Detection of metabolic gas from termites using ceramic gas sensors
2001 - IRG/WP 01-20222
To evaluate termite attacks in wooden constructions by detecting the metabolic gas from termite colony, the basic performance of three types of ceramic gas sensors (odor-, methane- and hydrogen-selective sensors) was investigated. Four termite groups of different combinations of workers (100 to 1000) and soldiers (10 to 100) of Coptotermes formosanus Shiraki and a small specimen of Japanese red pi...
Y Yanase, Y Fujii, S Okumura, T Maekawa, K Suzuki, T Yoshimura, Y Imamura
Biological resistance of wood-based composites under protected, aboveground conditions
2005 - IRG/WP 05-20312
Five kinds of wood-based composites (density fiberboard=MDF, hardwood plywood=HP, softwood plywood =SP, particleboard=PB and aspen oriented strand board=OSB) were tested for their resistance against subterranean termites and decay under protected aboveground conditions. The exposure method was previously developed for evaluating performance of sill plates (dodai) in Japanese homes. Ten replicates ...
K Tsunoda
IRG/COIPM INTERNATIONAL MARINE TEST - To determine the effect of timber substrate on the efectiveness of different preservatives in sea-water: Coding scheme
1976 - IRG/WP 420
It was agreed in Wildhaus on 15 May 1976 that preparations for the test detailed in Document No: IRG/WP/414 should commence immediately, but that initially only two water-borne preservatives should be used - a copper/chrome/arsenic (CCA) and a copper/chrome/boron (CCB) formulation respectively. PRL, England (R Cockcroft) would be responsible for supplying only the reference species treated with th...
Anonymous
Performance of borate-treated lumber in a protected, above-ground field test in Japan
2004 - IRG/WP 04-30344
This document is supplemental to the previous IRG document (Tsunoda et al., 2002).
An experiment to simulate the sill plate (dodai) of the Japanese houses was conducted at the termite field test site of the Wood Research Institute in Kagoshima, Japan where two economically important subterranean termite species [Coptotermes formosanus Shiraki and Reticulitermes speratus (Kolbe)] are established. ...
K Tsunoda, A Byrne, P I Morris, J K Grace
A new process for in situ polymerization of vinyl monomers in wood to delay boron leaching
1998 - IRG/WP 98-40110
Efforts were accelerated on effective use of boron compounds in wood preservation owing to their environmentally safe characteristics and relatively low costs in addition to their well-known high bioactivity and fire resistant properties. Although having these unique favorable properties, they are readily leachable from treated wood at humid conditions. Therefore, they had limited market for exter...
M K Yalinkilic, W Dwianto, Y Imamura, M Takahashi
IRG/COIPM INTERNATIONAL MARINE TEST - to determine the effect of timber substrate on the effectiveness of water-borne salt preservatives in sea-water. Progress Report 17: Report of fifth inspection (4 years) in Italy
1983 - IRG/WP 4103
The wood samples of Alstonia scholaris, Fagus sylvatica, Pinus sylvestris were submerged in the sea at Follonica, Italy, in April 1977. Follonica, latitude 42°55' North and longitude 10°45' East, is situated on the Tyrrhenian coast. The recorded temperature varies from 13°C to 25°C, salinity 37-38% and pH about 8. The inspections were carried out after 6 months (10/1977), 12 ...
A Gambetta, E Orlandi
Influence of the nature of the substrate and the method of inoculation on the degradative activity of soft rot fungi
1998 - IRG/WP 98-20133
The European Standard (ENV-807) determines the threshold of effectiveness of wood preservatives against the action of soft rot Ascomycetes fungi. Its application in the treatment of wood used in the hazard class 4 does not always offer repeatable results, which could be expected in an experimental norm.
For this reason, in this paper, we have evaluated the diverse variables that might influence t...
M T De Troya, A M Navarrete, F Rubio, J Jiménez, D Muñoz-Mingarro, C Rodríguez-Borrajo, F Llinares, M Yuste
Performance of borate-treated lumber in a protected, above-ground field test in Japan
2006 - IRG/WP 06-30395
This document is supplemental to the previous IRG document (Tsunoda et al. 2004).
An experiment to simulate the sill plate (dodai) of the Japanese houses was conducted at the termite field test site of the Research Institute for Sustainable Humanosphere of Kyoto University in Kagoshima Pref., Japan where two economically important subterranean termite species [Coptotermes formosanus Shiraki and R...
K Tsunoda, A Byrne, P I Morris, J K Grace
Performance of wood-based composites in a protected aboveground test in southern Japan
2008 - IRG/WP 08-40391
Five kinds of untreated wood-based composites (medium density fiberboard, hardwood plywood=HP, softwood plywood, particleboard and aspen oriented strand board, hereinafter abbreviated as MDF, HP, SP, PB and OSB, respectively) were exposed to subterranean termites and microbial (decay) attack under protected aboveground conditions in a southern part of Japan (Kagoshima Prefecture) for six years. An...
K Tsunoda
Feasibility study on three furfurylated non-durable tropical wood species evaluated for resistance to brown, white and soft rot fungi
2008 - IRG/WP 08-40395
Furfurylation can protect non-durable wood species against biological degradation, but the method used today cannot fully protect the heartwood of Scots pine due to insufficient penetration. In order to test alternative wood substrates for furfurylation, three Malaysian grown wood species (Kelempayan, Rubberwood and Sena) were furfurylated and subjected to soil block decay testing. Their performan...
T Mark Venås, A H H Wong
Aesthetic service life of coated and uncoated wooden cladding - influencing factors and modelling
2011 - IRG/WP 11-20470
Mould growth on exterior coated cladding façades is an undesirable element and will often shorten the aesthetical service life. Mould growth on painted surfaces is influenced by type and concentration of film fungicides, the paint formulation and the wood substrate itself, and wooden cladding may experience exponential fungal deterioration caused by variation in the climatic factors, often within...
L Ross Gobakken, O A Høibø
Using an accelerated laboratory method to evaluate Aureobasidium pullulans colonization on painted surfaces and underlying wood substrate
2012 - IRG/WP 12-20480
Mold growth on painted surfaces can lead to premature paint film failure and is unsightly. Aureobasidium pullulans has been identified as a major cause of black stain on surfaces painted with acrylic or latex paints. In this study, an accelerated laboratory method developed by Zabel and Horner (1981) was used with modifications to the type of agar used and sample evaluation methods. A study was ...
C Schauwecker, L Burns, A Preston
Modelling the risk for mould growth on timber stored outdoors protected from rain
2013 - IRG/WP 13-20529
A mould resistance design (MRD) model was used to calculate the maximum duration of storage of timber outdoors under cover (protected from rain) before the onset of mould growth on the surface of wood. The prediction model is based on laboratory tests performed in constant and cyclic climates and were also confirmed against exposure tests in attics and crawl spaces. The prediction model presented ...
E Frühwald Hansson, S Bardage, S Thelandersson
The resistance of composite boards protected with azole and inorganic nanoparticles to basidiomycetes and moulds
2015 - IRG/WP 15-40688
This paper presents a study on the resistance of wood composite boards, glued with silicone adhesive and obtained from chips of Scots pine Pinus silvestris L. and willow Salix viminalis L., to basidiomycetes and mould. The boards were protected in the production processes with fungicides based on metal nanoparticles, as well as on derivatives of 1,2,4-triazole, benzimidazole, and thiazole. The bio...
J Zabielska-Matejuk, I Frąckowiak, A Stangierska
Post-layup protection of mass timber elements in above ground protected exposures: 2-year results
2022 - IRG/WP 22-30766
Mass timber has seen increased use as a building material for low and mid-rise construction in recent decades. The durability of mass timber elements has not been fully examined and the effects of wood destroying organisms on this these materials merits attention. The effectiveness of currently labeled soil termiticides and passively applied biocides at post-construction or as remedial agents need...
M E Mankowski, T G Shelton, G T Kirker, J J Morrell
Premature adhesion failure of exterior wood coatings – The influence of substrate temperature at coating application and moisture accumulation during storage
2022 - IRG/WP 22-40937
The present study aimed at extending the knowledge about premature coating failures of industrially finished wood cladding. Two potential factors were studied: the influence of substrate temperature at coating application and moisture accumulation during storage on the adhesion of waterborne coating systems. In the first experiment, 4 batches of wood specimens were submitted to 4 different tempera...
U Hundhausen
Hydrothermal liquefaction of spent mushroom substrate as a source of antifungals
2023 - IRG/WP 23-30791
The aim of this study was to characterize the chemical composition of hydrothermal liquefaction (HTL) products from the spent mushroom substrate (SMS) of Agaricus bisporus (Lange) Imbach and Pleurotus ostreatus (jacq.) P. kumm. using high-resolution 1H nuclear magnetic resonance (NMR), and assess the antifungal properties of these thermal decomposition liquids against wood decaying fungi (Coniopho...
A Barbero-López, Y M López-Gómez, J Carrasco, N Jokinen, R Lappalainen, A Haapala
Evaluation of vacuum borate treated spruce or pine CLT in an above ground protected test in southern Mississippi
2024 - IRG/WP 24-41001
Cross laminated timber (CLT) has become a popular wood composite in large building applications that were previously limited to concrete and steel. To extend service and prevent biological attack, chemical protectants are often applied to wood. Cross laminated timber panels are not typically treated, in part due to a lack of data on efficient and effective methods for treating large panels. Ther...
M E Mankowski, A Taylor, G T Kirker