Your search resulted in 721 documents. Displaying 25 entries per page.
Vapour boron treatment of wood based panels: Mechanism for effect upon impact resistance
1994 - IRG/WP 94-40036
Samples of medium density fibreboard, chipboard and oriented strandboard (OSB) were treated to two retentions of boric acid by a vapour phase treatment. The results of a range of mechanical tests were reported by Hashim et al. (1992, 1993) in which a small reduction in impact resistance was observed. Several investigations were carried out to study how and where this loss in impact resistance occu...
R Hashim, R J Murphy, D J Dickinson, J Dinwoodie
Development on Damage Functions of Wood Decay for Building Envelope Design
2005 - IRG/WP 05-10556
For the hygrothermal analyses of building envelope systems for insulation design, we tried a natural decay test of wetted wood specimens without any inoculation of fungi. Three principal experimental types: under steady-state conditions (Experiment A), at a cyclic water dripping under Non-steady conditions (Experiment B) and at a cyclic water dipping under-steady conditions (Experiment C), were ca...
H Suzuki, Y Kitadani, K Suzuki, A Iwamae, H Nagai
Mechanical resistance of Pinus radiata CCA treated and face jointed with PVA adhesive
1999 - IRG/WP 99-40140
Due to the increased use of Pinus radiata timber composites (laminated structural members, panels, etc), its low natural durability and the toxicity of phenol-formaldehyde type adhesives, a PVA (polyvinyl acetate) adhesive was evaluated in machined and rough CCA treated and untreated face joint samples under DIN 68602 (EN 204-205) standard for groups of requirement 3 and 4. The results showed that...
M C Rose, L Reyes, P León
Susceptibility of harvested softwoods to infection by sap-staining fungi
2002 - IRG/WP 02-10435
In the UK a field study programme was carried out to compare the susceptibility of softwood timber from five different commercially important tree species to infection by sap-stain fungi. Logs cut from freshly felled Scots pine (Pinus sylvestris), Lodgepole pine (P. contorta var.
latifolia), Sitka spruce (Picea sitchensis), Norway spruce (P. abies) and Japanese larch (Larix leptolepis) were expo...
E J Young, R A Eaton, J F Webber
Evaluation of the fire retardant efficacy and leach resistance of an amino resin fire retardant - Preliminary report
1983 - IRG/WP 3260
The Early Fire Hazard Indices of untreated Pinus radiata were determined by testing to Australian Standard 1530, Part 3 - 1976. Differences in the performance of heartwood and sapwood were noted, with heartwood samples giving higher Ignitability, Heat Evolved and Spread of Flame indices. The treatability of Pinus radiata with Pyrogard H was assessed, and backsawn sapwood treated more effectively t...
W D Gardner, P N Alexiou, P Lind, D Butler
Review of Mold Issues in North America and Mold Research at Forintek
2003 - IRG/WP 03-10458
Over the last decade, air quality in homes and workplaces has become a high profile issue especially in relation to mold, receiving considerable media, public and legal attention. Forintek Canada Corp. and the wood industry in general have experienced large increases in inquiries regarding mold and the suitability of wood as substrate for its growth. Because wet wood supports growth of fungi the ...
A Uzunovic, A Byrne, Dian-Qing Yang, P I Morris
Calculation of preformance index of Bardac 20 (an alkylammonium compound) evaluated in a field stake test
1982 - IRG/WP 3206
Bardac 20 treated stakes have been in test for three years at the Westham Island test site near Vancouver, B.C. The Performance Index for the preservative was calculated and found to be 0.009 which infers that, at the standard retention, Bardac 20 added 0.9 y to the life of the stake. It may be concluded that when tested using a standard field stake test using ponderosa pine (Pinus ponderosa Laws)...
J N R Ruddick
Natural durability of Iranian saxual wood (Haloxylon persicum) against the fungal decay
1991 - IRG/WP 1515
Haloxylon persicum is vidly planted in the deserfic region of Iran. At the present time, in the age of 30, these small trees are ready for cutting for the different uses, specially for rural buildings. But there's any knowledge about its durability. In this study the laboratory tests were carried out in accordance to European Standard. 5 fungi were used as: Trametes versicolor, Coniophora...
D Parsapajouh, F H Schweingruber, K Richter
Leachability And Decay Resistance of Copper-Treated Wood
2004 - IRG/WP 04-30337
Samples of scots pine sapwood (Pinus sylvestris L.) were treated with solutions of (Copper II sulfat-5 hydro + fluoroboric acid) and (Copper II sulfat-5 hydro + fluoroboric acid + boric acid) in order to determining to leachability and decay resistance against brown rot fungus (Postia placenta) and white rot fungus (Coriolus versicolor).
Results indicated that the copper in treated wood is less s...
A Temiz, T Nilsson, I Deemirtas, Ü C Yildiz
Decay Resistance and Bonding Properties of Structural Flakeboard
2002 - IRG/WP 02-40233
Experimental structural flakeboard panels consisting of differing furnishes and resins were produced and tested for internal bond, linear expansion, thickness swell, and decay resistance. One group of panels was produced with recycled CCA-treated wood as the furnish and commercial phenol formaldehyde (PF) resin as the binder. Other groups of panels were produced with either mixed hardwoods or so...
T F Shupe, Chung-Yun Hse
Decrease of the antidecay resistance of beech wood treated with organotin fungicides after its natural ageing
1998 - IRG/WP 98-30185
The antidecay resistance of beech-wood samples (120 x 8.5 x 8.5 (MM)) treated with tributyltin fungicides gradually decreased due to prolongation of their natural ageing:
tributyltin fungicides (TBTO, TBTS, TBTCA, TBT-DEDTK were applied by pressure impregnation technique in ethanole solutions (c = 0. 1%, 0.33% or 1%);
treated beech-wood samples were naturally aged without their contact with grou...
L Reinprecht
Resistance of Teak, Balau, keruing and Chengal Wood species against marine borers attack
2004 - IRG/WP 04-10513
Wood samples of Teak (Tectona grandis) , Keruing (Dipterocarpus alatus),Yellow Balau (Shorea laevis) and Chengal (Balanocarpus heimii) were treated by Creosote, using Ruping method. The dimension of samples were 200 x 75 x 20 mm and the retention were 188, 186, 331, 40 kg /m3 respectively. Both treated and untreated samples were installed in sea water (Mahshar in Persian gulf and Bandar Torkman an...
A Rezanejad
Moisture condition in treated wood exposed outdoors. A progress report
1989 - IRG/WP 3533
Wood treated with water-borne preservatives, mainly CCA (copper/chromium/arsenic), CCB (copper/chrome/boron) or CC (copper/chrome) is often said among users in Sweden to absorb more water than untreated wood. In laboratory tests this statement has not been confirmed but no field tests have been carried out in Sweden to study this phenomenon. In 1986 a project was started to compare water absorptio...
M-L Edlund, C E Sundman
Durability of surface preserved wood particle boards submitted to atmospherical influence
1995 - IRG/WP 95-40039
The worldwide problem of the continuously growing deficit of high quality natural wood material has caused the attempts of many research workers to find effective composites such as wood particle boards (WPBs) for replacing the massive wood for constructive purposes, depending on where the boards are exploited - in the open or under a shed, they are submitted to various climatic factors such as he...
L Valcheva
Resistance of painted wood to mould fungi. Part 2. The effect of wood substrate and acrylate paint systems on mould growth
1997 - IRG/WP 97-10234
Resistance of acrylate paint systems on different types of pine and spruce sapwood to mould fungi was studied. Dipping into the preservative prior to painting, a primer with and without a fungicide (propiconazole + IPBC 0.50 + 0.2%) and a topcoat with and without a fungicide (propiconazole + IPBC 0.25 + 0.12%) were combinations of the treatments studied. The efficacy of the treatment systems varie...
H Viitanen, P Ahola
The effect of malt and agar trademarks on growth, decay and stilbene resistance of fungi
2000 - IRG/WP 00-20202
Effects of malt and agar trademarks used in growth media on growth of fungi in cultures, amount of decay they cause in birch samples and their resistance to stilbenes were tested. It was tested also had the conditions where fungus cultures were stored before inoculation of test plates some effect on the results. Fungi used in these tests were white rot fungus Trametes versicolor and brown rot fung...
L Syrjälä, L Paajanen, A Pappinen
Co-operative research project on L-joint testing. Progress report to March 1984
1984 - IRG/WP 2211
Each participant was intended to expose L-joints in the main trial on 1 April 1983 and the first sampling, after 8 months exposure, was to be undertaken on 1 December 1983. Some participants have had to vary this schedule. Results are presented from CTFT (France) and PRL (United Kingdom). These show a greater effectiveness by the double vacuum treatments compared with the 1 minute dip treatments. ...
J K Carey, A F Bravery
Comparative study on physical properties of four fast growing timber species of Bangladesh
2006 - IRG/WP 06-10570
Ghoraneem (Melia azedarach), Rain tree (Albizia saman), Sissoo (Dalbergia sissoo Roxb.) and Akashmoni (Acacia auriculiformis) plantations are started as a fast growing timber specie from a few years back in Bangladesh. Initian objectives were to get fuel wood only from those trees, but a very positive response was found for Ghoraneem, Rain Tree, Sissoo and Akashmoni timber in the users market by c...
M M Islam, B K Dey, M O Hannan, G N M Ilias
Practical consequences of the clarification of the chemical mechanism of CCA fixation to wood
1983 - IRG/WP 3220
Practical consequences derived from the chemical investigation of the mechanism of fixation of CCA to the wood constituents are discussed. Among these, formulas for the calculation of the time of hexavalent chrome fixation are presented. Furthermore, three parameters are shown to be important to the long-term effectiveness of CCA-treated timber: (i) the temperature of treatment, (ii) the initial p...
A Pizzi
Dip-diffusion of dressed timber - Effect of drying
1989 - IRG/WP 3509
The effect of drying on dip-diffused dressed freshly sawn timber was determined by the depth of penetration of boron achieved on the two test timber species, White cheesewood (Alstonia scholaris) and Light Hopea (Hopea papuana). The results obtained showed that light density White cheesewood was completely penetrated even after 3 days drying while Light hopea, treated immediately achieved 5.2 mm p...
H C Konabe
The effect of wick action on the moisture distribution in heartwood and sapwood stakes of Pinus radiata D. Don.
1999 - IRG/WP 99-40139
The pattern of moisture distribution in stakes of Pinus radiata D. Don. subjected to "wick action" is investigated. There was incomplete saturation of the stakes even after 93 days of continual soaking. Maximum moisture absorption occurred at the base of the stake and at the air/water interface of the stake. Incomplete saturation of the stake was thought to be due to air embolism within the wood. ...
J Hann, P Vinden
Diffusion of a copper naphthenate/boron paste through Douglas fir heartwood
1991 - IRG/WP 3671
Groundline wraps are an important portion of the remedial treatment strategies for protecting utility poles in North America from surface decay. The compositions of these wraps have recently shifted away from pentachlorophenol and creosote to formulations containing copper naphthenate and boron. These formulations have not yet been extensively tested, although the chemicals have been used for many...
P G Forsyth, J J Morrell
The efficacy of remedial treatments for controlling fungal decay in window millwork used in the United States
1987 - IRG/WP 3432
Conventional window millwork was subjected to basidiomycete decay by inoculation and sampled for active growth of the decay fungus before and eight months after remedial preservative treatment with fused disodium octaborate rods (IMPEL) at boric acid levels of 1.5 and 4.0 kg/m³ or liquid bifluoride injections (IMPROSOL) at 1 kg/m³. The elimination of decay fungus after remedial treatment was nea...
M G Dietz, E L Schmidt
Incorporation of phenyl boronic acid treatment with vapor phase formalization
1997 - IRG/WP 97-40083
Phenylboronic acid (PBA) treatment was incorporated with vapor phase formalization (VPF) in order to increase dimensional stability and boron fixation as well as enhancement of biological resistance. Five and ten hours VPF were applied after PBA treatment as 0.34, 0.50, 1.00 and 2.00% concs. aqueous solutions. Anti swelling efficiency (ASE) attended to 71% in specimens impregnated with 0.50% PBA s...
M K Yalinkilic, S Yusuf, T Yoshimura, W-Y Su, K Tsunoda, M Takahashi
Moisture uptake and volumetric swelling as probable factors also affecting leaching in CCA-treated wood. A preliminary study of treated Eucalyptus saligna sapwood
2003 - IRG/WP 03-30318
IRG/WP 03-30318
A number of factors affecting leaching of CCA from treated wood have been variously investigated and discussed. However, the possible effects of moisture movement in treated timbers on leaching have not received attention yet. The present study examines and compares moisture uptake and volumetric swelling in CCA-treated and untreated sapwood of Eucalyptus saligna, and tries to establish a correl...
R Venkatasamy