Buffered Amine Oxide Treatment Systems for Imparting Water Based Azoles/Insecticides in Douglas Fir and Eucalyptus
2015 - IRG/WP 15-40707
In today’s world, wood remains the most versatile, practical and sustainable building material. In contemporary countries, wood is a well-managed renewable resource that has a remarkably small carbon footprint compared to those of steel, aluminium, composites, and concrete. These alternative materials have continued to emerge as viable building materials given the durability issues of untreate...
R W Clawson Jr
Above-ground performance of a buffered amine oxide treatment system against Mastotermes darwiniensis
2016 - IRG/WP 16-10855
Above-ground H2 field tests against Mastotermes darwiniensis were conducted in far north Queensland to assess the efficacy of buffered amine oxide treatments in the softwoods Pinus sylvestris and P. radiata, and the hardwoods Eucalyptus regnans and E. diversicolor. Untreated hardwoods and slash pine bait wood (P. elliottii) were severely attacked or destroyed, while untreated P. sylvestris was mod...
L J Cookson, R W Clawson Jr
The termite resistance of wood impregnated with nano-zinc oxide and nano-zinc borate dispersions
2016 - IRG/WP 16-30691
In this work, the effects of the impregnation with nano-ZnO and nano-ZnB dispersions on the termite resistance of European beech wood were investigated. Three different concentrations (namely 0.5%, 1% and 2%) of the above two materials were tested. Water leaching effect was also investigated. It was concluded that a severe effect in terms of termite workers mortality is induced by the use of both ...
C Lykidis, T de Troya, M Conde, J Galván, G Mantanis
Untreated and copper-treated wood soaked in sodium oxalate: Effects of decay by copper-tolerant and copper-sensitive fungi
2017 - IRG/WP 17-10888
Copper is widely used as the primary component in wood protectants because it demonstrates a broad range of biocidal properties. However, a key concern with using copper in wood preservative formulations is the possibility for brown-rot basidiomycetes to resist the toxic effect. Many brown-rot basidiomycetes have evolved mechanisms, like the production and accumulation of oxalate, which helps thes...
K M Ohno, G T Kirker, A B Bishell, C A Clausen
Effect ofNano-Copper Oxide on Decay Resistance of Pistachio Twig-Plastic Composite
2019 - IRG/WP 19-30750
The goal of our study was to investigate the decay resistance of pistachio twig-plastic composite treated with nano-copper oxide against the white rot fungus Trametes versicoloer and the brown rot fungus Coniophora puteana. For this purpose, wood–polypropylene composites (WPCs) containing different loadings of nano-copper oxide, namely 0, 1, 2 and 3 percent (W/W), were made from pistachio (Pista...
M R M Farahani,S Pourabdollah
Mineralization of European oak with various ionic salt solutions to achieve an in situ precipitation of calcium oxalate
2019 - IRG/WP 19-40861
Thin specimens of European oak (Quercus spp.) with the dimensions of 4 × 20 × 50 mm3 were treated with various aqueous ionic salt solutions of calcium chloride, potassium oxalate and calcium acetate. Additionally, the oak was treated with combinations of calcium chloride and potassium oxalate, as well as calcium acetate and potassium oxalate with the aim to precipitate in situ the water insolubl...
T Franke, T S Volkmer
Study on Nailed Joint with Iron Contamination. Part1: Shear Performance of Nailed Joint with Iron Contamination
2019 - IRG/WP 19-50349
In Japan, The building standard law was amended in 2000.1) The use of metal joint was obligated by this law. Since then, metal joints have been largely used for wooden buildings. Also, Act on the Promotion of Popularization of Long-life Quality Housing was enacted in 2009 and leaving Long-life Quality Housing has been focused on2). However, leaving houses to posterity for a long time causes severa...
R Nakano, D Nakano, H Ishiyama
Study on Nailed Joint with Iron Contamination. Part2: Elucidation of the Occurrence Condition of Iron Contamination
2019 - IRG/WP 19-50350
In recent years, efforts towards wooden buildings are progressing in Japan. And many woods are used in various places. However, various problems have also occurred in wooden buildings. One of the problems is iron contamination which appears when wood and metal chemically react. At present, tree species that are prone to iron contamination and components that cause iron contamination are clarified....
D Nakano, R Nakano, H Ishiyama
NewSiest-Enhancement of UV stability of thermally modified wood through envelope impregnation with nanobased stabilisers
2020 - IRG/WP 20-40909
Thermal modification is a process which improves the properties of wood, resulting in a material that can be disposed at the end of the product life cycle without presenting an environmental hazard. Thermally modified wood retains as a natural product and the grain, original colour variances and characteristics of wood are still present. However, exposure to daylight causes brightening or greying ...
K Srinivasa, M Petrič
The iron reduction by chemical components of wood blocks decayed by wood rotting fungi
2021 - IRG/WP 21-10979
Brown-rot fungi, a group of wood rotting fungi, is well known to be one of major microorganisms that cause the deterioration of wooden buildings in Japan and have been considered to use chelator-mediated Fenton (CMF) reaction in concert with hydrolytic and redox enzymes for degradation of wood cell wall. CMF can be described as a non-enzymatic degradation system that utilizes hydroxyl radicals pro...
R R Kondo, Y Horikawa, K Ando, B Goodell, M Yoshida
Properties of Iron (II) Sulphate treated Norway Spruce
2022 - IRG/WP 22-30765
Exterior wood is exposed to various environmental factors that cause weathering. Weathering is important primarily from an aesthetic standpoint. However, not all parts of the building are equally susceptible to weathering. Parts exposed to moisture will discolour faster than protected parts, such as wood under roof overhangs. To achieve fast and uniform artificial greying, a surface treatment with...
B Lesar, M Humar, M Škamlec
Influence of weathering of wood surfaces before and after treatment with iron(II) sulphate
2023 - IRG/WP 23-30786
Outdoor wood is exposed to various factors that cause the wood to grey or age. The ageing processes can vary greatly depending on the exposure. Parts of the wood that are not exposed to external factors, e.g. under the eaves, are less exposed and the ageing process is therefore slower. This can be accelerated by solutions based on iron ions. In this way, the wood greys quickly and evenly. However,...
B Lesar, M Humar, F Osvald