Exposure monitoring of creosote vapors
1989 - IRG/WP 3511
Creosote oils contain hundreds of compounds. During impregnation and handling of treated wood the main component in the vapors released in air is naphthalene. Other main components are alkyl naphthalenes, indene, phenol and its methyl derivatives, benzothiophene, diphenyl, acenaphthalene and fluorene. In the measurement of creosote vapors, naphthalene can be used as an indicator agent. One of the ...
P Heikkilä, M Loutamo, V Riihimäki, M Romo
Sequential exposure of borate treated Douglas-fir to multiple Formosan subterranean termite colonies in a 40-week field test
1993 - IRG/WP 93-10006
Douglas-fir boards (ca. 74.5 g) pressure-treated with disodium octaborate tetrahydrate (DOT) retentions of 0 (controls), 0.88, 1.23, 1.60, or 2.10% (weight/weight) DOT were sequentially exposed to four active field colonies of Formosan subterranean termites, Coptotermes formosanus Shiraki (Isoptera: Rhinotermitidae), in an above-ground field test. Samples were placed in contact with each colony fo...
J K Grace, R T Yamamoto
Analysis of creosote posts after 40 years of exposure
1994 - IRG/WP 94-50035
In the early 1950s The Western European Institute for Wood Preservation (WEI) started a program for testing creosote and salt treated posts in three exposure sites in Europe. Of these only the site in Simlångsdalen in south western Sweden remains today. The purpose with this investigation was to demonstrate which creosote components are still retained in the posts after 40 years of exposure and w...
G Bergqvist, S Holmroos
Copper naphthenate-treated Southern Pine pole stubs in field exposure. -Part 2: Chemical characterization of full size pole stubs 12 years after treatment
2000 - IRG/WP 00-30246
This study examines the influence of pre-treatment and post-treatment steaming on the character and physio-chemical nature of copper naphthenate in hydrocarbon solvent treated pine in larger, pole diameter, pole stub-length samples. This work is the continuation of two projects that began almost a decade ago. Previous reports indicated that certain morphological changes might occur in small labora...
H M Barnes, D P Kamdem, M H Freeman
An Australian test of wood preservatives. - Part IV: The condition, after 35 years' exposure, of stakes treated with creosote oils and oilborne preservatives
2000 - IRG/WP 00-30241
This paper contains the first results dealing with creosote oils and oilborne preservatives from this in-ground field trial in Australia. The substrates impregnated with preservative were Pinus radiata D. Don sapwood and Eucalyptus regnans F. Muell. heartwood and sapwood. Data are reported from stakes exposed for 35 years at three Australian sites (Innisfail, Sydney, Walpeup). Comparisons were mad...
G C Johnson, J D Thornton
Biocides - Efficacy assessment and doses for wood preservatives (product type 8). Local/geographical aspects. Termite control as case study
1999 - IRG/WP 99-20181
Currently, the efficacy of a wood preservative, as biocidal product type 8, is assessed as a ‚critical value' (CV), an efficient dose (retention in wood at a given depth of penetration). CVs are planned to be adapted for exposure to basic target organisms (5 hazard classes) and additional requirements concerning the occurrence of local target organisms in relation with climate, building...
G Ozanne
Seasonal effects of the field evaluation on wood preservatives against mold fungi
1996 - IRG/WP 96-20087
For the purpose of the amelioration of field test methods, commercial preservatives against mold fungi were tested under two different seasons, in winter and in summer. The specimens were bundled and set over the water bath and all these systems were covered with plastic film. At top of the system under film, black films for regeneration of sunlight were put in, and windows for changing air were r...
K Suzuki, Y Sugai, K Ryugo, D Watanabe
Environmental exposure to wood preservatives
2000 - IRG/WP 00-50165
The OECD Working Group on Pesticides will hold a workshop on Assessing Environmental Exposure to Wood Preservatives within the context of its Biocides Programme (cf. IRG/WP 99-20182). In the area of risk assessment, OECD countries have given highest priority to developing guidance on how exposure assessments for biocides should be performed. Wood preservatives have been selected since most countri...
R-D Peek
Biological effectiveness of ground-contact wood preservatives as determined by field exposure stake tests
1984 - IRG/WP 3297
Field exposure tests conducted on stakes treated with different creosotes, mixtures of creosote and waxy oil as well as different CCA wood preservatives over a period of 25 years, gave the following results: The CCA preservatives provided excellent biological protection to treated stakes, especially against fungal attack. The CCA Type I, currently approved for use under South African conditions is...
W E Conradie, A Pizzi
Climate indices at work: Above ground decay L-joint tests (EN 330 and AWPA E9) at two sites 12000 km apart and with Scheffer climate indices of 60-65 and 300-330
1996 - IRG/WP 96-20095
Matched sets of Scots pine sapwood (Pinus sylvestris) L-joints were exposed above ground at two field sites for approximately five years. One site, at Garston, Watford, UK has a climate index between 60 and 65 while the other, close to Hilo, HI, USA has an index between 300 and 330. The joints were treated with a range of organic solvent treatments applied either by three minute dip immersion or b...
A F Preston, K J Archer, D M Roberts, J K Carey, A F Bravery
A natural exposure weathering test for the evaluation of preservative performance
1992 - IRG/WP 92-2400
Natural exposure weathering tests were carried out by externally exposing treated wood samples for varying periodes of time up to 36 months. In the laboratory these samples were assayed for residual preservative effeciveness using Coniophora puteana FPRL 11E. The results indicated a loss in efficacy over and above that determined using artificial ageing procedures such as EN73 (evaporative ageing)...
J Brown, G R Williams
Risk assessment and the approval of wood preservatives in the United Kingdom
1995 - IRG/WP 95-50040-23
An approval system operates in the United Kingdom (UK) for the regulation of wood preservatives. The regulatory authority uses a risk assessment approach to evaluate how far the potential for harm to people and the environment from wood preservatives is likely to be realised in practise, and hence the controls required for products to be, used safely. The evaluation for approval purposes also take...
R M Turner
Development of decay in untreated, second-growth Douglas-Fir using two exposure techniques in North Queensland
1997 - IRG/WP 97-20110
The results of two exposure techniques for evaluating the development of wood decay in untreated, mill-run lumber from second-growth Douglas-fir containing both sapwood and heartwood are presented. Nominal 50 mm by 100 mm by 2.5 m (2 in. by 4 in. by 8 ft) lumber, No 2 and better, was obtained from a production run in a mill that was processing second growth, Coastal Douglas-fir in western Oregon, ...
J Norton, S Kleinschmidt, R C De Groot, D Crawford
Effect of felling time related to lunar calendar on the durability of wood and bamboo
-Fungal degradation during above ground exposure test for 2 years- (Preliminary report)
2005 - IRG/WP 05-20311
Current study was carried out to know whether the felling time of trees and bamboos based on lunar calendar affects natural durability of felled wood-bamboo or not. Each of one sugi (Cryptomeria japonica) tree of 28 years old and one Moso bamboo (Phyllostachys heterocycla) of around 3 years old was cut 12 times between February and December in 2003. Six sets of sugi tree and bamboo were felled in ...
K Yamamoto, S Uesugi, K Kawakami
Decay patterns observed in butylene oxide modified ponderosa pine after exposure in unsterile soil
1982 - IRG/WP 3211
Small blocks of ponderosa pine (Pinus ponderosa Laws) chemically modified with butylene oxide to three different weight gains were exposed for 6 weeks in unsterile soil. Severe surface decay caused by soft rot fungi and tunnelling bacteria was observed in blocks with 8 weight percent gain. The soft rot attack was restricted to the outer parts of the radial walls in the latewood tracheids. Bacteria...
T Nilsson, R M Rowell
Marine performance of preservative treated Southern pine panels. Part 2: Exposure at Mourilyan Harbour, Queensland, Australia
2000 - IRG/WP 00-10337
Southern yellow pine panels treated with ACQ type B, ACQ type A, CCA type C, creosote, and copper naphthenate have been exposed at Mourilyan Harbour, north Queensland, Australia for almost 6 years. These panels have been inspected and rated for fouling and attack by Teredinid, Limnoria, Martesia, and Sphaeroma during this exposure. After 70 months exposure, overall performance of ACQ type B was eq...
A R Zahora, A F Preston, K J Archer, S Kleinschmidt
Effect of permeability and extractives on the decay rate of southern pine sapwood in above grund exposure
2005 - IRG/WP 05-20310
The effects of wood permeability and hydrophilic and hydrophobic extractives on the decay rate of southern pine sapwood in above ground exposure were investigated. Permeability was determined by water sorption measurements, and the effect of extractives was studied by pre-extracting the test samples prior to outdoor exposure using water to extract hydrophilic extractives or sequential methanol/cy...
D D Nicholas, T Schultz, L Sites, D Buckner
Physiologic response of Phanerochaete chrysosporium to exposure to triazole fungicides
1994 - IRG/WP 94-10066
Triazoles are increasingly important fungicides which are employed for a variety of applications included wood protection. Several recent studies suggest that white rot fungi are more tolerant of triazole compounds than other wood degrading fungi. Cultural studies using a white rot fungus, Phanerochaete chrysosporium, and 0.2 or 0.8 ppm of tebuconazole or propiconazole suggested that mycelial dry ...
J J Morrell, R K Velicheti
Comparison of decay rates of preservative-treated stakes in field and fungus cellar tests. Results after 40 months fungal cellar exposure
1983 - IRG/WP 2200
Decay rates of preservative-treated Pinus radiata stakes during 40 months exposure in the FRI fungus cellar were compared with those of similarly treated material in a field test. Decay rates in the fungus cellar were from 4 to 100 times higher than in the field, although for the majority of preservatives the rate was between 7 and 12 times higher. The lag phase before onset of decay, noticeable w...
M E Hedley
Moisture condition in treated wood exposed outdoors. A progress report after 5 years
1992 - IRG/WP 92-3720
Wood treated with water-borne preservatives, mainly CCA (copper, chromium and arsenic) and CCB (copper, chromium and boron) is often said to absorb more water than untreated wood. In laboratory tests this statement has not been confirmed (Johansson 1977). In 1986 a project was started to compare water absorption during outdoor exposure between wood stakes of pine, Pinus sylvestris L, and spruce, P...
M-L Edlund
Ammoniacal wood preservative for use in non-pressure treatment of spruce and aspen poplar. Part 1
1984 - IRG/WP 3273
End-matched lumber of Picea glauca (Moench)Voss (white spruce) and Populus tremuloides Michx. (aspen poplar) timbers was treated by a thermal diffusion process in open tank treating vessels using an ammoniacal copper-arsenate wood preservative. The process proved technically feasible with respect to controlling the vapourization of ammonia from open tanks during treatment at high temperatures. Tre...
C D Ralph, J K Shields
Bending creep test of plywoods under long term exposure to fungal attack
1981 - IRG/WP 2163
Bending creep test and decay test were coupled in order to evaluate the durability of structural plywoods and preservative efficacy. Experimental blocks, 5.0 x 1.2 cm² section x 35.0 cm length, were impregnated with distilled water and inoculated with mycelial fragments of test fungus. Polyethylene bags stretched with metal frame were used as decay chambers. The chambers containing inoculated blo...
M Takahashi
List of wood-destroying fungi in Iran
1976 - IRG/WP 138
This list gives information on the wood-destroying fungi collected in the Iranian forests and from felled logs and boards in sawmills until now. They are mainly from the region of the Caspian Forests and from the climatically dry region between Teheran and Azarbaidjan, North Iran. It is understood, that this document may help to give more knowledge outside the country about the specific problems o...
P Soleimani
Correlation between different international standard assessment procedures with termites. Part 1: Field exposure
1983 - IRG/WP 1198
Ramin treated with copper-chrome-arsenic (CCA), pentachlorophenate and lindane, each at three retentions, and three other untreated timbers were assessed in the field against Coptotermes lacteus and Nasutitermes exitiosus. Replicate specimens were exposed around five mounds of each termite species over a period of five years in south-eastern Australia. The field results provided the basis for judg...
M Lenz, C D Howick, N Tamblyn, J W Creffield, M Westcott
Moisture condition in treated wood exposed outdoors. A progress report
1989 - IRG/WP 3533
Wood treated with water-borne preservatives, mainly CCA (copper/chromium/arsenic), CCB (copper/chrome/boron) or CC (copper/chrome) is often said among users in Sweden to absorb more water than untreated wood. In laboratory tests this statement has not been confirmed but no field tests have been carried out in Sweden to study this phenomenon. In 1986 a project was started to compare water absorptio...
M-L Edlund, C E Sundman