Discovering anti-fungal agents in New Zealand native plants for use in wood protection
2009 - IRG/WP 09-10692
Extracts from Hinau (Elaeocarpus dentatus) leaves were tested in the laboratory for antifungal activity. In addition, the anatomical structure of the leaf was also examined by a combination of light and scanning electron microscopy. Chemical characterisation of the extracts and investigation into potential use of its components for wood protection is underway. A combination of light microscopy (...
C Rickard, T Singh, A Singh, R Newman
SEM-EDXA of CCA-treated Rubberwood (Hevea brasiliensis)
2009 - IRG/WP 09-20399
The microdistribution of chromated copper arsenate (CCA) preservative in rubberwood was studied using scanning electron microscope in conjunction with energy dispersive X-ray analyzer (SEM-EDXA). Bulk X-ray analysis showed that there was a high accumulation of chromium, copper, and arsenic in the vessels and lower concentration of the three preservative elements in fibres. Chromium appeared to rec...
I Jusoh, D P Kamdem
Weathering of Wood Modified with the N-Methylol Compound 1,3‑dimethylol-4,5-dihydroxyethyleneurea (DMDHEU)
2009 - IRG/WP 09-40467
Scots pine (Pinus sylvestris L.) sapwood boards were treated with a methylated 1,3‑dimethylol-4,5-dihydroxyethyleneurea (mDMDHEU) causing weight gains of approx. 25% and exposed to weathering for 18 months. Compared to untreated boards, treatment with mDMDHEU reduced surface discoloration mainly caused by staining fungi. Boards treated with mDMDHEU exhibited clearly lower moisture content th...
C Mai, Yanjun Xie, A Krause, K Urban, P D Evans, K Richter, H Militz
The Use of Micro-Tensile Testing to Assess Weathering Decay and Oxidative Degradation of Wooden Items
2010 - IRG/WP 10-20433
This paper presents a method to study the weathering performance of wooden items and to assess the oxidative degradation of wood via the Fenton reaction. Weathering resistance and photo-stability of wood was tested using pine wood (Pinus sylvestris) veneer strips measuring approximately 60 µm in thickness. The veneer strips were treated using a reactive chemical to impart surface protection. The ...
C Mai, Yanjun Xie, Zefang Xiao, P D Evans, H Militz
Analyzing hyphal growth of the bio incising fungus Physisporinus vitreus with light-, confocal laser scanning- and, Synchrotron X-ray tomographic microscopy
2010 - IRG/WP 10-20438
Norway spruce wood is an important building material for the forest and wood industry. To improve wood permeability and uptake of wood modification substances Physisporinus vitreus is employed as a bioincising agent. In this study wood specimens were incubated with P. vitreus to assess hyphal colonisation and structural alterations of Norway spruce wood. After different incubation periods, semi-th...
C Stührk, M Fuhr, M Schubert, F W M R Schwarze
Photostabilization of Wood with Higher Molecular Weight UV Absorbers
2010 - IRG/WP 10-30524
Higher molecular weight UV absorbers were created by reacting the epoxy-functionalized UV absorber 2-hydroxy-4(2,3-epoxypropoxy)-benzophenone (HEPBP) with maleic, phthalic or succinic anhydride. The ability of the UV absorbers to photostabilize wood was then examined. FTIR-spectroscopy confirmed that HEPBP reacted with phthalic anhydride to create a polyester that preserved the UV-absorbing benzop...
P D Evans, M J Chowdhury
Comparison of Micronized Copper Particle Sizes
2010 - IRG/WP 10-30538
The particle sizes of micronized copper formulations derived from treating liquids were compared with those deposited in wood treated with those liquids. The intent was to determine if agglomeration occurs in the liquids during the treatment process, if screening of the agglomerates occurs in the wood and if there are any apparent differences in the particle sizes in the wood. Three formulations...
C R McIntyre
Direct estimation of the durability of high-pressure steam modified wood by ESR-spectroscopy
2010 - IRG/WP 10-40508
Heat generated persistent free radicals have been detected by electron spin resonance measurement of thermally modified wood, prepared by high pressure superheated steam treatment. The specific density of these radicals have been correlated with the durability against basidiomycetes, as measured by the European standard EN113 test. In the lower range of specific radical densities, the found correl...
W Willems, A Tausch, H Militz
Multilayer hot-press drying and chemical modifying of poplar wood with urea-formaldehyde prepolymer
2011 - IRG/WP 10-40539
The objective of this study was to determine the technology of chemical modifying and multilayer hot-press drying on poplar wood. The chemicals were impregnated into cell lumen space by pulse-dipping machine to improve the dimension stability and mechanical property of timber. The timbers were compressed and dried by the multilayer hot-press drying to increase the density of timber. Results indica...
Guofeng Wu, Yifei Jiang, Sheng Yao, Junwen
Copper Nanoparticles in Southern Pine Wood Treated with a Micronised Preservative: Nanodistribution of Copper in the Pit Membrane and Border of an Earlywood Bordered Pit
2011 - IRG/WP 11-30566
Copper nanoparticles can penetrate the cell walls of unlignified parenchyma cells in southern pine wood treated with a micronised wood preservative, but they are excluded from lignified tracheid walls. This paper extends these observations to include the cell wall layers of the bordered pit. Focused ion beam and ion milling were used to make an ultra-thin section of the cell wall layers of an earl...
H Matsunaga, Y Kataoka, M Kiguchi, P Evans
Further Studies on the Distribution of Copper in Treated Wood Using an XRF Microscope Technique
2011 - IRG/WP 11-40549
There are two distinct forms of copper in aqueous copper based wood preservative systems that are currently used in the United States for treatment of southern pine lumber. These are systems using either soluble copper (typically amine based) or the more recent particulate or “micronized” copper as the primary biocide. Studies reported last year showed that there were distinct differences in...
A Zahora
Accessibility of Wood Cell Walls to Well-defined Platinum Nanoparticles
2012 - IRG/WP 12-20494
Copper nanoparticles are found in the walls of parenchyma cells in southern pine sapwood treated with a micronised wood preservative, but they are absent from tracheid walls. Hence, we hypothesized that small nanoparticles can penetrate the walls of unlignified parenchyma cells, but are excluded from lignified tracheid walls. This paper tests this hypothesis by treating pine sapwood with an aqueou...
H Matsunaga, Y Kataoka, M Kiguchi, P D Evans
Fire performance of the wood treated with retardant
2012 - IRG/WP 12-40591
To prepare the eco-friendly fire retardant wood, Japanese red pine (Pinus Densiflora), hemlock (Tsuga Heterophylla), and radiate pine (Pinus Radiata) were treated with inorganic chemicals, such as sodium silicate, ammonium phosphate, and ammonium boric acid. Different combination and concentration of those chemicals were injected by pressure treatment methods. The electron-beam treatment was used ...
Jong In Kim, Mi-ran kang, Sang bum Park, Dong won Son
Preliminary evaluation of degradation patterns in wood samples from the Yenikapı shipwrecks
2013 - IRG/WP 13-10798
The uncovering of several shipwrecks during the excavation of the Marmaray Rail Tube Tunnel Project in Istanbul provides an important opportunity to evaluate waterlogged woods buried for centuries. Identification of these woods showed that a variety of species was used in the ships. One shipwreck (a galley) from the Yenikapı Marmaray was examined using electron microscopy. The micrographs rev...
C Köse, A M Taylor
Moisture distribution in glulam beams with natural cracks observed with CT Scanning before and after rain
2013 - IRG/WP 13-20534
The way cracks in outdoor wooden constructions affect durability is an interesting topic, since a certain amount of cracks can always be found naturally in wood and glued laminated wood. The question in this was, can cracks lead water into the wood and thereby increase the risk for decay and reduce strength and service life. Moisture balance, i.e., water absorption and water distribution were stud...
K Sandberg
CT scanning of decay in creosoted poles for overhead lines
2013 - IRG/WP 13-30634
Creosote-treated poles have been examined by means of CT scanning in order to investigate the nature of soft spots that have been found more frequently during the last five years in Sweden. CT scanning provides a very good picture of the interior of the poles and decay can easily be detected. It was concluded that the soft spots in most cases were caused by decay which in turn had to do with extre...
C-J Johansson, A Clang, I Johansson, G Berggren
Curing kinetics of nano cupric oxide (CuO) modified PF resin as wood adhesive: Effect of surfactant
2013 - IRG/WP 13-40620
The effect of nano cupric oxide (CuO) in combination with surfactants on the curing kinetics of phenol formaldehyde (PF) resin, as well as the bonding strength of plywood prepared using the modified resin were investigated in this study using dynamic and isothermal differential scanning calorimetry (DSC). The result showed that the incorporation of nano CuO along with alkane surfactant made in the...
Wei Gao, Guanben Du
Effect of electron beam irradiation on the fire retardant penetration into wood
2013 - IRG/WP 13-40642
Electron beam processing which can fast and easy change the nature of the material has received considerable attention recently. Studies using electron beam has been conducted in various fields and it has been applied in many industrial sectors. Electron beam has higher energy than other electromagnetic waves. It has excellent object permeability. It affects degradation of intermolecular cross-lin...
Dong won Son, Jong Sin Lee, Mee Ran Kang, Sang Bum Park
Scanning Transmission X-ray Microscopy as a tool for examining chemical changes in wood cell walls due to enzymatic activity
2014 - IRG/WP 14-20556
As development of techniques for examining enzymatic activity on solid, complex biological materials, is considered to be an important factor in further development of enzyme applications and for understanding the decay of plant materials, this study explores applicability of Scanning Transmission X-ray Microscope (STXM) for determining chemical changes in enzymatically treated samples at the cell...
D Jeremic, R Goacher, R Yan, C Karunakaran, E R Master
Non-destructive monitoring of structure and moisture dynamics of plywood exposed outdoors to improve service life prediction and fit-for-purpose design
2015 - IRG/WP 15-20570
Plywood is an important construction material yet prone to water uptake, which can decrease strength and increase decay risk. To predict service life and improve fit-for-purpose design, it is crucial to understand the moisture behavior and structural changes of plywood. In this research, several plywood specimens were exposed outdoors for approximately one year. During this period, the moisture di...
W Li, J Van den Bulcke, I De Windt, M Dierick, J Van Acker
Development of a new characterization method to analyse Cypermethrin penetration in wood material by immunolabelling
2015 - IRG/WP 15-30674
The preservative efficacy of organic biocides is strongly related to their capacity of penetration and retention within wood tissues. The specific detection of the pyrethroid insecticide cypermethrin is currently obtained after extraction followed by chemical analysis by chromatography techniques. However visualizing the insecticide molecule within the wood structure requires specific probes toget...
S Tapin-Lingua, K Ruel, J-P Joseleau, D Messaoudi, O Fahy, M Jequel, M Petit-Conil
Terrestrial laser scanning (TLS) – a potential tool for improved utilisation of the natural durability of Scots pine for solid wood products
2019 - IRG/WP 19-50358
The natural durability of sapwood of most species is generally low, while heartwood can be more resistant to biodeterioration. For the sawmill industry various lumber products require certain diameters and lengths of the logs in addition to requirements for wood properties. When utilising the heartwood, it is therefore important to acquire information already in the forest about which trees that c...
P-O Flaete
Evaluation of chemical densification of three hardwood species through in-situ electron beam polymerization
2020 - IRG/WP 20-40893
Hardwoods are the most suitable species for wood flooring for their appearance as well as their hardness. Yet, improving hardness can provide substantial benefit for the wood flooring market. Chemical densification of wood and in-situ polymerization through electron beam technology was chosen to increase hardness of three hardwoods (Yellow birch (YB) (Betula alleghaniensis Britt.), Sugar maple (SM...
J Triquet, P Blanchet, V Landry
Surface chemical wood densification through in situ electron beam polymerization: description and dose study
2022 - IRG/WP 22-40933
Traditional wood chemical densification processes can be used to improve wood mechanical properties by increasing density of the material throughout its thickness. While mechanical surface densification has heavily been investigated, surface treatments involving impregnation of monomers remain unexplored. This study describes a new material, surface densified through lateral impregnation of acryla...
J Triquet, P Blanchet, V Landry
Assessment of historical pilings from Lisbon
2024 - IRG/WP 24-41004
The renovation and rebuilding of areas in Lisbon has led to work on buildings constructed in the Pombaline downtown district. These buildings were constructed on wooden pilings, as a means of stabilising unstable soils and transfer the loads from buildings to soils with adequate bearing capacity. These methods also increased the resilience of the reconstruction works to future possible earthquakes...
D Jones, S Duarte, J A J Huber, L Nunes