Resistance of Consolidated Deteriorated Wood to Wood Decay Fungi
2013 - IRG 13-10812
The main purpose of the experiment was to establish which consolidating products in impregnated wood are the most effective against wood decay fungi. Five different consolidators were tested: Paraloid B-72, Consolidating restaurateur, SG 715 BLANC (epoxy resin), R.712 polyester and the wood consolidant agent containing nano particles, which is still in development.
From the already damaged wood ...
F Pohleven, A Valantič, M Petrič
Determination of the natural durability of solid wood against wood-destroying fungi - a European round-robin test
2013 - IRG/WP 13-20511
In Europe the durability of wood against wood-destroying basidiomycetes is tested according to CEN/TS 15083-1 (2005). Hitherto existing experience with this standard is quite heterogeneous and results from previous round-robin tests have stayed unreported or have been reported incompletely. In particular the need for natural pre-weathering of the test specimens to allow potential detoxification of...
C Brischke, C R Welzbacher, A Gellerich, S Bollmus, M Humar, K Plaschkies, W Scheiding, G Alfredsen, J Van Acker, I De Windt
What molecular biology can tell us about the biodegradation of lignocellulose: the utilization of molecular techniques for the detection, identification and enhanced understanding of wood degrading organisms
2013 - IRG/WP 13-20528
Molecular techniques are now routinely used in the identification, detection and analysis of wood degrading organisms. An overview of some of the early work on nucleic acid isolation and characterization will be followed by a discussion of the power of sequencing and other procedures for better understanding: the mechanisms involved in the biological degradation of wood, the metabolic basis of pre...
J Jellison, B Goodell, G Alfredsen, D Eastwood, G Daniel, S M Cragg, J K Grace
Development of a rapid method to assess the rate of fungal colonization of wood
2013 - IRG/WP 13-20531
Testing of wood durability is today done mainly with accelerated exposure tests under rather realistic conditions (in ground, outdoors with moisture traps etc). Although such tests are accelerated with respect to the conditions that outdoor exposed wood structures are exposed to, they tend to take rather long time. The present paper presents the development of a rapid method intended to assess at ...
L Wadsö
Preparation of Copper Rosinate Emulsion and Its Resistance against Wood Decay Fungi
2013 - IRG/WP 13-30619
A leaching-resistant water-borne copper preservative was prepared by means of the following three steps: (1) Gum rosin was saponified with potassium hydroxide. (2) The soap reacted with copper sulfate to form copper rosinate. (3) The copper rosinate was emulsified with a mixture of Tween 20 and Span 80. Poplar (Populus ussuriensis) wood was impregnated with 0.5%, 1.0%, 1.5%, or 2.0% of the copper ...
Mingxin Zhang, Shujun Li, Qian Wang, Bo Li, Qiong Wu
Effect of the nature of the inert atmosphere used during thermal treatment on chemical composition, decay durability and mechanical properties of wood
2013 - IRG/WP 13-40625
Wood heat treatment is an attractive alternative to improve decay resistance of low natural durability wood species. Nowadays, several types of thermal treatments of wood exist. These treatments differ mainly by the nature of the inert atmosphere used to avoid wood combustion which may correspond to: nitrogen, vacuum, steam or oil. Decay resistances as well as mechanical properties are strongly co...
K Candelier, S Dumarçay, A Pétrissans, M Pétrissans, P Gérardin
Postia placenta cellulase gene expression in modified wood during incipient decay
2013 - IRG/WP 13-40626
In optimization of modified wood, it is important to understand the mode of action of the wood modification and how the fungi response to it. The aim of this study was to investigate the expression of cellulases during the first two weeks of Postia placenta exposure in acetylated, DMDHEU-treated and thermally modified as well as in untreated wood. Using real-time PCR, the gene expression patterns ...
R Ringman, A Pilgård, K Richter
Effect of bio-resin from cashew nut shell liquid (CNSL) on decay resistance properties of wood
2013 - IRG/WP 13-40649
This study assesses the decay resistance properties of bio-resin modified wood against decay fungi of the Basidiomycota according to the EN 113 protocol. A bio-resin system was developed by ozonolysis process from cashew nut shell liquid (CNSL), a naturally occurring mixture of phenolics. Small wood blocks from sapwood of Scots pine (Pinus sylvestris), Obeche (Triplochiton scleroxylon) and Gmelina...
M Ashaduzzaman, M D Hale, V Tverezovskiy, G A Ormondroyd
Effect of Nano-silver and Nano-copper and Nano-zinc oxide on Paulownia wood exposed to white-rot fungus
2013 - IRG/WP 13-30635
Paulownia is known as a fast growing tree and it can be used in several applications. The present study investigated the effect of Nano-silver and Nano-copper and Nano- zinc oxide on resistance of Paulowina (Paulownia fortunei) wood against the white rot fungus (Coriolus versicolor). Wood specimens with a dry density of 0.37g/cm3 were impregnated with a 400 ppm aqueous suspension of micronized na...
M Akhtari, M Ganjipour
Durability and Wood Protection for Historic Covered Bridges in the United States
2014 - IRG/WP 14-10829
A majority of the covered wooden bridges in United States were built in the mid -1800’s. These structures represent a unique cultural and technological heritage from that era. Over time, these bridges have been deteriorated by microorganisms and insects or damaged by acts of vandalism and arson. The National Historic Covered Bridge Preservation (NHCBP) Program sponsored by the Federal Highway Ad...
V W Yang, C A Clausen
Development of new wood treatments combining boron impregnation and thermo modification - Effect on decay and termites durability
2014 - IRG/WP 14-40666
Environmental pressures appeared in most European countries during the last decade has lead to the development of more environmentally acceptable preservation methods. In this context, wood heat treatment has been one of the most investigated alternative methods during the last years. Treated at temperatures ranging between 180 and 220°C, wood components undergo more or less important chemical mo...
S Salman, A Pétrissans, M-F Thévenon, S Dumarçay, B Pollier, P Gérardin
Influence of the moon phase on durability against wood decay fungi of Larix kaempferi and Pseudotsuga menziesii wood species
2015 - IRG/WP 15-10836
The analysis of the natural durability of wood is essential when establishing the level of protection required, depending on the designated end use of timber. On the other hand, there is a popular belief based on the influence of the moon phase in felling timber, recommending the waning moon as the optimum for felling trees. In fact, some companies now offer among their products, sawn timber felle...
M T Troya, M Conde, M J Barriola, F Llinares, V Dorronsoro
Short-term protection of palm wood against moulds and decay fungi by environment-friendly organic acids
2015 - IRG/WP 15-10843
Felled palm trunks are susceptible to fungi as long as their moisture content is above fibre saturation. During this period, it has to be protected against moulds and decay fungi. The study tested environmental-friendly organic acids for their protecting efficiency. Small samples of Date palm (Phoenix dactylifera) and Oil palm (Elaeis guineensis) wood were treated with weak organic acids and subse...
M Bahmani, O Schmidt
Factors Affecting Performance of Preserved Wood Decking Against Decay Fungi
2015 - IRG/WP 15-30663
Decking is the largest market for residential preserved wood in the United States. Preserved decking must be resistant to colonization by decay fungi initiating from spores, and occasionally from mycelia due to elevated soil levels or adjacent untreated wood. The most vulnerable parts of a preserved wood deck are untreated, or under-treated, wood that becomes exposed by field cuts and checking. Fi...
R Stirling, P I Morris
Mould growth on spruce claddings and the effect of selected influencing factors after 4 years of outdoor testing
2015 - IRG/WP 15-30671
Norway spruce (Picea abies) is the most frequently chosen wood species as claddings in façades in Norway, and is used both coated and uncoated. The visual changes that occur during weathering can be colour changes, abrasion or wear, blistering, flaking, and even cracks in the wood or coating, but more often growth of mould and blue stain fungi is the main challenge. A field test with synchronous monitoring of relative humidity, air temperature, material temperature and wood moisture content in Norway spruce claddings has been performed in southern Norway as part of the ClimateLife project. Visual evaluation of blue stain and mould growth according to EN 927-3 was performed, and evaluation data after 46 months exposure is presented. The objectives were to study the effect of 1) environment, 2) cardinal direction and 3) colour of the coated surface on growth of blue stain and mould fungi and to study the variation in relative humidity, air temperature, wood moisture content and material temperature. After 46 months exposure, the red coating system had generally the lowest mould ratings and the uncoated claddings had the highest. Of the white coloured claddings the ones facing south had lower mould ratings than those facing north, but the opposite were found for red coloured claddings. The relative humidity was higher in front of claddings exposed northwards and in a shaded environment compared to an open environment against south. In an open environment red coloured claddings had the lowest wood moisture content and highest material temperature, and red coloured claddings against south had the highest maximum material temperature.
L Ross Gobakken, G I Vestøl
A novel enzymatic treatment as a new approach for wood protection
2015 - IRG/WP 15-40701
Wood durability is a worldwide concern and most treatments tend to fail with regard to their efficacy along the time. Weather conditions lead to a loss of the treatment substances into the surrounding environment and, in consequence, generate also a public health concern.
Recently, the employment of oxidative enzymes, such as laccases, has been proposed as a tool for lignocellulosics modificatio...
C Fernández-Costas, S Palanti, M Ángeles Sanromán, D Moldes
Laboratory evaluations of woods from Pakistan and their extractives against Postia placenta and Trametes versicolor
2016 - M Mankowski, B Hassan, A Bishell, G Kirker
Natural durable wood species are those which exhibit innate tolerance to wood decay organisms such as fungi and termites. The goal of this study was to evaluate 4 wood species (Dalbergia sissoo, Cedrus deodara, Morus alba and Pinus roxburghii) from Pakistan in order to determine their resistance to both a model brown (Postia placenta) and white (Trametes versicolor) rot fungus compared to a durabl...
M Mankowski, B Hassan, A Bishell, G Kirker
Real-Time PCR Assays for the detection of the dry rot fungus Serpula lacrymans and its close relative Serpula himantioides
2016 - IRG/WP 16-10867
Prevention of wood decay by fungi of the phylum Basidiomycota is an important issue of wood protection. The most destructive fungus in buildings in Central Europe is the dry rot fungus Serpula lacrymans, which needs more extensive restauration measures than all other wood decay fungi. Its close relative S. himantioides occurs more frequently in outdoor environment. The assessment and remediation o...
K Jacobs, N Rangno
Decay of wood in outdoor above ground applications: Preview of results on the effect of climate and species in Spain
2017 - IRG/WP 17-20600
Within the framework of the Project BIA-42434R titled ‘Evaluation of the functional performance of wood in outdoor above ground applications’, seven trials containing seven pieces of sawn wood measuring 750x100x20mm3, belonging to seven different wood species (Scots pine, Radiata pine, Laricio pine, sweet chestnut, eucalyptus, Thermo-treated radiata pine and Spruce), were exposed to unprotecte...
J I Fernández-Golfin Seco, M Conde García, M R Diez Barra, M Conde García, L Acuña Rello, E Torres Álvarez, E Perea Alonso, M T Troya
Wood biodeterioration monitoring using molecular fluorescence
2016 - IRG/WP 16-20589
Wood is an extremely complex and heterogeneous biological material, susceptible to biodeterioration by wood-destroying organisms. This process can be evaluated by natural resistance tests or non-destructive techniques, such as molecular fluorescence. The fluorescence of wood can be attributed to the presence of fluorophores groups or extractives, as a characteristic of some species. This study aim...
E Meneses Oliveira, A Florian da Costa, J W Batista Brag
Assessment of the biological durability of wood treated with organosilicon compounds
2016 - IRG/WP 16-30685
The European wood construction market is in need of environmentally friendly wood-based products whose service life meets the expectations of end users. Non-biocidal silicon-based water repellents, which can be applied to different materials, help minimize their vulnerability/susceptibility to liquid water. Consequently, they have the potential of increasing wood’s resistance against decay fungi...
M Kutnik, M Montibus, S Derocker, S Salivati, J-P Lecomte
Effect of Nano-Silane on Permeability in MDF as a Result of Susceptibility to Moulds and Fungi
2016 - IRG/WP 16-40716
Effects were studied of vapor chamber on specific gas permeability of nanosilane-treated medium-density fiberboards (MDF). Size range of nanoparticles was 20 – 80 nm. Nano-silane (NS) was used at four consumption levels of 0, 50, 100, and 150 g/kg dry wood fibers. Density of all treatments was kept constant at 0.67 g/cm3. Specimens were kept for 18 weeks in vaporized chamber; their specific gas ...
H R Taghiyari, J Norton, A Moradiyan, M Sadegh Taher Tolou Del, H Siahposht, B Moradi-Malek, M Noferesti
Effect of different concentration of furfurylation on physical properties and decay resistance of Paulownia wood
2016 - IRG/WP 16-40762
The furfurylation process is an extensively investigated wood modification process. Penetration of Furfuryl alcohol molecules into the wood cell wall results in a permanent swelling. In the present study, different concentrations effect of furfuryl alcohol monomer on physico-biological properties such as water uptake, dimensional stability and decay resistance of wood polymer made by fast-growing ...
M Ghorbani, H Asghari
Decontamination of sludges, liquids and soils polluted by “class 1, 2 & 3a” and “temporary” wood treatment products from dipping tanks
2016 - IRG/WP 16-50315
Wood is one of the most widely used building materials as it is easy to find and process. As an organic material, time leads to a degradation of its substance, and even more so when it is exposed to pathogens such as fungi, bacteria and insects. In order to try and inhibit this phenomenon, several preservation treatments have been developed and applied thanks to the production of chemical biocides...
A Zaremski, E Wozniak, S Maman, C Zaremski, S Morel
Untreated and copper-treated wood soaked in sodium oxalate: Effects of decay by copper-tolerant and copper-sensitive fungi
2017 - IRG/WP 17-10888
Copper is widely used as the primary component in wood protectants because it demonstrates a broad range of biocidal properties. However, a key concern with using copper in wood preservative formulations is the possibility for brown-rot basidiomycetes to resist the toxic effect. Many brown-rot basidiomycetes have evolved mechanisms, like the production and accumulation of oxalate, which helps thes...
K M Ohno, G T Kirker, A B Bishell, C A Clausen