Evaluating the Effects of Post Dip-Treatment Laser Marking on Resistance to Feeding by Subterranean Termites
2016 - IRG/WP 16-10854
Dip-treatment of wood packing materials is often used instead of pressure treatment mainly because of issues relating to simplicity and cost. Packaging boxes fabricated for the United States Army are required to be dip-treated for at least one minute in an approved preservative solution prior to use. These boxes are expected to have a service life of up to 20 years in a wide variety of environment...
R A Arango, B Woodward, S Lebow
Above-ground performance of a buffered amine oxide treatment system against Mastotermes darwiniensis
2016 - IRG/WP 16-10855
Above-ground H2 field tests against Mastotermes darwiniensis were conducted in far north Queensland to assess the efficacy of buffered amine oxide treatments in the softwoods Pinus sylvestris and P. radiata, and the hardwoods Eucalyptus regnans and E. diversicolor. Untreated hardwoods and slash pine bait wood (P. elliottii) were severely attacked or destroyed, while untreated P. sylvestris was mod...
L J Cookson, R W Clawson Jr
Characterization of waste from Pinus radiata generated during industrial thermal-treatment
2016 - IRG/WP 16-20586
The thermal-treatment is an established chemical-free process to modify wood, improving the durability and physical properties of wood through its service life. During the hydro-thermolysis several reactions from wood components occur, releasing volatile and non-volatile compounds from wood to the chamber. Once the process is accomplished, solid residues agglomerate below the wood load and gaseous...
R Herrera, D Thomas da Silva, R Llano-Ponte, J Labidi
Performance of copper treated poles and posts after three to fifteen years of exposure
2016 - IRG/WP 16-20595
Copper based wood preservatives are one of the most important wood preservatives for heavy-duty applications. Wood treated with copper-based preservatives performs excellent if applied according to preservative specifications. If used improperly premature failures might appear. In order to elucidate properties of copper treated wood in use, utility poles and posts treated with copper-based preserv...
M Humar, N Thaler
A non-VOC approach of solvent-based wood preservatives for remedial treatment
2016 - IRG/WP 16-30681
Solvent-based wood preservatives are the workhorses in the field of remedial treatment. Due to new European regulations on the indoor air quality there is an increasing pressure on the VOC-content on these solvent-based product types. The transfer of these European regulations into national law is left up to each European member state and handled in different ways. E.g. France has introduced a VO...
M Pallaske, S Hellkamp, P Jüngel
Effect of the Storage Time of Logs in Anti-Stain Treatment Effectiveness
2016 - IRG/WP 16-30683
Storage of green lumber, for 7 months, operationally treated with anti-stain products, depending on the storage time of the logs (10, 20 and 30 days) post harvesting allows to affirm that with increasing storage time of the logs, occurs a progressive increase in intensity, severity and types of fungi present in the logs. It is further noted, a significant increase in the percentage of sawn lumber ...
M A Peredo, C Barria
Wood properties modification by an enzymatic assisted treatment with phenolic extractives
2016 - IRG/WP 16-30696
Extractives of sawdust and bark from P. pinaster and, condensed tannins (CTs) from P. radiata bark were used to treat beech and pine veneers in combination with an oxidative enzyme, in order to stably graft such extractives onto the veneers. First, the antifungal activity of P. pinaster phenolic extractives against wood decay fungi was studied. These extractives were also used to hydrophobize pi...
D Filgueira, C Fernández-Costas, D E García, D Moldes
Increasing the hardness of wood-composite panels by nanosilver
2016 - IRG/WP 16-40715
Effect of silver nanoparticles on hardness in medium-density fiberboard (MDF) was studied here. A 400 ppm aqueous nanosilver suspension was used at three consumption levels of 100, 150, and 200 mL/kg, based on the dry weight of wood fibers; the results were then compared with the control panels. The size range of silver nanoparticles was 30-80 nm. Composite mats were hot-pressed for 6, 8, and 10 m...
H R Taghiyari, J Norton, K Heidarhaee
Investigation of enzymatic effect on pit membranes by light and scanning electron microscopy
2016 - IRG/WP 16-40721
Spruce wood, one of the refractory wood species has pit membranes, which has an influence on the permeability of wood providing liquid flow between the wood cells. However, these membranes tend to close under the fiber saturated point (FSD), which makes impregnation more difficult. In this study spruce sapwood samples were treated with two different commercial enzymes to improve the permeability o...
S Durmaz, Ü C Yildiz, M Öztürk, B Serdar
Resistance of heat treated Ash wood under steam pressure: rot fungi, soil micro-organisms and termites
2016 - IRG/WP 16-40724
Thermal modification processes have been developed to increase the biological durability and dimensional stability of wood. The aim of this paper was to study the influence of ThermoWood® treatment intensity on wood decay resistance improvement against soil-inhabiting micro-organisms, brown/white rots and termite’s exposures. All of the tests were carried out in the laboratory with two differen...
K Candelier, S Hannouz, M-F Thévenon, D Guibal, P Gérardin, M Pétrissans, R Collet
Modifying wood with paraffin wax emulsion impregnation and thermal modification: hydrophobization effect and mechanism of the combined treatment
2016 - IRG/WP 16-40726
The aim of this study was to enhance the water repellency of wood by a combined treatment of paraffin wax emulsion (PWE) impregnation and thermal modification. Two different treating procedures were used to modify the southern pine (pinus spp.). One is first PWE impregnation and then thermal modification, another is first thermal modification and then PWE impregnation. The treated samples were imm...
Wang Wang, Jinzhen Cao, Cong Chen
Combustion and thermal characteristics of Korean wood species
2016 - IRG/WP 16-40727
This study examined the combustion and thermal characteristics of domestic woods in Korea. Wood was confirmed by a cone calorimeter according to the KS F ISO 5660-1 standard. The combustion properties of the wood were measured in terms of the heat release rate (HRR), total heat released (THR), mass lose rate (MLR), and ignition time (time to ignition; TTI). Also, the thermal properties were measur...
Huyun Jeong Seo, Jung-eun Park, Dong Won Son, Won-Joung Hwang
Superhydrophobic treatment of Norway spruce wood for improvement of its resistance against brown rot and moulds
2016 - IRG/WP 16-40734
Water repellence of wood can be increased and its some other properties influenced by introduction of hydrophobic chemicals into and on cell walls without affecting the wood’s bulk density due to lumen filling. Herein, a simple dipping method to insert octadecyltrichlorosilane (OTS) into cell walls and to deposit the self-assembled hydrophobic monolayers (SAMs) of OTS is reported. It was found o...
A Kumar, P Ryparová, P Hajek, B Kričej, M Pavlič, A S Škapin, M Šernek, J Tywoniak, J Žigon, M Petrič
Formation of hydrophobic wood surface by means of thermal treatment and surface modification with alkyl ketene dimer (AKD)
2016 - IRG/WP 16-40738
One of the major shortcomings of wood-based materials compared to technical materials is attributed to their poor dimensional stability in changing climates and in contact with liquid water. Heat treatment induces chemical change with a consequent decreasing of reactivity of the material showing unwanted surface inactivation. Alkyl ketene dimer (AKD) is a widely used sizing agent in papermaking, w...
T Lovaglio, T Meints, L Todaro, W Gindl-Altmutter
Exterior birch plywood: potentiality of the thermo-hydro treatment
2016 - IRG/WP 16-40743
It has been found in the present study that, in laboratory fungi tests after leaching with water (EN 84), exterior birch (Betula spp.) plywood, as birch solid wood, is subjected to degradation by rot fungi. This limits the use of such plywood outdoors or in building structures in high humidity conditions. The possibility to improve the birch plywood fungal resistance was investigated in two ways: ...
B Andersons, I Andersone, A Meija-Feldmane, I Irbe, A Janberga, J Grinins
Development of a new method for wood hydrophobizing and fixation of copper compounds by chemical hardening of vegetable based modified oils
2016 - IRG/WP 16-40754
Wood products with ground and direct water contact, but without sufficient biological durability, have to be protected against biological degradation by fungi and other microorganisms. Due to European legislation (Biocidal Products Regulation 528/2012), the selection of possible chemical agents, which are still allowed to be used, is diminishing rapidly. The use of previously widely applied, very ...
C Swaboda, M Fischer, K Jacobs
Effect of insitu polymerization on practical properties of heat treated wood
2016 - IRG/WP 16-40763
This research was conducted to investigate the effect of combined modification; heat treatment and impregnation with styrene monomer on physical and mechanical properties of poplar wood (Populus deltoides). Test samples were grouped in six levels of control, wood polymer made from styrene, heat treatment at 170 ºC and 200ºC and combined modification; first hat treated at 170 ºC and 200ºC and t...
M Ghorbani, M Mohseni Shaktaei
Decontamination of sludges, liquids and soils polluted by “class 1, 2 & 3a” and “temporary” wood treatment products from dipping tanks
2016 - IRG/WP 16-50315
Wood is one of the most widely used building materials as it is easy to find and process. As an organic material, time leads to a degradation of its substance, and even more so when it is exposed to pathogens such as fungi, bacteria and insects. In order to try and inhibit this phenomenon, several preservation treatments have been developed and applied thanks to the production of chemical biocides...
A Zaremski, E Wozniak, S Maman, C Zaremski, S Morel
Influence of organosilicon compounds and nanocellulose treatment on dimensional stability of waterlogged elm wood
2017 - IRG/WP 17-10891
Commonly used agents for waterlogged wood consolidation (including the most popular polyethylene glycol) have proved ineffective and even dangerous to the preserved objects, jeopardising their integrity. Finding new, effective alternatives for safe preservation of wooden cultural heritage is therefore of key importance. The future conservation agents should, first and foremost, provide the integri...
M Broda, B Mazela, I Dąbek, A Dutkiewicz, H Maciejewski, R Markiewicz, M Grzeszkowiak, S Jurga
Novel wood treatments improve resistance to the wood-boring marine isopod Limnoria quadripunctata
2017 - IRG/WP 17-10899
The marine isopod Limnoria quadripunctata degrades wooden structures in the sea and causes significant economic damage. Broad-spectrum biocides and naturally resistant tropical hardwoods have failed to prevent feeding by Limnoria and have caused ecological damage. Wood modification is now the favoured method, and resin-based modifications have been effective, while the efficacy of silica-based mod...
H Bowen, M Montibus, M Kutnik, S M Cragg
Possibility of using lichen (Usnea filipendula) and mistletoe (Viscum album L.) extracts as potential natural wood preservative
2017 - IRG/WP 17-30712
Increasing environmental pressures on toxic chemical wood preservatives lead to the development of natural and environmentally friendly wood preservatives. In this study, using possibilities of lichen (Usnea filipendula) and leaves of mistletoe (Viscum album L.) as potential natural wood preservative were researched. Treatment solutions have been prepared with two different solvents, water and met...
Ü C Yildiz, C Kiliç, A Gürgen, S Yildiz
Weathering protection of European hardwoods through double modification
2017 - IRG/WP 17-30715
Beech and poplar were thermally modified, treated with melamine resin and both treatments were combined. The weathering performance (cracks and general appearance) of modified beech and poplar was assessed in natural weathering and correlated to material properties such as work in bending (WB) and Brinell hardness. In addition, the equilibrium moisture content after exposure of 12 months and subse...
G Behr, A Gellerich, S Bollmus, H Militz
Permeability of Eucalyptus wood improved by microwave treatment
2017 - IRG/WP 17-40773
The wood species with low permeability may cause many problems during timber manufacturing. Extreme difficulties take place in fabricating new wood-based composites by impregnating low- permeability timber with functional materials, such as flame retardant, preservatives and resins. Microwave (MW) treatment can increase the permeability of wood both in transverse and longitudinal directions. The e...
Xia He, Xianjun Li, Jie Xie, Xingyang Xiong
Treatability of beechwood railway sleepers with potential creosote substitutes
2017 - IRG/WP 17-40790
Maintenance of an efficient railway infrastructure still requires the use of wooden railway sleepers, particularly because wooden sleepers have more favourable properties for intensified vibrations than concrete or steel sleepers. Creosote, used for decades for the impregnation of railway sleepers, will possibly no longer be available for this application due to European legislation. This reveals ...
N Pfabigan, E Habla, R Gründlinger
Borate and Copper Naphthenate Dual Treatment of Bridge Timbers-Borate movement over time
2017 - IRG/WP 17-40795
Preservative treated wooden bridge ties in the South Eastern USA have a service life of about 15 to 20 years, which falls well below the average service life of 40 years of railroad cross ties (sleepers). It has been shown that cross tie life is significantly extended using borate dual treatment and this is now commercialized in bridge timbers using borate inserts. In previous research, it was dem...
J-W Kim, J D Lloyd