Wood cement composites using spent CCA treated wood
1999 - IRG/WP 99-50126
The feasibility of using spent or out-of-service CCA treated wood as a component of wood/cement composites was evaluated. Cold pressed wood particle cement boards were made using CCA treated particles from a red pine (Pinus resinosa Ait.) pole removed from service and from untreated red pine wood from a new pole. Boards were manufactured using a range of wood to cement ratios and water to cement r...
Chen Huang, P A Cooper
Resistance of board materials against fungal decay: A comparative experiment on Kolle flask tests method and direct test method
1985 - IRG/WP 2243
Two sets of plywood (Aucoumea klaineana Pierre) 7 and 11 ply, treated by two preservatives, and untreated, were tested by two methods: 1. Kolle flask test method on malt-agar substrate according to the French standard NF B 51.295; 2. A direct test method in non sterile conditions according to DocNo: IRG/WP/2214. The exposure time far both methods was 12 weeks. After exposure, the degree of attack ...
G R Y Déon, L N Trong
Alternative methodology for the environmental impact assessment of treated wood: the wood emissions ecotoxicology
2000 - IRG/WP 00-50161
Preservative products and technologies are important for optimising the use of wood and wood products in our society. The regulations of their use under the european Biocidal Products Directive 98/8/EC will require an evaluation of the environmental impact of treated wood. The methodology currently used for this determination is the PEC/PNEC ratio. It consists of calculating PEC values (Predictive...
P Marchal, H W Wegen, J Van Acker, E Melcher, R-D Peek, W J Homan, D Aston, D Rudolph, E F Baines
Minimisation of the Environmental Impacts of Coatings on Exterior Wood by Optimisation of their Life Spans
2003 - IRG/WP 03-50197
The study has shown that the environmental impacts from coatings on exterior wood are dependent criteria on their life spans. A minimisation of the environmental impacts can be performed with the help of the integrated design model, which is tested in this study. The optimal life spans, found as reference service lives from the exposure tests, statistical evaluation and the assessment of experts w...
L Strömberg
Effects of CCA treatment on settlement and growth of barnacles under field conditions
1998 - IRG/WP 98-50116
As part of a field experiment at seven European marine sites evaluating the effects of CCA treatments on non-target marine organisms, panels treated to nominal loadings of 12, 24 and 48 kg/m3 CCA were exposed at marine sites around the coast of Europe. Within two weeks of exposure, a heavy settlement of barnacles took place on the panels exposed intertidally in France. The intensity of settlement ...
S M Cragg, C Brown, R M Albuquerque, R A Eaton, P Goulletquer
Environmental impact of PCP and NaPCP in the aquatic and atmospheric compartment
1995 - IRG/WP 95-50040-06
PCP and NaPCP were studied for their aquatic toxicity on bacteria, microalgae and daphnids and for their behaviour in the atmospheric compartment with a climatic chamber. Results of aquatic toxicity bioassays showed that toxicity was higher at low pH. This can be explained by the pKa value of 4.7 of PCP and the higher concentration of the non dissociated form of the pesticide at more acidic pH. Vo...
P Marchal, P Vasseur, G Ozanne
Social and economocal impact of an extension of service life resulting of an adequate preventive treatment. Application to wooden components used in urban areas with a high density of population
1993 - IRG/WP 93-50001-15
Le document évalue les problèmes rencontrés en zone urbaine pour le sauvetage des constructions: coordination de la lutte, délimination des chantieres et des périmètres d'investigation, nuisances causées par les interventions, risques pour la santé, risques pour l'environnement. Coûts. Comparaison socio-économique du traitement préventif et des interventions à posteri...
A T De Lelis, G A C Lopez
Effect of wood decay on the proportional limit of thin wood samples stressed in the bending mode
2006 - IRG/WP 06-20334
When using bending stiffness as a measure of wood decay it is advantageous to repeatedly test individual samples after they are exposed to decay fungi for varying periods of time. In order to obtain reliable results, variation in modulus of elasticity (MOE) values of the test samples that are repeatable bent to a given deflection must be considered. In this study it was shown that sound 3mm thick ...
G Li, D Nicholas, T Schultz
High-energy multiple impact (HEMI)-test – Part 2: A mechanical test for the detection of fungal decay
2006 - IRG/WP 06-20339
The suitability of the high-energy multiple impact (HEMI)-test for detection of early fungal decay was examined. The HEMI – test characterizes the treatment quality of thermally modified wood by stressing the treated material by thousands of impacts of pounding steel balls. This method differentiates between heat treatment intensities, which are expressed by structural changes of the wood. Simil...
C R Welzbacher, C Brischke, A O Rapp
Mechanical strength of wood from the Vasa shipwreck
2008 - IRG/WP 08-20381
Samples from three ancient ship wrecks (Vasa, Elefanten, and Gröne Jägaren) and recent oak samples as reference were examined with regard to mechanical strength using the high-energy multiple impact (HEMI) - test method, which delivers the resistance to impact milling (RIM) of a material. Adoption and optimisation of the test method for the particular sample size of the wooden drilling cores was...
A O Rapp, C Brischke, C R Welzbacher, T Nilsson, C Björdal
The effect of gamma radiation on selected wood properties
2008 - IRG/WP 08-40394
As an easy, fast, and effective sterilisation method, gamma irradiation changes molecular structures not only in pest’s living cells, but also in wooden cell walls. Radiation-induced depolymerisation causes significant changes in some properties of wood crucial for restoration and for laboratory testing of wood-preservative effectiveness. The influence of gamma radiation concerning total amount ...
R Despot, M Hasan, A O Rapp, C Brischke, C R Welzbacher
Bending Properties of Southern Pine Treated with Micronized Preservative Systems
2008 - IRG/WP 08-40414
This study indicates that treatment of southern pine with micronized copper systems have no
deleterious effect on the residual strength property values. No statistical differences between wood treated with micronized systems and water-treated controls were noted when means were compared using either Tukey’s test or S-N-K mean comparison tests. Using the more discriminating Least Squares anal...
H M Barnes, G B Lindsey, J Hill, M Pompeo, R Hodge
Cantilever bending test of furfurylated poles
2008 - IRG/WP 08-40424
Ten, 8 m long poles of Scots pine (Pinus sylvestris) were treated with furfuryl alcohol to a WPG of approximately 40 %. A bending test was performed according to the principles in the draft European standard for wooden poles, prEN 14229 - Structural timber - Wood Poles for overhead lines. The bending strength and stiffness (MOE) for the poles tested were compared to an earlier study by the Swedish Wood Preservation Committee. In the latter study untreated, CCA-treated, ammoniacal Cu-PCP treated and creosoted poles were tested in bending. These types of poles were considered not to differ in strength and stiffness. The results of the furfurylated poles fit well with the results from the previous study. The bending strength and MOE values obtained are compared to the upper and lower 95-percentile values of the results from the previous study and all poles treated with furfuryl alcohol fit within this interval.Thus, this study indicates that a treatment with furfuryl alcohol does not result in a decrease of strength or stiffness. Further testing with a larger population of poles is necessary in order to get a statistically reliable result. In addition to further demonstration of the durability, the
treatment process must be optimised to ensure full sapwood penetration and measures have to be taken to avoid the serious cracking observed in this trial before furfurylation can be considered for treatment of Pinus sylvestris poles.
R Ziethén, J Jermer, A Clang
Material properties of acetylated beech plywood
2008 - IRG/WP 08-40425
The effect of acetylation process on dimensional stability and mechanical properties of plywood made by Oriental beech layers (Fagus orientalis Lipsky) were studied. The layers cut into sizes of 200×200×2 mm and acetylated in 120°C for 30 and 60 min.
Thickness swelling (TS%), water absorption (WA%) and anti-swelling¬ efficiency (ASE%) of specimens were measured. Mechanical properties (MOE, MO...
A Talaei
Drywood termites in the Azores: Problems and tentative solutions
2009 - IRG/WP 09-10698
The detection in 2002 of drywood termites in the islands of Azores has became an urgent issue to be coped with given the fast degradation that structural elements can show after a short period of installation of a colony. A recent study indicates drywood termite presence in about half of the buildings of the historic centre of Angra do Heroísmo (a World Heritage site) in Terceira Island and timbe...
L Nunes, C Amaral, S Duarte, M Gaju
Impact of decay and blue stain causing fungi on the structural integrity of wood
2009 - IRG/WP 09-10699
The potential influence of diverse decay patterns caused by different brown rot provoking basidiomycetes on the structural integrity of wood was investigated. Additionally the potential impact of blue stain on the structural integrity was examined. Therefore decayed Norway spruce (Picea abies Karst.) specimens representing a wide range of mass loss, caused by four different brown-rot fungi and one...
C Brischke, C Welzbacher, T Huckfeldt, F Schuh
Impact of an Antioxidant on the Efficacy of Quaternary Ammonium Compounds (Quats) and Triazoles – Seven Year Above-Ground Study
2009 - IRG/WP 09-30504
It has been reported that antioxidants have great potential for use with organic biocides in the area of wood protection. This paper demonstrates the impact of a low level of the antioxidant butylated hydroxytoluene (BHT) on the efficacy of quat-based and triazole-based formulations. A seven year lap joint test revealed a positive effect of BHT on the efficacy of quat-based formulations, especiall...
Xiao Jiang, D Biro, W Holcombe
Barefoot-heat-impact of oil-heat-treated wood: An important thermal property of decking boards
2009 - IRG/WP 09-40458
In this study the phenomenon of sensual heat impression was examined, when walking with bare feet on sun exposed wood based decking boards. A suitable method for measuring the heat flux from decking boards into an artificial foot was developed. The method and measuring device is described as well as results from measuring three different decking board materials: Oil-heat-treated spruce (OHT), untr...
A O Rapp, C R Welzbacher, C Brischke
Estimating the heat treatment intensity through various properties of thermally modified timber (TMT)
2009 - IRG/WP 09-40459
The suitability of different measures for prediction of the heat treatment intensity was investigated. Therefore, the resistance to impact milling (RIM), the lightness L*, the equilibrium moisture content (EMC), the anti swelling efficiency (ASE) and the total amount of soluble carbohydrates (TSC) of heat treated specimens were correlated with corresponding fungal resistance achieved by heat treat...
C R Welzbacher, C Brischke, A O Rapp
Diagnosis of failures in wood beams from historical house in Banská Štiavnica – Relations between ultrasonic measurements and bending properties
2010 - IRG/WP 10-20437
Various degrees of rot and other damages in ceiling beams with dimensions of 6500-8800 x 160-200 x 240-310 mm (length x height x width) situated in one historical bourgeois house in the UNESCO town Banská Štiavnica, Slovakia were determined visually and by the PUNDIT-plus ultrasonic device. Subsequently, for seventeen of the most bio-damaged fir (Abies alba Mill.) beams chosen for exchange were ...
L Reinprecht, M Pánek
Service life prediction of wooden components – Part 2: Impact of material, exposure and design details
2010 - IRG/WP 10-20440
Dose-response functions permit to estimate the moisture and temperature induced decay potential for any wooden building component and exposure, and thus the service life to be expected. In part 1 of this series dose-response functions were established as a result of double layer field trials carried out at 24 European test sites over up to eight years. Using them makes it no longer necessary to co...
C Brischke, B Lauenstein, M Bilstein, T Bornemann, A O Rapp
Impact of climate change on wood deterioration - Challenges and solutions for cultural heritage
2010 - IRG/WP 10-20441
Deterioration of wood in cultural assets follows the same physiological mechanisms as in modern structures. Therefore rules and data for prediction of service life derived from old wooden structures can be used to model the service life of recent wooden structures and vice versa. The latter is done in this paper: From experimental test set ups in the field spread over Europe, climatic data, wood t...
C Brischke, A O Rapp, M Hasan, R Despot
Repairing of wooden elements by beta-method using carbon, steel or beech rods
2010 - IRG/WP 10-40488
Presented paper is focused on repairing of wooden elements by Beta joints reinforced with carbon, steel or beech rods, and on comparing the efficiency of these joints with traditional carpentry joints. In model laboratory experiments have been determined the bending strength (fm) and the modulus of elasticity (E) of control or original elements (fm-Control; Eo) from Norway spruce (Picea abies Kars...
L Reinprecht
Hydrothermal modification for upgrading the durability properties of soft deciduous wood
2010 - IRG/WP 10-40494
To extend the application potentialities of soft deciduous wood, upgrading the durability properties, hydrothermal modification (HTM) of aspen alder and birch wood was investigated. The treatment was conducted in a multifunctional laboratory device WTT. In the previous cases it has been found that the treatment at 160oC improves the durability insufficiently. The modification at 180oC ensured a hi...
B Andersons, I Andersone, V Biziks, I Irbe, J Chirkova, E Sansonetti, J Grinins, H Militz
TMT–Interlab–Test to establish suitable quality control techniques - Structure and first results
2010 - IRG/WP 10-40503
As a result of growing quality demands from manufacturers and end-consumers of thermally modified timber (TMT) recent scientific research activities are increasingly focussed on modification mechanisms and by this on the development of suitable quality control methods. To deepen the knowledge in modification mechanisms and to obtain a larger variety of scientific data for TMT depending on the trea...
C R Welzbacher