Accidental mold/termite testing of high density fiberboard (HDF) treated with borates and N’N-naphthaloylhydroxylamine (NHA)
2003 - IRG/WP 03-10462
High density fibreboard (HDF) was made from beech and pine furnish (50:50) and treated with boric acid (0.1-3%), borax (0.1-3%) or N'-N-(1,8-naphthalyl) hydroxylamine (NHA) (0.1-1%) prior to gluing with urea formaldehyde (UF) resin in order to determine resistance to Eastern subterranean termites (Reticulitermes flavipes Kollar), the most economically important termite species in North Am...
S N Kartal, H H Burdsall Jr, F Green III
Performance of preservative-treated timber commodities in above-ground service tests
1995 - IRG/WP 95-20064
Service tests established by NZ FRI are of commodities where treatment has been undertaken in commercial plants and although such data as preservative uptake of individual items is recorded and sample analysis undertaken, material is usually "run-of-mill" for the commodity being treated. The NZ FRI Service Test database includes a wide range of preservative/species combinations in virtually all ab...
M E Hedley, D R Page
The wood preservative performance of biocide mixtures containing chlorpyrifos
1994 - IRG/WP 94-30055
Chlorpyrifos (O,O-diethyl[3,5,6trichloro-2-pyridyl]phosphorothioate) was evaluated as a wood preservative insecticide in two long term field tests. In the first project, pine sapwood blocks treated with chlorpyrifos (CPF) were exposed to Coptotermes formosanus using an above-ground test format. CPF is effective in protecting wood from attack by this termite, but its activity appears to decrease wi...
P E Laks
Administration of wood preservative usage in New Zealand
1977 - IRG/WP 395
Principal administration of the preservative treatment of timber in New Zealand is by the Timber Preservation Authority (TPA). The TPA was established in 1955 by Act of Parliament and is under the jurisdiction of the Minister of Forests who appoints its members. Its field staff are Forest Service employees. The Authority comprises twelve members and includes representatives of timber trade associa...
M E Hedley
Objectives of future collaborative soft rot tests
1972 - IRG/WP 209
Progress has been made towards acceptance of a defined laboratory test method for determining the toxicity of preservatives against soft rot fungi (Documents IRG/WP/201 and IRG/WP/208) and, at the 1971 meeting in Brussels, the framework of collaboration for the next phase of testing was discussed. Time available at Brussels did not permit restatement of objectives, consideration of the stages by w...
J G Savory
Exposure of preservative treated wood to terrestrial microcosms, pure cultures of fungi and in the field
1997 - IRG/WP 97-20114
Small stakes (5x10x100 mm3) of treated and untreated Pinus sylvestris sapwood were exposed in terrestrial microcosms with different soils, two taken from test fields in Sweden, one soil from a conifer forest and one garden compost soil. Stakes of the same size were also exposed to pure cultures of the brown and white rot fungi, Postia placenta and Phanerochaete chrysosporium. After exposure, weigh...
M-L Edlund
Benzalkonium chloride (an AAC preservative): Criteria for approval, performance in service, and implications for the future
1985 - IRG/WP 3328
The data base generated for benzalkonium chloride was considered adequate for commercial approvals, particularly after revision in late 1982. Field trials, although not part of the approval criteria, generally supported commercial use; decay observed in one test (post and rails) after 6 years' exposure would have resulted in some caution in setting retentions. No laboratory trial, nor fie...
J A Butcher
Evaluation of a laboratory soft rot test on basis of weight loss and residual strength
1989 - IRG/WP 2336
Based on the principles of different previously reported experimental procedures dealing with laboratory soft rot testing, a study was conducted on treated poplar and beech. Preservatives used were CCA, CCF, AAC, Azaconazole and TCMTB. Treated samples were exposed for three months in a vermiculite substrate to Chaetomium globosum. Evaluation was based on absolute mass loss, percentage weight loss ...
W Verbeke, J Van Acker, M Stevens
Potential toxicants for controlling soft rot in preservative treated hardwoods. Part 2: Laboratory screening tests using sawdust
1977 - IRG/WP 2101
A technique is described for the rapid screening of toxicants against microorganisms, represented by the brown rot, Gloeophyllum trabeum, and a natural inoculum from soft rotted wood. Sawdust, in this case from sapwood of Eucalyptus maculata, is pretreated with the candidate formulation and moistened before inoculation. Visual scoring of growth can be used to discriminate suitable candidates as ea...
J D Thornton
The development of a new boron-based wood preservative
1995 - IRG/WP 95-30085
The paper describes a new boron based wood preservative for the treatment of green timber. The product offers many benefits over conventional boron diffusion treatment including: 1. high viscosity, high concentration formulation; 2. permits dip treatment of a wide range of sawn board and pole sizes at ambient temperatures; 3. permits full cross section diffusion of borates without block stacking a...
P Turner, D Conradie
Gaseous preservative treatment of wood
1990 - IRG/WP 3631
A recent development in processing wood with a gaseous preservative means that dry, treated wood can be produced in under 30 hours with the benefits of product diversification, faster stock turnover and the ability to respond to short term demand. About 400,000 m³ of wood are treated each year in New Zealand with boron salts to protect from borer infestation. Traditionally this treatment is effec...
R Burton, A J Bergervoet, K Nasheri, P Vinden, D R Page
The examination of preservative-treated radiata pine using electron spin resonance spectroscopy
1987 - IRG/WP 3423
Electron spin resonance spectroscopy (ESR) may be used to characterise the molecular environment of chemical species containing unpaired electrons. These species include free radicals, bi-radicals, point defects in solids, localised crystal imperfections and many transition metal ions. ESR has previously been applied to the examination of wood weathering or wood pyrolysis and now FRI and Massey Un...
D V Plackett, E W Ainscough, A M Brodie
A new factory applied preservative treatment for joinery
2002 - IRG/WP 02-40246
Conventional pre-treatment processes involve the principle of applying preservatives to the external surfaces of wood to achieve the necessary penetration and retention of the chemicals although the heartwood remains difficult to treat.
The present development involves the production of internal reservoirs within new joinery components, which are subsequently filled with a specially developed g...
I M Robertson, W Beauford
A technique for measuring preservative loss or redistribution during leaching
1983 - IRG/WP 2199
Radiata pine sapwood stakes were treated with benzalkonium chloride (AAC) or copper-chrome-arsenate (CCA). After fixation and drying the outer 2 mm and 2-4 mm layers were removed from one radial longitudinal face. The planed face was coated with a waterproof coating and AAC-treated stakes were leached for 6, 12 or 18 weeks; 12 weeks for the CCA-treated stakes. After airdrying three 2 mm layers (0-...
J A Drysdale
Conservation of Nypa fruticans and Indigenous Timber Species of Sundarban Mangrove Forest of Bangladesh by Using Preservative Treatment.
2005 - IRG/WP 05-40297
This report describes the possibilities and benefits of preservative treatment of some Bangladeshi wood species. It is concluded that:
Heartwood of Sundri is not easily treatable. The treating schedule of 14.1 kg/cm² pressure and eight hours treatment period may be used for treating sundry logs. During the treatment of Sundri wood must not mix with other species. Other timber species such as Gew...
G N M Ilias
Performance of preservative-treated rubberwood (Hevea brasiliensis) in Goa and Kochi waters (west coast of India).
1997 - IRG/WP 97-20104
Performance of rubberwood (Hevea brasiliensis) against biodeterioration, when pressure-treated with Copper-Chrome-Arsenic (CCA) and Copper-Chrome-Boric (CCB) and exposed in Mandovi estuary (Goa) and in Kochi waters for a period of 32 months and 9 months respectively, has been discussed. The control panels were completely destroyed within a period of 4 to 6 months at both the localities. The resist...
L N Santhakumaran, M V Rao
Copper based wood preservative - A new approach using fixation with resin acids of rosin
2000 - IRG/WP 00-30249
Copper soaps with carboxylic acid groups of resin acids of rosin were shown to be potential long-term wood preservatives. The principle involved is the attachment of copper to the network formed by the inorganic part of the preservative (rosin) through the -COOH groups. The mechanisms of fixation have been studied, and it has been shown that this association could be obtained : (1) by forming the ...
C Roussel, J P Haluk, A Pizzi, M-F Thévenon
A technique for determining the efficacy of water diffusible preservative plugs for implanting in joinery in service
1987 - IRG/WP 2291
A technique is described for determining the efficacy of soluble, diffusible preservative plugs for eradicating decay in joinery. It uses blocks of Scots pine sapwood or heartwood adjusted to known moisture contents prior to the establishment of the test fungus Coniophora puteana, from a single longitudinal dowel and the subsequent introduction of the preservative plugs. Prevention of decay, eradi...
J K Carey, A F Bravery
A comparison of analytical and visual techniques used for assessment of weathering properties of chromium and copper azole treated timber
1994 - IRG/WP 94-20023
The weathering properties of preservative treated timber were studied by measuring surface lignin loss and by microscopic examination after weathering, and results were related to qualitative assessments of visual appearance after weathering. Measurement of relative rates of delignification of untreated and preservative treated timber obtained by FTIR analysis, and weight loss determined on thin v...
J A Cornfield, M D C Hale, G Fettis
Preliminary pole treatment trials with chlorothalonil in hydrocarbon solvent
1994 - IRG/WP 94-40027
A series of 460-mm long, end-sealed southern pine pole stubs were treated with chlorothalonil in hydrocarbon solvent. Over sixty sections were treated using various combinations of initial seasoning (kiln-drying, steam-conditioning), treating temperature (ambient, 200°F), initial air pressure, and final conditioning (steam flash + vacuum, expansion bath + vacuum, steam distillation + vacuum). Dis...
H M Barnes
Performance of Copper-Chrome-Arsenic (CCA) and Copper-Chrome-Boric (CCB) treated panels of Bombax ceiba and Paraserianthus falcataria against bio-deterioration at Krishnapatnam harbour, east coast of India
2003 - IRG/WP 03-30310
Results of investigations on the durability of light weight timber species (Specific gravity below 0.4) i.e., Bombax ceiba and Paraserianthus falcataria in treated and untreated condition conducted at Krishnapatnam harbour (Lat 13o28’ to 13o59’ N; Long: 80o10’ to 80o16’E) along the east coast of India are reported in the paper. Exposure trails were conducted with panels (Size: 30 x 3.8 x...
B Tarakanadha, N R Raveendra Prasad, K S Rao
Durability of some alternatives to preservative treated wood
2004 - IRG/WP 04-30353
The environmental discussion in Sweden has lead to an increasing use of naturally durable domestic wood species and wood treated according to alternative methods for use above ground. A number of these alternatives have been tested according to field- and laboratory tests and compared to wood treated with preservatives for above ground use. Seven untreated wood species, four alternative wood treat...
M-L Edlund
Fluoride and chromium concentrations in soil adjacent to remedially treated distribution poles
1996 - IRG/WP 96-50066
Soils adjacent to Rentex treated 'on-line' distribution poles were analysed for total fluoride and chromium content for comparison with background values of these elements. Soil samples 6 cm and 25 cm downslope of selected poles were recovered at 1 week, 1 month, 6 and 12 months after treatment. Background soil samples were taken 50 m from the poles at sampling times. Fourteen po...
D C R Sinclair, G M Smith, A Bruce, H J Staines, P Durrant
Examination of preservative-treated Pinus sylvestris using electron paramagnetic resonance
1992 - IRG/WP 92-3710
EPR is currently being used to help elucidate the nature and extent of the chemical reactions occurring between wood and copper based timber preservatives. In the work reported here treated Scots pine samples were examined at room temperature and in the frozen state. Plots of the electronic parameters A|| vs. g|| were found to be a useful index of the electronic properties of the various formulati...
A S Hughes, R J Murphy, J F Gibson, A J Cornfield
The influence of timber species and preservative treatment on spore germination of some wood-destroying Basidiomycetes
1988 - IRG/WP 2300
Basidiospores from six wood decay fungi exhibited varying germination rates on untreated softwood and hardwood blocks. Germination inhibition of all test fungi was recorded on pine sapwood. No preference for a certain timber species by a particular fungus was evident. Whereas almost complete inhibition of germination occurred on wood treated with a quarternary-ammonium based wood preservative, mos...
B M Hegarty, G Buchwald