The termite resistance of wood impregnated with nano-zinc oxide and nano-zinc borate dispersions
2016 - IRG/WP 16-30691
In this work, the effects of the impregnation with nano-ZnO and nano-ZnB dispersions on the termite resistance of European beech wood were investigated. Three different concentrations (namely 0.5%, 1% and 2%) of the above two materials were tested. Water leaching effect was also investigated. It was concluded that a severe effect in terms of termite workers mortality is induced by the use of both ...
C Lykidis, T de Troya, M Conde, J Galván, G Mantanis
Effect of Nano-Silane on Permeability in MDF as a Result of Susceptibility to Moulds and Fungi
2016 - IRG/WP 16-40716
Effects were studied of vapor chamber on specific gas permeability of nanosilane-treated medium-density fiberboards (MDF). Size range of nanoparticles was 20 – 80 nm. Nano-silane (NS) was used at four consumption levels of 0, 50, 100, and 150 g/kg dry wood fibers. Density of all treatments was kept constant at 0.67 g/cm3. Specimens were kept for 18 weeks in vaporized chamber; their specific gas ...
H R Taghiyari, J Norton, A Moradiyan, M Sadegh Taher Tolou Del, H Siahposht, B Moradi-Malek, M Noferesti
Modifying wood with paraffin wax emulsion impregnation and thermal modification: hydrophobization effect and mechanism of the combined treatment
2016 - IRG/WP 16-40726
The aim of this study was to enhance the water repellency of wood by a combined treatment of paraffin wax emulsion (PWE) impregnation and thermal modification. Two different treating procedures were used to modify the southern pine (pinus spp.). One is first PWE impregnation and then thermal modification, another is first thermal modification and then PWE impregnation. The treated samples were imm...
Wang Wang, Jinzhen Cao, Cong Chen
Impregnation of railway sleepers - Pressure gradient and transversal penetration
2016 - IRG/WP 16-40731
Based on the possible ban of creosote in the future, the need for oil based alternative products has gained in importance. Due to possible differences in impregnation properties compared to creosote the need for re-implementing former technology is given, to determine if momentarily used impregnation processes have to be modified. The here reported tests measure the pressure gradient during the im...
M Starck, A Gellerich, H Militz
Dynamic mechanical analysis of viscoelastic properties of heat treated glycerol-impregnation poplar wood
2016 - IRG/WP 16-40732
The viscoelastic properties of glycerol-impregnated poplar wood after heat treatments at various temperatures were examined by dynamic-mechanical analysis. The spectra of storage modulus (E’) and loss tangent (tgδ) in the frequency at 10 Hz were measured at the temperature range from -100 to 300℃. Compared to no peak in E’ spectra and two relaxation processes in tanδ spectra of...
Li Yan
The effect of acetylation on physical properties of beech (Fagus orientalis) and Alder (Alnus subcordata) wood
2016 - IRG/WP 16-40759
In this study the effect of acetylation on physical properties such as water absorption, volumetric swelling and anti-shrink efficiency (ASE) of beech and alder were investigated. After 24 hours soaking in acetic anhydride, in order to achieving two surface of weight gains, acetylated samples were heated in oven at 120 0C for 90 and 360 minutes. Then water absorption and dimensional stability in...
M Akhtari, M Arefkhani
Improvement of wood properties by impregnation with liquefied spruce bark based resins
2016 - IRG/WP 16-40761
In this paper, biobased phenolic thermosetting resins are designed to be used as wood stabilization treatment. The originality of the study stands in substituting part of phenol by spruce (picea abies) bark: this is achieved by a liquefaction process in phenol in the presence of sulfuric acid as catalyst. Next, thermosetting resins are synthetized from liquefied bark by condensation on formaldehy...
X Duret, E Fredon, E Masson, P Gérardin
A Treatability Study of Western Wood Species with Water Based Azoles and Insecticides Using Buffered Amine Oxides
2016 - IRG/WP 16-40766
The use of Western U.S. Wood Species remains small in today’s global wood product market when compared to the use of other commercially available softwoods. One reason that other fiber sources, those that may be less naturally durable or exhibit slightly inferior mechanical properties, are utilized is ease of treatment. In an attempt to ensure adequate penetration in commercially important an...
R W Clawson Jr, C N Cheeks, K A Cutler
Development of Wood Modification – High melting point wax and hot oil treatments
2016 - IRG/WP 16-40768
This study covers an introduction to the projects where new facilities were created for developing wood modification. In this new research environment it is possible to treat wood with versatile equipment. First modifications with this equipment are going to be done in high temperature and pressure using high melting point waxes and hot oils.
Earlier studies, tests and commercial products show...
H Turunen, L Linkosalmi, J Peura, O Paajanen
Quality of the impregnated wood in the Slovenian hardware stores
2017 - IRG/WP 17-20606
Ten different samples from Slovenian hardware stores were analysed. Samples were treated with copper based wood preservatives and designed and advertised to be used in heavy duty applications in use classes 3.2 or 4. In order to determine the quality of the treatment penetration, retention and fungicidal properties were determined. Retention was determined with XRF analysis, while modified EN 113 ...
M Humar, B Lesar, N Thaler, D Kržišnik, N Kregar, S Drnovšek
Efficacy of Erythropleum suaveolens (potrodom) and Distemonanthus benthamianus (bonsamdua) water extractives on the durability of five Ghanaian less used timber species of varying perviousness and retentiveness
2017 - IRG/WP 17-30705
Conventional wood preservatives are not only toxic to target bio-deterioration organisms but also to humans, other organisms and the environment. In an effort to find preservatives that are less toxic or non-toxic to man, other organisms and the environment, efficacy of branch bark and heartwood water extracts (0.65 g/ml) of Erythropleum suaveolens (potrodom) and Distemonanthus benthamianus (bonsa...
A Asamoah, K Frimpong-Mensah, C Antwi-Boasiako
Copolymers of tannin extracts as wood protection agents
2017 - IRG/WP 17-30709
Wouldn´t be a dream to preserve wood with the substances which the nature already synthesizes for protecting itself? The idea we would like to pursue is simple: Increase the concentration of these substances, the tannins, trying to fix them properly in wood. It appears easy but it is not. Sensibility against leaching, fungal decay and weathering were observed. In this paper new flavonoid co-polym...
G Tondi, L Sommerauer, A Oberle, A Petutschnigg, M-F Thevenon
Effects of Nano-Wollastonite Impregnation on Fire Properties of Some Thermally-Treated Solid Wood Species
2017 - IRG/WP 17-40771
The effects of nano-wollastonite (NW) suspension impregnation on the fire-retarding properties of heat-treated solid wood of three species (beech, poplar, fir) were studied. Heat treatment was performed at two temperatures of 180 °C and 200 °C. Impregnation was carried out at a pressure of 3 bars for 30 min. The fire properties included ignition time, glowing time, back-darkening, back-splitting...
H R Taghiyari, R Hossinpourpia, S Adamopoulos, A Jahangiri, D Rabie
Penetration behaviour of different hydrophobic carrier substances for oily wood preservatives in Beech and Scots pine sapwood
2017 - IRG/WP 17-40804
The use of creosote as a wood preservative has a long history. Current areas of application are railway sleepers, transmission poles, timber bridges and marine applications. If the approval for creosote will not be prolonged, alternative wood preservatives will be needed. As the penetration behaviour after pressure impregnation of different alternative oily products in this fields of application i...
M Starck, A Gellerich, H Militz
Organosilicon-based impregnation hydrophobers for wood
2017 - IRG/WP 17-40808
The SILEX project “Improving sustainability of construction materials using innovative Silicon based treatment” is a Life+ project with reference LIFE+11 ENV/BE/1046 and started in April 2013. This project intends to demonstrate that a new class of compounds can be used for wood treatment for an extended service life combined with enhanced new testing methodology. The project aims at demonstra...
J-P Lecomte, J Van Acker, J Van den Bulcke, M Kutnik, M Montibus, S Salvati, S Derocker
Influence of hygro-thermal treatment temperature and duration on dimensional stabilisation of wood modified with poly(butylene succinate)
2017 - IRG/WP 17-40813
To improve wood properties, especially dimensional stability, a treatment based on poly(butylene succinate) oligomers (OBS) was experimented. After impregnation in wood, a further hygro-thermal treatment (HTT) was carried out in a pressurized reactor at 100% relative humidity (RH) at differing temperatures for differing durations. The aim of HTT is to induce partial swelling of wood cell walls so ...
C Grosse, M Noël, L Rautkari, P Gérardin
Water absorption characteristics of CLT
2017 - IRG/WP 17-40817
CLT is initialism of Cross Laminated Timber. CLT is generally large-sized panel which can use many woods efficiently, so it is attracted attention recently in Japan. Therefore, many studies about CLT are carried out. However, there are few studies about durability of CLT. Avoiding water infiltration is important for durability of wooden building. CLT has many edge-glued points which has risk of w...
D Yokoi, H Ishiyama, Y Hirano
Influence of sea water on timber and metal joints
2017 - IRG/WP 17-40818
In the Great East Japan Earthquake that occurred in March 2011, many buildings suffered from seawater immersion caused by the tsunami. Saito's study revealed that corrosion progresses on metal plate that experienced seawater immersion 1). However, the detailed mechanism of corrosion progresses has not yet been clarified. Therefore, in this study, salinity which is one of causes of corrosion w...
T Nishimura, H Ishiyama, F Hirose, N Wada
The Impact of Cryopreservation Techniques and of Water Quality on the Wood Degrading Ability of Fungal Strains: Recommendations for Maintenance and Culturing Procedures
2018 - IRG/WP 18-20636
In order to establish an optimal cryopreservation method, strains of Basidiomycete and Ascomycete fungi, which are among the most frequently used for wood durability testing, were evaluated using three cryopreservation procedures at -80°C. The main objective was to prevent decrease of the fungal virulence that may occur due to repeated routine sub-culturing procedures and to optimize the reactiva...
A Stum, M Montibus, I le Bayon, M Kutnik
Material Resistance and Chemical Composition of Italian Stone Pine (Pinus pinea)
2018 - RG/WP 18-20645
Relevant properties of stone pine (Pinus pinea) wood have been only fragmentarily addressed in the past, which has been recognized as a limiting factor for its potential applications. The amount of the respective wood species on the market will likely increase in the future. The sorption properties, permeability to water, extractives content and durability against fungi of Pinus pinea sapwood and ...
M Humar, M De Angelis, M Romagnoli, V Vek, I Poljanšek, P Oven, N Thaler, B Lesar, D Kržišnik
Performance of acetylated wood in aquatic applications
2018 - IRG/WP 18-40822
Acetylation of wood to enhance its resistance against wood decaying fungi and insects has been studied extensively under both laboratory and terrestrial field trials. Also several studies are investigating the performance of acetylated wood in marine and fresh water exposures. This paper updates nine year marine tests with acetylated radiata pine in Hejlsminde (Denmark) and presents data on 3 year...
F Bongers, S Palanti, A Gellerich, J J Morrell, J Creemers, J Hague
Multiscale modification on water resistance and dimensional stability of Populus cathayana by alkali lignin combined with heat treatment
2018 - IRG/WP 18-40826
The aim of this study was to enhance the water resistance and dimensional stability of fast growing wood by alkali lignin combined with heat treatment. Poplar (Populus cathayana) samples were first impregnated with alkali lignin solution and then subjected to heat treatment at 140, 160, and 180°C respectively for 2h. Properties of leachability, moisture adsorption and water absorption, contact an...
H Zhou, J Li, E Ma
An examination of the potential for the use of the Maillard reaction to modify wood
2018 - IRG/WP 18-40829
Finding efficient ways to decrease wood decay caused by fungi and increasing its dimensional stability is an important issue in the timber construction. A possible way to avoid wood decay by fungi is by reducing the water content of wood, since water is a primary condition for fungal growth. Bulking of the wood cell wall by chemical reagents occupies the space where water normally occurs. At the s...
K Peeters, E Larnøy, A Kutnar, Č Tavzes, C A S Hill
Hydrolytic stabilization of chemically modified Bambusa vulgaris Shrad ex JC Wendl
2018 - IRG/WP 18-40830
The main drawback which greatly limit the utilisation of bamboos is their high moisture intake, biodegradation and physical properties changes with environmental variations. To prevent excessive dimensional changes and improve moisture properties of bamboo, Bambusa vulgaris was chemically treated with acetic-anhydride without co-solvent. To evaluate the influence of acetylation on the moisture pro...
N A Sadiku, S M Akintayo
A Synergistically Stabilized Oil-in-Water Paraffin Pickering Emulsion Used in Wood Treatment
2018 - IRG/WP 18-40840
Pickering emulsions (emulsions stabilized by solid particles) are attractive as they have strong similarities with traditional surfactant-stabilized emulsions. In this study, an oil-in-water (O/W) paraffin Pickering emulsion system with satisfying stability and small droplet size distribution was developed by hydrophilic silica particles and traditional surfactants as mixed emulsifiers. The drople...
J Jiang, J Cao