Mold resistance of heat-treated wood
2007 - IRG/WP 07-40358
The resistance of heat-treated sugi sapwood against three mold fungi was evaluated. Wood specimens were first subjected to heat treatments at 180 and 220ºC for 2 and 4 hours. Mold growth on the surface of the specimens was measured 1, 2, 4 and 6 weeks after the inoculation with the fungi in laboratory conditions. Laboratory decay tests were performed using two brown and white-rot fungi along with...
S N Kartal
The effects of chemical modification on the biological properties of alder and spruce particleboards
2007 - IRG/WP 07-40363
This study is evaluated by measuring the weight loss, and the ability of white and brown-rot fungi to attack unmodified and modified particleboards manufactured using spruce (Picea orientalis (L.) Link.) and alder (Alnus glutinosa) chips. The chips were reacted with acetic, succinic, maleic and phthalic anhydride at constant temperature for 3 hours then, hot pressed at 150 °C by using phenol for...
Ü C Yildiz, E Dizman, S Yildiz, A Temiz, M Aslan, E D Gezer
Multivariate analysis of infrared spectra for the prediction of the mechanical performance and dimensional stability of thermally modified wood
2007 - IRG/WP 07-40367
The use of calibrated mid-infrared Fourier transform (FTIR) spectroscopy for predicting the main bending strength parameters of thermally modified wood is described for the first time. The analysis is based on the handling of OSC-filtered FTIR data from control and treated wood samples, using partial least squares (PLS) regression.
Sets of Norway spruce, Scots pine and Beech wood samples were th...
M M González-Peña, M D C Hale
Fire Safety of Wood Floor Assembly: Model and Full-scale Test
2007 - IRG/WP 07-20375
The present paper describes the model for the prediction of fire safety of wood floor assemblies. The model includes heat transfer model for the calculation of the flow of heat in floor assembly and structural model for the analysis of the mechanical performance of wood joists. The floor assemblies considered in this paper are constructed with nominal 2x10 (38x241mm) wood joists lined by Type X ...
H Takeda
Decay Resistance Properties of Hemicellulose-Extracted Oriented Strand Board
2008 - IRG/WP 08-10644
There is increasing interest in using cellulosic biomass as the basis for a renewable source of energy. Although the traditional focus has been on cellulose, researchers are also exploring the possibility of using hemicelluloses because they can be removed with hot water leaving the wood product intact for other applications. However, there is concern that removing hemicelluloses from the precur...
C Howell, J Paredes, S Shaler, J Jellison
A step towards a better understanding of fungal colonization of modified wood - QRT-PCR studies
2008 - IRG/WP 08-10653
The area of wood protection is in a period of change. New wood protection systems have been developed while their mode of action remains insufficiently understood. The development of molecular methods provides potential tools to investigate the interaction between modified wood and decay fungi. One small step to tackle some of the unsolved questions about the mode of action of modified wood is tak...
G Alfredsen, A Pilgård, A Hietala
Evaluation and identification of extractives from Iranian walnut (Juglans regia L.) by GC/MS technique for protection of non-decay resistant species
2008 - IRG/WP 08-10670
The use of walnut extractives is interest as environment friendly wood preservatives in the wood preservation industry. In this study, organic solvents were used to remove extractives from Iranian walnut heartwood samples. The solvent was removed by rotoevaporation, and Identification of chemical compounds in the Walnut extractives was done by using GC/MS technique. The toxicity of various extract...
S K H Hashemi, D Parsapajouh, H Khademi Eslam
Relationship between coating properties and their performance on treated wooden decks
2008 - IRG/WP 08-30454
Preservative treated wood benefits from the application of a surface coating to protect it from weathering (UV and rain). Different preservative formulations may affect surface properties of treated wood differently; therefore compatibility of coatings with different preservative treated wood types should be considered. This paper examines coatings characteristics and their weathering performance ...
M Ahmadinejad, P A Cooper
Mechanical strength of wood from the Vasa shipwreck
2008 - IRG/WP 08-20381
Samples from three ancient ship wrecks (Vasa, Elefanten, and Gröne Jägaren) and recent oak samples as reference were examined with regard to mechanical strength using the high-energy multiple impact (HEMI) - test method, which delivers the resistance to impact milling (RIM) of a material. Adoption and optimisation of the test method for the particular sample size of the wooden drilling cores was...
A O Rapp, C Brischke, C R Welzbacher, T Nilsson, C Björdal
Influence of Polyvinyl acetate emulsion (PVA) on boron leaching and fungicidal properties
2008 - IRG/WP 08-30451
Boron compounds are very effective fungicides, but unfortunately they leach from wood. In order to improve boron fixation, boric acid, borax were combined with polyvinyl acetate emulsion (PVA). For comparison copper salts were included into this research as well. Selected preservative solutions were chosen for impregnation of Norway spruce wood specimens (Picea abies). Wood blocks were exposed to ...
M Humar, B Lesar, P Kralj
Investigation into the antifungal properties of herbal remedies for potential use in the wood preservation industry
2008 - IRG/WP 08-30462
The efficacy of herbal remedies as potential antifungal agents was evaluated against two sapstain and three decay fungi. Sapstain fungi included Sphaeropsis sapinea, and Leptographium procerum, and decay fungi were Oligoporus placenta, Coniophora puteana, and Schizophyllum commune.
Out of six herbal remedies tested, three showed moderate to high antifungal activity. Caprylic acid had high antif...
D O’Callahan
The effect of gamma radiation on selected wood properties
2008 - IRG/WP 08-40394
As an easy, fast, and effective sterilisation method, gamma irradiation changes molecular structures not only in pest’s living cells, but also in wooden cell walls. Radiation-induced depolymerisation causes significant changes in some properties of wood crucial for restoration and for laboratory testing of wood-preservative effectiveness. The influence of gamma radiation concerning total amount ...
R Despot, M Hasan, A O Rapp, C Brischke, C R Welzbacher
Preliminary investigation of biological resistance, water absorption and swelling of thermally compressed pine wood panels
2008 - IRG/WP 08-40396
Wood can be modified by compressive, thermal and chemical treatments. Compression of wood under thermal conditions is resulted in densification of wood. This study evaluated decay and termite resistance of thermally compressed pine wood panels at either 5 or 7 MPa and at either 120 or 150?C for one hour. The process caused increases in density and decreases in thickness of the panels; however, lab...
Ö Ünsal, S N Kartal, Z Candan, R Arango, C A Clausen, F Green III
Heat treatment, thermal treatment, thermal degradation of wood, carbon nanotubes and Damascus steel swords. What do they all have in common?
2008 - IRG/WP 08-40399
Thermal degradation of wood is a well known phenomenon. Yet heat-treatment of wood can also provide protection for wood against certain environmental hazards. This paper explores some of the aspects of thermal degradation of wood fiber at relatively low temperatures with a surprising result. Carbon nanotubes (CNTs) were produced when a specific heating regime was used to carbonize the wood fiber. ...
Xinfeng Xie, B Goodell, Yuhui Qian, G Daniel
Thermal treatment of Nigerian-grown Albizzia zygia and Funtumia elastica wood in soy oil medium.
2008 - IRG/WP 08-40413
Thermal treatment in soy oil medium is one of the techniques used as a substitute to the chemical treatment in wood preservation. However, the effects of this technique vary from one species to another and hence the need to investigate the response of individual species to it. Thermal treatment of air-dried Nigerian-grown Albizzia zygia and Funtumia elastica wood was carried out in a vessel contai...
L Awoyemi
Bending Properties of Southern Pine Treated with Micronized Preservative Systems
2008 - IRG/WP 08-40414
This study indicates that treatment of southern pine with micronized copper systems have no
deleterious effect on the residual strength property values. No statistical differences between wood treated with micronized systems and water-treated controls were noted when means were compared using either Tukey’s test or S-N-K mean comparison tests. Using the more discriminating Least Squares anal...
H M Barnes, G B Lindsey, J Hill, M Pompeo, R Hodge
The effect of treatments in boron steaming medium on boron leaching and strength properties of wood
2008 - IRG/WP 08-40409
The combined effect of boric acid impregnation together with boron steaming and steaming heat treatments were evaluated in this study. Boric acid pre-treated wood samples and untreated ones subjected to steaming heat and direct steaming treatment in a close reactor at 13 bar pressure and 180 ºC for 30 minutes. Compression strength parallel to grain of wood samples, leaching test and pH measuremen...
E D Tomak, Ü C Yildiz, S Yildiz, E Pesman
Effects of planning and sanding on penetration and retention properties of some softwood species treated with copper azole
2008 - IRG/WP 08-40410
This work investigates the effect of some woodworking treatments on penetration and retention properties of four different (scotch pine—SP, Siberian scotch pine—SSP, Siberian larch—SL, and oriental spruce—OS) heartwood species with the waterborne preservative copper azole (CBA-A). A 2.4% active ingredient solution of CBA-A was applied for use in vacuum/pressure treatment of the heartwood s...
Ü C Yildiz, S Yildiz
Material properties of acetylated beech plywood
2008 - IRG/WP 08-40425
The effect of acetylation process on dimensional stability and mechanical properties of plywood made by Oriental beech layers (Fagus orientalis Lipsky) were studied. The layers cut into sizes of 200×200×2 mm and acetylated in 120°C for 30 and 60 min.
Thickness swelling (TS%), water absorption (WA%) and anti-swelling¬ efficiency (ASE%) of specimens were measured. Mechanical properties (MOE, MO...
A Talaei
High Temperature Treated Wood
2008 - IRG/WP 08-40429
High temperature can modify internal structure and physic-chemical properties of wood by a controlled pyrolysis process. Such treatment, among other changes in properties, modifies the wood color in a way that resembles exotic species, increasing its market value. The main objective of this work is to determine the changes in wood properties caused by the effect of temperature and time, in order t...
C C Borges, A L Barbosa, R Faber de Campos, S T Targas
Leaching properties of copper and triazole
2009 - IRG/WP 09-30509
The leaching rate of copper and triazole (such as tebuconazole and propiconazole) in different preservative formulations was determined according to AWPA E11-06. Of all copper triazole and ACQ formulations, copper fixation rate of ammonia based was higher than that of ethanolamine based and the mixture of them. Copper fixation rate at relatively higher retention was slight higher than that at lowe...
Zhiqiang Li, Xiaowen Li, Ying Zhang, Mingliang Jiang
Thermal behavior of zinc borate-treated wood
2009 - IRG/WP 09-30511
The objective of this study was to investigate the thermal behavior of zinc borate (ZnB)-treated solid wood by thermal analysis (TA). Thermogravimetry (TG) and differential thermogravimetry (DTG) curves obtained from TA showed that ZnB-treated wood specimens had higher char yields and lower maximum thermal decomposition temperature than untreated wood specimens. Reducing thermal decomposition temp...
E Terzi, H Sutcu, S N Kartal
Use of wax emulsions for upgrading of wood properties
2009 - IRG/WP 09-40451
Waxes are used for treatment of wood surfaces for several decades, predominately as surface treatments, because they did not penetrate into the wood. In order to overcome this issue, water emulsions were applied in present experiment. Five water emulsions of various concentration was used namely; two emulsions of montan wax (LGE, MW1), emulsion of polyethylene (WE1), emulsion of ethylene copolymer...
B Lesar, F Pohleven, M Humar
Wettability and bonding strength of wood thermally-treated with different combinations of soy oil and chemical additives
2009 - IRG/WP 09-40454
Thermal treatment is a method which has gained wider acceptability as an alternative to the chemical treatment in wood preservation. In order to maximize the benefits of this technique several options have been adopted including the use of soy oil in transferring the heat to the wood. Available information on thermal treatment in general and the oil method in particular show that there are still n...
L Awoyemi, P A Cooper, T Ung
Barefoot-heat-impact of oil-heat-treated wood: An important thermal property of decking boards
2009 - IRG/WP 09-40458
In this study the phenomenon of sensual heat impression was examined, when walking with bare feet on sun exposed wood based decking boards. A suitable method for measuring the heat flux from decking boards into an artificial foot was developed. The method and measuring device is described as well as results from measuring three different decking board materials: Oil-heat-treated spruce (OHT), untr...
A O Rapp, C R Welzbacher, C Brischke