Quantification of copper and chromium in field stakes after different exposure times: Remaining metal content and distribution
2013 - IRG/WP 13-50291
In order to determine the distribution of copper and chromium as well as their remaining concentration EN 252 specimens and thicker pine sapwood stakes (non standard format) were treated with a commercial CC salt in a vacuum pressure process. The stakes were installed in the test field of the Institute of Wood Research, Hamburg, in August 2010. In all cases three stakes were removed after 4, 8, 12...
T Liese, M Bahmani, E Melcher
Effect of silver nanoparticles on the rate of heat transfer to the core of the medium-density fiberboard mat
2014 - IRG/WP 14-40653
Effect of silver nanoparticles on the rate of heat transferred to the core section of medium-density fiberboard (MDF) mat was studied here. A 400 ppm aqueous nanosilver suspension was used at three consumption levels of 100, 150, and 200 mL/kg based on the weight of dry wood fibers; the results were then compared with the control MDF panels. The size range of silver nanoparticles was 30-80 nm. Res...
H Reza Taghiyari, O Schmidt, E Bari, P M Tahir, A Karimi, P Nouri, A Jahangiri
Effect of exposure site on metal migration from copper azole, alkaline copper quat or chromated copper arsenate treated southern pine decking
2015 - IRG/WP 15-50313
Metal migration from chromated copper arsenate, copper azole or alkaline copper quaternary compound treated southern pine lumber was assessed at sites in Mississippi and Oregon. Metal levels tended to be consistently higher in decks exposed in Mississippi. Rainfall characteristics did differ slightly at the two sites, but the levels did not appear to be of a magnitude that might affect metal mobi...
J J Morrell, H M Barnes
Increasing the hardness of wood-composite panels by nanosilver
2016 - IRG/WP 16-40715
Effect of silver nanoparticles on hardness in medium-density fiberboard (MDF) was studied here. A 400 ppm aqueous nanosilver suspension was used at three consumption levels of 100, 150, and 200 mL/kg, based on the dry weight of wood fibers; the results were then compared with the control panels. The size range of silver nanoparticles was 30-80 nm. Composite mats were hot-pressed for 6, 8, and 10 m...
H R Taghiyari, J Norton, K Heidarhaee
Case study: “Riesenbühlturm”
2017 - IRG/WP 17-20599
In this case study four 7 m long Douglas fir crossbeams were investigated regarding the remaining metal and moisture content. The crossbeams were replaced from a timber tower after 10 years of service in the Black Forest region (South Germany) due to fungal decay. From each of the crossbeams five stem discs were taken and relevant parameters (density, moisture and remaining metal content) were de...
E Melcher, J Müller
Surface Protection of Wood with Metal Acetylacetonates
2017 - IRG/WP 17-40802
Metal acetylacetonates are coordination complexes of metal ions and the acetylacetonate anion. They have diverse uses as catalysts, cross-linking and curing agents and adhesion promotors. Some metal acetylacetonates can photostabilise polymers whereas others are photocatalysts. We hypothesise that the ability of metal acetylacetonates to photostabilise wood will vary depending on the metal in the ...
Yuner Zhu, P D Evans
A Green and Novel Technology for Recovering Copper and Wood from Treated Wood Waste – Part II: Optimization, copper metal recovery, and process design
2017 - IRG/WP 17-50326
The US consumes 70 million pounds of copper and produces 580 million cubic feet treated wood annually. The EPA disallows burning and reusing treated wood waste due to health/environmental concerns. Vast quantities of copper and wood are landfilled. Two safe and low cost extraction systems, citric acid and ammonium citrate, were identified in Part I of this study. In Part II of the study, effects o...
S Chen, R Patel
Influence of sea water on timber and metal joints
2017 - IRG/WP 17-40818
In the Great East Japan Earthquake that occurred in March 2011, many buildings suffered from seawater immersion caused by the tsunami. Saito's study revealed that corrosion progresses on metal plate that experienced seawater immersion 1). However, the detailed mechanism of corrosion progresses has not yet been clarified. Therefore, in this study, salinity which is one of causes of corrosion w...
T Nishimura, H Ishiyama, F Hirose, N Wada
Mechanism of nano metal fluorides against fungi
2018 - IRG/WP 18-30730
Metal fluoride nanoparticles are promising because of their low water solubility, which reduces the need for fixatives required in widely used active ingredient in wood preservatives such as copper and boron. Wood specimens treated with fluoride sols of MgF2 and CaF2 have been tested against brown-rot fungi (Coniophora puteana and Rhodonia placenta) in accordance with EN 113 and against termites (...
S M Usmani, K Klutzny, I Stephan, T Hübert, E Kemnitz
Biocidic effect of nano metal fluorides against brown-rot fungi
2019 - IRG/WP 19-30732
Metal fluoride nanoparticles are promising because of their low water solubility, which reduces the need for fixatives required in widely used active ingredients in wood preservatives such as copper and boron. The effectiveness of nano metal fluorides was compared to sodium fluoride treated wood samples. Wood specimens treated with homo-dispersed sols of MgF2 and CaF2 were tested against brown-rot...
S M Usmani, K Klutzny, I Stephan, E Kemnitz
Application of nano metal fluorides against termites
2019 - IRG/WP 19-30733
Recent research has shown that fluorides such as NaF have potential as a wood preservative against termite attack (Pan and Wang, 2015). However, NaF has high leaching susceptibility because of its solubility (40 g/l ) which can reduce its efficacy over long term. Metal fluoride nanoparticles such as MgF2 and CaF2 present a viable alternative to water soluble fluoride-based wood preservatives as th...
S M Usmani, K Klutzny, Y de Laval, R Plarre, D McMahon, I Stephan, T Hübert, E Kemnitz
Effect of damage to polyurea coatings on metal losses from ammoniacal copper zinc arsenate treated Douglas-fir pile sections
2019 - IRG/WP 19-40867
Metal-based preservatives remain the most widely used treatments for protecting wood in soil or water contact. While these treatments are highly effective, one drawback is a tendency for small amounts of metal to migrate into the surrounding environment. The greatest risk in this regard is copper because many organisms are highly sensitive to this metal. While post treatment practices can reduce ...
M J Konkler, J J Morrell
Yellow birch fire-protection using polyelectrolytes complexes
2020 - IRG/WP 20-30755
Fire protection has been a major challenge in wood construction for many years. The demand for high-performance, environmentally friendly treatments respecting the physical and chemical characteristics of the material has been accentuated in recent years. Halogenated fire-retardant (FR) compounds were commonly used from the 70’s for their low-cost and high efficiency. They are able to form radic...
M Soula, F Samyn, S Duquesne, V Landry
Wood Protection Using Nano Metal Oxides in Propylene Glycol
2022 - IRG/WP 22-30760
Metals and metal oxides are known to have properties that can protect wood from degradation. Nanoparticles, due to its unique physical and chemical properties can enhance the protection to a much greater extent. Major constraints in dealing with nanoparticle dispersion can only be resolved by identifying a proper dispersive medium. Studies were carried out by preparing nanodispersion of four metal...
S Nair, G B Nagarajappa, K K Pandey
Outdoor performance of Tanalith® K treated timber: Dimensional stability and corrosivity towards metal fasteners
2023 - IRG/WP 23-30798
This study was carried out to investigate dimensional stability and corrosivity towards metal fasteners in radiata pine (Pinus radiata D. Don) treated with Tanalith® K to Hazard class 4 (H4) retentions in comparison with chromated copper arsenic (CCA) treated timber. For corrosion test, untreated and treated matched specimens were prepared from Australian-grown radiata pine, tested with mild stee...
G Rassam, J Hague, D Humphrey
Quantifying metal migration from a deck constructed with copper-azole-treated lumber
2024 - IRG/WP 24-50391
Soluble copper or micronized copper wood preservatives are the most common available wood preservative systems for residential applications in the United States. Copper containing wood preservatives have been scrutinized for their potential negative impacts on the environment, across many jurisdictions. Concerns arise from the potential for preservatives to migrate out of treated wood upon water e...
G Presley, M Konkler