Post-Manufacture Biocide Treatment of Engineered Wood I-Joists
2012 - IRG/WP 12-40596
Engineered wood I-joists, fabricated from laminated veneer lumber (LVL) flanges and oriented strand board (OSB) webs, offer many advantages over solid sawn lumber joists in residential and light commercial construction. With the expanded use of these products has come an increasing need to be able to treat them with biocides to prevent attack from decay fungi and termites during service. Historic...
A S Ross, R W Clawson
Scale-up of a chemical process for copper-based preservative-treated wood wastes recycling
2012 - IRG/WP 12-50286
In recent years, the development of appropriate wood waste disposal options has been encouraged by severe regulations and expensive fees associated with wastes landfilling or burning. An efficient and economically attractive leaching process was developed at laboratory scale (200 mL) for CCA-, ACQ- and CA-treated wood wastes recycling. This leaching process consisted of three leaching steps of 2 h...
L Coudert, L Gastonguay, J F Blais, G Mercier, P Cooper, P Morris, A Janin, N Reynier
Tar-oil uptake vs time in immersion treatment of short pine posts: A simple technique applicable to rural communities of Papua New Guinea
2012 - IRG/WP 12-40608
Pinus caribaea and Araucaria cunninghamii logs ca. 100 mm in diameter were shortened to lengths 25-30 cm, conditioned to at/below fibre saturation point (FSP) for immersion/dip treatment using a hot- and- cold bath open- tank process. Before oven-drying and subsequent treatment, individual test specimens were numbered, their green weights and volumes, and dry weights recorded for basic density, vo...
B K Gusamo, R Tulo
Observation of Boring Process of Larvae of the Bamboo Powder-post Beetle (Dinoderus minutus)
2014 - IRG/WP 14-10821
The bamboo powder-post beetle Dinoderus minutus is a major pest of felled bamboo in Japan. X-ray computer tomography (CT) was applied to non-destructively trace the movement of the larvae of this beetle inside the infested bamboo samples. The bamboo samples were prepared from pieces of the Japanese timber bamboo Phyllostachys bambusoides culms that were enclosed with adult D. minutus beetles for a...
H Watanabe, Y Yanase, Y Fujii
Study of in-situ gel polymerization established by Si-O-Si framework within wood micropores
2014 - IRG/WP 14-40672
Sodium silicate was used to form Si–O–Si framework by gel process and optimize the effect of the methylolurea impregnation on poplar wood. The modifier cured within the wood micropores by in-situ gel polymerization during the kiln drying. The results showed that treated wood acquired higher mechanical strength, but lower hygroscopicity. New positions of the XRD peaks appeared which caused by s...
Zeng Bi, Qian Lang, Heyu Chen, Junwen Pu
Effect of natural variability of European Oak wood on heat treatment process and potential implication on wood durability
2015 - IRG/WP 15-40693
Environmental pressures appeared in France and in most European countries during the last decade has led to the development of more environmentally acceptable preservation methods. In this context, wood heat treatment has been one of the most investigated alternative method during the last years. Treated at temperatures ranging between 180 and 220°C, wood components undergo more or less important...
J Hamada, A Pétrissans, F Mothe, M Pétrissans, P Gérardin
Polyamidoamines (PAA) functionalized with siloxane fragments as potential wood preservatives
2015 - IRG/WP 15-40708
Polyamidoamines (PAAs) utilized in this research were obtained by the reaction between N,N-methyl-bis-acrylamide (MBA) and Ethanolalmine (EtA) and/or aminopropytriethoxysilane (APTES). Different combinations between them were tested as wood preservatives against fungal decay. First, in situ impregnations of PAAs, with the reagents above described in different ratio, were performed and the effectiv...
S Palanti, G Predieri, E Feci, L Bergamonti
How intraspecific radial variability of the European Oak’s may influence mild pyrolysis process and durability of the material
2016 - IRG/WP 16-40725
Last decades wood is promoted as building material. Unprotected wood exposed to outdoor conditions undergoes a variety of degradation induced essentially by fungi attacks. Heat treatment of wood by mild pyrolysis (180°C T 240°C under inert atmosphere) is a preservation process with a weak environmental impact, and therefore, is viewed as an interesting alternative to the chemical impregnation me...
J Hamada, A Pétrissans, F Mothe, M Pétrissans, P Gérardin
The influence of log soaking temperature and thermal modification on the properties of birch veneers
2016 - IRG/WP 16-40749
In veneer manufacture the logs are routinely soaked in heated water baths in order to soften the wood prior to peeling. The temperature of the water may vary greatly between batches; however, the influence of log soaking temperature on veneer properties has had little research attention. Uncontrolled moisture is known to cause problems in wood-based materials, while thermal modification offers a m...
S Källbom, K Laine, M S Moghaddam, A Rohumaa, K Segerholm, M Wålinder
Chemical, physical-mechanical characterization and durability of thermally modified beech and ash wood by thermo-vacuum process (Termovuoto)
2016 - IRG/WP 16-40758
The paper illustrates part of the results from the CIP Eco-innovation project “Thermo-vacuum: new process for new generation of thermally modified wood”. The project is part of the 7th Framework Programme for European Research and Technological Development, and thermo-vacuum modified wood is already on the European market. The project was selected by the European Commission, EASME Agency, as "...
M Jebrane, I Cuccui, O Allegretti, N Terziev
Hybrid green composites manufactured with glass fiber and jute fabric skin by VARTM process: Fungal, mold, and termite resistance tests
2017 - IRG/WP 17-40780
Hybrid green composites are increasingly used in building applications due to the development of new production approaches. Biological performance of such composites is needed when they are employed in extreme conditions. Hybrid composite panels were manufactured by wood furnish, glass fiber, and jute fabric skin by the vacuum assisted resin transfer molding (VARTM). Petri dish test method was fol...
S N Kartal, E Terzi, M Muin, A H Hassanin, T Hamuoda, A Kilic, Z Candan
Decay resistance variability of European wood species thermally modified by industrial process
2017 - IRG/WP 17-40807
Thermal modification is now considered as a new ecofriendly industrial wood modification process improving mainly the material decay resistance and its dimensional stability. Most industrial thermal treatment processes use convection heat transfer which induces sometimes heterogeneous treatment temperature propagation within the oven and lead to the heterogeneity in treatment efficiency. Thus, it ...
K Candelier, L Pignolet, S Lotte, A Guyot, E Cuny, B Bousseau, M-F Thévenon
A Green and Novel Technology for Recovering Copper and Wood from Treated Wood Waste – Part II: Optimization, copper metal recovery, and process design
2017 - IRG/WP 17-50326
The US consumes 70 million pounds of copper and produces 580 million cubic feet treated wood annually. The EPA disallows burning and reusing treated wood waste due to health/environmental concerns. Vast quantities of copper and wood are landfilled. Two safe and low cost extraction systems, citric acid and ammonium citrate, were identified in Part I of this study. In Part II of the study, effects o...
S Chen, R Patel
Thermodynamic properties of furfurylated wood during moisture adsorption process
2018 - IRG/WP 18-40828
Furfurylation of wood seems a promising wood modification method considering the wide raw material source of furfuryl alcohol (FA) and overall performance of FA modified wood. However, the modification mechanism of furfurylation is still not clear and needs further investigation. In this study, poplar (Populus cathayana Rehd.) samples with the size of 1(R) mm × Ф4 mm, were impregnated with ...
J Wang, J Cao, T Yang, E Ma, W Wang
Visualization of Feeding Process of Larvae of the Wood-boring Beetles Using X-ray Computer Tomography
2019 - IRG/WP 19-10953
X-ray computer tomography (CT) was applied to observe the movement of the larvae of the wood-boring beetles Lyctus brunneus, Lyctus africanus, and Heterobostrychus aequalis inside the infested wood specimens. The larvae bred with artificial diet were inserted into the hole of wood specimens of rubber wood Hevea spp. or Japanese oak Quercus crispula. The wood specimens with larvae were scanned usin...
Y Yanase, H Watanabe, I Fujimoto, T Yoshimura, Y Fujii
Exploring the use of X-ray micro CT as a tool for the monitoring of moisture production and mass loss during lab-based fungal degradation testing
2019 - IRG/WP 19-20654
Bio-based building materials, such as wood and wood-engineered products, are susceptible to degradation by decay fungi. In-depth knowledge on the intricate material-fungus relationship as well as performance data for many bio-based building materials are still lacking, and especially knowledge on how a material’s structure and moisture properties affect the degradation process is missing. Althou...
L De Ligne, J Van den Bulcke, A De Muynck, J M Baetens, B De Baets, L Van Hoorebeke, J Van Acker
Investigations into the use of Maleic Anhydride/Sodium Hypophosphite as a Wood Modification Process
2020 - IRG/WP 20-40891
The formation of crosslinked bonds between wood constituents is believed to be an effective way to stabilize wood against wet conditions. The possibility to use maleic anhydride (MA) combined with sodium hypophosphite (SHP) as crosslinking agents was studied, using Scots pine sapwood and a model compound. The modified wood showed weight gain and bulking effect after treatment and subsequent Soxhle...
I Kim, D Jones, O Karlsson, D Sandberg, O N Antzutkin, F Ullah Shah
Field test methods as long-term aging – report of selective wood properties
2023 - IRG/WP 23-40962
Wood samples from a long-term field test are a valuable compendium of information about the material in the context of its aging processes. In the current work, wood samples from the round-robin test within the ECOMOD project were used as a material for the natural aging process (III and IV class of utility). The research scope was to determine selected properties of this wood which can be partial...
W Perdoch, M Benc, B Mazela, A Szulc, J Cegiela
New wood-modification process based on grafted urethane groups: Durability of carbamamylated Scots pine (Pinus sylvestris L.) wood
2023 - IRG/WP 23-40974
Substituting commonly used toxic preservatives with wood modification treatments can make the wood material less prone to water and moisture uptake. This approach favours a more sustainable protection of wood against biodegradation. In this study, Scots pine sapwood was full-cell impregnated with an aqueous solution of urea (30%), dried at 40°C for 24h, and subsequently heat-treated at 150°C for...
C-F Lin, O Myronycheva, O Karlsson, D Jones, D Sandberg
Evaluation of the effectiveness of soaking of high-temperature plywood in low-temperature oil-based wood
2023 - IRG/WP 23-40991
We conducted a preliminary investigation to determine if soaking high-temperature plywood in a low-temperature preservative solution could achieve deeper penetration of the preservative, even in plywood made with refractory wood species such as Japanese larch. Specimens cut from commercial plywood (Japanese larch) were stored at various temperatures before being soaked in the preservative solution...
T Miyauchi, S Isaji, H Shibui, N Furuta, J Miyazaki, H Matusnaga
Exploring bio-based chemicals in the residual stream from the thermal wood modification process
2024 - IRG/WP 24-30799
Numerous chemical-free processes have emerged in the wood processing industry to enhance the durability and optimize the service life of wooden elements exposed to exterior conditions. One such method, the hygrothermolytic modification process, patented as FirmoLin®, represents an industrial treatment for thermal modification of wood. This involves subjecting solid wood to a pressurized unsaturat...
R Herrera, W Willems, W Pajerski, A Selmanović, A Sandak