The Use of Modulus of Elasticity and Modulus of Rupture to Assess Wood Decay in Laboratory Soil-Bed Test
2006 - IRG/WP 06-20338
The efficacy of wood preservatives were determined in a soil-bed test. Samples of alder wood sapwood (Alnus glutinosa subsp. barbata) (5x10x100 mm) were treated with Solutions of CCA (1 % and 2 %), ACQ-1900 (2 % and 3 %), ACQ-2200 (1 % and 2 %), Tanalith E 3491 (2 % and 2.8 %), Wolmanit CX-8 (% 1 and 2 %). Modulus of Elasticity, modulus of rupture, mass loss and decay rate according to AWPA E7 wer...
A Temiz, Ü C Yildiz
Measuring Soil Respiration as a New Approach to Describe the Interaction Between Wood (Treated and Untreated) and Microbiologically Active Soil
2006 - IRG/WP 06-20344
Soil respirometry was employed to examine the relationship between both the performance of copper organic preservatives in contact with and the amount of carbon dioxide evolved from soil and the effect of wood treated with preservatives on carbon turnover in soil. Wood was treated with a range of copper organic preservatives intended for use in ground contact as well as an organic preservative in...
I Stephan, W Mierke
Qualitative and quantitative assessment of chemicals used for wood durability improvement by Near Infrared Spectroscopy
2006 - IRG/WP 06-20349
The Near infrared spectroscopy (NIRS) could be a suitable technique to assess chemicals used for wood durability improvement in the forest products industry. NIRS methodology can be used to obtain results more quickly, less costly and without damaging the wood. In this study, wood samples selected from heartwood and sapwood of Maritime Pine (Pinus pinaster) were prepared to assess the artificial d...
S Zahri, F Charrier, H Baillères, B Charrier
Addition of boron compounds and octanoic acid for improvement of biocidal properties and copper fixation at copper-ethanolamine based wood preservatives
2006 - IRG/WP 06-30408
Copper-ethanolamine based wood preservatives became important active substance (formulation) for wood protection, novelty. As copper itself can not ensure sufficient protection against wood destroying organisms and fixation in wood we combine it with other biocides like ethanolamine, boron and octanoic acid. This investigates were performance on spruce wood impregnated with different combination o...
F Pohleven, M Humar
Copper borate for the protection of engineered wood products
2006 - IRG/WP 06-40334
Copper borate was evaluated for use in protecting oriented strand board (OSB) from mould, decay, and termites. Aspen OSB bonded with either phenolic or isocyanate resin was treated with several formulations of copper borate at various loadings from 0.26 to 4 percent by weight. These panels were then tested to determine the impact of the preservative on mechanical properties as well as resistance ...
R Smart, W Wall
The Effect of Wick Action upon Moisture Distribution in Ellagate Treated Pinus radiata Wood
2006 - IRG/WP 06-40328
Sapwood stakes of Pinus radiata D. Don were treated with water-soluble tetraguanidinium, tetracholine and tetrakis-benzyltrimethylammonium ellagates. The effect of these treatments upon moisture distribution was investigated by wick action. Given that chemical reactions within the wood substrate between nutrients and treatment solutions may alter the properties of the wood with regard to moistur...
S R Przewloka, B J Shearer, J A Hann
Corrosion of metal fasteners in contact with copper preservative treated wood
2007 - IRG/WP 07-20370
The corrosion rates of metal fasteners in contact with alkaline copper quat (ACQ) treated wood with or without commercially available water repellent was compared to that of cedar. In this experiment, fasteners were sandwiched between two pieces of treated wood and exposed to a humid environment at a slightly elevated temperature. The use of a “sandwich” design allowed periodic examination of ...
BaekYong Choi, J N R Ruddick
Influence of ethanolamine on lignin depolymerization and copper leaching from treated Norway spruce and beech wood
2007 - IRG/WP 07-30423
Copper-ethanolamine based wood preservatives are replacing several classical copper-chromium based solutions, due to foreseen ban of chromium. Fixation of copper-ethanolamine based wood preservatives is not as good as fixation of copper-chromium ones. The main object of this manuscript was to prove, that ethanolamine is the prime reason for insufficient fixation of copper-ethanolamine formulations...
M Humar, B Bucar, M Zupancic, D Žlindra, F Pohleven
Micro-Distribution of Metals in Wood Treated with a Nano-Copper Wood Preservative
2007 - IRG/WP 07-40360
The microdistribution of copper in southern pine treated with a newly-developed nano-copper wood preservative was examined to determine if it differed from that reported for wood treated with conventional copper-based wood preservatives. Field Emission Scanning Electron Microscopy (FE-SEM) in combination with x-ray microanalysis (EDX) revealed the presence of nano-sized copper and iron particles i...
H Matsunaga, M Kiguchi, P Evans
Effects of sodium hypochlorite on compression strength and copper retention of spruce wood treated with copper azole and alkaline copper quat
2007 - IRG/WP 07-40362
This work investigates the effects of sodium hypochlorite on compression strength values and copper retention ratios of refractory spruce wood (Picea oriental L.) treated with the waterborne preservative Copper Azole, (CBA-A, Tanalith-E 3492) and alkaline copper quat (ACQ-2200). Before the copper azole and alkaline copper quat treatment, the samples were immersed in 500 ml of sodium hypochlorite s...
S Yildiz, E Dizman, A Temiz, Ü C Yildiz
Refinement of emission values for preserved wood in the ‘Storage Scenario’, for use in the environmental risk assessment of Wood Preservatives under the Biocidal Products Directive
2007 - IRG/WP 07-50244
The evaluation of an active substance or a biocidal product under the Biocidal Products Directive (BPD) requires that an environmental risk assessment is carried out. The risk assessment for wood preservatives includes a scenario for the treated wood in storage after treatment, in which the predicted environmental concentration (PEC) in soil, surface water and groundwater is calculated, using emis...
E F Baines
The effect of additives on copper losses from alkaline copper treated wood
2007 - IRG/WP 07-50246
The replacement of chromated copper arsenate (CCA) by alkaline copper compounds has heightened awareness of the potential impact of copper losses on aquatic organisms. While there remains a healthy debate concerning the actual risk of copper leaching from wood preservatives into aquatic ecosystems, it is clear that reducing these losses will be necessary to avoid continued regulatory actions aga...
J Mitsuhashi, J J Morrell, L Jin, A F Preston
Evaluating the Process of ACQ-Treated Woods with TGAand CEM Analysis
2007 - IRG/WP 07-20374
To provide an understanding of the fundamental thermal behaviour and the disposal-end products of ACQ-treated woods, this study is comprised of two categories of examination. The first is related to the use of TGA under different thermal decomposition conditions (nitrogen or air, and 5 or 40 oC/min), and the use of EDX to examine certain residual elements of the char. The second applies the CEM ...
Han Chien Lin, Tsang-Chyi Shiah, Jung Ting Tsai
Influence of Polyvinyl acetate emulsion (PVA) on boron leaching and fungicidal properties
2008 - IRG/WP 08-30451
Boron compounds are very effective fungicides, but unfortunately they leach from wood. In order to improve boron fixation, boric acid, borax were combined with polyvinyl acetate emulsion (PVA). For comparison copper salts were included into this research as well. Selected preservative solutions were chosen for impregnation of Norway spruce wood specimens (Picea abies). Wood blocks were exposed to ...
M Humar, B Lesar, P Kralj
Preliminary evaluation of efficacy of copper in combination with boron and NHA (N'-N-(1, 8-naphthalyl) hydroxylamine) against wood decay
2008 - IRG/WP 08-30452
In this study, efficacy of various combinations of copper sulfate with either boric acid or calcium precipitating agent, NHA-Na (N'-N-(1, 8-naphthalyl) hydroxylamine) was evaluated. Wood specimens were treated with either 1%, 0.5%, or 0.1% concentrations of copper sulfate, boric acid, NHA-Na, copper sulfate + boric acid, or copper sulfate + NHA-Na mixtures. Treated specimens were subjecte...
E Terzi, C Köse, S N Kartal
Formation and Structure of Metal Azole Complexes
2008 - IRG/WP 08-30469
Divalent copper and zinc complexes with metal:azole ratio 1:2 were readily formed at room temperature with the fungicides tebuconazole and propiconazole. The structure of copper and zinc tebuconazole acetate and zinc cis-propiconazole chloride were examined by X-ray crystallography. In copper tebuconazole acetate, the copper atom lies on a crystallographic inversion centre and is coordinated to tw...
P D Evans, K J Schmalzl, C M Forsyth, G D Fallon, S Schmid, B Bendixen, S Heimdal
Effects of Murgul Copper Process flue gases (SO2) on compression strength parallel to the grain of Beech (Fagus orientalis Lipsky.) wood
2008 - IRG/WP 08-40404
In this study was investigated the effect on the compression strength parallel to the grain as mechanical properties of Fagus orientalis Lipsky. wood exposed to SO2 gas and non-exposed.
In the experiments the two of four (total) were obtained from Artvin-Ortaköy region and the other two from Artvin-Murgul region. The compression strength parallel to the grain was calculated at the compare of ...
N Ay, E Topaloglu, A Uncu
Effects of acetic acid and nitric acid pre-treatment on copper content of spruce wood treated with CBA-A and CCA
2008 - IRG/WP 08-40406
This work investigates the effects of nitric acid and acetic acid on compression strength values and copper retention contents of refractory spruce wood (Picea oriental L.) treated with the waterborne preservative Copper azole, (CBA-A, Tanalith-E 3492) and copper / chrom / arsenic (CCA). Before the CBA-A and CCA treatment, the samples were immersed in 500 ml of nitric and acetic acid solutions for...
S Yildiz, E Dizman, Ü C Yildiz
Thermochemical Remediation of Preservative-Treated Wood
2008 - IRG/WP 08-50254
Remediation methods continue to be developed and refined for CCA-treated wood in order to divert this material from landfills and create secondary products from the wood fiber. A two-step thermochemical remediation method was developed to assess the efficiency of metal removal from CCA-treated spruce flakes. Nearly all the metals (As, Cr, and Cu) were thermochemically extracted from chromated copp...
R Sabo, C A Clausen, J E Winandy
Leachability of Arsenic, Chromium and Copper from Weathered Treated Wood
2008 - IRG/WP 08-50255
The objective of this study was to quantify the loss of arsenic, chromium and copper from weathered treated wood under normal field conditions as most residential structures currently in service in the U.S. have been constructed at least 3 years ago. For comparison, leaching from different retention levels of weathered CCA treated wood (low, medium and high) is compared to leaching from new ACQ tr...
A R Hasan, Ligang Hu, H M Solo-Gabriele, Yong Cai, L A Fieber
Emission Rates of Active Substances from Preserved Wood in Use Class 3
2008 - IRG/WP 08-50256
The evaluation of an active substance or a biocidal product under the Biocidal Products Directive (BPD) requires that an environmental risk assessment is carried out. The risk assessment for wood preservatives includes scenarios for preserved wood (e.g. cladding on a house), in which the
predicted environmental concentration (PEC) in soil is calculated, using an emission rate for the active subs...
E F Baines
Biological Performance of micronized copper wood preservative formulations in field and laboratory tests
2008 - IRG/WP 08-30488
Micronized Copper wood preservative formulations with different co-biocides were exposed to brown rot fungi in an 8-week AWPA E10 soil block decay test and two AWPA E7 ground-contact decay tests in Hawaii. The micronized copper formulations performed well against decay at or above the AWPA UC3 and UC4 retentions stipulated by the ICC-ES. Micronized copper preservatives performed comparably to a ...
G M Larkin, J Zhang, D L Richter, R J Ziobro, P E Laks
Laboratory Studies on Copper Availability in Wood Treated with Soluble Amine Copper and Micronized Copper Systems
2008 - IRG/WP 08-30489
A laboratory method has been employed to investigate the level of soluble copper in wood treated with various copper-based preservative systems, such as micronized copper (particulate copper) and amine copper solutions. This report describes the methodology and preliminary results on determination of the soluble copper in the treating solutions and the treated wood by these systems, as well as th...
L Jin, P Walcheski, A Preston
Alkaline copper treated wood for use in residential decking
2008 - IRG/WP 08-30490
Alkaline copper quaternary ammonium compound (ACQ) treated decking was exposed in a field experiment and the mobile copper assessed based on that collected in the leachate. The amount of copper which leached was modeled after 4 years. The results showed that boards which leached most chemical initially provided the greatest loss over four years. The reduction in the mobility of copper with time wa...
J N R Ruddick
Corrosion of fastener and connector in contact with alkaline copper treated wood – it is a problem
2008 - IRG/WP 08-40437
For many decades, chromated copper arsenate (CCA) was the most common wood preservative used in North America for residential and industrial applications. Since December 31, 2003, the use of CCA for residential application was voluntarily terminated. One of the most widely accepted alternative wood preservatives in Western Canada is Alkaline Copper Quaternary Compound (ACQ). This paper will compar...
J N R Ruddick