Micronized Copper Preservative Systems: Observations on the Release of Cupric ion (Cu2+) from Treated Wood and Performance against Wood Decay Fungi
2009 - IRG/WP 09-30519
In an attempt to address the mechanism of action of micronized copper preservatives, a 20-week continuous water leaching study was conducted. The leaching results indicated that, once impregnated in wood, micronized copper preservatives continuously release cupric ion, and the levels of cupric ion released from micronized copper treated wood are higher than those released from CCA treated wood, a...
J Zhang, R Ziobro
Assessment of decay risk of airborne wood-decay fungi
2012 - IRG/WP 12-10787
The decay risk of airborne wood-decay fungi was investigated by using an air sampler. Japanese cedar disks measuring about 8 cm in diameter and 3 mm in thickness with moisture content at about 100 % were placed in a “BIOSAMP” air sampler and exposed to 1000 liters of air. Air sampling was carried out from June to September at the same sampling site in Tsukuba, Japan. The exposed disks were the...
I Momohara, Y Ota, K Sotome, T Nishimura
The resistance of thermo-oil modified wood against decay and mould fungi
2009 - IRG/WP 09-40448
Thermally modified wood in comparison to natural wood demonstrates some advantageous functional properties like decreased hygroscopicity, higher dimensional stability. It also has increased durability and improved resistance to fungal decay. However thermal modification of wood may lead to reduced strength properties what may limit the use of wood in mechanically beared constructions. The changes ...
A Fojutowski, A Kropacz, A Noskowiak
Use of wax emulsions for upgrading of wood properties
2009 - IRG/WP 09-40451
Waxes are used for treatment of wood surfaces for several decades, predominately as surface treatments, because they did not penetrate into the wood. In order to overcome this issue, water emulsions were applied in present experiment. Five water emulsions of various concentration was used namely; two emulsions of montan wax (LGE, MW1), emulsion of polyethylene (WE1), emulsion of ethylene copolymer...
B Lesar, F Pohleven, M Humar
Biological Performance of Boron-based Chemicals Treated Wood Composites
2009 - IRG/WP 09-40464
In this study, the biological performance of wood-based composites panels treated with boron containing chemicals against to a fungus was determined. Boric acid, borax, zinc borate and agricultural borate (Tarım-bor™), developed and patented by National Boron Research Institute, were mixed with wood chips or fibers and then particleboard, medium strand board and middle density fiberboar...
Ü C Yıldız, H Kalaycıoğlu, S Yıldız, A Temiz, E Tomak Dizman, A Çavdar Dönmez
Modelling hyphal growth of the bio-incising fungus Physisporinus vitreus
2010 - IRG/WP 10-10710
The white-rot fungus Physisporinus vitreus preferentially degrades the pit membranes of bordered pits in tracheids and subsequently enhances wood permeability. Thus, P. vitreus can be used to improve the uptake of wood preservatives and environmentally-benign wood modification substances. This process can be used to enhance the use and sustainability of native conifer wood species by the wood indu...
M Fuhr, C Stührk, F W M R Schwarze, M Schubert, H J Herrmann
The invasion channels of damage fungi in bamboo lumber
2010 - IRG/WP 10-10712
The micro-agents on bamboo lumber damage are mould, stain, and decay fungi. This research is about invasion channels of bamboo lumber damage fungi by scanning electron microscope (SEM). The results showed that the conidia of mould were only accumulated on the surface of bamboo and no hyphae detected in bamboo vascular bundle, and hyphae of stain penetrated into bamboo and grew in metaxylem vessel...
Xingxia Ma, Mingliang Jiang, Daochun Qin
Protection mechanisms of modified wood against decay by white and brown rot fungi
2010 - IRG/WP 10-10713
The resistance of beech and pine wood blocks treated with 1,3-dimethylol-4,5-dihydroxyethylene urea (DMDHEU) against T. versicolor and C. puteana increased with increasing WPG. Full protection (mass loss below 3%) was reached at WPGs of approximately 15% (beech) and 10% (pine). Metabolic activity of the fungi in the wood blocks was assessed as heat or energy production determined by isothermal mic...
C Mai, P Verma, Yanjun Xie, J Dyckmans, H Militz
Fungal Attack on Lignin and Cellulose: Elucidation of Brown- and White-Rot Mechanisms Comparing Biomimetic and In-Vivo Degradation Patterns
2010 - IRG/WP 10-10714
This paper examines research and hypotheses that have been developed over several years on wood degradation mechanisms. This information is combined with new data and analyses to explain why wood decay patterns caused by brown-rot fungi and specific types of white-rot fungi are different. New data, including work with both biomimetic studies on low molecular weight compounds, degradative enzymes, ...
V Arantes, B Goodell, A M F Milagres, Yuhui Qian, T Filley, J Jellison, S Kelley
Microscopy evaluation of microbial decay patterns in wood stakes after 6 years in soil contact
2010 - IRG/WP 10-10715
Most studies on wood modification have so far been concerned with service life predictions rather than investigating the decay protection mechanism. Very little is known about the mode of action of these new treatments and about the strategies used by wood degraders in order to utilize the wood material despite a treatment. Access to such knowledge would allow further modification and improvement ...
A Pilgård, C G Björdal
Influence of extractives on durability of Cupressus lusitanica heartwood
2010 - IRG/WP 10-10716
Identification of extractives present in Cupressus lusitanica heartwood has been conducted using GC-MS analyses. The chromatogram of toluene/ethanol extracts indicated the presence of high amounts of benzaldehyde and numerous of terpenic compounds such as cedrol, agathadiol, epimanool, bornyl acetate, -cedrene and -cedrene. Effect of extractives on cypress natural durability has be...
A Mohareb, P Sirmah, L Desharnais, S Dumarçay, M Pétrissans, P Gérardin
A genomic sequencing approach to study wood decay and copper tolerance in the brown rot fungus, Antrodia radiculosa
2010 - IRG/WP 10-10720
We used Illumina paired-end short read sequencing (76 nt, 300 bp insert size) to produce a de novo assembly of the genome of Antrodia radiculosa, a copper-tolerant brown rot fungus that is capable of aggressive wood decay. Quality analysis of the base calls in the dataset (8.95 Gb) showed that the majority of the nucleotide sequence was of the highest quality with 5% in the lowest quality group. ...
J D Tang, T Sonstegard, S Burgess, S V Diehl
Frequency of fungal decay in softwood windows in Germany
2010 - IRG/WP 10-10725
Knowing how often fungal decay occurs is a fundamental basis for general recommendations of preservative measures. To optimize the German recommendations for chemical wood preservation of windows made out of pine or spruce more than 2000 windows have been inspected. All windows had an opaque coating and were between 2 and 17 years old. The selection of the inspected windows was kept as randomly as...
D Lukowsky, O Moarcas, A Luette
Qualitative - Quantitative Analysis of Wood-Inhabiting Fungi in External Wooden Structures of the Latvian Cultural Heritage
2010 - IRG/WP 10-10728
The frequency and diversity of wood inhabiting fungi in the exterior wood were established in the Araishi lake fortress, the Lielvarde wooden castle, the Latvian Ethnographic Open-Air Museum, Riga, and twelve wooden heritage objects in the Eastern part of Latvia (Latgale). The inspected wooden structures of the external woodwork included windows, stairs, walls, floorings, roofs, fences, and benche...
I Irbe, M Karadelev, B Andersons
Chemical mediated depolymerization of cotton cellulose for the understanding of non-enzymatic fungal decay
2010 - IRG/WP 10-10731
Small, low molecular weight non-enzymatic compounds have been linked to the early stages of brown rot decay as the enzymes involved with holocellulose degradation are found to be too large to penetrate the S3 layer of intact wood cells. The most pronounced of these which were analyzed in this study are hydrogen peroxide, iron, and oxalic. The compounds related to the Fenton reaction: the combinati...
A C Steenkjær Hastrup, B Jensen, F Green III
Structural changes, basidiomycete richness, enzyme activity and proteomic profiling of decay resistant and non-resistant woods over 18 months in soil contact
2010 - IRG/WP 10-10733
Wood decay fungi damage wood by production of enzymes that attack the structural components. The objective of this study was to better understand which suite of decay genes and proteins are expressed during biodeterioration of three different wood types in forest soil over time. Variation in decay genes and proteins were determined for pine (non-resistant), cedar (naturally durable), and ACQ-treat...
Youngmin Kang, S Diehl, L Prewitt, D Nicholas
Towards Understanding the Biology of Wood Decay
2010 - IRG/WP 10-10739
Our previous research has focused primarily on ways to identify the wood decay fungi and microbial community. We continue to explore this complex and dynamic community and its interactions through microbial community ecology studies, gene expression interactions and proteomics. However, in order to better understand the mechanisms of fungal decay, we have sequenced the genome of a copper tolerant...
J Tang, K Jenkins, L Parker, S V Diehl
Decay Resistance of Maple (Acer Insigne) Wood Against White Rot
2010 - IRG/WP 10-10740
In this study, the decay resistance of maple (Acer insigne) in natural state and treated with ACC (Acid copper chromate) was investigated against the white rot fungus (Coriolus versicolor). ACC is a kind of water borne preservatives that was used in this study for treating specimens under vacuum and pressure (Bethell procedure) with 3 percent concentration. In conducting mentioned evaluation, koll...
V Tazakor Rezaei
The Relative Performance of an Organic Preservative System under UC3A and UC3B Conditions using Two Test Methods
2010 - IRG/WP 10-20429
Coated L-joints have been used for decades to evaluate the performance of wood preservatives in protected environments. This study was conducted using matched coated and uncoated L-joints to simulate above ground protected and unprotect exposures. When exposed to constant moisture in a greenhouse environment, coated and uncoated L-joints give very similar performance results. In contrast, exposi...
C F Schauwecker, A Zahora, A F Preston
Simulation and Investigation of Wood Degradation by Erosion Bacteria in Laboratory Experiments
2010 - IRG/WP 10-20431
A Microcosm experiment was successfully set up to establish, monitor and manipulate bacterial wood degradation under low oxygen conditions. Sound pine sticks were placed in waterlogged sediment from a heavily decayed pine pile foundation site in Amsterdam. The system was subject to different gassing treatment regimes in order to investigate the role of oxygen in the bacterial degradation process o...
J Gelbrich, E I Kretschmar, N Lamersdorf, H Militz
The Use of Micro-Tensile Testing to Assess Weathering Decay and Oxidative Degradation of Wooden Items
2010 - IRG/WP 10-20433
This paper presents a method to study the weathering performance of wooden items and to assess the oxidative degradation of wood via the Fenton reaction. Weathering resistance and photo-stability of wood was tested using pine wood (Pinus sylvestris) veneer strips measuring approximately 60 µm in thickness. The veneer strips were treated using a reactive chemical to impart surface protection. The ...
C Mai, Yanjun Xie, Zefang Xiao, P D Evans, H Militz
Stained wood: The identification of natural dyes and mordants in wooden works of art
2010 - IRG/WP 10-20434
On the basis of current knowledge only natural-colored wood species crafted to veneers were used for the decorative design of furniture and wooden interior in classical antiquity.First applications of artificially stained wood can be dated to the late Middle Ages. In the Renaissance wooden works of art were manufactured by using intarsia of natural-colored, fungus-stained and artificially stained ...
A Unger, W Unger
Service life prediction of wooden components – Part 1: Determination of dose-response functions for above ground decay
2010 - IRG/WP 10-20439
Scots pine sapwood (Pinus sylvestris L.) and Douglas fir heartwood (Pseudotsuga menziesii Franco) specimens were exposed in double layer field trials at 24 different European test sites under different exposure conditions (in total 28 test sets). The material climate in terms of wood moisture content (MC) and wood temperature was automatically recorded over a period of up to eight years and compar...
C Brischke, A O Rapp
Profiling fungal community in wood decay ecosystem by Denaturing High-Performance Liquid Chromatography
2010 - IRG/WP 10-20443
A DNA-based fingerprinting technique, Denaturing High Performance Liquid Chromatography (DHPLC) was developed to profile fungal communities colonizing indoor timber. Molecular fungal diversity was assessed using amplification based on the Internal Transcribed Spacer (ITS1) rDNA of 74 wood samples collected from infected buildings in France. Due to its high sensitivity, the PCR-DHPLC technique was ...
S Maurice, G Le Floch, M Le Bras-Quéré, J P Rioult, G Barbier
A Review on Conditions for Decay Initiation and Progression
2010 - IRG/WP 10-20444
This paper reviews the key publications available on service life prediction of exterior wood applications, critical conditions for decay initiation and progression, and the impact of decay on wood strength. While it is helpful to use climatic data to predict general trend of decay potential, more precise decay initiation and progression information is required by hygrothermal modeling for its dam...
Jieying Wang, P I Morris