Long-term field exposure of wood-plastic composites processed on a commercial-size extruder
2020 - IRG/WP 20-40894
Wood-plastic composites (WPC) contain wood fiber (or flour), thermoplastics and additives and are exposed to UV light, moisture, and biological deterioration in outdoor installations. Accelerated laboratory tests can help to predict the durability of WPCs, but long term evaluations are needed to validate these results. Field exposed above-ground WPC deck boards (30.5 x 139.7 x 609.6 mm) and in-gro...
R E Ibach, C M Clemmons, N M Stark
Macro biological degradation of wood treated with sorbitol and citric acid – first results from marine environment and termite exposure
2020 - IRG/WP 20-40901
Most European wood species are rapidly and severely degraded in termite-infested areas and the marine environment. There is a need for new solutions, especially in the marine environment, since we lack wood preservatives approved for marine applications in Europe. Several wood modification systems show high resistance against both marine borers and subterranean termites. However, the existing comm...
A Treu, L Nunes, E Larnøy
Effect of MVOC exposure on mycelial growth of wood rotting fungi
2021 - IRG/WP 21-10977
It is well known that wood rotting fungi produce microbial volatile organic compounds (MVOCs) as metabolites. In our previous studies, we have found that some MVOCs produced by wood rotting fungi are common to fungal species tested in the studies, while others are specific to each species. Furthermore, it has been also shown that each wood rotting fungi do not always produce the same type of MVOCs...
S Horikawa, R Konuma, M Yoshida
Analysis of wooden shingles after seven years of exposure
2022 - IRG/WP 22-20690
Wood is a traditional roofing material in the Alpine regions. In the 17th century, wooden roofing was typically used on more important buildings. Still, today it is predominately used on huts and houses in the hilly regions of northern and north-western Slovenia. Because wooden roofing is expensive, we investigated the possibility of extending the service life of the roofing through impregnation a...
M Humar, B Lesar, D Kržišnik, E Keržič, B Jemec
Properties of Iron (II) Sulphate treated Norway Spruce
2022 - IRG/WP 22-30765
Exterior wood is exposed to various environmental factors that cause weathering. Weathering is important primarily from an aesthetic standpoint. However, not all parts of the building are equally susceptible to weathering. Parts exposed to moisture will discolour faster than protected parts, such as wood under roof overhangs. To achieve fast and uniform artificial greying, a surface treatment with...
B Lesar, M Humar, M Škamlec
Effect of nano-particle characteristics and concentration on UV protection of timber: A field exposure test
2022 - IRG/WP 22-40941
Wood has a well-known susceptibility to ultra-violet light degradation, leading to premature replacement. A variety of products have been developed to protect against this damage, but most provide less than 12 months of protection and must be regularly reapplied. Developing improved coatings would help reduce wood losses and reduce maintenance costs. Nano-particles have a variety of attractive pro...
T Yi, J J Morrell
Mechanical Properties of Thermally Modified Wood after twelve Months of Field Exposure
2022 - IRG/WP 22-40945
This study aimed to evaluate the durability and mechanical properties of two different woood species, namely beech (Fagus sp.) and silver fir (Abies alba), from Bosnia and Herzegovina thermally modified at three different temperatures and duration at maximum temperature. Samples of the mentioned wood species wood (Abies alba) were prepared according to EN 408+A1 standard. The maximum 4-point bendi...
R Hasanagić, M Bahmani, L Fathi, M Humar
Synergized pyrethrins insecticide as a spot treatment option for West Indian drywood termites
2023 - IRG/WP 23-11004
Pyrethrin is a natural biopesticide with relatively low mammalian toxicity. Two identical products in Australia contain pyrethrin in liquid CO2-propelled aerosol, Pestigas from BOC international and SupaPy Supagas. In the current study, the toxicity of SupaPy was tested against West Indian drywood termite Cryptotermes brevis as an option for spot treatment of this pest. Termites were exposed to wo...
B Hassan, C J Fitzgerald
Long-term Performance of Treated Timbers in a Sub-tropical Marine Exposure
2023 - IRG/WP 23-11015
The long-term performance of preservative-treated and modified wood in marine exposures was assessed in Brisbane, Queensland, Australia. This report describes the final destructive assessment of the surviving Australian panels after 11 years of exposure. This site presents the potential for attack by shipworms (likely Bankia spp.), pholads (Martesia striata), Limnoria and Sphaeroma terebrans. Mos...
E L Galore, J Norton, A Zahora
Performance of a noise barrier with different wood materials – results from a service trial after 25 years of exposure
2023 - IRG/WP 23-30776
In connection with the construction of the railway connection between Stockholm Arlanda airport and Stockholm city, an 11 km long noise barrier made of untreated European larch was built along the railway line. This provided an opportunity to implement a full-scale study comparing different untreated wood species and preservative treatments. Thus, in March 1996 ten test sections including untreate...
J Jermer, M Westin
Outdoor performance of Tanalith® K treated timber: Dimensional stability and corrosivity towards metal fasteners
2023 - IRG/WP 23-30798
This study was carried out to investigate dimensional stability and corrosivity towards metal fasteners in radiata pine (Pinus radiata D. Don) treated with Tanalith® K to Hazard class 4 (H4) retentions in comparison with chromated copper arsenic (CCA) treated timber. For corrosion test, untreated and treated matched specimens were prepared from Australian-grown radiata pine, tested with mild stee...
G Rassam, J Hague, D Humphrey
Exposure tests on railroad ties treated with DOT
2024 - IRG/WP 24-20705
Keruing railroad ties were treated with disodium octaborate tetrahydrate (DOT) to retentions of 0.7 to 1.7% boric acid equivalent (BAE) and selected borate treated ties were subsequently over treated with creosote/diesel fuel mixture. The treated ties were exposed in a simulated railway track test bed in Malaysia. The leaching of borate was measured over 5 years. BAE in the ties after 5 years of e...
L Arthur, J-W Kim
Evaluation of the water exclusion ability and inherent bioactivity of heartwood against decay in Japanese and European wood species via above-ground exposure and water absorption tests
2024 - IRG/WP 24-40998
The natural durability of wood has been thought to mainly depend on bioactive extractives and the water exclusion ability. To clarify the contribution of each factor to wood durability, above-ground exposure tests were conducted on Japanese and European wood species. A double-layer test was carried out using heartwood specimens of four wood species, i.e., Japanese cedar, Japanese cypress, Scots pi...
T Osawa, R Noda, K Yamamoto
Outdoor termite resistance performance of zinc borate (Borogard® ZB) treated parallel strand lumber (PSL) – 15 years field test results
2024 - IRG/WP 24-40999
This report discloses the outdoor termite resistance performance of PSL samples treated with zinc borate at a dosage of 0.85% BAE and 1.72% BAE in Wuxi, China. The outdoor field trial lasted for 15 years and observations were made after 6 months, 3 years, 5 years 1 month, 6 years 6 months and 15 years. The retaining rates of B2O3 and ZnO in the final samples were also tested, and the hypothesis wa...
S Shi, E Laval, K Lung, F Ascherl, R Williams, W Li, X Li
How personality traits influence the perception of fungal decay in a wooden cladding – A survey in three Modelling wood moisture content in outdoor conditions from measured data
2024 - IRG/WP 24-41002
This study examined perceptions of fungal decay damage on wooden cladding across Norway, Sweden, and Germany. The majority of respondents across all countries did not find the fungal decay damage in question acceptable, with the least acceptance in Norway. This could be due to Norway having the highest frequency of wooden residential buildings and the most experience with maintaining wooden claddi...
G W Gustavsen, G Alfredsen, P B van Niekerk, J Niklewski, C Brischke
Modelling wood moisture content in outdoor conditions from measured data
2024 - IRG/WP 24-41005
Sustainable use of wood requires an understanding of expected service life, particularly when the material is exposed to outdoor conditions and, thus, fungal decay. Since moisture is the primary vector for fungal decay, accurate moisture prediction is a key component in service life assessment. For this purpose, the present study leverages existing measured data for linear regression of in-field m...
J Niklewski, P B van Niekerk, L Meyer-Veltrup, J Sandak, C Brischke