Exposure of preservative treated wood to terrestrial microcosms, pure cultures of fungi and in the field
1997 - IRG/WP 97-20114
Small stakes (5x10x100 mm3) of treated and untreated Pinus sylvestris sapwood were exposed in terrestrial microcosms with different soils, two taken from test fields in Sweden, one soil from a conifer forest and one garden compost soil. Stakes of the same size were also exposed to pure cultures of the brown and white rot fungi, Postia placenta and Phanerochaete chrysosporium. After exposure, weigh...
M-L Edlund
On the possibilities of the use of juvenile hormone in wood protection
1976 - IRG/WP 363
The annual world-wide extent of losses caused by wood-destroying insects in timber in buildings and timberyards is very difficult to estimate. In general exact values are only known in cases of claims for damages from insurance companies or in litigation. At present the best known wood destroying insects in Switzerland are the house longhorn beetle (Hylotrupes bajulus) and the common furniture bee...
P Tscholl
Co-operative research project on L-joint testing. Sampling after 4 years exposure
1987 - IRG/WP 2274
In September 1983, Document No: IRG/WP/2208 was distributed giving guidance on sampling after 8 months exposure and including tables on which to record the test results. Similarly in September 1984, Document No: IRG/WP/2233 was distributed concerning sampling after 18 months exposure. No major problems have been notified to Princes Risborough Laboratory concerning the sampling method. It is theref...
J K Carey, A F Bravery
Field test of wood preservatives with Nasutitermes rippertii RAMBUR in Cuba
1996 - IRG/WP 96-10181
A field test of wood preservatives was carried out with Nasutitermes rippertii RAMBUR in the vicinity of the Material Testing Centre „Alexander von Humboldt" in Santiago de las Vegas/ Havana (Cuba) for 12 and 24 months. Test specimens of Pinus sylvestris L., Picea abies (L.) Karst. and Fagus sylvatica L. with dimensions of 25 x 25 x 490 mm³ were arranged vertically or horizontally in a circle o...
W Unger
Wood preservation research in Tanzania: Priorities and challenges
1988 - IRG/WP 3462
Tanzania provides some of the highest rates of wood deterioration in service leading to alarming economic losses and yet no serious concern is shown in search for solutions to the problem. The paper attempts to point out some of the priority areas in the field of wood preservation research that demand urgent attention if timber is to be used judiciously in this country. An account is given of the ...
K K Murira, R Cockcroft
Treatment groups and remedies for CCA treated hardwood and softwood poles
1999 - IRG/WP 99-40142
Different hardwood and softwood species from Bangladesh and Bhutan was investigated regarding density, green fiber stress, natural durability of heartwood and CCA treated sapwood, CCA treatability grades, sapwood thickness, and kiln-drying properties for long term use as electric poles. These properties along with the past service records for nineteen years, separated ten heardwood and five softwo...
A K Lahiry
Long-term preservation technology for a large-scale timber structure building in Japan
2001 - IRG/WP 01-40203
Several 1.000-year-old Buddhist temples and shrines built of wood are surviving in Nara, some areas of which are inscribed on the World Heritage List. These old buildings are indicative of excellent timber construction technology having existed in ancient Japan, though it is thought that such technology has not been handed down. This paper introduces one of large-scale wood buildings built in rece...
Y Iimura
Information from the COIPM wood group. (With Appendix: Préserver les matériaux en milieu marin sauvegarder l'environment marin telles sont la vocation et la mission du C.O.I.P.M.)
1989 - IRG/WP 4156
During the last COIPM Meeting, up to date information on cooperative work to test the resistance of plastic wrapping for pilings were submitted and discussed. In 1986 untreated wood samples wrapped with shrinkable polyolefin sleeves were submerged in 9 stations, situated in temperate and tropical waters. After 1 or 2 years of immersion the samples showed no sign of penetration by marine borers and...
A Gambetta
Screening of fungal strains for wood extractive degradation
1998 - IRG/WP 98-10254
Fungal strains were screened for their ability to degrade apolar extractives in wood from scots pine. The degradation of total wood extractives by 91 different strains was monitored in stationary batch assays incubated for 6 weeks. The results obtained show that the ability of wood-inhabiting fungi to utilize wood extractives varied greatly, even for different isolates of the same species. Fungal ...
J Dorado, M J Martinez-Inigo, T A van Beek, F W Claassen, J B P A Wijnberg, R Sierra-Alvarez
Screening of the technical performance and aquatic toxicity of N-methylolacrylamide treated wood
2000 - IRG/WP 00-40166
In the course of the last decades chemical modification of wood species, with a limited natural durability, has been subjected to intensive research. As a possible alternative and supplementary treatment of non-durable wood in a range of applications it remains one of the major topics in the wood preservation world. Different modification systems have been scaled-up and are now in an industrialisi...
V Rijckaert, S De Geyter, J Van Acker, M Stevens
A technique for measuring preservative loss or redistribution during leaching
1983 - IRG/WP 2199
Radiata pine sapwood stakes were treated with benzalkonium chloride (AAC) or copper-chrome-arsenate (CCA). After fixation and drying the outer 2 mm and 2-4 mm layers were removed from one radial longitudinal face. The planed face was coated with a waterproof coating and AAC-treated stakes were leached for 6, 12 or 18 weeks; 12 weeks for the CCA-treated stakes. After airdrying three 2 mm layers (0-...
J A Drysdale
Characteristics of thermally modified wood in vacuum
2004 - IRG/WP 04-40287
In commercial thermal wood modification processes nitrogen, steam or oil has been used for the reduction of oxygen content in the reactor atmosphere. In present study no special heating medium, but an initial vacuuming step has been used for this purpose. Mass loss, resistance to fungal decay, dimensional stability, bending strength and modulus of elasticity of heat treated wood were evaluated and...
G Rep, F Pohleven, B Bucar
Testing blue stain fungicides for joinery timber in combination with natural weathering
1976 - IRG/WP 268
Joinery timber in outside use becomes affected by blue-stain after a short time of exposure. This is especially the case with pine sapwood treated with unpigmented lacquer, but also with other timber species as well as different types of surface treatment. According to the basic investigations of BUTIN this is due to special types of blue-stain fungi, called "Lack-bläue" (lacquer blue-stain), in ...
H Willeitner
Preliminary investigation on the natural durability of Guayule (Parthenium argentatum)-based wood products
2000 - IRG/WP 00-40154
Conventional preservatives used to protect wood from insect and microbial damages are presently of major concern to human health and the environment. Finding alternative and economical preservatives has not been successful. Previous studies have shown that the resinous material extracted from the guayule plant (Parthenium argentatum, Gray) has both insect- and microbial-resistant properties. Unfor...
F S Nakayama, P Chow, D S Bajwa, J A Youngquist, J H Muehl, A M Krzysik
Soft-rot testing. Memo to CEN
1983 - IRG/WP 2206 A
1. Development of a single test procedure to assess performance of preservatives against soft rot fungi is an ideal that cannot be realised at present, if results are to be both reproducible between laboratories and pertinent to the practical requirements of individual countries.
2. Consensus opinion amongst members of Sub Group I - Soft rot tests, of Working Group II - Fundamentals of Testing, of the IRG, is that the immediate needs of CEN would be best answered by: (a) a code of recommended practice, (b) a multiplicity of test procedures, and (c) a degree of flexibility in test procedures.
3. The code of recommended practice should recognise the need for: (a) a pure culture, synthetic medium (sand or vermiculite + nutrients), single wood species test to be adopted by all laboratories as a common reference point of testing, (b) mixed inoculum and/or unsterile soil laboratory or fungus cellar tests which account for local variations in the fungal flora, (c) incorporation of a range of wood species where applicable (i.e. where mixed hardwoods comprise the main resource), (d) provision of local internal standards of known performance under field conditions, (e) incorporation of leaching procedures other than standard methods with deionized water (e.g. mild acid, milk alkali, ionic solutions of various salts) where applicable to local exposure conditions, (f) precise definition of the criteria used for establishing toxic thresholds (mass loss, strength loss, microscopic examination).
4. Initial screening tests should remain the province of the individual research worker.
5. The code of recommended practice should have the sole purpose of establishing provisional retention levels for subsequent confirmation by field trial.
6. IRG should list and approve test procedures considered adequate to establish toxic thresholds for preservatives against soft rot fungi.
7. It should be clearly understood that when using a series of test techniques, it is inevitable that a range of toxic thresholds will be obtained for the same preservative.
8. Guidelines should be drawn up for interpretation of test data for subsequent transformation to provisional retention levels.
9. Adoption of the broad principles outlines above is recognition of the dynamic nature of toxic thresholds. The additional information obtained by a more flexible, and complex, approach to testing may make interpretation more difficult but should provide data from which response of preservatives to varying biological and environmental hazards can be more realistically assessed.
10. It is recommended that CEN adopt, in principle, the basic philosophy of testing outlined above and move towards formulation of a Working Document in collaboration with IRG
J A Butcher, D J Dickinson
The ground proximity decay test method
2000 - IRG/WP 00-20205
A decay field test method, which has been recently proposed for the standardization by the AWPA, is described for evaluating the relative performance of wood samples in a severe above ground situation exposed to the weather. Data is presented on the relative performance of untreated control samples and standard preservative systems exposed at the same site at different time periods, or at differen...
A F Preston, P J Walcheski, K J Archer, A R Zahora, L Jin
Durability of Sugi (Cryptomeria japonica D.DoN ) wood treated in high temperature liquid paraffin
2002 - IRG/WP 02-40221
Sugi(Cryptomeria japonica D.DoN )wood was subject to a heat treatment in high-temperature liquid paraffin for the purpose of improving the resistance against fungi and termites without chemicals. The bath of paraffin liquid, which can provide a uniform heat transfer (±2?), was used at temperatures of 90?,120?and 150?.?ecay resistance according to JIS K 15711) was evaluated using a brown rot fungu...
Y Matsuoka, W Ohmura, S Fujiwara, Y Kanagawa
An analysis of the effects of some factors on the natural durability of pine (Pinus sylvestris L.) and spruce (Picea abies Karst.)
1986 - IRG/WP 1279
The effects of some factors on the natural resistance of pine and spruce sapwood against fungal decay and against attack of house-longhorn beetle larvae have been studied in laboratory tests and the results are evaluated by analysis of variance and regression analysis. Following conclusions were reached: Wood from summer-felled trees did not have a lower inherent natural durability against fungal ...
J B Boutelje, T Nilsson, S Rasmussen
Permeability measurements on surface layers for detecting wood with abnormally high permeability
1988 - IRG/WP 2298
Wet storage of timber during the warm period of the year may lead to an increased permeability of the wood, an undesirable phenomenon for several wood industries and also for many end-uses. Neither before nor after drying, such wood with "wet storage damage" can be visually distinguished from wood with a normal permeability. A non-destructive method for inspecting the permeability of surface layer...
J B Boutelje, G Hägglund
Glue-line additives for protecting plywood. A review
1978 - IRG/WP 2102
The conclusions of this review are: 1) Insecticidal glue-line additives can be used satisfactorily to protect plywood against insect attack. 2) It is uncertain, in spite of some claims, wether fungicidal glue-line additives can be similarly used to protect plywood against fungi under damp conditiones. There is a need for further work to validate the mycological tests that may be used to investigat...
R Cockcroft
Durability of some alternatives to preservative treated wood
2004 - IRG/WP 04-30353
The environmental discussion in Sweden has lead to an increasing use of naturally durable domestic wood species and wood treated according to alternative methods for use above ground. A number of these alternatives have been tested according to field- and laboratory tests and compared to wood treated with preservatives for above ground use. Seven untreated wood species, four alternative wood treat...
M-L Edlund
A field study on the suitability of the European lap-joint test
2001 - IRG/WP 01-20239
Within the framework of the European SM&T Research Project "Co-normative research on field tests for wood preservatives out of ground contact in conjunction with methods for preconditioning test specimens prior to test" (FACT) one aim was to establish the suitability of the European lap-joint test (as it is described in ENV 12037:1996) to assess wood preservatives in the field in EHC 3. Scots ...
M Grinda, Ö Bergman, H-V Borck, D Dickinson, P Esser, R Gründlinger, H Leithoff, S Molnar, L Paajanen, N Pfabigan, E D Suttie, F Thomassin, T Nilsson, J Van Acker, M Van Der Zee, A Voss
Life Cycle Assessment of borate treated wood
2005 - IRG/WP 05-50224-12
Life Cycle Assessment (LCA) is being used increasingly around the world by decision-makers to help incorporate the environmental component of sustainability into their activities. U.S. Borax regularly assesses how its products contribute to sustainable development. Using data gleaned from LCA of its products, the company recently completed its first ISO 14040 compliant cradle-to-grave LCA of lum...
M J Manning
Present status of using treated wood and private house owner’s expectations in Bangladesh
2004 - IRG/WP 04-30329
In a developing country like Bangladesh more than 80 % of the total population lives in rural areas where building materials are mainly comprised of wood, bamboo, thatch grass, golpata, etc. All these materials, being cellulosic, are easily infected by deteriorating agencies like fungi, termites, beetles etc., as climatic condition of the country is ideal for their thrive. This is a great wastage ...
M A Islam, A K M A Bosunia, S C Ghosh, M O Hannan, A K Lahiry
A 53-year old field trial to evaluate the performance of a range of chemical treatments on eucalypt poles
1989 - IRG/WP 3526
Hardwood pole stubs of Eucalyptus maculata, Eucalyptus pilularis, Eucalyptus saligna and Eucalyptus paniculata were examined for termite attack and fungal decay after 53 years in ground contact. The trial compared eight different chemical treatments with untreated pole stubs of the four species investigated. Untreated Eucalyptus paniculata, a Class I durability species, performed particularly well...
R S Johnstone, R A Eaton