Decay and water resistance of Siberian and European larch wood
2019 - IRG/WP 19-10941
The occurrence of larch wood is rather frequent in civil engineering. Namely, in building façades, terraces and balcony fences. In Slovenia and other central European countries, the use of the Siberian larch is especially popular. In this research, the durability against decay fungi in laboratory conditions and water exclusion ability of plantation-grown and naturally grown Siberian larch (Larix ...
B Lesar, D Krzisnik, M Humar
Natural durability of four Tunisian Eucalyptus wood species and their respective compositions in extractives
2019 - IRG/WP 19-10942
In the 50’s, Tunisia government introduced more than 11 Eucalyptus wood species. Eucalyptus species were planted in Tunisia in different arboreta throughout the country for close observation and adaptation to climate and soil. These fast-growing wood species were mainly used as fire wood, for the production of mine wood and to fight against the erosion. These tree species were adapted themselve...
S Ben Ayed, M T Elaieb, S Dumarçay, B De Freitas Homen De Faria, M-F Thévenon, P Gerardin, K Candelier
Quantifying the effect of microclimatic parameters on the moisture-induced decay risk of wooden structures
2019 - IRG/WP 19-20649
Wood exposed outdoors is prone to fungal degradation. Besides its material-inherent resistance, numerous factors are impacting on its service life with both, climate and design having a major effect. In addition, topography, shading, wind barriers, and other local parameters have an effect on the microclimatic conditions at site and therefore need to be quantified for service life prediction of wo...
L Emmerich, C Brischke
Exploring the use of X-ray micro CT as a tool for the monitoring of moisture production and mass loss during lab-based fungal degradation testing
2019 - IRG/WP 19-20654
Bio-based building materials, such as wood and wood-engineered products, are susceptible to degradation by decay fungi. In-depth knowledge on the intricate material-fungus relationship as well as performance data for many bio-based building materials are still lacking, and especially knowledge on how a material’s structure and moisture properties affect the degradation process is missing. Althou...
L De Ligne, J Van den Bulcke, A De Muynck, J M Baetens, B De Baets, L Van Hoorebeke, J Van Acker
Impact of water holding capacity and moisture content of soil substrates on the moisture content of wood in terrestrial microcosms
2019 - IRG/WP 19-20662
Terrestrial microcosms (TMC) are frequently used for testing the durability of wood and wood-based materials as well as the protective effectiveness of wood preservatives. In contrary to experiments in soil ecology sciences, the experimental set-up is usually rather simple. However, for service life prediction of wood exposed in ground, it is of immanent interest to better understand the different...
C Brischke, F L Wegener
Relative efficacy of various oxine copper formulations against brown-rot fungi
2019 - IRG/WP 19-30741
This paper investigates the relative resistance of three different oxine copper formulations (oil-borne, water-borne, water-borne with pH-adjustment) as a preservative treatment for wood against brown-rot fungi. Impregnated southern pine sapwood cubes were exposed to R. placenta and G. trabeum cultures in a soil-block test. After eight weeks, the weight losses of the cubes were examined in relatio...
M Petruch, J Lloyd, A Taylor
The development of a suitable fire retardant for Radiata pine and other species
2019 - IRG/WP 19-30744
The use of fire retardant chemicals, with the overarching aim of creating a safer environment is not a new one, however it is generally under-developed and is often afflicted with an image of environmental and health issues and misperceived high costs. There is an ever-increasing need and desire for effective fire retardancy in timbers to inhibit or suppress the combustion process. This is paramou...
B R Derham, M R Fortune
Effect ofNano-Copper Oxide on Decay Resistance of Pistachio Twig-Plastic Composite
2019 - IRG/WP 19-30750
The goal of our study was to investigate the decay resistance of pistachio twig-plastic composite treated with nano-copper oxide against the white rot fungus Trametes versicoloer and the brown rot fungus Coniophora puteana. For this purpose, wood–polypropylene composites (WPCs) containing different loadings of nano-copper oxide, namely 0, 1, 2 and 3 percent (W/W), were made from pistachio (Pista...
M R M Farahani,S Pourabdollah
Development of beech wood thermo-chemical modification treatments based on different vinylic derivatives of glycerol and polyglycerol
2019 - IRG/WP 19-40855
In this study, a combination between chemical and thermal wood modification has been investigated. Seven types of a low concentration of 10% aqueous additive solution of vinylicglycerol [glycerol-maleic anhydride (Gly-MA), glycidyl methacrylate (GM), and Glycerol methacrylate-maleic anhydride (GM/MA(2eq))], vinylicpolyglycerol [polyglycerol-maleic anhydride (PG-MA), polyglycerol methacrylate (PGM...
M Mubarok, S Dumarcay, H Militz, K Candelier, M-F Thevenon, P Gerardin
Dimensional stability and decay resistance of montmorillonite- furfuryl alcohol modified wood
2019 - IRG/WP 19-40856
Poplar (Populus cathayana) wood was impregnated successively by organo-montmorillonite (OMMT; in concentration of 2%) and furfuryl alcohol (FA, in concentrations of 15%, 30% and 50%) in a two-step method to prepare OMMT-FA modified wood. The modified wood samples were characterized using X-ray diffraction (XRD) and field emission scanning electron microscopy (FE-SEM). Moreover, wood physical and a...
L Zhang, J Cao
Monitoring of the building made of CLT in Ljubljana
2019 - IRG/WP 19-40860
Wood is one of the most important construction materials and its use in building applications has further expanded in recent decades, predominately due to development of the modern composites, like cross-laminated timber. In order to enable even more extensive and reliable use of wood in outdoor applications, factors affecting wood’s service life need to be understood. It is well known that fung...
M Humar, D Krzisnik, B Lesar, N Thaler, B Dujic
Thermal performance and fire safety properties of traditional circumferential log-cabin walls
2019 - IRG/WP 19-40872
The paper describes the experiment of fire resistance of a circumferential log-cabin wall fragment using various structural modification of the gap between two log members. The influence of the gap structural modification on the criterion of fire resistance E (envelop integrity) and I (insulation) is evaluated. The evaluating criteria are represented by the development of temperatures measured in ...
S Jochim, L Makovicka Osvaldova, M Zachar, Z Danihelova
Durability testing of mass timber building elements: a call for a collaborative trial
2019 - IRG/WP 19-40875
Mass timber buildings have captured the imagination of architects and engineers seeking more environmentally friendly building materials. The mass timber movement has tremendous potential to markedly increase timber use in mid-rise to high rise buildings. With great promise, however, comes great risk. Most mass timber structures that have been built or are being planned use no protective treatm...
J J Morrell
The impact of additional interior layers to the moisture dry-out and mould growth risk of CLT walls
2019 - IRG/WP 19-40876
The objective of this study was intended to determine the maximum allowable initial moisture content for CLT walls having both exterior and interior thermal insulation. A laboratory test was conducted, for which four test walls with two different insulation solutions and two different initial moisture contents were built. Based on the test results a simulation model was configured and simulations ...
V Kukk, J Kers, T Kalamees
Fungal damages in Norwegian massive timber elements – causes and measures
2019 - IRG/WP 19-40879
Massive wood elements are relatively new in Norway but the use is growing quickly, primarily the use of cross-laminated timber (CLT). Moisture performance of massive timber elements has been examined by some researchers, but more knowledge is needed. There is uncertainty regarding the need for vapour barriers or retarders in roof assemblies, and for practical reasons buildings are rarely assembled...
M S Austigard, J Mattsson
Novel approaches for improvement of dimensional, photo- and thermal stability of wood through liquefied wood polyols impregnation
2019 - IRG/WP 19-40884
The major problems encountered in both indoor and outdoor utilization of wood are due photo instability and dimensional instability. The modification of Melia dubia wood for ultraviolet resistance and dimensional stability with liquefied wood has been carried out through impregnation method under solvent free conditions. The level of impregnation in modified wood was estimated by weight perc...
A Kumar, A John, T S Mehra
Durability and climate change - implications for wood building structures
2019 - IRG/WP 19-50361
Sustainable building practices are rooted in the need for reliable information on the long-term performance of building materials; specifically, the expected service-life of building materials, components, and assemblies. This need is ever more evident given the anticipated effects of climate change on the built environment and the many governmental initiatives world-wide focused on ensuring that ...
M Lacasse
Moisture and temperature conditions in an old, highly moisture-loaded timber building in the Røros municipality, Norway
2020 - IRG/WP 20-10966
A 150 years old log building near Røros, Norway, has been in active use as a cowshed since its erection. The animals are kept inside the cowshed all winter and this causes a situation of a high moisture load on the wooden floor, wooden walls and ceiling. Logging of temperature and humidity over one year shows that there are favourable levels of moisture in the wood and air for development of moul...
M Sand Austigard, J Mattsson
Resistance against marine borers: About the revision of EN 275 and the attempt for a new laboratory standard for Limnoria
2020 - IRG/WP 20-20669
Wood protection technology in the marine environment has changed over the last decades and will continue to do so. New active ingredients, newer formulations, and novel wood-based materials including physically- and chemically-modified wood, together with increasing concerns over environmental impacts of wood preservatives, urgently demand a major revision of EN 275 “Wood preservatives – Deter...
S Palanti, S Cragg, R Plarre
Studying amount, location and state of water in modified wood at moisture levels relevant for fungal degradation
2020 - IRG/WP 20-40889
Water is an essential parameter for fungal degradation of wood, but degradation primarily occurs at high moisture levels at water potential in the range of -4 to -0.1 MPa, which corresponds to 97-99.9% relative humidity. At these moisture levels, water is present in the wood structure both in and outside of cell walls. The majority of previous studies on the interaction between wood and water for ...
M Fredriksson, E Engelund Thybring, Ramunas Digaitis
Limiting Polysaccharide Motion Protects Wood From Decay
2020 - IRG/WP 20-40890
It is well known that chemical modifications to improve decay resistance also reduce the equilibrium moisture content (EMC) of wood. The mechanism of this action, however, has been the subject of much debate. Several groups have suggested that decay resistance is a result of lower diffusion rates of fungal degradation agents through the wood cell wall. A recent paper explained the fundamental prin...
C G Hunt, S L Zelinka, J E Jakes
Long-term field exposure of wood-plastic composites processed on a commercial-size extruder
2020 - IRG/WP 20-40894
Wood-plastic composites (WPC) contain wood fiber (or flour), thermoplastics and additives and are exposed to UV light, moisture, and biological deterioration in outdoor installations. Accelerated laboratory tests can help to predict the durability of WPCs, but long term evaluations are needed to validate these results. Field exposed above-ground WPC deck boards (30.5 x 139.7 x 609.6 mm) and in-gro...
R E Ibach, C M Clemmons, N M Stark
Impregnation of railway sleepers - Investigation of a system-sleeper as an alternative for creosote treated sleepers
2020 - IRG/WP 20-40896
For nearly 200 years wooden railway sleepers are impregnated with creosote. After initially using vacuum pressure processes for impregnation, empty-cell processes have been developed quickly and are used until today. Because of political developments, creosote will probably be banned on the European market in the near future. The Fürstenberg-System-Sleeper, which combines for Europe innovative as...
M Starck, A Heidel, C Brischke, H Militz
Biological durability of sapling wood
2020 - IRG/WP 20-10967
Sapling-wood products from different wood species such as willow (Salix spp.) and Common hazel (Corylus avellana) are frequently used for gardening and outdoor decoration purposes. Remaining bark is suggested to provide additional biological durability. Even for temporary outdoor use it seemed questionable that durability of juvenile sapwood can provide acceptably long service lives of horticultur...
C Brischke, L Emmerich, D G B Nienaber, S Bollmus
Validating a short-term laboratory method to assess the resistance of timber to biodegradation by marine wood-borers
2021 - IRG/WP 21-10975
Novel approaches to protecting wood in coastal and marine environments are needed as the use of traditional broad-spectrum biocides are now restricted. Wood is widely utilised in marine environments where it can be rapidly degraded by wood-boring organisms, causing billions of dollars of damage per annum. Biocidal compounds such as CCA and creosote have been popular treatments for timber products ...
L S Martin, J R Shipway, G P Malyon, S M Cragg