Your search resulted in 3298 documents. Displaying 25 entries per page.
Practical extraction of metals from CCA-treated wood
2014 - IRG/WP 14-50305
The extraction effects of acid concentration, reaction time and temperature in a microwave reactor on recovery of chromated copper arsenate (CCA)-treated wood were evaluated. Extraction of copper, chromium, and arsenic metals from CCA-treated southern pine wood samples with three different wood particle sizes (i.e., (1) 0.5 cm3, (2) 0.5x05x1.0 cm, and (3) 0.5x0.5x1.5 cm) was investigated using a m...
Bin Yu, Chung Y Hse, T F Shupe
VOC-free remedial treatment agent on organic solvent basis with surface cleaning by photocatalysis using titanium dioxide
2014 - IRG/WP 14-40651
Due to the EU Regulations according to the harmonisation of the European market of biocidal products and the EU Regulations regarding emissions of volatile organic compounds in residential properties a new VOC free yet organic solvent based remedial treatment agent is introduced including a potential method to clean up the wooden surface of remaining biocides after a remedial treatment using photo...
H Ahl, J Fromm, P Jüngel, E Melcher, M Pallaske
Nano-Zycosil in MDF. Part I: Gas and Liquid Permeability
2014 - IRG/WP 14-40652
Effects were studied of zycosil nanoparticles, with size range from 20 to 80 nm, on liquid and gas permeability of medium density fiberboard. Nanozycosil was used at four consumption levels of 0, 50, 100, and 150 g/kg dry wood fibers. Density of all treatments was kept constant at 0.67 g/cm3. The obtained results indicated that the addition of zycosil to the mat resulted in a significant increase...
H Reza Taghiyari, A Karimi, P M D Tahir, O Schmidt, E Bari, P Nouri , A Jahangiri
Effect of silver nanoparticles on the rate of heat transfer to the core of the medium-density fiberboard mat
2014 - IRG/WP 14-40653
Effect of silver nanoparticles on the rate of heat transferred to the core section of medium-density fiberboard (MDF) mat was studied here. A 400 ppm aqueous nanosilver suspension was used at three consumption levels of 100, 150, and 200 mL/kg based on the weight of dry wood fibers; the results were then compared with the control MDF panels. The size range of silver nanoparticles was 30-80 nm. Res...
H Reza Taghiyari, O Schmidt, E Bari, P M Tahir, A Karimi, P Nouri, A Jahangiri
Evaluation of vessel features on physical and mechanical properties of wood of Common black poplar (Populus nigra L.) grown at different elevations in the region with a continental climate
2014 - IRG/WP 14-40656
This study essentially examined the effect of elevation on the anatomical structure, and the physical and mechanical properties of Common black poplar (Populus nigra L.) wood. The scope of the study was to observe the variability of vessel element features on physical and mechanical properties of Common black poplar (Populus nigra L.) in relation to habitat at different elevations. For this purpos...
I Usta
The resistance of Accoya® and Tricoya® to attack by wood-destroying fungi and termites
2014 - IRG/WP 14-40658
The resistance of high acetyl WPG solid timber (Accoya®) and medium density fibreboard (Tricoya®) to attack by wood-destroying fungi and termites was investigated under both laboratory and field conditions. Laboratory decay studies were conducted in Australia and New Zealand. Field studies were conducted in Australia, Japan, New Zealand, Thailand and USA. The results of the laboratory and field ...
J Alexander, J Hague, F Bongers, Y Imamura, M Roberts
Full-scale impregnation of wood with siloxane using supercritical carbon dioxide
2014 - IRG/WP 14-40659
Full-scale impregnation of wood with siloxane was carried out using supercritical carbon dioxide as solvent. A batch of 3530 kg of Scots pine sapwood was impregnated to a retention of approximately 1.3% siloxane. The treatment also consisted of a simultaneous impregnation with organic biocides. The performance of the wood was evaluated in terms of capillary water uptake according to a modified EN ...
A Kjellow, F Imsgard, J Fernandes, R Wagner, J Delis
The effect of UV irradiation on some technological properties of different polyurethane varnishes coated plywood panels from veneers dried at different temperatures
2014 - IRG/WP 14-40661
In this study, the effect of UV irradiation on some technological properties of three different polyurethane varnishes coated plywood panels produced from Scots pine (Pinus sylvestris L.) and Maritime pine (Pinus pinaster L.) veneers manuactured and dried at different temperatures was studied. Accordingly, 32°C log peeling temperature and three different veneer drying temperatures (110, 140 and ...
Ö Özgenç, C Demirkir, Ü C Yildiz, G Çolakoğlu
Effect of Nano-Wollastonite on Water Absorption in Particleboard
2014 - IRG/WP 14-40662
Effects of wollastonite nanofibers on physical properties of particleboard were studied. Nano-wollastonite (NW) was applied at 5, 10, 15, and 20 g/kg, based on the dry weight of wood-chips, and compared with control specimens. Two application methods of NW were used: surface application (SA), and internal application (IA). Density was kept constant at 0.68 g/cm3 for all treatments. Tests were carr...
S Karimi, H Reza Taghiyari, A Karimi, P M Tahir, J Abdul Halip
Improving dimensional stability of thermally treated wood by secondary modification – potential and limitations
2014 - IRG/WP 14-40664
The potential of treating thermally modified wood with melamine resin to improve the dimensional stabilization is tested in this research. Two different boards of poplar (Populus ssp.) were cut into two halves. One half of each board was thermally modified (T1 and T2) in a commercial process, the other half was used as untreated reference material. The material was thermally modified using the vac...
G Behr, K-C Mahnert, S Bollmus, H Militz
Development of new wood treatments combining boron impregnation and thermo modification - Effect on decay and termites durability
2014 - IRG/WP 14-40666
Environmental pressures appeared in most European countries during the last decade has lead to the development of more environmentally acceptable preservation methods. In this context, wood heat treatment has been one of the most investigated alternative methods during the last years. Treated at temperatures ranging between 180 and 220°C, wood components undergo more or less important chemical mo...
S Salman, A Pétrissans, M-F Thévenon, S Dumarçay, B Pollier, P Gérardin
Performance of some wood modification treatments against marine borers
2014 - IRG/WP 14-40668
Since some years, new treatment technology to protect wood against wood destroying fungi is introduced. Limited knowledge on their resistance to water organisms is available. Therefore, the resistance of chemically modified wood was assessed in a field test according to the European Standard EN 275 over a period of 3 resp. 5 years at sites in the North Sea and the Baltic Sea. Scots pine (Pinus syl...
A Klüppel, C Mai, H Militz, S Cragg
A guideline for sorting easy to impregnate Scots pine sapwood based on three treatability studies from Northern Europe
2014 - IRG/WP 14-40669
Scots pine sapwood is generally considered an easy to impregnate wood species, though it reportedly faces challenges towards a homogeneous impregnation and large variations in treatability are reported for the material.
This study comprises the results of three treatability tests that were performed on Scots pine (Pinus sylvestris) sapwood. The material impregnated was originated from a large ...
K Zimmer, E Larnøy, A Treu
Study of in-situ gel polymerization established by Si-O-Si framework within wood micropores
2014 - IRG/WP 14-40672
Sodium silicate was used to form Si–O–Si framework by gel process and optimize the effect of the methylolurea impregnation on poplar wood. The modifier cured within the wood micropores by in-situ gel polymerization during the kiln drying. The results showed that treated wood acquired higher mechanical strength, but lower hygroscopicity. New positions of the XRD peaks appeared which caused by s...
Zeng Bi, Qian Lang, Heyu Chen, Junwen Pu
Development of composite furniture using bamboo strips, bamboo mat and rubber wood veneer
2014 - IRG/WP 14-40679
Bamboo offers cost-effective component in panel form is well suited to wood substitute can be used as furniture components. In the present study, borak (Bambusa balcooa ) bamboo were used for manufacturing bamboo panel. Mitinga (B. tulda) bamboo were used for making mat and rubber wood veneers were used for manufacturing mat overlaid veneer board. Borax-boric acid (BB) treatments were given to enh...
K Akhter, M Mahabubur Rahaman, M H Chowdhury, M Zahirul Alam
Compatibility of Acetylated Wood and Wet Concrete
2014 - IRG/WP 14-40673
One of the newer commercial technologies to provide stability and durability to wood and wood composites is the process of acetylation (the reaction of acetic anhydride with wood). Wood is often used in contact with concrete, although only a very limited amount of species are suitable for this type of application because of durability issues. From this perspective durability class 1 timber such ...
R Rowell, C Lankveld, J Alexander
Possible targets of wood modification in brown rot degradation
2014 - IRG/WP 14-40676
Wood modification protects wood from fungal degradation in a non-toxic manner. However, the mechanisms behind the decay resistance in modified wood are currently unknown. The aim of this study was to discuss the i) colonisation, ii) nutrient recognition, iii) transcription, iv) depolymerisation and v) hydrolysis steps in the brown rot degradation progress and explore whether they are inhibited by ...
R Ringman, A Pilgård, G Alfredsen, B Goodell, K Richter
Lignin Modification to Produce Sustainable Polyurethane Resin for Wood Coatings
2014 - IRG/WP 14-40682
The use of lignin as the most abundant aromatic natural polymer has been evaluated for use in the production of lignin-based polyurethane resin for coating applications. Coatings are made of resins (ca. 50%), which today are mainly derived from petroleum-based polymers. This study is focused on the development of an environmentally friendly method of modifying lignin to be used as source of natura...
M Nejad, M Arefmanesh, S Chandra, J Mostaghimi, E Master
The susceptibility of oriented structural straw board (OSSB) to damage by subterranean wood-destroying and grass-feeding termites in Australia
2014 - IRG/WP 14-40683
The field performance of untreated oriented structural straw board (OSSB) made from wheat straw was evaluated against two economically important Australian species of wood destroying subterranean termite, Coptotermes acinaciformis and Mastotermes darwiniensis, and two Australian species of grass-feeding subterranean termite, Amitermes meridionalis and Nasutitermes triodiae. Oriented strand board (...
J Hague, D Scown, J Creffield, M Neal
Leachability and Dimensional Stability of Nanosilver-Steamed Densified Poplar
2014 - IRG/WP 14-40684
This study was aimed to investigate leachability and dimensional stability of nanosilver impregnated poplar (Popolus alba), steamed before hot compression. Wood samples were impregnated with nanosilver suspension (200 and 400 ppm) under pressure of 4 bar for 20 minutes. Steam treatment was carried out at 150°C for 2 hours. Then samples were compressed (33%) radially in a hot press at 170°C for 3...
G Rassam, A Talaei, A Ahmadi
Buffered Amine Oxide Treatment Systems for Ammonical Copper Wood Preservatives
2014 - IRG/WP 14-40685
Wood is the most versatile, practical and sustainable building material in the world. In modern countries, wood is a well-managed renewable resource that has a small carbon footprint. Wood does suffer from a lack of durability against invasive organisms such as insects and fungi. Steel, aluminum and composites have emerged as viable alternative building materials. These sectors market the defi...
R W Clawson Jr
Laboratory Study of Relative Leachability of Chromated Copper Arsenate Preservative from Treated Woods among Soil Types of Sarawak
2014 - IRG/WP 14-50307
Wood and soils are important natural resources from the environment and serves mankind well respectively as structural materials and natural platform erecting such materials. With shortfalls of naturally durable timber species for protected in-ground uses under Malaysian environments, Chromated Copper Arsenate (CCA) treated woods are widely used instead, incurring serious potential threats of pres...
A H H Wong, P K F Chong
Ammoniacal zinc borate as solid wood preservative
2014 - IRG/WP 14-30659
Zinc borate, well-known for its fungicidal, insecticidal and flame resistant properties, is widely used in manufacture of lignocellulose particle board. This form of borate is the least water soluble form available providing advantages as well as disadvantages for use as a wood preservative. This form does not leach from wood under conditions of high humidity, but it is also very difficult to appl...
C Ibáñez, C Mantero, A Ibarra, M Rabinovich
Douglas-fir PSL Treated with Oilborne Copper Naphthenate – Treatment Experience & Efficacy
2014 - IRG/WP 14-40687
Treating characteristics, field stake efficacy and the results from treatment trials for oilborne copper naphthenate (CuNap) and Douglas-fir parallel strand lumber (PSL) are summarized in this paper. Treatment with a P9 Type-C based solution in laboratory tests showed full cross section penetration of large cross sections could be achieved. Commercial treatment trials using a P9 Type-A solution ...
G P Merrick
Influence of the moon phase on durability against wood decay fungi of Larix kaempferi and Pseudotsuga menziesii wood species
2015 - IRG/WP 15-10836
The analysis of the natural durability of wood is essential when establishing the level of protection required, depending on the designated end use of timber. On the other hand, there is a popular belief based on the influence of the moon phase in felling timber, recommending the waning moon as the optimum for felling trees. In fact, some companies now offer among their products, sawn timber felle...
M T Troya, M Conde, M J Barriola, F Llinares, V Dorronsoro