Long-Term Release of Arsenic, Chromium, and Copper from CCA-Treated Wood and Ash
2005 - IRG/WP 05-50227
In this study, laboratory long-term leaching studies were conducted to characterize the leaching behavior of arsenic, chromium, and copper from CCA-treated wood samples (block, chip, and sawdust) and CCA-wood ash and to determine the rate of release of the metals from the CCA wood products. The leaching solutions were periodically collected and analyzed for the concentrations of arsenic, chromium,...
Hyunmyung Yoon, Heeseok Kang, Yong-Chul Jang
Effect of soil chemistry and physical properties on wood preservative leaching
1998 - IRG/WP 98-50111
When treated wood is placed in contact with soil, complicated mass transfer and chemical reactions occur which causes the preservative components to leach from the wood. There are several factors that are known to affect the amount of chemical leached from wood. These are properties of the preservative and carrier, preservative retention, degree of fixation, exposure time, grain orientation, surfa...
Joan-Hao Wang, D D Nicholas, L S Sites, D E Pettry
Fixation of chromated wood preservatives through technical drying
1990 - IRG/WP 3623
Twin samples of sawn timber of Pinus sylvestris and Picea sp. were treated with copper-chromate-containing wood preservatives and subsequently kiln resp. air dried. After drying, the distribution of preservative and rate of fixation were determined. Drying of freshly treated wood in a condenser type kiln at temperatures of 60°C and 80°C and in a vacuum type kiln at 55°C with a pressure of about...
R-D Peek, H Klipp
Ecotoxicological effects of exposed CCA preservative treated wood in environments
2001 - IRG/WP 01-50173
For the evaluation of environmental effect of CCA treated wood exposd in the field, the simulated soil pot system of the laboratory was used. The effective components of preservatives were leached and determined after artificially conditioning a soil pot of CCA treated wood with more than 500mm water, the average monthly precipitation. As the water passed through the soil, As, Cr and Cu in the soi...
Dong-heub Lee, Dong-won Son
CCA type C depletion of Southern yellow pine utility poles
1995 - IRG/WP 95-50049
Depletion and redistribution of preservative components were evaluated on five CCA-C treated poles in service for over six years in Conley, Georgia. A statistical approach was taken in which retentions below ground were compared to retentions above ground due to a lack of initial data on individual poles. It was hypothesized that the below ground retentions should be lower than the corresponding a...
P D Osborne, R F Fox
Upgrading the fungal resistance of OSB
1999 - IRG/WP 99-40138
There is a perception that oriented strand board (OSB) is less resistant to fungl than plywood under conditions of moderate exposure to moisture. Douglas fir-faced plywood (DFP) has been suggested as a benchmark for acceptable durability under such conditions. This project was initiated to determine the minimum level of low-toxicity chemical treatment needed to upgrade the fungal resistance of OSB...
P I Morris, J E Clark, D Minchin, R Wellwood
Influence of fungal exposure on the redistribution of copper in treated spruce wood
2002 - IRG/WP 02-10450
The redistribution of copper in treated wood after exposure to basidiomycete decay fungi is described. The micro-distribution of copper in copper(II) sulphate or copper(II) octanoate/ethanolamine treated Norway spruce wood before and after exposure to 3 different wood decay fungi was studied using transmission electron microscopy with X-ray microanalysis. The copper content of the mycelium and the...
M Humar, F Pohleven, R J Murphy, D J Dickinson, I Moris, M Zupancic, P Kalan, M Petric
Effects of the sulfuric acid modification of CCA treating solution
1987 - IRG/WP 3415
Sulfuric acid modification of CCA treating solution is often used to control the formation of sludges and undesirable deposits on the surface of treated wood. The consequences of sulfuric acid addition are examined in this work and negative effects are shown to far outweigh any benefits. Major risks include the loss of copper due to leaching from treated wood and the accelerated corrosion of treat...
R F Fox, H J Fry, E A Pasek, A S Ross
Evaluation of hydroxamates as wood preservatives
2004 - IRG/WP 04-30330
Fungicidal activity of different hydroxamates was investigated by laboratory malt-agar block tests to evaluate their potential as wood preservatives. Results obtained indicate that benzohydroxamic acids substituted or not on the aromatic nuclei were unable to protect wood blocks against the white rot fungus Coriolus versicolor while 2-hydroxypyridine-N-oxide (2-HPNO) possesses an interesting activ...
P Gérardin, S Dumarçay, E Gelhaye, A Mbamba, V Mussavu
The effect of stack height on the performance of preservatives used for the prevention of sapstain on seasoning wood
1997 - IRG/WP 97-10192
The performance of three anti-sapstain preservatives was investigated under field conditions in south east England. The preservatives under test were: copper-8-quinolinolate (Mitrol PQ8) trimethylalkylammoniumchloride and sodium hexanoate (Sinesto B) and chlorothalonil (Tuff Brite). The preservatives were tested on Corsican Pine grown in south east England. The field trial was set up to investigat...
J R Williams, D J Dickinson, J F Webber
Interactions between soft rot fungi and CCA preservatives in Betula verrucosa
1988 - IRG/WP 1367
Ultrastructural investigations were carried out to obtain information on the cell wall distribution of CCA elements during soft rot decay of 4% K33 CCA preservative treated birch (Betula verrucosa) wood. TEM observations on fibres at various stages of S2 cavity formation by mutabilis showed a distinct pattern of electron dense materials to occur within the S2 cell wall region. These materials (gra...
G F Daniel, T Nilsson
Environmental Impacts of CCA-Treated Wood: A Summary from Seven Years of Study Focusing on the U.S. Florida Environment
2003 - IRG/WP 03-50205
Wood treated with chromated copper arsenate (CCA) was identified in 1995 as the cause of elevated arsenic concentrations within wood fuel used for cogeneration within Florida. Since this time a research team from the University of Miami and University of Florida has evaluated the environmental impacts of CCA-treated wood within the State. Research has focused on two distinct areas: in-service l...
H M Solo-Gabriele, T G Townsend, J D Schert
Bioefficacy of Cunapsol® treated western cedar and southern yellow pine
1996 - IRG/WP 96-30120
Western red cedar and southern yellow pine sapwood were dip treated with a new formulation of waterborne copper naphthenate (Cunapsol®) which complies with VOC regulations. Cunapsol dip treated samples were oven dried at 50°C for 48 hours and then water leached for two weeks. Decay resistance and leachability of preservatives from dip treated specimens were evaluated according to AWPA (American ...
D P Kamdem, M H Freeman, T L Woods
The susceptibility to sludging of sulfate and oxide CCA
1990 - IRG/WP 3599
Radiata pine sapwood was treated separately with a sulphate CCA-C and an oxide CCA in a pilot scale pressure plant using a full cell process. CCA solutions were recovered from the final vacuum phase, placed in plastic tubes, and their susceptibility to sludging determined by examining changes in solution pH, time required for sludge to form and weight and chemical composition of sludge formed. Sul...
B T Mutandadzi, P D Evans
The influence of UV and IR radiation on leaching of copper and chromium from preservative-treated pine and spruce
1992 - IRG/WP 92-3687
The influence of artifical UV- and IR-radiation on the leaching of copper and chromium components of a CCB-preservative from freshly treated pine and spruce was evaluated. On small pinewood samples it could be shown, that the leaching of copper and chromium can considerabely be reduced by UV-radiation. A Philips HPA lamp type reduced the leaching most effective. IR-radiation lead to higher leachin...
H Militz
Fungal degradation of wood treated with metal-based preservatives. Part 1: Fungal tolerance
1996 - IRG/WP 96-10163
In recent years, concerns have arisen about the leaching of heavy metals from wood treated with chromated copper arsenate (CCA), particularly because of the large amount of CCA treated wood that will be discarded in the coming years. The long term objectives of this work are to determine the fate of copper, chromium and arsenic with the aging and potential decay of CCA-treated wood, and to develop...
B Illman, T L Highley
Chromated copper arsenate preservative treatment of hardwoods. Part 1: CCA fixation performance of seven North american hardwoods
1997 - IRG/WP 97-30131
There has been an increased interest in utilisation of hardwoods from eastern North America for exterior applications which require protection with preservatives such as CCA. We have examined CCA fixation at two selected temperatures of seven common North American species: red maple (Acer rubrum L.,), white birch (Betula papyrifera ), yellow poplar (Liriodendron tulipifera L.), trembling aspen (Po...
T Stevanovic-Janezic, P A Cooper, Y T Ung
Effects of hard water, sea water and humic acid on the release of CCA components from treated wood
2005 - IRG/WP 05-50228
Leaching medium is an important factor affecting release of preservative components from treated wood because physical and chemical characteristics of medium increase or decrease the solubility of fixed preservative components. This study evaluated the leaching properties of copper, chromium and arsenic elements from chromated copper arsenate (CCA)-treated wood specimens subjected to laboratory le...
S N Kartal, W J Hwang, Y Imamura
Wood preservation sites polluted by CCA. Is potassium diphosphate incubation a catalyst for the electrodialytic remediation of these soils?
1998 - IRG/WP 98-50106
As part of an evaluation of a newly developed electrodialytic soil remediation technique, we investigated the incubation of a contaminated soil (from a Portuguese wood preservation site polluted with CCA) with potassium diphosphate as a possible catalyst for the removal of heavy metals and metalloids. A chemical sequential extraction scheme (SE) applied to the soil has shown that the potassium dip...
A B Ribeiro, G Bech-Nielsen, A Villumsen, A Réfega, J Vieira e Silva
The influence of cement and calcium compounds on the performance of CCA preservatives
1983 - IRG/WP 3221
The influence of cement and calcium compounds on the durability of untreated and CCA treated wood is considered. Calcium compounds were found to reduce the toxicity of a CCA preservative to a soft rot fungus at copper to calcium ratios of 1:1 and 1:10 using a cellulose filter paper technique. Further studies are outlined and some possible mechanisms by which cement and calcium compounds may affect...
R J Murphy
Efficacy of a novel copper-based organic solvent preservative in laboratory and fungus cellar tests
1995 - IRG/WP 95-30071
The efficacy of Chemicca 4, a novel copper-based organic solvent preservative, was compared with that of other LOSP in pure culture laboratory decay tests and with that of CCA and TBTO in a fungus cellar exposure. It was markedly superior to copper and zinc naphthenates at equivalent metal retentions in laboratory decay tests, and similar in activity to TBTO. After 60 months' fungus cella...
M E Hedley, P N Maynard
A physiological role of the glyoxylate and TCA cycles in fruitbody formation of the coppertolerant brown-rot fungus Fomitopsis palustris
2002 - IRG/WP 02-10430
Changes in activity of the representative enzymes involved in biosynthesis of oxalic acid (oxalate) and carbon metabolism of glucose were investigated in relation to the fruit body formation of the copper-tolerant brown-rot fungus Fomitopsis palustris. Changes in specific activities of the two glyoxylate (GLOX) cycle key enzymes (isocitrate lyase (ICL) and malate synthase (MS)), the two oxalate-fo...
Jeong-Jun Yoon, T Hattori, M Shimada
Correlation between modulus of elasticity, mass losses and FTIR spectra of copper treated decayed wood
2006 - IRG/WP 06-10580
The composition of copper-based preservatives will change from copper-chromium to copper-ethanolamine, due to environmental demands. The most important drawback of copper-impregnated wood is the presence of tolerant fungal organisms that have developed an ability to degrade such preserved wood. In order to elucidate these processes, specimens (0.5×1.0×15 cm) made of Norway spruce (Picea abies) w...
M Humar, B Bucar, F Pohleven
The role of oxalic acid in tolerance to N’N-naphthaloylhydroxylamine in Tyromyces palustris
2006 - IRG/WP 06-10584
Certain wood decay fungi exhibit tolerance to one or more wood preservatives. Copper tolerance of brown-rot fungi has been studied in our laboratory for the past six years. We have observed some degree of tolerance to N’N-naphthaloylhydroxamine (NHA), a recently patented termite bait, by the brown-rot fungus Tyromyces palustris TYP-6137. In an effort to try and confirm this tolerance in other is...
R A Arango, C A Clausen, F Green III
Is Field Test Data from 20 x 20mm Stakes Reliable? Effects of Decay Hazard, Decay Type and Preservative Depletion Hazard
2006 - IRG/WP 06-20327
Effects of decay hazard, decay type and preservative depletion hazard on the performance of variously preservative treated 20 x 20 x 500 mm Radiata pine and Fagus sylvatica test stakes across 13 field test sites in New Zealand and Queensland Australia were determined.
Radiata pine treated with an ammoniacal copper quaternary preservative (ACQ) (1.56% m/m a.i.) and copper chrome arsenate (CCA) (...
R Wakeling