Influence of carboxylic acids on LEACHING of copper amine based preservatives
2005 - IRG/WP 05-30365
The importance of chromium free preservatives is increasing. Leaching of copper from wood preserved with such solutions is still higher compared to leaching from wood impregnated with copper chromium ones. In order to decrease leaching, different carboxylic acids (octanoic, 2-etilheksanoic, decanoic) were added to copper/amine/boron aqueous solutions. Experiment of leaching of copper from Norway s...
M Humar, P Kalan, F Pohleven


Fundamentals on steam fixation of chromated wood preservatives
1988 - IRG/WP 3483
Weathering of treated wood directly after impregnation leaches up to 2% of copper-chromate-containing wood preservatives. Almost total fixation of Cr+6 is achieved by steaming the treated wood at 100°C to 120°C, preferably 110°C. To initiate such spontaneous fixation 85°C to 90°C inside the wood are essential, which requires heating times ranging from 20 to 80 min, depending on timber species...
R-D Peek, H Willeitner


Performance of preservative-treated wood not in ground contact
1975 - IRG/WP 254
Experimental sash units of Pinus strobus L. and Pinus resinosa Ait. wood were removed from a test fence at Ottawa, Canada after outdoor exposure of over 20 years. The units were superficially treated, prior to painting, with preservatives containing either copper naphthenate, pentachlorophenol or a combination of zinc naphthenate and pentachlorophenol. Results indicated that all treatments were ef...
J K Shields, J Krzyzewski


Leachabilty and efficacy of fatty acid derived boron esters as wood preservatives - leachability and efficacy of fatty acid derived boron esters as wood preservatives
2004 - IRG/WP 04-30351
Borates have many advantages as wood preservatives. However, boron is susceptible to depletion under humid conditions and this restricts its outdoor use. In order to reduce boron leachability in treated wood, one of the anticipative approaches is to use organic fixed boron-based preservatives. This study investigated the leachability of six boron ester compounds as potential preservatives. Scots p...
A Mohareb, J Van Acker, M Stevens


Laboratory evaluation of the termiticidal effectiveness of TanalithÒ 3485
1995 - IRG/WP 95-10109
The termiticidal effectiveness of the copper azole TANALITH 3485 was evaluated with the benchmark preservative TANALITH C in a laboratory bioassay using two species of subterranean termites, Mastotermes darwiniensis Froggatt and Coptotermes acinaciformis (Froggatt). Retentions of TANALITH 3485 tested were 0.15, 0.24, 0.285 and 0.40% m/m Cu and for TANALITH C 0.025, 0.05, 0.08 and 0.095% m/m Cu. Un...
J W Creffield, J A Drysdale, N Chew, N-K Nguyen


Influence of acidification on decay processes of CCB treated wood
2004 - IRG/WP 04-10514
The phenomenon of copper tolerance by brown rot fungal strains has been known for a long period but the complete mechanism of copper tolerance by these fungi is not understood yet. Copper tolerance has previously been linked to oxalic acid excreted by copper tolerant brown rot fungal strains. This acid reacts with copper in the wood to form an insoluble and therefore less toxic copper oxalate. The...
M Humar, S A Amartey, M Šentjurc, F Pohleven


The remaining concentration of inorganic wood preservative components in EN 252 stakes after ground contact
2000 - IRG/WP 00-50159
In order to determine the biological efficiency and the remaining concentration of different inorganic and organic active ingredients during service, EN 252 specimens were impregnated with 3 copper based wood preservatives. The stakes were installed in the test field of the DESOWAG GmbH, Rheinberg, for at least 7 years. At the end of the field test some of these stakes were divided into 10 uniform...
E Melcher, H-W Wegen


Laboratory studies of CCA-C-leaching: influence of wood and soil properties on extent of arsenic and copper depletion
2002 - IRG/WP 02-50186
The extent which a wood preservative leaches is important for efficacy studies and environmental concerns. However, little information exists on the effect soil properties have on leaching. This study investigated leaching of stakelets which had been cut from five different southern yellow pine (SYP) sapwood boards then treated with CCA-C to a target retention of 6.4 kgm-3 (0.4 pcf). All stakel...
D Crawford, R F Fox, D P Kamden, S T Lebow, D D Nicholas, D Pettry, T Schultz, L Sites, R J Ziobro


Water repellency of wood treated with alkylammonium compounds and chromated copper arsenate
2000 - IRG/WP 00-30231
The comparative water sorption properties of southern pine treated with CCA and several alkylammonium compounds was evaluated for freshly treated wood and for wood after exposure in a fungus cellar. It was found that CCA imparts considerable water repellency to wood which is reduced somewhat after exposure to wet soil. With the exception of a long chain (C20 -C22) compound, the alkylammonium compo...
D D Nicholas, A Kabir, A D Williams, A F Preston


Preservative treatment of wood by diffusion processes - Simulation of commercial treatment processes
1988 - IRG/WP 3498
Spruce (Picea abies), Scots pine (Pinus sylvestris) and birch (Betula pendula) were preservative treated by diffusion with mixtures of copper sulphate and arsenic pentoxide. The preservative was fixed after a suitable diffusion storage period by soaking in ammonia solution. A high standard of treatment could be achieved in spruce sapwood. This was attributed to its low wood density, and high wood ...
P Vinden


Persistance of active ingredients in treated wood
1993 - IRG/WP 93-50001-20
Disposing of chemically protected waste wood implies the distinction between surface and pressure treatment. Considering that barked round-wood merely contains, after 7 months open storage, less than 30 g per ton of bark or 25 mg per ton of sapwood, depending on the type of insecticide, the bark or sapwood shavings may be incinerated normally, according to less severe legal prescriptions than for ...
E Graf, P Manser, S Rezzonico, B Zgraggen


Leaching of preservative components from pine decking treated with CCA and copper azole, and interactions of leachates with soils
2001 - IRG/WP 01-50171
Radiata pine decking was treated with CCA and copper azole preservatives to Australian H3 retention using conventional and modified Bethel schedules, and air-dried. Treated decking boards and durable hardwood controls were subjected to leaching in weather-exposed decks, and matching 19mm cubes were leached in extended AWPA E11-97 lab tests. Deck runoff and E11 leachate water was analysed after rai...
M J Kennedy, P A Collins


Environmental fate of copper-based wood preservatives in different soil substrates - Part 1: Screening of the metal adsorption potential
1998 - IRG/WP 98-50101-21 a
In treatment plants, spillage of wood preservatives onto soil may be of environmental concern. This potential soil contamination served as an objective for a screening study. Three different mineral soils, a mineral substrate and two horticultural substrates are examined for their sorptive potential of copper through mixing with wood preservative solutions. Depending on the soil/substrate charact...
G M F Van Eetvelde, J M Mwangi, F Tack, R Hartmann, M Stevens


Microwave digestion of preserved wood for the determination of Cu, Cr, As, B and P in quality control
1991 - IRG/WP 2364
A microwave digestion method for the determination of copper, chromium, arsenic, boron and phosphorus in preserved woods is described. Samples were digested with nitric acid in pressure-relief type teflon PFA vessels by microwave heating in a commercial laboratory microwave oven. Fast, efficient and complete digestion was achieved within 29 min for 12 samples. The digestion time compared favourabl...
N Bernth, L B Sheard


International collaborative laboratory comparison of two wood preservatives against subterranean termites: Second update
1995 - IRG/WP 95-10117
As was agreed by members at the termite workshop at the 24th annual meeting of IRG in Orlando, USA, in May 1993 to initiate an international subterranean termite laboratory bioassay to compare the various preferred termite protocols used by IRG termitologists was initiated. The author was nominated to co-ordinate this comparative laboratory evaluation of two wood preservatives (CCA and Cu-naphthen...
J R J French


Diffusion modeling of inorganic wood preservative leaching in service
2005 - IRG/WP 05-50224-5
To evaluate the potential environmental and health implications of leaching of inorganic wood preservatives in service under different conditions, there is a need for a predictive model that provides estimates of the rate and extent of leaching over a wide range of product dimensions and exposure conditions. In this paper, we show that the leaching behavior of inorganic preservative components fr...
L Waldron, P A Cooper, Y T Ung


Mechanistic aspects of the reactions of copper complexes with lignin in the presence of hydrogen peroxide and lipid hydroperoxide model compounds as proposed for white rot fungi
2001 - IRG/WP 01-10399
The structural principles and the oxidative reactions of the catalytic system consisting of copper, hydroperoxides, and copper coordination compounds that contain aromatic nitrogen atoms are similar to those of catalytic centers of oxidative enzymes involved in delignification reactions of white rot fungi. The system is capable of selectively degrading lignin and its low molecular weight would all...
K Fackler, P Lamaipis, E Srebotnik, M Humar, C Tavzes, F Pohleven, M Sentjurc, T Watanabe, K Messner


Preservative treatment of rubber wood (Hevea brasiliensis) to increase its service life
2005 - IRG/WP 05-40320
Rubber wood (Hevea brasiliensis) possess excellent properties for interior designing, wood working and furniture making. But it is very much susceptible to sap stain and mould fungi which decreases the service life. For profitable uses , it is necessary to increase the service life of rubber wood. To protect the rubber wood from wood degrading agents, the sawn timber were treated with Borax – b...
K Akhter


Influence of variable lignin content amongst hardwoods on soft-rot susceptibility and performance of CCA preservative
1982 - IRG/WP 1151
This paper presents the outline of an argument, based on both new and established data, which relates varying lignin content to variation of soft-rot susceptibility between hardwood species and of performance of CCA preservatives in controlling soft-rot. Although more data need to be generated to prove this relationship, sufficient evidence exists for the hypothesis to be given close attention, pa...
J A Butcher, T Nilsson


Determination of the amine to copper ratio remaining in wood after leaching
2002 - IRG/WP 02-30285
The effectiveness of the protection and the environmental impact of the treated wood are two of the most important aspects that need to be understood for all preservatives. Both are particularly influenced by the loss of biocidal components from treated wood. For amine copper preservatives, copper fixation determines the leaching resistance of the copper and amine compounds formed in wood. Previou...
N Lucas, J N R Ruddick


Weathering of copper-amine treated wood
2000 - IRG/WP 00-40155
Copper ethanolamine (Cu-EA) treated southern pine (SP) were artificially weathered with a QUV Weathering Tester. The weathering regime was composed of a continuous UV-light irradiation for 2 hours followed by a water spray for 18 minutes for a total time of 1200 hours. The changes on the surface of the weathered samples were characterized by Fourier transform infrared spectroscopy (FTIR) analysis,...
J Zhang, D P Kamdem


A possible role of unique TCA cycles in wood-rotting basidiomycetes
2003 - IRG/WP 03-10461
The copper tolerant brown-rot fungus, Fomitopsis palustris, acquires metabolic energy by use of the constitutively-occurring Kornberg’s glyoxylate cycle coordinating with oxalate biosynthesis and glucose oxidation (Erman Munir et al. Proc. Natl. Acad. Sci. USA, (2001) 98, 11126-11130). Furthermore, this fungus does not have the normal TCA cycle, lacking 2-oxoglutarate dehydrogenase which is a ke...
E Munir, T Hattori, M Shimada


Studies of the mechanism of chromated-copper preservative. Fixation using electron spin resonance
1992 - IRG/WP 92-3701
Two softwoods and one hardwood species were treated with chromium trioxide, copper sulphate, chromated-copper wood preservative (CCA). The treated wood samples were analyzed during fixation by electron spin resonance (ESR). ESR spectra indicated that more than one Cr(V) species was generated from Cr(VI) soon after CCA treatment. The Cr(V) signal became strong within increased several hours followe...
K Yamamoto, J N R Ruddick


Fouling organisms as indicators of the environmental impact of marine preservative-treated wood
1995 - IRG/WP 95-50063
This study evaluates the use of fouling organisms (epibiota) to assess the environmental impact of preservative treated wood. This paper presents initial findings from treated panels exposed for 6 months at Sagres, Algarve, Portugal. Panels were treated with CCA, two copper-containing quaternary ammonium (ACQ) formulations and creosote, with nominal retentions from 10 to 40 kg/m³ (creosote 25 pcf...
R M Albuquerque, S M Cragg


Properties of particleboard made from recycled CCA-treated wood
2000 - IRG/WP 00-50146
Recovery of chromated copper arsenate (CCA)-treated wood for reuse ha s been the focus of several international research groups due to the imminent disposal problem created when large quantities of CCA-treated wood ultimately come out of service. Bioleaching with Bacillus licheniformis CC01 and oxalic acid extraction are two methods known to remove significant quantities of metals from CCA-treated...
C A Clausen, S N Kartal, J H Muehl