Testing of the resistance of acetylated wood against marine borers at three Italian sites
2017 - IRG/WP 17-30719
The aim of this research is the determination of resistance of acetylated wood against marine biodeterioration in use class 5 (EN 335) in temperate sea waters. The resistance of acetylated Pinus radiata (radiate pine) in solid and MDF form is compared with that of the untreated radiata pine and other untreated wood of European species such as Fagus sylvatica (European beech) Castanea sativa (chest...
S Palanti, M Faimali, D Tagliapietra, M Andrenacci, M Anichini, M Sigovini
Effects of exposure time on detection of the behavior of white-rot fungi on Oriental beech wood properties
2017 - IRG/WP 17-10902
The comparison of fungal degradation of Orientalis beechwood by two white-rot fungi was evaluated in this study. Biological, mechanical, and chemical assessments of beech wood were carried out at 30 day interval for 120 days. The results demonstrated that both fungi have greater effects on beech wood during each exposure time. However, Trametes versicolor degraded beech wood more effectively than ...
E Bari, D D Nicholas, K M Ohno
UV-curable coatings developed for aesthetic and biological protection of wood outdoors
2017 - IRG/WP 17-40821
To avoid wood greying, dimensional variations, and degradation by biological agents wood is protected with preservation products and coatings when used outdoors. For some wood species used for cladding, a treatment with a preservation product is required, and is frequently additionally protected with a coating. In this study, Mäder Group developed a new UV-curable coating for outdoors application...
C Reynaud, A S Schuller, M Kutnik, L Podgorski
Interactions between wood polyphenols and detoxification enzymes of the white rot Trametes versicolor
2018 - IRG/WP 18-10906
Wood decay fungi have complex detoxification systems that enable them to cope with secondary metabolites produced by plants. Although the number of genes encoding for glutathione transferases (GSTs) is especially expanded in lignolytic fungi, little is known about their physiological target molecules. In this study, by combining thermal shift assay and affinity crystallography we highlighted inter...
M Schwartz, T Perrot, E Aubert, S Dumarçay, F Favier, P Gérardin, M Morel-Rouhier, G Mulliert, F Saiag, C Didierjean, E Gelhaye
Termite resistance of wood-plastic composites made with acetylated wood flour, coupling agent or zinc borate
2018 - IRG/WP 18-10917
There is little published scientific literature on the laboratory or field testing of wood-plastic composites (WPC) against termite attack. Therefore, the objective of this research was to investigate termite resistance (both laboratory and field) of 5 different extruded WPC blends of 50% western pine wood flour (WF) and high-density polyethylene (HDPE), and untreated pine solid wood. The study in...
R E Ibach, Y S Hadi, C M Clemons, S Yusuf
Understanding of the effect of ancestral and natural saltwater treatment on durability, fibers densification and chemical modification of palm wood
2018 - IRG/WP 18-10921
The palm-tree sector plays a very important role on both the socioeconomic and ecological levels, in Tunisia. There are three million trees in Tunisian palm plantations, ensuring a potential significant wood production, mainly in the craft and furniture industries.
In the past, Date Palm wood (Phoenix dactylifera L.,) was also used as structural material. Its low natural durability and its low m...
M T Elaieb, A Namsi, M Tella, M-F Thévenon, K Chandelier
Impact of sapwood portions on the durability of adjacent heartwood of Pinus sylvestris, Pseudotsuga menziesii and Quercus robur. Part 1: Laboratory studies
2018 - IRG/WP 18-10922
Sapwood is generally considered as non-durable and assigned to durability class DC 5 according to European standards independent from the wood species. It is commonly agreed that sapwood decays faster than adjacent heartwood, but it is controversially discussed whether sapwood serves as feeder material and thus accelerates onset and progress of decay in more durable heartwood or decays independent...
C Brischke, P Homann, A Gellerich
Use of x-ray microdensitometry for assessing the resistance to the fungus C puteana of a hybrid larches population
2018 - IRG/WP 18-10923
The aim of this research was to utilize the X-ray microdensitometry to determine the natural durability and its variability of a hybrid larch population. The method was applied on slices obtained by increment cores collected on standing trees before cutting them down. The methodology was discussed also in order to propose as a new screening method especially suited for trees populations. X-ray mic...
S Palanti, F Alderighi, F Stefani, J P Charpentier, L E Pâques
Natural resistance of Bambusa vulgaris to termite and powder-post beetle attack in laboratory and graveyard tests
2018 - IRG/WP 18-10925
Deterioration is the major setback to the utilisation of bamboo products. To enhance bamboo utilization, an understanding of the level of resistance to degradation is important. In this study, level at which Bambusa vulgaris will naturally resistant attack by subterranean termites and powder-post beetles were evaluated. B. vulgaris aged 2, 3 and 4 years were subjected to attack by subterranean ter...
N A Sadiku, S O Bada
Rapid Screening test of potential antimicrobial agents for wood coatings
2018 - RG/WP 18-20644
A two-part screening test has been developed to evaluate additives for wood coatings. First, an additive is tested in the microbial laboratory and evaluated based on its inhibitory properties against selected test organisms, directly on agar plates. A microbial growth analysis is prepared and evaluated. If the additive is considered effective, it will be tested in a standard top coating (acrylic o...
J Stenbæk, E Morsing, T Østergaard Jensen
Material Resistance and Chemical Composition of Italian Stone Pine (Pinus pinea)
2018 - RG/WP 18-20645
Relevant properties of stone pine (Pinus pinea) wood have been only fragmentarily addressed in the past, which has been recognized as a limiting factor for its potential applications. The amount of the respective wood species on the market will likely increase in the future. The sorption properties, permeability to water, extractives content and durability against fungi of Pinus pinea sapwood and ...
M Humar, M De Angelis, M Romagnoli, V Vek, I Poljanšek, P Oven, N Thaler, B Lesar, D Kržišnik
Resistance of modified wood to termite attack assessed in laboratory and field testing: A review of internal research
2018 - IRG/WP 18-40824
Within the past decades, new wood modification technologies have been investigated in order to improve certain wood characteristics and enable the use of timber products for outdoor applications. Some of these non-biocidal technologies have been developed and commercialized recently. Thus, various material properties were studied intensively and shown to be improved. To a great extent, previous re...
L Emmerich, P Gascón-Garrido, H Militz
Multiscale modification on water resistance and dimensional stability of Populus cathayana by alkali lignin combined with heat treatment
2018 - IRG/WP 18-40826
The aim of this study was to enhance the water resistance and dimensional stability of fast growing wood by alkali lignin combined with heat treatment. Poplar (Populus cathayana) samples were first impregnated with alkali lignin solution and then subjected to heat treatment at 140, 160, and 180°C respectively for 2h. Properties of leachability, moisture adsorption and water absorption, contact an...
H Zhou, J Li, E Ma
Selection of heat flux value for wood fire retardants testing using MLC
2018 - IRG/WP 18-40846
One of more crucial elements of investigating treated wood combustion properties with the use of a cone calorimeter is a proper selection of heat flux (HF). The HF level is directly reflected in time to ignition and a thermal degradation degree. The ignition of raw wood or of wood ineffectively protected against fire occurs at a low HF level, i.e. 10-20 kW/m2. By contrast, the ignition of wood whi...
B Mazela, W Perdoch, W Grześkowiak, A Batista
The biodegradation of creosote oil by various species of white rot fungi and bacteria isolated from the contaminated soil
2018 - IRG/WP 18-50334
The aim of the study was to determine biodegradation effectiveness of the selected polycyclic aromatic hydrocarbons (PAHs) contained in creosote oil, by two white rot fungal species (Bjerkandera adusta and Irpex lacteus) and three bacterial species (Pseudomonas putida, Pseudomonas sp. OS4 and Rahnella aquatilis). Bacteria were isolated from the soil contaminated with petroleum hydrocarbons from th...
M Sydow, J Zabielska-Matejuk, E Kaczorek, AStangierska, A Kropacz
Decay and water resistance of Siberian and European larch wood
2019 - IRG/WP 19-10941
The occurrence of larch wood is rather frequent in civil engineering. Namely, in building façades, terraces and balcony fences. In Slovenia and other central European countries, the use of the Siberian larch is especially popular. In this research, the durability against decay fungi in laboratory conditions and water exclusion ability of plantation-grown and naturally grown Siberian larch (Larix ...
B Lesar, D Krzisnik, M Humar
Natural durability of four Tunisian Eucalyptus wood species and their respective compositions in extractives
2019 - IRG/WP 19-10942
In the 50’s, Tunisia government introduced more than 11 Eucalyptus wood species. Eucalyptus species were planted in Tunisia in different arboreta throughout the country for close observation and adaptation to climate and soil. These fast-growing wood species were mainly used as fire wood, for the production of mine wood and to fight against the erosion. These tree species were adapted themselve...
S Ben Ayed, M T Elaieb, S Dumarçay, B De Freitas Homen De Faria, M-F Thévenon, P Gerardin, K Candelier
From fungal detoxification systems to wood durability in neotropical forests
2019 - IRG/WP 19-10946
White-rot fungi are able to mineralize all the wood components due in particular to an efficient detoxification system. We hypothesised that components of this detoxification systems, glutathione transferases, could be used as tools to explore the natural durability of neotropical wood species. Analysis of the interactions between six glutathione transferases of Trametes versicolor and extracts of...
T Perrot, G Salzet, N Amusant, J Duchene, E Gelhaye
Performance of wood decking after 5 years of exposure: verification of the combined effect of wetting ability and durability
2019 - IRG/WP 19-20647
Wood is one of the most important construction materials and its use in building applications has further expanded in recent decades. In order to enable even more extensive and reliable use of wood, factors affecting wood’s service life need to be understood. More recently, a new concept to characterize the durability of wood-based materials and to predict the service lives of wood was proposed,...
M Humar, D Krzisnik, B Lesar, C Brischke
Impact of water holding capacity and moisture content of soil substrates on the moisture content of wood in terrestrial microcosms
2019 - IRG/WP 19-20662
Terrestrial microcosms (TMC) are frequently used for testing the durability of wood and wood-based materials as well as the protective effectiveness of wood preservatives. In contrary to experiments in soil ecology sciences, the experimental set-up is usually rather simple. However, for service life prediction of wood exposed in ground, it is of immanent interest to better understand the different...
C Brischke, F L Wegener
The development of a suitable fire retardant for Radiata pine and other species
2019 - IRG/WP 19-30744
The use of fire retardant chemicals, with the overarching aim of creating a safer environment is not a new one, however it is generally under-developed and is often afflicted with an image of environmental and health issues and misperceived high costs. There is an ever-increasing need and desire for effective fire retardancy in timbers to inhibit or suppress the combustion process. This is paramou...
B R Derham, M R Fortune
Effect ofNano-Copper Oxide on Decay Resistance of Pistachio Twig-Plastic Composite
2019 - IRG/WP 19-30750
The goal of our study was to investigate the decay resistance of pistachio twig-plastic composite treated with nano-copper oxide against the white rot fungus Trametes versicoloer and the brown rot fungus Coniophora puteana. For this purpose, wood–polypropylene composites (WPCs) containing different loadings of nano-copper oxide, namely 0, 1, 2 and 3 percent (W/W), were made from pistachio (Pista...
M R M Farahani,S Pourabdollah
Using X-ray scattering to elucidate the mechanisms behind the moisture and fungal decay resistance of epoxybutene modified wood
2019 - IRG/WP 19-40854
Chemical modification of the hydroxyl groups of wood can improve the properties of wood by providing moisture and biological resistance, as well as dimensional stability. Southern pine solid wood was chemically modified to various weight percentage gains (WPG) with epoxybutene (EpB, 8%-38% WPG). After modification, specimens were extracted with a toluene: ethanol (2:1) solution for 2 hours or wate...
R E Ibach, N Plaza
Development of beech wood thermo-chemical modification treatments based on different vinylic derivatives of glycerol and polyglycerol
2019 - IRG/WP 19-40855
In this study, a combination between chemical and thermal wood modification has been investigated. Seven types of a low concentration of 10% aqueous additive solution of vinylicglycerol [glycerol-maleic anhydride (Gly-MA), glycidyl methacrylate (GM), and Glycerol methacrylate-maleic anhydride (GM/MA(2eq))], vinylicpolyglycerol [polyglycerol-maleic anhydride (PG-MA), polyglycerol methacrylate (PGM...
M Mubarok, S Dumarcay, H Militz, K Candelier, M-F Thevenon, P Gerardin
Dimensional stability and decay resistance of montmorillonite- furfuryl alcohol modified wood
2019 - IRG/WP 19-40856
Poplar (Populus cathayana) wood was impregnated successively by organo-montmorillonite (OMMT; in concentration of 2%) and furfuryl alcohol (FA, in concentrations of 15%, 30% and 50%) in a two-step method to prepare OMMT-FA modified wood. The modified wood samples were characterized using X-ray diffraction (XRD) and field emission scanning electron microscopy (FE-SEM). Moreover, wood physical and a...
L Zhang, J Cao