination of leachability showed that this was not the cause. The present study investigated the possibility that staining fungi, (which have been observed to rapidly infect the field stakes), degrade the AAC wood preservative. Soil-blocks were tr...
J N R Ruddick
Preference of swarming termites for various colored lights
1984 - IRG/WP 1238
The ability of the alates of the drywood termite Bifiditermes beesoni (Gardner) to discriminate ten different colored lights was studied. When an alternative choice of any of two colors was offered, the light-blue was preferred to all other tested colors by 97.7% of the alates. A lower degree of attractivity was found for some other colors and certain other colors were indistinguishable. Furthermo...
M Afzal
Wood and filter paper degradation, phenol oxidase and one-electron oxidation activities by the white rot fungus Ceriporiopsis subvermispora
2003 - IRG/WP 03-10486
The activities of one-electron oxidation and phenol oxidase during incubation of cultures of the white-rot basidiomycete Ceriporiopsis subvermispora containing either glucose or wood were periodically measured. Further, the degradation activities against wood and filter paper were examined during the course of cultivation. Weight losses of Japanese beech wood and Japanese cedar wood after 12 wee...
H Tanaka, S Itakura, A Enoki
Chemical and biological investigations of double-vacuum treated windows after 5 years in service
1983 - IRG/WP 3219
In 1980 The Swedish Wood Preservation Institute initiated an investigation to study the degradation of TBTO and possible fungal attack in double-vacuum treated window joinery in service during 5 years. A hospital in Gothenburg was chosen that was built during 1969 to 1976. Both untreated and double-vacuum treated windows of Pinus sylvestris were used. A brown alkyl oil type paint (Nordsjö system ...
J Jermer, M-L Edlund, B Henningsson, W Hintze, S V Ohlsson
Immunolocalization of extracellular metabolites from Poria placenta
1988 - IRG/WP 1361
Polyclonal antisera produced to Poria placenta extracellular metabolites was used in immuno-fluoresence microscopy and immuno-gold TEM studies. In the fluorescence work, labelling of Poria placenta hyphae in wet fixed wood material was observed but not in infected wood which was oven dried prior to sectioning and immunolabelling. TEM studies provided better resolution, with gold labelling detected...
B Goodell, G F Daniel, J Jellison, T Nilsson
Effects of wood-inhabiting marine fungi on food selection, feeding intensity and reproduction of Limnoria tripunctata Menzies (Crustacea, Isop.)
1981 - IRG/WP 480
The paper gives a condensed survey on laboratory tests with Limnoria tripunctata Menzies and pure cultures of 9 different marine wood-inhabiting fungi. Limnoria is able to distinguish between fungus-infested and non-infested wood. Wood with dead mycelium mostly proved to be less attractive or even repellent and was initially consumed less than with living fungi. On non-infested wood, initial feedi...
H Geyer