Observation on the performance of CCB and creosote treated fence posts after 18 years of exposure in Greece
2002 - IRG/WP 02-30288
The effect of 18 years exposure on toughness of CCB and creosote combination treated pine was examined. Vacuum CCB treated fence posts were subsequently treated at their lowest part (ground contact) with creosote using the open hot and cold tank process. After 18 years exposure under warm dry temperate climatic conditions in Greece, samples were taken from the above ground contact, top, middle a...
J A Kakaras, G J Goroyias, A N Papadopoulos, M D C Hale
Effects of air-seasoning on fungal colonization and wood strength of Douglas fir poles
1987 - IRG/WP 1315
Air seasoning economically reduces the moisture content of Douglas fir poles before pressure treatment with preservatives. Advanced decay in poles in service has resulted when decay fungi (Basidiomycetes) colonized poles during air-seasoning and survived the treatment process. These problems have led to recommendations to severely limit this practice. To determine the role of these fungi in peeled...
J J Morrell, M E Corden, R D Graham, B L Kropp, P Przybylowicz, S M Smith, C A Sexton
Marine performance of preservative treated Southern pine panels. - Part 1: Exposure in Newport, Oregon
2000 - IRG/WP 00-10368
The ability of selected wood preservative to protect southern pine sapwood against marine borer attack was evaluated over a 6 year period in Yaquina Bay, Oregon. The site exposed the wood to potential attack by both Teredo navalis and Limnoria spp. Both creosote and CCA provided excellent protection at moderate retentions, while ACQ produced slight differences in performance depending on the coppe...
R G Rhatigan, J J Morrell, A R Zahora
Eradication of wood decay fungi by means of radio frequency
1998 - IRG/WP 98-10292
High frequency electromagnetic fields i.e. radio frequency (RF) are used in wood industry for heating, gluing and bending of wood and are also appropriate for eradicating of wood decay fungi and insects. We investigated the effects of RF exposure on wood samples which were in vitro infected by Coniophora puteana, Gloeophyllum trabeum and Lentinus lepideus. For each fungus, the lethal temperature a...
F Pohleven, J Resnik, A Kobe
The influence of staining fungi on the decay resistance of wood treated with alkylammonium compounds
1984 - IRG/WP 3308
Although found to be very effective in laboratory tests, alkylammonium compounds (AAC's) have failed to perform as well in field stake tests. Examination of leachability showed that this was not the cause. The present study investigated the possibility that staining fungi, (which have been observed to rapidly infect the field stakes), degrade the AAC wood preservative. Soil-blocks were tr...
J N R Ruddick
Comparison of the in-ground performance of pigment emulsified creosote (PEC) and high temperature creosote (HTC)
2000 - IRG/WP 00-30217
A long-term field trial was conducted in Australia to compare the in-ground performance of two oil-borne preservative formulations, conventional high temperature creosote (HTC) and a modified creosote formulation, pigment emulsified creosote (PEC). Three retentions (50, 100 and 200 kg/m³) were targeted for each formulation. An additional retention of PEC formulation (308 kg/m³), which contained ...
J W Creffield, H Greaves, N Chew, N K Nguyen
Environmentally benign wood preservatives based on organic biocide antioxidant combinations: A brief review of laboratory and field exposure results and discussion of a proposed mechanism
2004 - IRG/WP 04-30335
The combination of various organic biocides with commercial antioxidants generally increased the biocides’ efficacy 2-3 fold against wood-destroying fungi in short-term laboratory decay tests, and some positive results have been obtained after 2-4 years of outdoor exposure. The two antioxidants principally examined, propyl gallate and butylated hydroxytoluene, are low cost and, since both are f...
T Schultz, D D Nicholas, W Henry, C Pittman, D Wipf, B Goodell
The effects of preservative treatment and exposure to wood degrading fungi on fiber reinforced polymer (FRP) materials used for structural wood reinforcement
2001 - IRG/WP 01-40204
Glass fiber reinforced phenolic (GFRP) composite materials are becoming increasingly accepted for use in the construction industry because they combine advantages of both wood and advanced polymeric materials. Addition of only 1-3% FRP in the tension zone, for example, can typically improve the strength of the hybrid system by 200%. As more applications are found for wood/FRP hybrids, (e.g. lamina...
C Tascioglu, B Goodell
Fungal detoxification of organotin biocides
1985 - IRG/WP 1258
The ability of a range of wood decaying fungi to inactivate bis(tri-n-butyltin) oxide (TnBTO) in the extracellular growth medium, in stationary liquid culture was determined. A distinction between the ability to tolerate the fungicide and to inactivate it was made: the white-rot organism Coriolus versicolor being the most efficient inactivator. In an attempt to determine the extracellular agents r...
P S Belford, D J Dickinson
International standards – which future?
2003 - IRG/WP 03-20277
A review of past and current activities at CEN/TC/38, within the scope of "wood durability, in relation with exposure" suggest that former activities linked to wood preservative efficacy shall formally include the balance safety/efficacy as a main part of the risk/benefit patterns. One way is an extensive development of liaisons. The case of OECD/CEN cooperation on emission assessment is a positiv...
G Ozanne
Occupational exposure risk assessment at a commercial treatment plant using copper azole preservative
1998 - IRG/WP 98-50101-15
Experience with traditional water-based preservatives such as chromated copper arsenate (CCA) applied in closed system vacuum pressure impregnation plants has shown that operator atmospheric exposure is low during normal operation.
TANALITH E is a commercially available copper azole wood preservative introduced as a chrome and arsenic-free alternative to CCA based on the actives copper, tebuconaz...
A S Hughes, M Connell
Possible durability transfer from durable to non durable wood species. The study case of teak wood
2001 - IRG/WP 01-10392
Teakwood is well known for its excellent natural durability, mostly due to its high proportion of extracts. Amongst these extracts, quinones, and more precisely some naphtoquinones (such as lapachol) and anthraquinones (such as tectoquinone) appear to play a crucial role in the resistance to wood decay organisms. At a laboratory scale, sawdust from malaysian teak heartwood has been extracted under...
M-F Thévenon, C Roussel, J-P Haluk
Comparison of the anti-fungal efficacy of Cobra with drill perforation on oscillating pressure treated spruce transmission poles -Laboratory test
1988 - IRG/WP 3469
A laboratory method for measuring the depth of penetration of the fungicidal concentrations effective against basidiomycetes (brown rot) was developed. The tests on CCB oscillating pressure treated spruce transmission poles have shown that the depth of salt penetration can be increased by about 10 mm by a drill perforation before the impregnation. An even better penetration is reached, however, if...
E Graf, B Zgraggen
A study of fungal biodeterioration in unseasoned, packaged hem-fir lumber
1978 - IRG/WP 2116
This study was undertaken to determine the extent of biodeterioration that could occur within British Columbia (BC) prior to the export of packaged Canadian Lumber Standard Hem-Fir (Tsuga heterophylla, Abies amabilis and small amounts of Abies grandis). By examining the anti-stain treatments received by the lumber and identifying and characterizing the organisms responsible for the biodeterioratio...
P W Perrin, A J Cserjesi
Resistance of acrylic paints on wood against growth of the rot fungus Dacrymyces stillatus
1990 - IRG/WP 2345
In the last few years the presence of the rot fungus Dacrymyces stillatus has been repeatedly confirmed in external wood panels, particularly from wood painted with water based paints. A laboratory method for testing of the fungal resistance of paint films on wood has been developed.This method has been used to test the efficacy of the fungicides Parmetol DF 18 and Parmetol HF 25 against attack by...
J Bjurman
Occurrence and importance of various types of fungal and bacterial decay in CCA-treated horticultural pine posts in New Zealand
1984 - IRG/WP 1234
A detailed microscopical examination has been carried out on samples taken from CCA-treated pine posts exposed in horticultural soils. The following decay types were observed: white rot, brown rot, soft rot, tunnelling bacteria, cavitation bacteria, and bacterial erosion. The occurrence and importance of the various decay types between different regions, and plots within a specific region, varied ...
T Nilsson
A biochemical explanation for the observed patterns of fungal decay in timber
1980 - IRG/WP 1111
Experiments designed to compare the degree of localization of the cellulase enzymes of some white, brown and soft rot organisms are described. The site and nature of binding of the enzymes is discussed. The technique is ellution of mycelium grown in liquid culture with a variety: of agents including acetate buffer, carboxymethyl cellulose solution, borate/glycerol buffer and urea. The mycelium was...
N B Green, D J Dickinson, J F Levy
Imaging fungal deterioration of wood using x-ray microtomography
1997 - IRG/WP 97-10240
Nondestructive tomographic images of solid Southern yellow pine (SYP) wood and SYP during deterioration by wood decay fungi were obtained by using a new class of synchrotron X-ray computed microtomography (CMT). The CMT images will provide information about spatial relationship between degrading fungi and wood structures. Wood samples were scanned with synchrotron-generated X-rays at high resoluti...
B Illman, B A Dowd
The effect of soil pre-exposure on the results of laboratory Basidiomycete testing
1991 - IRG/WP 2385
Scots pine sapwood blocks were treated with several concentrations of copper chrome arsenic (CCA), copper chrome boron (CCB) and a copper modified quaternary ammonium compound (CMAAC). Leached and unleached samples were exposed in a basidiomycete monoculture test using Coniophora puteana, a copper tolerant brown rot. Prior to testing half of the blocks were buried in unsterile soil for 4 weeks. Th...
S M Gray
Effects of the specimen position on fungal colonisation and wood decay by en 113 test fungi
1998 - IRG/WP 98-20136
For testing wood preservatives according to EN 113 it is common practice to plant the test blocks on neutral supports in order to prevent (1) a diffusion of chemicals into the agar medium and (2) an excessive moistening of the specimens. The procedure was employed in EN 350-1 for testing the natural durability of solid wood.
It turned out to be of problematic nature because of the individual requ...
G Kleist, M-T Lenz, R-D Peek
Fungal decay resistance of Rubber wood treated with heartwood extract of Rosewood
2005 - IRG/WP 05-30367
Alcoholic extract of Dalbergia latifolia heartwood was studied for its toxicity towards wood decaying fungi. Rubber wood blocks were treated with this extract to three different retention levels (0.1%, 0.2% & 0.5%) and the treated wood blocks were assessed for their resistance towards two white rot and two brown rot fungi. Treated blocks showed improved resistance over the control blocks. At 0...
A K Sethy, H C Nagaveni, S Mohan, K T Chandrashekar
The Protection of Plywood with Benzalkonium Chloride (BAC) Wood Preservative
2002 - IRG/WP 02-40219
Alkyldimethylbenzyl ammonium chloride (benzalkonium chloride) (BAC) and alkyldimethylamine acetates were approved by the Timber Preservation Authority of New Zealand in 1978 for the protection of radiata pine that was destined for above ground, weather exposed applications. As a result of continuing failures, the use of AACs was stopped in New Zealand in the mid 1980s.
The Plywood Association of ...
J Norton
Anti-fungal properties of pyrolytic oils derived from softwood bark
2000 - IRG/WP 00-30218
Thermal decomposition of balsam fir and white spruce mixed bark residues at 450°C and under vacuum (< 20 kPa abs.) results in high yields of pyroligneous liquors rich in phenolic content. This vacuum pyrolysis process has been scaled-up to a pyrolysis plant with a feed capacity of 3.5 t/h of softwood bark, which is the largest plant of this type in the world. The pyrolytic aqueous condensates ...
D Mourant, Dian-Qing Yang, Xiao Lu, C Roy
Evaluation of white-rot fungal growth on Southern Yellow pine wood chips pretreated with blue-stain fungi
2000 - IRG/WP 00-10349
White-rotting basidiomycetes do not colonize on southern yellow pine. This study seeks to reduce the resinous extractive content of southern yellow pine by treating it with blue stain fungi. The mycelial growth of wood-inhabiting ligninolytic white-rot fungi can be achieved on pretreated southern yellow pine wood. Aureobasidium, Ceratocystis, and Ophiostoma spp. removed 70% to 100% of the extracti...
S C Croan
Fungal decay of acrylate treated wood
2004 - IRG/WP 04-30357
Natural durability of wood species is variable. Chemical wood preservatives, such as biocides are necessary for extension of their service life. Many methods have been developed to increase the resistance of wood and wood products against wood-destroying organisms during the last years. The most frequently used methods are chemical and thermal modification of wood. In wood modification the basic c...
Z Tiralova, L Reinprecht