Micromorphology of oak wood degraded by brown rot fungus Coniophora puteana
2000 - IRG/WP 00-10356
To characterize the degradation of hardwood by brown rot fungus, Coniophora puteana was incubated on the wood blocks of Quercus accutissima. For comparison, the same fungus was also incubated on the pine wood blocks of Pinus densiflora. In softwood, the shape of the wood cells and thickness of the cell appeared unchanged even the loss of birefringence in the affected areas. In contrast, oak wood d...
Yoon Soo Kim, Seung-Gon Wi, Kwang-Ho Lee
A real scale evaluation method and results on termite resistance of housing wall systems and floor framings
1999 - IRG/WP 99-10314
For evaluating the termite resistance of real scale houses especially housing wall systems and floor framings, a experimental building was prepared. After initial feeding of termite, this house was constructed. In this experimental building, several parts which were built by different wall systems and floor framing. The room temperature of these parts were controlled. Water can be provided in the ...
K Suzuki, K Okada, K Hagio, Y Tanaka
Cavitation bacteria
1984 - IRG/WP 1235
A form of bacterial wood degradation is described. The term "cavitation bacteria" has been coined in order to describe the discrete cavities that are formed within the wood cell walls. The bacteria observed within the cavities appeared to be polymorphic with rounded as well as filamentous forms recognised. TEM studies suggest that the bacteria produce diffusable wood-degrading enzymes. Cavitation ...
T Nilsson, A P Singh
The development of soft rot decay in bamboo fibres
1992 - IRG/WP 92-1572
The development of decay by soft rot fungus Chaetomium globosum was investigated in young and mature culms of bamboo Phyllostachys virideglaucescens. Soft rot decay was influenced both quantitatively and qualitatively by the differing levels of lignification in the material. Weight loss was significantly greater in the younger culm compared with the older, more heavily lignified culm. The distribu...
O Sulaiman, R J Murphy
Bacterial degradation of wood cell wall: A review of degradation patterns
1990 - IRG/WP 1460
Information from bacterial degradation studies of 60's and 70's was reviewed by Nilsson in 1982. The application of electron microscopy to this area in recent years has provided much useful information and has eliminated earlier scepticism among workers about the ability of bacteria to degrade lignified wood cell walls. Studies using transmission electron microscopy together with...
A P Singh, J A Butcher
Utilisation of carbohydrates by stain fungi in agar culture
1998 - IRG/WP 98-10248
Stain fungi are often defined by their ability to utilise the starch and free sugars found in ray parenchyma cells, and their inability to utilise other wood constituents. However, several species of stain fungi produce bore holes in wood cell walls. This suggests that enzymatic activity capable of degrading structural polysaccharides and/or lignin is associated with the growth of the appressorium...
J Snow, P Vinden, S M Read
Degradation of woods by obligately anaerobic fungi
1990 - IRG/WP 1452
Little is known about the processes occurring during the degradation of wood by obligately anaerobic fungi. When woods from a range of hardwood species were incubated for 11 days with a strain of the Chytrid Neocallimastix frontalis many of the woods were measurably fermented; Fagus sylvatica (23%) was the most highly degraded. Microscopic examination of Populus tremuloides wood after incubation w...
K N Joblin, G E Naylor
A Novel Type of Multiple Cavity Attack in Wood Cell Walls of Heat-treated Timber Exposed in Seawater – Preliminary Observations
2004 - IRG/WP 04-10523
Samples of untreated and heat-treated Norway spruce and Douglas fir were submerged in Langstone Harbour, Portsmouth for 4 years at a depth of ca. 0.3 metres. The heat-treated samples had been prepared using the Plato process. Samples were initially assessed for the severity of marine borer damage and were then examined microscopically for evidence of microbial decay. Longitudinal and transverse wo...
R A Eaton, C Björdal, T Nilsson
Exclusion of anions from the wood cell wall
1991 - IRG/WP 3661
Anionic components of wood preservatives and fire retardants such, as arsenates and phosphates, equilibrate at much lower concentrations in the cell wall bound water than in the free solution in the cell lumens. A degree of anion exclusion is expected in wood, due to the Donnan membrane effect. Fixed anions in the wood cell wall, produced by pH-dependent dissociation of the weak acid groups in woo...
P A Cooper
Chitin synthetase activity in cellular fractions of wood-decay fungi
1992 - IRG/WP 92-1524
This study was an attempt to explain the variability of in vivo sensitivity of wood decay fungi to the chitin synthetase (CS) inhibitor, polyoxin, by comparing CS distribution in cellular fractions. The five species studied were the brown-rot fungi Coniophora puteana, Gloeophyllum trabeum, Fibuloporia vaillantii, and the white-rot fungi Schizophyllum commune and Ganoderma applanatum. The CS activi...
B R Johnson, S C Croan, B Illman
Amenability of radial permeability of Sitka spruce (Picea sitchensis (Bong.) Carr.) as affected by aspects of cell ends in uniseriate ray parenchyma tissue
2003 - IRG/WP 03-40252
The principal objective of this article was to recognise and understand the amenability of ray parenchyma cell ends (end platform) in uniseriate ray tissue to influence the radial permeability of Sitka spruce (Picea sitchensis (Bong.) Carr.) by examination of most (Queen Charlotte Islands in Rhondda, South Wales) and the least (South Oregon in Dalby, North-East England) seed origins that grown in ...
I Usta, M D C Hale
Preservative treatment of round bamboos by a new technique - Some further studies. Part 1
1990 - IRG/WP 3607
In general, the easy susceptibility of bamboos to wood destroying agencies is a major constraint in its rational utilisation. This is more so in tropical countries like India where wood destroying agencies are quite active. In an earlier publication, it was reported that round bamboo specimens of Bambusa balcooa, having three nodes, could be satisfactorily treated by CCA by a new technique develop...
V R Sonti, B Chatterjee
Micromorphological Characteristics of Degradation in Bamboo Attacked by White Rot Fungus Lentinus edodes
2006 - IRG/WP 06-10575
In comparison with micromorphological works for wood decay, little known is about the decay pattern of bamboos by wood decay fungi. The present work was undertaken to understand the general degradation pattern of bamboo and the influence of polylaminate layers in bamboo fiber walls on the restriction of fungal decay. The weight loss of bamboo species Phyllostachys puberscens against the white rot ...
Chang Hyun Cho, Kwang Ho Lee, Yoon Soo Kim
Copper borate for the protection of engineered wood products
2006 - IRG/WP 06-40334
Copper borate was evaluated for use in protecting oriented strand board (OSB) from mould, decay, and termites. Aspen OSB bonded with either phenolic or isocyanate resin was treated with several formulations of copper borate at various loadings from 0.26 to 4 percent by weight. These panels were then tested to determine the impact of the preservative on mechanical properties as well as resistance ...
R Smart, W Wall
Effect of fungal attack on maximum load capacity of simulated wall assemblies
2007 - IRG/WP 07-20363
The effects of moisture intrusion and fungal attack on the maximum load capacity of nailed assemblies was investigated using one white and one brown rot fungus against 4 material combinations over a 20 week period. Wetting significantly reduced the maximum load capacity of all four material combinations, while wetting and autoclaving only affected the OSB sheathing/spruce stud. The white rot fung...
N Melencion, J J Morrell
End Coating Masson Pine Grown in South China to Prevent the Development of Blue Stain
2007 - IRG/WP 07-30428
One end (randomly selected) of logs of mason pine (Pinus massoniana) were coated with a wax-type end coating called ANCHORSEAL® immediately after tree cutting. The logs were then stored in summer weather in Guangxi, China. During the storage, at week 1, 2, 3, 4, 6, 8 and 12, five logs of mason pine were sawn into lumber or veneer for the visual observation and measurement of blue stain at the coa...
Zhao Youke, Qin Li, Huang Rongfeng, Lu Jianxiong
Micro-Distribution of Metals in Wood Treated with a Nano-Copper Wood Preservative
2007 - IRG/WP 07-40360
The microdistribution of copper in southern pine treated with a newly-developed nano-copper wood preservative was examined to determine if it differed from that reported for wood treated with conventional copper-based wood preservatives. Field Emission Scanning Electron Microscopy (FE-SEM) in combination with x-ray microanalysis (EDX) revealed the presence of nano-sized copper and iron particles i...
H Matsunaga, M Kiguchi, P Evans
Micro-Distribution of Micronized Copper in Southern Pine
2008 - IRG/WP 08-30479
For copper-based preservatives to be used in ground contact, penetration of copper into the cell wall is believed to be important to protect the wood from soft rot fungi. Preservatives containing soluble copper are known to do this. It is not known whether preservatives containing particulate copper will also migrate into the cell wall in sufficient quantities to control soft rot decay. An AWPA st...
R Stirling, J Drummond, Jun Zhang, R J Ziobro
Performance of dip and pressure treated wood in termite ground proximity exposures in Hilo, HI, and Colombia
2008 - IRG/WP 08-30491
A number of preservative systems were evaluated for their ability to control termite attack when applied as both dip and pressure treatments. With dip treatments, better performance was observed with southern pine than spruce-pine-fir using the same solution strength treatment, probably as a result of the about 50% greater uptake with southern pine and associated deeper preservative penetration. B...
P Walcheski, A Zahora
Re-Distribution of Copper in the Cell Walls of Wood Treated with Micronized Copper Quat
2009 - IRG/WP 09-30506
Wood treated with copper-based preservatives to be used in ground contact may fail to inhibit soft rot fungi if penetration of copper into the cell wall is insufficient. Preservatives containing soluble copper are known to penetrate the cell wall; however, it is not known whether preservatives containing particulate copper will also migrate into the cell wall in sufficient quantities to control so...
R Stirling, J Drummond
Protection mechanisms of modified wood against decay by white and brown rot fungi
2010 - IRG/WP 10-10713
The resistance of beech and pine wood blocks treated with 1,3-dimethylol-4,5-dihydroxyethylene urea (DMDHEU) against T. versicolor and C. puteana increased with increasing WPG. Full protection (mass loss below 3%) was reached at WPGs of approximately 15% (beech) and 10% (pine). Metabolic activity of the fungi in the wood blocks was assessed as heat or energy production determined by isothermal mic...
C Mai, P Verma, Yanjun Xie, J Dyckmans, H Militz
Copper nanoparticles in southern pine wood treated with a micronised preservative: Can nanoparticles penetrate the cell walls of tracheids and ray parenchyma?
2010 - IRG/WP 10-30547
This study tests the hypothesis that copper nanoparticles can penetrate the cell walls of southern pine wood treated with a micronised preservative. We examined the nanodistribution of particles in tracheid and ray parenchyma cell walls using state-of-the-art HR (High Resolution)-TEM and HR-STEM (Scanning Transmission Electron Microscope)-EDX. These devices are capable of atomic-scale resolution. ...
H Matsunaga, Y Kataoka, M Kiguchi, P Evans
Chapter 11 - Preservation of talla bamboo
2007 - IRG/WP 07-10635-11
Researches revealed that the talla bamboo (Bambusa tulda Roxb.))
in Bangladesh could be full-cell pressure treated with CCA in green
and dry conditions. The dry bamboo gives higher loading
absorptions than green one when impregnated at same treating
conditions. Also higher absorptions are obtained at nodes rather
than internodes. Adequate penetration and retention results for
ground and wate...
A K Lahiry
Chapter 12 - Treatment Groups of Bamboo
2007 - IRG/WP 07-10635-12
Study on distribution of CCA in three major bamboo species in
Bangladesh, full-cell pressure treated at green and dry conditions
revealed two treatment groups and some treating principles. Higher
adequate treatment for ground and water contact use is only
possible by treating problematic bamboo species pre-kiln dried up to
half of its FSP and non-problematic species pre-dried up to FSP
(20% ...
A K Lahiry
Novel microscopic approaches to visualise chitosan within impregnated wood
2012 - IRG/WP 12-20485
Chitosan, a deacetylated product of an abundant naturally occurring biopolymer chitin, has been used in a range of applications, particularly in food and health areas, as an antimicrobial agent. In the work reported here Pinus radiata wood was impregnated with chitosan as an environmentally compatible organic biocide. It is important to understand micro-distribution of bioprotectants in impregnate...
A Singh, T Singh