Your search resulted in 173 documents. Displaying 25 entries per page.
A note on the distribution of copper-chrome-boric (CCB) along the culm length of freshly felled bamboo treated by modified Boucherie process
2005 - IRG/WP 05-40317
Preservative treatment of green and dry bamboo poses severe problems. A number of bamboo/ wood preservatives (Chemical formulations) for the destroying organism like fungi, borers and termites etc. In this paper we reported preliminary results of treatment of fresh green round bamboo attached with baranches by modified Boucheri process. Sample full length of an Indian species of bamboo Dendrocalam...
R Lal, C N Vani
The biological effectiveness of wood modified with heptadecenylsuccinic anhydride against two brown rot fungi: Coniophora puteana and Gloeophyllum trabeum
1992 - IRG/WP 92-3705
A modified soil block test was carried out using wood samples reacted with heptadecenylsuccinic anhydride (ASA). This modification gave good resistance to decay brought about by the brown rot fungi Coniophora puteana and Gloeophyllum trabeum during the twelve week exposure period. Results indicated that there was a good correlation between increased loading of modifying reagent and an increase in ...
C Codd, W B Banks, J A Cornfield, G R Williams
Evaluation of outdoor weathering performance of modified wood
2004 - IRG/WP 04-20296
Interlace treated, oil treated, silicon treated as well as untreated Scots pine samples have been exposed outdoors. For evaluating the samples on their long term performance an internal standard had been developed. Parameters to be determined were the uptake of liquid water (submersion test), weight variation during exposure, crack performance, surface roughness and colour change.
This paper disc...
Y Schulte, S Donath, A Krause, H Militz
Field Trials with mini-stakes
2002 - IRG/WP 02-20244
In 1995 an extensive field test program with wood mini-stakes, 8 x 20 x 200 mm, was started. In these trials a large number of parameters are being evaluated, including several new wood preservatives, differently chemically modified woods and natural durability of various wood species. The test sites are three fields in Sweden for in-ground and “close to ground” testing, one subterranean termi...
M Westin, A O Rapp, Y S Hadi, T Nilsson
Results on field stake tests against termite – Maximum for 8 years examination at Kumamoto in Japan
2003 - IRG/WP 03-10463
Various preservative treated or modified wood and charcoal painting stakes were tested in field, maximum for eight years in Kumamoto, distributed two main termite species, Coptotermes formosanus and Reticulitermes speratus. After two years in field, untreated sapwood of sugi (Cryptomeria japonica) were observed severe attacks by termites, but the preservative treated stakes were observed no signif...
K Suzuki
The Effect on Biological and Moisture Resistance of Epichlorohydrin Chemically Modified Wood
2002 - IRG/WP 02-40224
Southern pine solid wood and fiber were chemically modified with epichlorohydrin to help in understanding the role of moisture in the mechanism of biological effectiveness of chemically modified wood. The solid wood had weight gains from 11% to 34%, while the fiber had weight gains from 9% to 75%. After modification, part of the specimens were water leached
for 2 weeks or extracted for 2 hours ...
R E Ibach, B-G Lee
Screening of modified linseed oils on their applicability in wood protection
2004 - IRG/WP 04-30346
In this study modified linseed oils, rape oil and three waxes were screened on their efficacy as wood protecting agents. By testing all products when impregnated with high retentions in Scots Pine sapwood on water repellence qualities, additionally an accelerated weathering test, drying quality, accelerated brown rot and blue stain test, an indication is formed of the capability of these products ...
A Treu, J Lückers, H Militz
Industrial fixation of chromium based wood preservatives
1990 - IRG/WP 3630
Fixation is an abstract and non-defined process. Nevertheless it is a specified requirement in most impregnation standards. The impregnation industry is facing increased pressure to deliver fixed products and to increase the safety of the handling of impregnated products. Industrial fixation of impregnated wood can be obtained by using different methods. The purpose of the process is to transform ...
T Christensen
Comparison of thermally modified wood originating from four industrial scale processes – durability
2002 - IRG/WP 02-40229
This study examined the differences in biological wood properties of heat treated wood originating from four different European industrial heat treatment plants. The manufacturers of heat treated material were: PLATO Hout B.V./Netherlands, Thermo Wood/Finland, New Option Wood/France and Menz Holz/Germany where Oil-Heat treated Wood (OHT) is produced.
The results of miniblock tests with basidiomyc...
C R Welzbacher, A O Rapp
A quantitative weathering study of wood surfaces modified by chromium VI and iron III compounds
1989 - IRG/WP 2330
Thin veneers of Pinus radiata were treated with dilute aqueous solutions of chromium VI and iron III compounds and exposed to natural weathering for 35 days. Zero-span tensile strength and weight losses of treated veneers were compared with losses observed in untreated specimens In a study designed to demonstrate the applicability of strength and weight loss measurements to the rapid quantitative ...
P D Evans, K J Schmalzl
Characteristics of thermally modified wood in vacuum
2004 - IRG/WP 04-40287
In commercial thermal wood modification processes nitrogen, steam or oil has been used for the reduction of oxygen content in the reactor atmosphere. In present study no special heating medium, but an initial vacuuming step has been used for this purpose. Mass loss, resistance to fungal decay, dimensional stability, bending strength and modulus of elasticity of heat treated wood were evaluated and...
G Rep, F Pohleven, B Bucar
Chemically modified tannin and tannin-copper complexes as preservatives for wood
2001 - IRG/WP 01-30271
The efficacy of Mimosa tannin, chemically modified tannin, and tannin-copper complexes as wood preservatives was studied. When the tannin-ammonia-CuCl2 solutions were impregnated into wood specimens in a one-step procedure, a large quantity of the tannin-copper complex was fixed in the specimens. Little of the complex was leached from specimens by a weathering treatment, and these specimens showed...
H Yamaguchi
A field evaluation of modified and unmodified alkylammonium compounds
1987 - IRG/WP 3436
Laboratory soil block studies of alkylammonium compounds (AAC's) at Forintek and other research establishments have shown that they can prevent decay by standard wood-destroying fungi. Their performance in field tests, however, has been disappointing. Following investigation of possible causes for this poor field performance, stakes treated with modified AAC's were installed at W...
J N R Ruddick
Blue Staining of Coated Modified and Unmodified Wood
2006 - IRG/WP 06-10589
We investigated resistance of unmodified, DMDHEU modified and oil heat treated uncoated and coated Scots pine wood against blue stain fungi. Both EN 152-1 and the reverse exposure tests showed excellent resistance of DMDHEU and especially of oil heat treated wood against blue staining. It is not needed to add any additional protective coating layers to prevent modified wood from staining. However,...
M Petric, M Pavlic, M Humar, M Tomažic
Identification of fungi colonising coated and modified wood exposed outdoors using sequencing and T-RFLP profiling
2006 - IRG/WP 06-20326
Wood decay and staining fungi are known to colonize coated and modified wood. Rapid and reliable ways of identifying fungi on coated and modified wood may improve diagnostics and product development. In this work nine fungi growing in painted wood panels exposed outdoors at a test field in Uppsala, Sweden, were identified using sequencing and T-RFLP (Terminal Restriction Fragment Length Polymorphi...
U Råberg, J Bijelovic, C J Land, S Bardage, N Terziev
High-energy multiple impact (HEMI)-test – Part 1: A new tool for quality control of thermally modified timber
2006 - IRG/WP 06-20346
Thermal modification processes improve durability and dimensional stability of wood, but the strength properties, especially the dynamic ones, are compromised and need to be considered with respect to industrial quality control. Results from standard dynamic strength testing, such as impact bending tests, suffer from high variability, and therefore require a high number of replicates. To overcome ...
C Brischke, A O Rapp, C R Welzbacher
Wood plastic composites from modified wood; Part 1 - Conceptual idea, mechanical and physical properties
2006 - IRG/WP 06-40338
Wood plastic composites, WPCs, are rapidly taking shares from preservative treated wood on the decking market. However, the long term performance of the WPC products in this application is uncertain. Therefore, in an attempt to increase the long term performance and durability, the substitution of the unmodified wood component with modified wood has been studied in the work presented in this paper...
P Larsson Brelid, B K Segerholm, M Westin, M E P Wålinder
Chemical reactions involved in furfurylation of solid wood - An investigation by ATR-IR spectroscopy
2006 - IRG/WP 06-40347
Wood modification with furfuryl alcohol (FA) has gained renewed interest during the last five to ten years because of advances in process technology and because of increased focus on the environmental hazards of traditional wood impregnation. The reaction mechanisms involved in the furfurylation process are not yet understood in detail. In the work presented here, the chemical reactions and their ...
T Mark Venås, L Garbrecht Thygesen, S Barsberg
Furfurylated wood - An alternative to Preservative-treated wood
2006 - IRG/WP 06-40349
Chemically modified wood is currently being marketed as a non-toxic alternative to traditional preservative treated wood (wood impregnated with biocides). Over the last decade the authors have developed modernised processes for wood modified by furfurylation. These new systems do not add metals or halogens to the product, which is important for an environmentally acceptable product. This presentat...
S Lande, M H Schneider, M Westin, J Phillips
Wood plastic composites from modified wood. Part 2 - Durability in laboratory decay tests
2006 - IRG/WP 06-40353
The decay resistance of wood plastic composites, WPCs, was tested according to modified versions of AWPA E10 (soil-block test) and ENV 807 (tests in three un-sterile soils, terrestrial microcosms, TMCs). The WPC materials were conically extruded profiles with 30% polypropylene content. The 70% wood content was untreated Scots pine sapwood, acetylated pine and heat treated Norway spruce, respective...
M Westin, P Larsson Brelid, M L Edlund, G Alfredsen
Photo-degradation of modified and non-modified wood, coated with water borne acrylic coatings during artificial light exposure
2007 - IRG/WP 07-30416
A series of experiments were carried out to investigate photo-degradation of thermally modified (at 210oC and – 0.9 bars for two hours) and non-modified spruce wood (Picea abies L (Karst)), coated with transparent and semitransparent (with 3% pigment content) acrylic coatings during artificial UV light irradiation for 200 hours. Photo-degradation was evaluated in terms of colour changes througho...
M Deka, M Tomažic, M Petric
Microwave curing of furfuryl alcohol modified wood
2007 - IRG/WP 07-40371
Furfurylated wood has shown to have promising properties for a wood modification agent during the last years. In this paper, an alternative curing method for furfuryl alcohol modified pine sapwood by means of microwave radiation was investigated.
Different process parameters of microwave treatment such as output power, exposure time to microwave radiation, initial wood moisture content and evapor...
A Treu, E Larnøy, H Militz
Marine Borer Resistance of Modified Wood - Results from Seven Years in Field
2007 - IRG/WP 07-40375
Wood modified by several methods has been tested for seven years in a marine field with high marine borer activity. Several wood modification methods were included, e.g. thermal modification (with different processes), acetylation, maleoylation, succinylation, furfurylation, treatment with methylated melamine resin and modification with reactive linseed oil derivative. Furthermore, some combinatio...
M Westin, A O Rapp, T Nilsson
Protection of wood for above ground application through modification with a fatty acid modified N-methylol/paraffin formulation
2007 - IRG/WP 07-40378
Hydrophobic chemical modification can be regarded as an alternative approach to conventional wood preservation using biocides in order to protect wood in hazard class 3 according the European Standard EN 335-1.
A formulation containing fatty acid modified N-methylol/paraffin and an aluminium salt catalyst was used to change the material properties of wood in order to protect wood from fungal dec...
Nguyen Hong Minh, H Militz, C Mai
Multivariate analysis of infrared spectra for the prediction of the mechanical performance and dimensional stability of thermally modified wood
2007 - IRG/WP 07-40367
The use of calibrated mid-infrared Fourier transform (FTIR) spectroscopy for predicting the main bending strength parameters of thermally modified wood is described for the first time. The analysis is based on the handling of OSC-filtered FTIR data from control and treated wood samples, using partial least squares (PLS) regression.
Sets of Norway spruce, Scots pine and Beech wood samples were th...
M M González-Peña, M D C Hale