Use of the Pilodyn to assess deterioration of treated aspen waferboard after 30 months of outdoor exposure
1986 - IRG/WP 2254
Samples of preservative treated aspen waferboard exposed outdoors for 30 mo. were compared using pin penetrations of the 6 Joule Pilodyn. These results correlated well with rankings of treatment performance based on more laborious standard mechanical tests, and demonstrate the potential for use of the Pilodyn as a tool to evaluate wood composites in test exposures with minimal destruction....
E L Schmidt, M G Dietz
Fixation of CCA in Pinus sylvestris after kiln-drying
1990 - IRG/WP 3594
Tanalith C Paste is 98% fixed and Tanalith Oxide C is 99% fixed irrespective of whether treated Pinus sylvestris is kiln or air dried. A schedule suitable for kiln drying of CCA treated Pinus sylvestris is described....
P Warburton, J A Cornfield, D A Lewis, D G Anderson
Decay patterns observed in butylene oxide modified ponderosa pine after exposure in unsterile soil
1982 - IRG/WP 3211
Small blocks of ponderosa pine (Pinus ponderosa Laws) chemically modified with butylene oxide to three different weight gains were exposed for 6 weeks in unsterile soil. Severe surface decay caused by soft rot fungi and tunnelling bacteria was observed in blocks with 8 weight percent gain. The soft rot attack was restricted to the outer parts of the radial walls in the latewood tracheids. Bacteria...
T Nilsson, R M Rowell
Water-borne preservative marine trials in Western Canada
1981 - IRG/WP 470
Red pine boards treated with chromated copper arsenate, ammoniacal copper arsenate, copper zinc arsenic additive, a modified ammoniacal copper arsenate, and zinc arsenic additive, have been installed in a marine field test at West Vancouver, British Columbia. After two and a quarter years exposure, all the test samples are in excellent condition with the exception of those treated with the zinc ar...
J N R Ruddick
Disposal of CCA treated waste wood by combustion - An industrial scale trial
1996 - IRG/WP 96-50068
Totally 272 m³ (62.7 t) of CCA treated utility poles were chipped and incinerated at Jalasjärvi Gasification Plant. In average the whole batch of chips contained 57 kg of elementary copper, 95 kg chromium and 76 kg arsenic. During the 56 h combustion trial the measured arsenic emission to the air was 76 g in total. Copper and chromium emission was less than 1 g. The condensing water from the coo...
A J Nurmi
The effect of steam conditioning on Southern yellow pine treated with copper naphthenate
1997 - IRG/WP 97-40086
The current study was undertaken to investigate the influence of steam conditioning on Southern yellow pine treated with copper naphthenate (Cu-N). Pre-steamed and /or kiln-dried Southern yellow pine were pressure treated with Cu-N. After treatment, one group of samples were post-steamed. It was found that samples changed color from green to dark-brown after post-steaming. To elucidate the effect ...
Jun Zhang, D P Kamdem, M H Freeman, R D Arsenault
Recycling of impregnated timber: Part 2: Combustion trial
1999 - IRG/WP 99-50132
Totally 270 m3 (61,3 t) of CCA impregnated wood was chipped and incinerated at the combustion plant of Jalasjärvi. After the normal gas cleaning venture scrubbers were tested. After the trial a metal balance was calculated. Ash was treated at the copper smelter of Outokumpu Harjavalta Metals Oy. Condensate waters were transfered to the Outokumpu's CCA production plant and utilized by the...
L Lindroos
Contribution of wood components on the absorption of copper amine
2000 - IRG/WP 00-30216
The contribution of wood components on the absorption of copper amine was investigated. Holocellulose, lignin and xylan absorbed significant amount of copper. The amount of copper absorbed by cellulose was almost negligible. The removal of extractive also decreased the amount of copper absorption. This study clearly indicates the importance of lignin, hemicellulose in the absorption of copper amin...
D P Kamdem, Jun Zhang
Copper based water-borne preservatives: The use of a thin section technique to compare the protection of wood by copper based preservatives against soft-rot and bacterial decay
1987 - IRG/WP 2286
This paper describes the techniques developed and gives examples of results obtained for the performance of copper based wood preservatives against both the bacterial and fungal hazards....
A M Wyles, D J Dickinson
The Effect of Heat on the Retention of Ammoniacal Copper Quat (ACQ-AB) onto Scots Pine (Pinus Sylvestris L.) Wood
2008 - IRG/WP 08-40390
In this study, the sapwood of Scots pine (Pinus sylvestris L.) were treated with ammonical copper quat type (ACQ-AB), which is one of the environmentally friendly wood preservatives, by using soaking method as a functions of various temperatures and time. The results indicated that the retention behaviour of ACQ onto the wood was considerably affected by temperature of ACQ solution and treatment t...
M Hakki Alma, A Mukremin Kara
Water-borne wood preservatives against marine borers. Results from NWPC marine trials started in 1972 and 1976
1990 - IRG/WP 4162
The paper presents the results from NWPC (Nordic Wood Preservation Council) marine trials started in 1972 and 1976. The trials are carried out according to the NWPC Standard No. 1.4.2.2./73 "Marine test - a test against marine wood boring organisms in sea water". The test site is Kristineberg Marine Biology Station on the west coast of Sweden. The wood blocks used in the trials were made from sapw...
Ö Bergman, C Lundberg
Marine performance of preservative treated Southern pine panels. Part 2: Exposure at Mourilyan Harbour, Queensland, Australia
2000 - IRG/WP 00-10337
Southern yellow pine panels treated with ACQ type B, ACQ type A, CCA type C, creosote, and copper naphthenate have been exposed at Mourilyan Harbour, north Queensland, Australia for almost 6 years. These panels have been inspected and rated for fouling and attack by Teredinid, Limnoria, Martesia, and Sphaeroma during this exposure. After 70 months exposure, overall performance of ACQ type B was eq...
A R Zahora, A F Preston, K J Archer, S Kleinschmidt
Preservative performance of copper naphthenate (SANPRESER-OGR) in brush treatment of timber
1991 - IRG/WP 3663
Preservative efficacy of copper naphthenate (SANPRESER-OGR) was evaluated in the laboartory and field trials when timber was treated by brushing. Results of field trial indicated that service life of the brush-treated timber could be approximately 10 years or longer under ground contact conditions, although life span was slightly varied with timber species and test sites. After four years&apos...
Y Sugai, K Hamada, M Kitada, K Tomoi
Leaching of copper, chromium and arsenic from CCA-treated slash pine heartwood
1994 - IRG/WP 94-50020
Drying green slash pine with any of three high temperature drying schedules produced a product in which both the sapwood and the heartwood could be penetrated with CCA using a modified Bethell treatment schedule. Required H3 retentions were achieved in both sapwood and heartwood, from 200 litres per m³ charge uptake. Post-treatment fixation/drying was accomplished by three different regimes, incl...
M J Kennedy, G Palmer
The Effect of Soil pH on the pH of Treated Southern Pine in Ground Contact after 12 Months
2011 - IRG/WP 11-50281
Southern pine samples treated with soluble and particulate copper solutions were subjected to three soils that had been amended to provide acidic, neutral and alkaline conditions. Wood pH was measured prior to, and after 6 and 12 months after being placed in the soil to determine the effect of soil pH on wood pH....
L Jin, C Schauwecker, C Vidrine, P Walcheski, A Preston
In-ground evaluation of a copper azole wood preservative (Tanalithâ E) at a tropical Australian test site
1996 - IRG/WP 96-30100
A field trial to determine the in-ground termite and decay resistance of Pinus radiata D. Don impregnated with a copper azole formulation, TANALITHâ E, has been established at a tropical site in the Northern Territory of Australia. Four retentions of TANALITHâ E, containing 1.54, 2.08, 2.92 and 4.30 kg/m³ of Cu, are being evaluated. For comparison, Pinus radiata specimens treated to two retenti...
J W Creffield, J A Drysdale, N Chew
Copper-resistant fungi on pressure impregnated wood in Denmark
1994 - IRG/WP 94-10078
The occurence of Amorphotheca resinae Parbery and its asexual stage Cladosporium resinae (Lindau) de Vries on CCA and CCB treated wood has previously been shown. In the autumn 1993 some other blue stain fungi were found on CCP and CCB treated pine timber, such as Ophiostoma minus (Hedgc.) H. and P. Sydow, Ophiostoma pilifera (Fr.) H. and P. Sydow and Ophiostona piceae (Munch) H. and P. Sydow. The ...
J Bech-Andersen, S A Elborne
Leaching of CCA components from treated wood under acidic conditions
1993 - IRG/WP 93-50004
The leaching of CCA components from treated wood under acidic conditions were investigated. Western hemlock treated with three types of CCA and two levels of target retention was subjected to leaching at four different levels of pH. After leaching tests, leached samples were subjected to laboratory decay and soft rot tests. The amount of CCA components leached was dependent on acidity of leaching ...
Jae-Jin Kim, Gyu-Hyeok Kim
The course of fixation of Cu-Cr-As wood preservatives
1972 - IRG/WP 307
Copper-chrome-arsenic (CCA) preservatives in contact with wood result in an instant extensive increase of pH, because of ion-exchange and adsorption reactions with the wood. During precipitation of the active elements the pH continuously increases but reaches a maximum, when all chrome is consumed. Some of the early reaction products are unstable and slowly convert via dissolution into stable comp...
S-E Dahlgren
Ten year field test with a copper-borate ground line treatment for poles
1993 - IRG/WP 93-30017
A wood preservative paste consisting of borax and copper naphthenate has been tested to determine its efficiency in protecting wood from decay fungi and insects. The paste was applied to polyethylene-backed wraps that were fastened to the below-ground portions of unseasoned southern pine pole stubs. After 4 years of exposure in Mississippi, the untreated control stubs were completely deteriorated....
T L Amburgey, M H Freeman
Chemical analyses of IRG/COIPM INTERNATIONAL MARINE TEST (to determine the effect of timber substrate on the effectiveness of water-borne salt preservatives in sea-water) samples
1987 - IRG/WP 4114
Chemical analysis of CCA and CCB treated timber was carried out after exposure at tropical and temperate marine sites. Results indicated that losses of all elements had occurred. In particular, losses of boron were severe. Arsenic and copper were also lost. The chromium components in both formulations was the most dominant metal remaining. The results suggest that chromium modification was importa...
L E Leightley
Durability of wood in the area of wood-inhabiting termites in Slovenia
1981 - IRG/WP 1139
This report describes a research dealing with resistance and durability of five different species of wood. The experiment was made in natural conditions in the Slovene area of wood-inhabiting termites. The results of our experimental field, which correspond to the results of the former laboratory experiments, show a very weak resistance of spruce-wood, fir-wood, and beech-wood. They also show thei...
L Kervina
Retention and distribution of copper/chrome/arsenic (CCA) in pressurised sap-displaced UK grown spruce and pine
1986 - IRG/WP 3366
Increment cores were taken from UK grown Scots pine (Pinus sylvestris L.), Corsican pine (Pinus nigra var. maritima Ait), Sitka Spruce (Picea sitchensis (Bong) Carr), and Norway spruce (Picea abies (L) Karst) distribution poles treated by pressurised sap-displacement using a 1.8% copper, chrome, arsenic (CCA) solution. Each increment core was sectioned radially and the copper, chrome, and arsenic ...
P D Evans, G M Smith, B King
Comparisons of differences in electrical conductivity and corrosivity between CCA-oxide and CCA-salt treated wood
1981 - IRG/WP 3178
CCA preservatives have served well in many applications throughout the world. In developed areas it is the preservative in demand for clean dry paintable surfaces with long durability. In developing areas it is widely used for economic and logistical reasons. With the current emphasis on energy resources, the CCA preservatives are gaining greater acceptance as a substitute for hydrocarbon-related ...
J A Taylor
The volatilization of arsenic on burning copper-chrome-arsenic (CCA) treated wood
1978 - IRG/WP 3111
Small scale burning experiments are described involving copper-chrome-arsenic treated wood. Approximately 20 per cent of the arsenic was volatilised when the wood was burned in air but 60 per cent when burned in an oxygen-enriched atmosphere, this increase is attributed to an increase in combustion temperature. Although a small increase in arsenic evolution was found with an increased concentratio...
A-J Dobbs, C Grant