Natural decay resistance of some lesser known /used timber species from the forests of Tanzania
2005 - IRG/WP 05-10557
In order to manage the Tropical forest in a sustainable manner and increase the resource base for their wood industries, many Tropical African timber producing countries including Tanzania are promoting the many lesser known/used timbers in their forests as alternative sources of wood to the over-exploited primary timber species. Four lesser known/utilized timber species from the forests of Tanzan...
S A Amartey, P R Gillah, R C Ishengoma, J Gabriel, D H Kitojo
Water transfer in wood in relation to fungal attack in building - Effect of condensation and diffusion
1992 - IRG/WP 92-1543
Wood is continuously exchanging moisture with the surrounding atmosphere, the temperature and relative humidity are important factors. Wood moisture in this case is not enough to provoque decay by fungi. However, when, during the night, condensation appears cyclically, wood absorbs water and moisture content may be sufficiently high to allow development if drying does not take place. The water tra...
D Dirol, J-M Vergnaud
Wood cement composites using spent CCA treated wood
1999 - IRG/WP 99-50126
The feasibility of using spent or out-of-service CCA treated wood as a component of wood/cement composites was evaluated. Cold pressed wood particle cement boards were made using CCA treated particles from a red pine (Pinus resinosa Ait.) pole removed from service and from untreated red pine wood from a new pole. Boards were manufactured using a range of wood to cement ratios and water to cement r...
Chen Huang, P A Cooper
Upgrading the fungal resistance of OSB
1999 - IRG/WP 99-40138
There is a perception that oriented strand board (OSB) is less resistant to fungl than plywood under conditions of moderate exposure to moisture. Douglas fir-faced plywood (DFP) has been suggested as a benchmark for acceptable durability under such conditions. This project was initiated to determine the minimum level of low-toxicity chemical treatment needed to upgrade the fungal resistance of OSB...
P I Morris, J E Clark, D Minchin, R Wellwood
Production of monoclonal antibodies to fungal metabolites
1986 - IRG/WP 1306
The role of fungal extracellular enzymes in wood biodegradation is incompletely understood. Our lab is beginning a project utilizing monoclonal antibodies to characterize extracellular metabolites of the brown rot fungus Poria placenta Fr. (Cooke). Monoclonal antibody technology takes advantage of the ability of antibody secreting spleen cells from immunized mice to fuse in the presence of polyeth...
J Jellison, B Goodell
Effects of heart wood extractives in Dahoma (Piptadeniastrum africanum) on decay resistance to white- and brown-rot fungi
2004 - IRG/WP 04-10536
Dahoma (Piptadeniastrum africanum) is a durable but a lesser utilised tropical hardwood species from Ghana that has the potential of being used as an alternative to Iroko (Milicia excelsa) for many end uses. However, the timber gives off a strong odour especially when wet and during processing. The high durability and the strong odour of the timber could be due to the presence of extractives in th...
Zeen Huang, K Maher, S A Amartey
Bioefficacy of Cunapsol® treated western cedar and southern yellow pine
1996 - IRG/WP 96-30120
Western red cedar and southern yellow pine sapwood were dip treated with a new formulation of waterborne copper naphthenate (Cunapsol®) which complies with VOC regulations. Cunapsol dip treated samples were oven dried at 50°C for 48 hours and then water leached for two weeks. Decay resistance and leachability of preservatives from dip treated specimens were evaluated according to AWPA (American ...
D P Kamdem, M H Freeman, T L Woods
The resistance of wood coated with different water-borne paints against colonisation by decay fungi
1996 - IRG/WP 96-10165
The susceptibility of wood painted with model paints of known composition to decay fungi was tested without previous weathering. Included in the study were five alkyd emulsion paints and five acrylic paints; one linseed oil paint and two solvent-borne alkyd paints. It was found that several components influenced the susceptibility of these paints. The results of the present study indicate that the...
J Bjurman
Fun with Soil Block Jars: Teaching fungal wood decay in the classroom
2006 - IRG/WP 06-10574
In this world of increasing complexity and technological advancements, it is ever more important to raise scientifically literate children. The National Science Foundation Teaching Fellowship Program (NSF GK-12) at the University of Maine provides an opportunity for advanced graduate students in science, mathematics and engineering to bring their knowledge, as well as the latest equipment, to stud...
C Howell, L Gott, B Meehan
Laboratory Evaluation of Soft Rot Resistance of Non-Durable Lesser-Known Malaysian Hardwoods
2006 - IRG/WP 06-10582
Resistance of six non-durable lesser-known Malaysian hardwoods, Pulai (Alstonia spp.), Rubberwood (Hevea brasiliensis), Ludai (Sapium spp.), Jelutong (Dyera costulata), Gaham Badak (Blumeodendron tokbrai) and Kayu arang (Diospyros spp.) compared with temperate Scots pine sapwood (Pinus sylvestris), were evaluated using the unsterile soil burial (mixed with Chaetomium globosum) versus vermiculite-b...
A H H Wong
Comparative studies of natural durability of Japanese cedar (Cryptomeria japonica D. Don) among the geographic cultivates
2006 - IRG/WP 06-10592
Variation of natural durability of Japanese cedar (Cryptomeria japonica D. Don) (also known as Sugi) was investigated by accelerated tests for decay (Fomitopsis palustris (Berk. et Curt.) Murr.) and termite (Reticulitermes speratus Kolbe) attacks on 13 clones of Sugi trees from Kyushu-Okinawa Region (Fukuka, Ooita, Saga, Miyazaki, Kagoshima). For this purpose, 57 twenty-five years old Sugi trees o...
I Usta, K Takata, S Doi
Decay resistance of coconut and rubber woods. Alternative wood species from Ghana
2006 - IRG/WP 06-10596
With the expanding local and world wide demand for tropical timbers, there is increased interest in the suitability of lesser–used timber species as alternatives for the forest based industries in order to ensure sustainable forest management. In the forests of Ghana, there are quite a number of timber species that are lesser known and have not been adequately used due to the absence of informat...
S Amartey, M Humar, B Donkor, F Pohleven
Resistance of pine and spruce heartwood against decay - The effect of wood chemical composition and coating with water-borne wood oil product
2006 - IRG/WP 06-10597
Natural durability of wood has been widely studied, but the combination of the natural durability and different treatments has not been the focus of many studies. The durability of wooden products is mainly based on the water permeability and the resistance against organisms. In this study, the water absorption and decay resistance of sapwood and heartwood of Scots pine and Norway spruce were exam...
H Viitanen, S Metsä-Kortelainen, T Laakso
Predicting the decay resistance of timber above-ground: 1. Climate effects
2006 - IRG/WP 06-20330
Despite the benefits of using timber as a building product, it is disadvantaged by current Australian Standard durability classifications which lack the sensitivity desired by engineers and architects. To address the need for more sensitive timber service-life information in Australia, an above-ground durability research program was established in 1987. One focus of research is the relationship be...
L P Francis, J Norton
Investigation on a Wood Decay Biomarker
2006 - IRG/WP 06-20336
HPLC evolution of beech wood extractives was investigated with or without exposure to Coriolus versicolor during one month. The nature and the quantity of extracts depends on the extraction conditions, but were also strongly influenced by the wood drying temperature and time leading to an important modification for higher drying temperature. After two weeks of exposure to Coriolus versicolor, resu...
S Mounguengui, S Dumarçay, P Gérardin
High-energy multiple impact (HEMI)-test – Part 2: A mechanical test for the detection of fungal decay
2006 - IRG/WP 06-20339
The suitability of the high-energy multiple impact (HEMI)-test for detection of early fungal decay was examined. The HEMI – test characterizes the treatment quality of thermally modified wood by stressing the treated material by thousands of impacts of pounding steel balls. This method differentiates between heat treatment intensities, which are expressed by structural changes of the wood. Simil...
C R Welzbacher, C Brischke, A O Rapp
Tree crown architecture: a tool for decay resistance evaluation
2013 - IRG/WP 13-10793
The variability of natural durability contributes to the bad perception of some wood end-users. In our search, we need to adjust our methods and strategies to estimate natural durability and extract higher value from wood resources. Architectural analysis is essentially a detailed, multilevel, comprehensive and dynamic approach to plant development. Numerous biological process which impact some wo...
N Amusant, J-B Anouhé Say, A Amissa, J Beauchène, F Niamké, E Nicolinni
Assessment of the Envelope Effect of Three Hot Oil Treatments: Resistance to Decay by Coniophora puteana and Postia placenta
2006 - IRG/WP 06-40344
Timber of Corsican pine (Pinus nigra var. maritima) and Norway spruce (Picea abies) was treated in hot linseed oil, rapeseed oil and a proprietary resin derived from linseed oil. The samples were immersed in oil or resin under reduced pressure at temperatures of 180°C and 200°C. Very high uptakes of the oils or resin were recorded for pine, while spruce showed lower weight percent gains, below...
M J Spear, C A S Hill, S F Curling, D Jones, M D C Hale
Furfurylated wood - An alternative to Preservative-treated wood
2006 - IRG/WP 06-40349
Chemically modified wood is currently being marketed as a non-toxic alternative to traditional preservative treated wood (wood impregnated with biocides). Over the last decade the authors have developed modernised processes for wood modified by furfurylation. These new systems do not add metals or halogens to the product, which is important for an environmentally acceptable product. This presentat...
S Lande, M H Schneider, M Westin, J Phillips
Resistance of DMDHEU-treated pine wood against termite and fungi attack in field testing according to EN 252. Results after 30 months
2006 - IRG/WP 06-40354
The aim of this study was to determine the effectiveness against decay and termite attack of pine sapwood treated with pure and modified DMDHEU in a field test according to European Standard EN 252. Some of the treatments tested were able to increase, within the period of the test reported (30 months), the resistance of the wood both to micro-organisms and termites. The curing process seems to be ...
S Schaffert, L Nunes, A Krause, H Militz
Biological Protection of Composite Panel from Moulds and Decay
2007 - IRG/WP 07-10612
Composite panels, such as oriented strand board (OSB), are widely used in house construction in North America. These structural panels are normally made of non-durable wood species and are susceptible to moulds and decay when exposed to wet conditions. Building envelope failures due to moulds, decay or poor construction practices can negatively impact the image of wood. To ensure durability of com...
Dian-Qing Yang, Xiang-Ming Wang, Hui Wan
Detecting fungal DNA in treated and non-treated wood
2007 - IRG/WP 07-10621
Isolating fungi from wood has long involved culturing on selective media followed by identification using various keys. This process can be cumbersome, costly, and, most importantly, not always capable of detecting all of the fungi present. The recent development of molecular methods for isolation and identification of fungi has created tremendous opportunities for expanding our knowledge of the...
C Freitag, M Freitag, J Morrell
Effect of fungal attack on maximum load capacity of simulated wall assemblies
2007 - IRG/WP 07-20363
The effects of moisture intrusion and fungal attack on the maximum load capacity of nailed assemblies was investigated using one white and one brown rot fungus against 4 material combinations over a 20 week period. Wetting significantly reduced the maximum load capacity of all four material combinations, while wetting and autoclaving only affected the OSB sheathing/spruce stud. The white rot fung...
N Melencion, J J Morrell
Predicting the decay resistance of timber above-ground: 2. When can reliable field data be obtained?
2007 - IRG/WP 07-20368
Application of modern performance-based engineering and design requires building products that are thoroughly characterised in terms of their ability to perform as expected over time. The engineering community is attempting to use this information to provide predicted service-lives for various building elements. Increasingly, this service-life prediction must be based on objective measurement coup...
L P Francis, A J Swain, J J Morrell
Some textile auxiliaries as wood protective agents
2007 - IRG/WP 07-30417
This study evaluated some textile auxiliaries applicable for wood protection. Commercial alkoxysilane quarternary ammonium formulation and fluorocarbon based water-oil repellent were tested for their ability to provide hydrophobicity and antifungal effect to solid wood samples. Scots pine (Pinus sylvestris L.) sapwood samples were impregnated with 25, 50 and 100 % concentrations of the above menti...
E Dizman, A Temiz, N Terziev, Ü C Yildiz