Effects of pre-harvest girdling on selected properties of red pine, red maple and Eastern larch
1999 - IRG/WP 99-40137
Trees of three species - tamarack (Larix laricina), soft maple (Acer rubrum) and red pine (Pinus resinosa) - were girdled immediately below the crown,one to two years before felling. The wood from these trees was compared with wood taken from un-girdled control trees felled at the same. Sapwood and heartwood, from the controls, and from above and below the girdle of treated trees, were examined fo...
A Taylor, P A Cooper
Effect of soil chemistry and physical properties on wood preservative leaching
1998 - IRG/WP 98-50111
When treated wood is placed in contact with soil, complicated mass transfer and chemical reactions occur which causes the preservative components to leach from the wood. There are several factors that are known to affect the amount of chemical leached from wood. These are properties of the preservative and carrier, preservative retention, degree of fixation, exposure time, grain orientation, surfa...
Joan-Hao Wang, D D Nicholas, L S Sites, D E Pettry
Bamboo: A Material Rediscovered
2006 - IRG/WP 06-10577
Bamboo has resurfaced as a valuable raw material as an inexpensive substitute for wood and a variety of value added products for engineered composites. Being a fast growing material available in the tropics, its real value was not realized until recently. Property evaluation studies and efforts to develop processing methods were initiated in the bamboo growing countries in the nineteenth century....
S Kumar
Correlation between modulus of elasticity, mass losses and FTIR spectra of copper treated decayed wood
2006 - IRG/WP 06-10580
The composition of copper-based preservatives will change from copper-chromium to copper-ethanolamine, due to environmental demands. The most important drawback of copper-impregnated wood is the presence of tolerant fungal organisms that have developed an ability to degrade such preserved wood. In order to elucidate these processes, specimens (0.5×1.0×15 cm) made of Norway spruce (Picea abies) w...
M Humar, B Bucar, F Pohleven
Moldicidal properties of seven essential oils
2006 - IRG/WP 06-30404
When wood and wood products are exposed to moisture during storage, construction or while in-service, mold growth can occur in 24 to 48 hours. Mold growth could be suppressed or prevented if wood was treated with an effective mold inhibitor. The objective of this study was to evaluate the mold inhibiting properties of natural plant extracts such as essential oils. Seven essential oils were evaluat...
V W Yang, C A Clausen
High-energy multiple impact (HEMI)-test – Part 2: A mechanical test for the detection of fungal decay
2006 - IRG/WP 06-20339
The suitability of the high-energy multiple impact (HEMI)-test for detection of early fungal decay was examined. The HEMI – test characterizes the treatment quality of thermally modified wood by stressing the treated material by thousands of impacts of pounding steel balls. This method differentiates between heat treatment intensities, which are expressed by structural changes of the wood. Simil...
C R Welzbacher, C Brischke, A O Rapp
High-energy multiple impact (HEMI)-test – Part 1: A new tool for quality control of thermally modified timber
2006 - IRG/WP 06-20346
Thermal modification processes improve durability and dimensional stability of wood, but the strength properties, especially the dynamic ones, are compromised and need to be considered with respect to industrial quality control. Results from standard dynamic strength testing, such as impact bending tests, suffer from high variability, and therefore require a high number of replicates. To overcome ...
C Brischke, A O Rapp, C R Welzbacher
Addition of boron compounds and octanoic acid for improvement of biocidal properties and copper fixation at copper-ethanolamine based wood preservatives
2006 - IRG/WP 06-30408
Copper-ethanolamine based wood preservatives became important active substance (formulation) for wood protection, novelty. As copper itself can not ensure sufficient protection against wood destroying organisms and fixation in wood we combine it with other biocides like ethanolamine, boron and octanoic acid. This investigates were performance on spruce wood impregnated with different combination o...
F Pohleven, M Humar
Heat treatment of less-valuable Nigerian-grown Ceiba pentandra wood for improved properties
2006 - IRG/WP 06-40332
The hardwood Ceiba pentandra locally known as “ araba “ in Nigeria is rarely used for structural and construction works due to its high dimensional instability, low strength and durability values. Samples (10 x 10 x 150mm) were removed from four green boards (25 x 200 x 3000mm) of this species originating from a natural forest stand in Nigeria and subjected to 2-hour heat treatment at 160°C a...
L Awoyemi
Copper borate for the protection of engineered wood products
2006 - IRG/WP 06-40334
Copper borate was evaluated for use in protecting oriented strand board (OSB) from mould, decay, and termites. Aspen OSB bonded with either phenolic or isocyanate resin was treated with several formulations of copper borate at various loadings from 0.26 to 4 percent by weight. These panels were then tested to determine the impact of the preservative on mechanical properties as well as resistance ...
R Smart, W Wall
Wood plastic composites from modified wood; Part 1 - Conceptual idea, mechanical and physical properties
2006 - IRG/WP 06-40338
Wood plastic composites, WPCs, are rapidly taking shares from preservative treated wood on the decking market. However, the long term performance of the WPC products in this application is uncertain. Therefore, in an attempt to increase the long term performance and durability, the substitution of the unmodified wood component with modified wood has been studied in the work presented in this paper...
P Larsson Brelid, B K Segerholm, M Westin, M E P Wålinder
The commercialisation of ThermoWood® products
2006 - IRG/WP 06-40339
The concept of thermally modifying timber is well established, which has achieved a limited market breakthrough to date. Commercial application has mainly occurred within Finland, though recent years has seen market gain in several other European countries. This paper reviews the known properties of ThermoWood® timber, based on the combined work of the Finnish ThermoWood® Association, alongside ...
D Jones, E Suttie, J Ala-Viikari, N Bergstrom, D Mayes
Characteristics of treated oriented strand lumber using recycle chips
2006 - IRG/WP 06-40343
The Kyoto Protocol for preventing global warming has come into effect, and the Cabinet Council was decided on the amount of carbon dioxide exhaust to be reduced in Japan. Moreover, the recycling of demolition waste wood is mandated under the “Construction Material Recycling Law” as one of the mechanisms for Japan to form the recycling society. The law encourages the utilization of demolition w...
T Shibusawa, A Miyatake, K Yamamoto, K Hashimoto, H Sonobe
Influence of Acetylation on Fire Resistance of Beech Plywood
2006 - IRG/WP 06-40326
Influence of acetylation on fire resistance was studied in beech plywood. Beech layers were acetylated in a reactor with acetic anhydride at 120ºC for varying durations. Plywoods were made from the acetylated layers and directly exposed to burning flame from their edges for 60s according to ISO 11925-3. Ignition and glowing time were measured in samples. Results were analyzed statistically based ...
B Mohebby, A Talaii, A Karimi , S Kazemi Najafi
Effect of fire retardants (monoammonium phosphate and diammonium phosphate, mixture of monoammonium phosphate and borax and ammonium sulphate) on beech wood with dipping and Lowry methods
2006 - IRG/WP 06-40350
In this study, the possibilities of using four kinds of chemicals as fire retardants with 12% concentration for beechwood (Fagus orientalis Lipsky) was surveyed. Providing testing samples that are related to the measurement of fire resistance properties according to JIS A-1321-1975 standard were evaluated. Wood samples were impregnated with Lowry and dipping methods. In this study, samples impregn...
M Akhtari, D Parsapajouh, M Arefkhani
Effect of fire retardants (monoammonium phosphate and diammonium phosphate, mixture of monoammonium phosphate and borax and ammonium sulphate) on beech wood with dipping and Lowry methods
2006 - IRG/WP 06-40350
In this study, the possibilities of using four kinds of chemicals as fire retardants with 12% concentration for beechwood (Fagus orientalis Lipsky) was surveyed. Providing testing samples that are related to the measurement of fire resistance properties according to JIS A-1321-1975 standard were evaluated. Wood samples were impregnated with Lowry and dipping methods. In this study, samples impregn...
M Akhtari, D Parsapajouh, M Arefkhani
Effects of heat treatments on decay resistance and material properties of ponderosa pine and yellow poplar
2007 - IRG/WP 07-40374
The potential for using heat treatment to improve the properties of North American fenestration species was evaluated on ponderosa pine (Pinus ponderosa L) and yellow poplar (Liriodendron tulipifera L) treated using the ThermoWood process at various treatment temperatures and times. Soil block tests using Gloeophyllum trabeum, Postia placenta, or Trametes versicolor showed that durability was enh...
C Vidrine, C Freitag, J Nicholson, J J Morrell
Influence of ethanolamine on lignin depolymerization and copper leaching from treated Norway spruce and beech wood
2007 - IRG/WP 07-30423
Copper-ethanolamine based wood preservatives are replacing several classical copper-chromium based solutions, due to foreseen ban of chromium. Fixation of copper-ethanolamine based wood preservatives is not as good as fixation of copper-chromium ones. The main object of this manuscript was to prove, that ethanolamine is the prime reason for insufficient fixation of copper-ethanolamine formulations...
M Humar, B Bucar, M Zupancic, D Žlindra, F Pohleven
The effect of an ionic liquid of imidazolium tetrafluoroborates series on Scots pine wood properties
2007 - IRG/WP 07-40357
Ionic liquids (ILs) of imidazolium tetrafluoroborates series penetrate Scots pine wood very well and are active against wood destroying fungi. The requirement to use ILs as wood preservatives is determined by the liquid influence on the functional properties of wood. Investigations were undertaken to clarify the influence of an ionic liquid, 3-heptyloxymethyl-1-methylimidazolium tetrafluoroborate ...
A Fojutowski, R Szukala, J Pernak
Mold resistance of heat-treated wood
2007 - IRG/WP 07-40358
The resistance of heat-treated sugi sapwood against three mold fungi was evaluated. Wood specimens were first subjected to heat treatments at 180 and 220ºC for 2 and 4 hours. Mold growth on the surface of the specimens was measured 1, 2, 4 and 6 weeks after the inoculation with the fungi in laboratory conditions. Laboratory decay tests were performed using two brown and white-rot fungi along with...
S N Kartal
The effects of chemical modification on the biological properties of alder and spruce particleboards
2007 - IRG/WP 07-40363
This study is evaluated by measuring the weight loss, and the ability of white and brown-rot fungi to attack unmodified and modified particleboards manufactured using spruce (Picea orientalis (L.) Link.) and alder (Alnus glutinosa) chips. The chips were reacted with acetic, succinic, maleic and phthalic anhydride at constant temperature for 3 hours then, hot pressed at 150 °C by using phenol for...
Ü C Yildiz, E Dizman, S Yildiz, A Temiz, M Aslan, E D Gezer
Fire Safety of Wood Floor Assembly: Model and Full-scale Test
2007 - IRG/WP 07-20375
The present paper describes the model for the prediction of fire safety of wood floor assemblies. The model includes heat transfer model for the calculation of the flow of heat in floor assembly and structural model for the analysis of the mechanical performance of wood joists. The floor assemblies considered in this paper are constructed with nominal 2x10 (38x241mm) wood joists lined by Type X ...
H Takeda
Decay Resistance Properties of Hemicellulose-Extracted Oriented Strand Board
2008 - IRG/WP 08-10644
There is increasing interest in using cellulosic biomass as the basis for a renewable source of energy. Although the traditional focus has been on cellulose, researchers are also exploring the possibility of using hemicelluloses because they can be removed with hot water leaving the wood product intact for other applications. However, there is concern that removing hemicelluloses from the precur...
C Howell, J Paredes, S Shaler, J Jellison
Relationship between coating properties and their performance on treated wooden decks
2008 - IRG/WP 08-30454
Preservative treated wood benefits from the application of a surface coating to protect it from weathering (UV and rain). Different preservative formulations may affect surface properties of treated wood differently; therefore compatibility of coatings with different preservative treated wood types should be considered. This paper examines coatings characteristics and their weathering performance ...
M Ahmadinejad, P A Cooper
Influence of Polyvinyl acetate emulsion (PVA) on boron leaching and fungicidal properties
2008 - IRG/WP 08-30451
Boron compounds are very effective fungicides, but unfortunately they leach from wood. In order to improve boron fixation, boric acid, borax were combined with polyvinyl acetate emulsion (PVA). For comparison copper salts were included into this research as well. Selected preservative solutions were chosen for impregnation of Norway spruce wood specimens (Picea abies). Wood blocks were exposed to ...
M Humar, B Lesar, P Kralj