Colour change monitoring of photodegradation in Scots pine (Pinus sylvestris) – a short term focus
2009 - IRG/WP 09-40442
Colour change monitoring of photodegradation is a quick and easy method for monitoring rates of photodegradation in timber. A study was undertaken to compare this technique to other monitoring methods, including microtensile strength changes and weight loss. Colour changes due to accelerated sunlight exposure were monitored using a Datacolor check spectrophotometer and compared with a set of contr...
V Sharratt, C A S Hill, D P R Kint
Wood properties influencing the penetration of Scots pine (Pinus sylvestris) sapwood with the wood modification agent furfuryl alcohol
2009 - IRG/WP 09-40470
The European standard EN 350-2 classifies Scots pine sapwood as class 1 (easy to treat). However large variations in sapwood penetration exist which affect a homogenous distribution of preservatives. Hence individual penetration schemes have to be developed and adjusted to the material most difficult to treat in order to provide adequate sapwood penetration. To ensure better economic process con...
K Zimmer, E Larnøy, G Koch
Microscopy evaluation of microbial decay patterns in wood stakes after 6 years in soil contact
2010 - IRG/WP 10-10715
Most studies on wood modification have so far been concerned with service life predictions rather than investigating the decay protection mechanism. Very little is known about the mode of action of these new treatments and about the strategies used by wood degraders in order to utilize the wood material despite a treatment. Access to such knowledge would allow further modification and improvement ...
A Pilgård, C G Björdal
Adsorption of ionic liquids by Scots pine wood (Pinus sylvestris L.) and beech (Fagus sylvatica L.): equilibrium and kinetic modeling
2010 - IRG/WP 10-20447
In this paper methods for the adsorption study of quaternary ammonium-based ionic liquids on Scots pine (Pinus sylvestris L.) and beech (Fagus sylvatica L) are presented. Kinetic and equilibrium adsorption of compounds were evaluated. The equilibrium data fitted very well to the Langmuir adsorption models. The highest correlation coefficients determined from the pseudo-second order kinetic model ...
J Zabielska-Matejuk, A Stangierska, M Kot
Chemical protection of historic timber structures: Results and future needs
2010 - IRG/WP 10-40487
The paper concentrates on the analysis of the effectiveness of chemical protection for timber structures in the Russian State Museums “Kizhi” (Karelia) and “Vitoslavlitsy” (Novgorod).
The condition of historic timber was tested at the monuments treated with PCP, borax, potassium carbonate, boric acid, Pinotex chemicals in the 1970-80. Long-term analysis revealed that in many cases the...
M Kisternaya, V Kozlov
Comparison of exterior performance of two coating systems based polyurethane applied Pinus sylvestris L. and Picea orientalis L. wood
2012 - IRG/WP 12-40588
Some surface changes in sapwood and heartwood of two species before applying clear-coating were characterized after accelerated weathering time. Wood specimens covered with two types polyurethane (PU) films were also observed in accelerated weathering exposure. In this study, changes on the wood surface were compared of between wood specimens covered with two types polyurethane (PU) films after ir...
Ö Özgenç, Û Cafer Yıldız
Effect of preservative treatment on mechanical performance of round and square poles made of small diameter Scots pine
2012 - IRG/WP 12-40612
A growing proportion of harvested Scots pine (Pinus sylvestris L.) timber originates from the first or second commercial thinning stands. There is a need to find economically viable and high quality wood products that can be manufactured from this raw material. Small log volume means not only demands of increased efficiency for material handling in logistics and manufacturing processes, but also c...
V Möttönen, R Stöd, K Heikkilä, H Heräjärvi
Water absorption and desorption of non treated, pressure impregnated, and pine oil treated glulam made of small diameter Scots pine and Norway spruce
2012 - IRG/WP 12-40616
A growing proportion of harvested timber originates from the first or second commercial thinning stands in Finland, which means smaller average log volumes in comparison to final felling stands. Smaller log volume means challenging wood properties such as higher proportion of juvenile wood and sapwood. Due to these facts, products made of small diameter logs are prone to twist and check, and have ...
H Heräjärvi, V Möttönen, R Stöd
Inhibitory extractives or nutrients? Mould growth on coated heartwood and sapwood of Pinus sylvestris and Gleditsia triacanthos
2013 - IRG/WP 13-10806
Sometimes mould fungi grow over weathered coated sapwood, whereas the coated heartwood is not colonised. Two factors may be responsible for these differences: Either the larger content of nutrients in the sapwood, or the content of biocidal extractives in the heartwood. In this study the factors for the difference in mould growth on coated heartwood and sapwood of Pinus sylvestris (Scots Pine) and...
D Lukowsky, N Buddruhs
System treatments of Pinus sylvestris - influence on moisture, decay and discoloration
2013 - IRG/WP 13-30612
Biological activity can cause challenges for the use of wood in outdoor exposure. Decay and discolouring fungi influence the service life of wooden constructions, and the moisture content of the wood is often an important factor. The aim of this study was to evaluate the performance of different combinations of preservative/modified wood protection treatments and surface treatments for wooden deck...
A Schabacker, G Alfredsen, L Ross Gobakken, H Militz, P O Flæte
Copper leaching from copper-ethanolamine treated wood during exposure to terrestrial microorganisms
2013 - IRG/WP 13-30621
Copper-ethanolamine based wood preservatives are still the most important solutions for protection of wood in ground applications in Europe. Wood in ground is exposed to variety of organisms, which can act synergistically. In order to simulate these conditions in laboratory, Scots pine (Pinus sylvestris) specimens impregnated with copper-ethanolamine preservative of three different concentrations ...
M Humar, N Thaler, B Lesar
A guideline for sorting easy to impregnate Scots pine sapwood based on three treatability studies from Northern Europe
2014 - IRG/WP 14-40669
Scots pine sapwood is generally considered an easy to impregnate wood species, though it reportedly faces challenges towards a homogeneous impregnation and large variations in treatability are reported for the material.
This study comprises the results of three treatability tests that were performed on Scots pine (Pinus sylvestris) sapwood. The material impregnated was originated from a large ...
K Zimmer, E Larnøy, A Treu
Performance of kiln-dried and air-dried anti-sapstain treated pallet timber under use scenarios against wood discolouring fungi
2015 - IRG/WP 30669
During their lifespan there is a high probability that wooden pallets and packaging material will be exposed to rainfall or rewetting conditions, increasing the risk of growth of discolouring fungi. Kiln-drying of wooden pallets and packaging material without anti-sapstain treatment does not give efficient protection against wood discolouring fungi during rewetting periods. However additional temp...
A Steitz, E Stoyanova, N Pfabigan, R Gründlinger
Impact of early lignification of ray parenchyma cells on the treatability of Scots pine sapwood
2015 - IRG/WP 15-40706
The wood anatomy of Scots pine sapwood can influence its treatability. A microscopic analysis on the wood material from four different stands in Northern Europe was performed using tangential sections from the outer part of Scots pine sapwood. Single correlations of the ray composition and lignification state of the ray parenchyma showed the influence of these factors on radial penetration depth a...
K Zimmer, A Treu
Above-ground performance of a buffered amine oxide treatment system against Mastotermes darwiniensis
2016 - IRG/WP 16-10855
Above-ground H2 field tests against Mastotermes darwiniensis were conducted in far north Queensland to assess the efficacy of buffered amine oxide treatments in the softwoods Pinus sylvestris and P. radiata, and the hardwoods Eucalyptus regnans and E. diversicolor. Untreated hardwoods and slash pine bait wood (P. elliottii) were severely attacked or destroyed, while untreated P. sylvestris was mod...
L J Cookson, R W Clawson Jr
Evaluation of Commercially Available Polyurethane Resin to Develop Non-biocidal Wood Preservation Treatments
2016 - IRG/WP 16-40751
Evaluation of commercially available polyurethane (PU1 and PU2 and polyisocyanate (PNCO) to develop non-biocidal wood preservation treatments have been conducted. A simple method by vacuum impregnation of these resins into beech wood (Fagus sylvatica L) and pine wood (Pinus sylvestris L.) samples followed by varied curing process at ambient temperature, 103oC, and 200oC have been performed. Based ...
M Mubarok, Y Sudo Hadi, J Suryana, I W Darmawan, F Simon, S Dumarcay, C Gérardin, P Gérardin
Impact of sapwood portions on the durability of adjacent heartwood of Pinus sylvestris, Pseudotsuga menziesii and Quercus robur. Part 1: Laboratory studies
2018 - IRG/WP 18-10922
Sapwood is generally considered as non-durable and assigned to durability class DC 5 according to European standards independent from the wood species. It is commonly agreed that sapwood decays faster than adjacent heartwood, but it is controversially discussed whether sapwood serves as feeder material and thus accelerates onset and progress of decay in more durable heartwood or decays independent...
C Brischke, P Homann, A Gellerich
Effect of long-term immersion in fresh and salt water on mould growth on Scots pine (Pinus Sylvestris L.) wood
2020 - IRG/WP 20-10962
Wood exposed outdoors will eventually be degraded by fungi, depending on exposure and material characteristics. Numerous wooden constructions in the Røros municipality have existed since the 17th century, but wood used in recent repairs have decayed faster than expected. Before 1970 timber was mainly transported by log driving or rafting, and the logs were immersed in water for longer or shorter ...
M Sand Austigard, J Mattsson
Monitoring uptake and penetration of pesticides during impregnation of pine (Pinus sylvestris) and spruce (Picea abies) wood with bio-based microemulsion gel formulations
2020 - IRG/WP 20-30756
Even in dry state wood is susceptible to biological degradation. Preservation against biological decay in exposed conditions is conventionally achieved by impregnating the wood with pesticides applied at professional and industrial levels. Impregnation of wood with preservatives is a complex process that involves wood macro- and microstructure, and the physical characteristics of woods. Here we fo...
D Messaoudi, K Ruel, J-P Joseleau
Durability of thermotreated Pinus sylvestris and Eucalyptus nitens against wood decay organisms
2022 - IRG/WP 22-40949
One of the alternative treatments to avoid the application of biocides is thermal modification of wood, which increases the durability of wood against attack by wood decay organisms. The durability of Pinus sylvestris and Eucalyptus nitens thermotreated at 180 and 212 ºC, was studied. The results show that thermotreatment against wood decay fungi in P. sylvestris is slightly more effective than i...
M T Troya, S M Santos, L Robertson, N Pérez-Molina, V Baños, A Dieste
New wood-modification process based on grafted urethane groups: Durability of carbamamylated Scots pine (Pinus sylvestris L.) wood
2023 - IRG/WP 23-40974
Substituting commonly used toxic preservatives with wood modification treatments can make the wood material less prone to water and moisture uptake. This approach favours a more sustainable protection of wood against biodegradation. In this study, Scots pine sapwood was full-cell impregnated with an aqueous solution of urea (30%), dried at 40°C for 24h, and subsequently heat-treated at 150°C for...
C-F Lin, O Myronycheva, O Karlsson, D Jones, D Sandberg
Properties of thermal modified wood of Pinus pinaster and Pinus radiata from Galicia, Spain
2023 - IRG/WP 23-40985
This article provides the results of a research about the properties of thermal modified wood of maritime pine (Pinus pinaster Ait.), radiata pine (Pinus radiata D.Don) and Scots pine (Pinus sylvestris L.) from Galicia, Spain, thermal treated in the industrial vacuum-heat autoclave plant of FINSA group in Galicia, Spain. These three pine wood species are used in different solid products but due th...
D Lorenzo, J Benito, J Arancón, J Crespo
Properties of thermal modified wood of Pinus pinaster, Pinus radiata and Pinus sylvestris from Galicia, Spain
2024 - IRG/WP 24-30800
This paper provides the results of a research about the properties of thermal modified wood of maritime pine (Pinus pinaster Ait.), radiata pine (Pinus radiata D. Don) and Scots pine (Pinus sylvestris L.) from Galicia, Spain, thermal treated in the industrial vacuum-heat autoclave plant of FINSA group in Galicia, Spain. These three pine wood species are used in different solid products but due the...
D Lorenzo, J Benito, J Arancon, J Crespo