Leaching amount of wood preservatives from treated wood in different size during outdoor exposure for 6 months
2000 - IRG/WP 00-50160
Eighteen impregnated specimens with CCA, ACQ, and BAAC preservatives were subjected to a outdoor leaching test. Test specimens, 10 x 10 x 25 cm3, 5 x 10 x 25 cm3, 2 x 10 x 25 cm3 in size, were cut from Japanese cedar (Cryptomeria japonica). Both of end surfaces were sealed with a silicone sealer in the half number of specimens. Total leaching amounts of copper from the open-end ACQ specimens of 10...
K Yamamoto, S Motegi, A Inai
Effects of cyproconazole and copper sulphate on the length of the hyphal growth unit (HGU) of the white-rot fungus Coriolus versicolor
2003 - IRG/WP 03-10473
Wood decay basidiomycetes have been shown to produce appreciable quantities of extracellular mucilaginous materials (ECMM). The relationship between ECMM and total biomass production has been investigated in the white-rot fungus Coriolus versicolor (CTB 863 A). Differences in the amount of ECMM produced by the fungus proportionally to the total biomass, were observed under a range of physiological...
D Vesentini, D J Dickinson, R J Murphy
Chromium in wood preservation: Health and environmental aspects
1978 - IRG/WP 3120
The majority of water-borne salts in current use contain hexavalent chromium, usually as dichromate or chromium trioxide. In about 1913 it was suggested that chromates, phosphates or borates could be added to the sodium fluoride and dinitrophenol mixtures then in use in order to inhibit corrosion. Dichromates were found to be most suitable and the resulting mixture known as Thriolith and later Tri...
T R G Cox, B A Richardson
Heat transfer and wood moisture effects in moderate temperature fixation of CCA treated wood
1994 - IRG/WP 94-40022
Practical aspects of heat transfer and fixation of wood exposed to drying conditions after CCA treatment are considered. The rates of heat transfer and CCA fixation are substantially influenced by the cooling effect of water evaporating from the wood surface when drying occurs during fixation. At least in the early stages of fixation, the wood temperature approaches the wet bulb temperature, rathe...
J Chen, M Kaldas, Y T Ung, P A Cooper
Laboratory termite testing of copper boron tebuconazole
2000 - IRG/WP 00-20192
The American Wood Preservers' Association laboratory choice and no choice termite test (AWPA E1-97) was performed on a formulation of copper azole, which is comprised of copper, boric acid, and tebuconazole. The formulation tested has a ratio of copper:boric acid:tebuconazole of 25:25:1. So as to examine the impact of leaching, the southern yellow pine wafers were treated with and without...
R F Fox, E A Pasek, J Patel
Difference of CCA efficacy among coniferous wood species
1990 - IRG/WP 3601
Wood blocks of Cryptomeria japonica, Tsuga heterophylla, and Pinus radiata successively extracted with n-hexane, ether, and methanol were treated with various concentrations of CCA type 3, which were subjected to the decay by Tyromyces palustris. The weight loss were different among species and kinds of extraction. Cryptomeria japonica treated with CCA had higher fungal resistance than Tsuga heter...
K Yamamoto, M Inoue
Wood surface pretreatments with metal tannates
1989 - IRG/WP 3552
The sequential application of aqueous solutions of tannins derived from radiata pine bark and water-soluble metal salts was examined as a means of improving the water repellency of wood surfaces. Nine metal salts were screened in combination with tannin solutions and, based on water repellency of pretreated filter paper, four were selected for further study. The two-step application of tannin solu...
D V Plackett, D R Cronshaw
Observations on preservative penetration in poplar
1991 - IRG/WP 3662
In the course of studies on the CCA treatment and durability of poplar timber a zone of refractory wood at the sapwood/heartwood boundary was observed. Further studies were conducted to investigate the causes of this refractory behaviour. The initial results have suggested that the presence of lipid storage products in the ray tissue may lead to impermeability, either by directly blocking pits or ...
R J Murphy, S U Din, M J Stone
Status of wood preservation industry in India
2005 - IRG/WP 05-30388
The paper traces the history of wood preservation industry in India, listing various mile stones for creation of treating capacity. The preservation industry developed with the development of rail road system on the line of most other developed countries. The most popular wood preservatives are CCA, CCB, ACC, Creosote and recently LOSP have also appeared in the market. The major users of CCA is th...
S Kumar
Influence of carboxylic acids on LEACHING of copper amine based preservatives
2005 - IRG/WP 05-30365
The importance of chromium free preservatives is increasing. Leaching of copper from wood preserved with such solutions is still higher compared to leaching from wood impregnated with copper chromium ones. In order to decrease leaching, different carboxylic acids (octanoic, 2-etilheksanoic, decanoic) were added to copper/amine/boron aqueous solutions. Experiment of leaching of copper from Norway s...
M Humar, P Kalan, F Pohleven
Settlement of fouling organisms on CCA-treated Scots pine in the marine environment
1997 - IRG/WP 97-50094
As part of an EU project to investigate the effects of CCA loading on non-target marine fouling animals, exposure panels of Scots pine treated to 12, 24 and 48 kgm-3 CCA and untreated controls were submerged at seven coastal sites (Portsmouth, UK: Kristineberg, Sweden: La Tremblade (2 sites), France: Ria Formosa, Portugal: Sagres, Portugal: Athens, Greece). Inspections were made at 6 and 12 months...
C J Brown, R A Eaton
IRG/COIPM INTERNATIONAL MARINE TEST - to determine the effect of timber substrate on the effectiveness of water-borne salt preservatives in sea-water. Progress Report 3: Report of first inspection of samples at Lae, Papua New Guinea
1978 - IRG/WP 446
Samples for the international marine test were placed on frames numbered I to VII. Frames numbered VII of both CCA and CCB trials are being stored dry in the laboratory at F.P.R. & D.C. Frames I to VI of both trials were suspended in the sea at Lae Harbour (Morobe Province, Papua New Guinea) on 6th December 1977. The first inspection of the CCA trial was carried out on 8th June 1978, at which ...
S M Cragg, C R Levy
Comparison of performance of wood preservatives in laboratory and field tests of treated commodities
1993 - IRG/WP 93-20010
The purpose of laboratory tests for evaluating efficacy of wood preservatives is usually to establish toxic values against standard strains of wood decay fungi. Exposure conditions are usually chosen as optimal for fungal growth. Toxic values so determined serve as a guide as to expected performance of the preservative in field stake tests or in above ground exposure tests. Test material is select...
M E Hedley
Fundamentals on steam fixation of chromated wood preservatives
1988 - IRG/WP 3483
Weathering of treated wood directly after impregnation leaches up to 2% of copper-chromate-containing wood preservatives. Almost total fixation of Cr+6 is achieved by steaming the treated wood at 100°C to 120°C, preferably 110°C. To initiate such spontaneous fixation 85°C to 90°C inside the wood are essential, which requires heating times ranging from 20 to 80 min, depending on timber species...
R-D Peek, H Willeitner
Solidification - A viable option for the safe disposal of CCA treatment plant wastes
1993 - IRG/WP 93-50001-21
Treatment plant operations generate small quantities of waste materials contaminated with wood preservatives - for example, sludges, contaminated sawdust, yard dirt. A practical system involving the immobilisation of such wastes has been established to assist the operators to safely dispose to landfill sites. The results of cold water and hot dilute acid leaching regimes are described, which simul...
M R Gayles, D Aston
The treatment of Douglas fir fence posts: specification and compliance using new European standards
1999 - IRG/WP 99-20178
New European standards for the preservative pre-treatment of timber require the results of the treatment process to be specified and subsequently verified by examination of the treated timber for penetration and retention of the preservative. For penetration, the standards are restrictive in that there are only a limited number of options available to the specifier. Thus for ground contact service...
R J Orsler, H Derbyshire
Performance of preservative-treated wood not in ground contact
1975 - IRG/WP 254
Experimental sash units of Pinus strobus L. and Pinus resinosa Ait. wood were removed from a test fence at Ottawa, Canada after outdoor exposure of over 20 years. The units were superficially treated, prior to painting, with preservatives containing either copper naphthenate, pentachlorophenol or a combination of zinc naphthenate and pentachlorophenol. Results indicated that all treatments were ef...
J K Shields, J Krzyzewski
Field evaluation of the above-ground susceptibility of Pinus heartwood and untreated or treated sapwood to two species of Australian subterranean termites
1996 - IRG/WP 96-10147
Plantation-grown Pinus elliottii, Pinus caribaea and Pinus radiata specimens containing heartwood and untreated or preservative-treated sapwood were exposed above ground to the subterranean termites Coptotermes acinaciformis or Mastotermes darwiniensis near Sydney (NSW), Brisbane and Townsville (Qld), and Darwin (NT), using a variety of exposure techniques. Heartwood of Pinus elliottii and Pinus c...
M J Kennedy, J W Creffield, R H Eldridge, B C Peters
Patterns of decay in CCA-treated horticultural post populations - A fungus cellar simulation
1986 - IRG/WP 1286
The distribution of decayed posts in 10-, 14-, and 18-year-old vineyards supported a hypothesis to explain variability in intensity of decay found among posts in New Zealand horticultural properties. The development of decay patterns between samples in a simulated vineyard plot established in the Forest Research Institute fungus cellar gave additional support to the hypothesis that decay within la...
M E Hedley
Premature failure of CCA treated vineyard posts from brown rot
1993 - IRG/WP 93-10016
A survey of CCA (AWPA Type C) treated posts used as grape vine trellis supports, to determine the extent and type of decay was carried out at a terraced vineyard in the Hawkes Bay region of the North Island of New Zealand. Of 357 posts examined out of a total of 970 in the vineyard, 47% had moderate to severe decay or had failed, 20% had established decay, 10% had a trace of decay and 23% had no s...
R N Wakeling, A P Singh
An appraisal of the vertical distribution of attack of untreated and treated wood by warm water sphaeromatids at some tropical sites - A discussion paper
1986 - IRG/WP 4124
Examples of the vertical distribution of burrows of warm water sphaeromatids relative to tide levels and mud line from sites in India, Papua New Guinea and tropical Australia are discussed in detail. These data show clearly that these animals concentrate their attack of resistant natural wood or resistant treated wood in the tidal zone, particularly around Mean Sea Level. Supportive evidence from ...
J E Barnacle, L J Cookson, C N McEvoy
Electrochemical removal of Cu, Cr and As from CCA-treated waste wood
2001 - IRG/WP 01-50166-18
CCA-treated waste wood poses a potential environmental problem due to the content of copper, chromium and arsenic. This paper presents the results obtained by electrodialytic remediation of CCA-treated waste wood. It is found that more than 90% Cu, and approximately 85% Cr and As was removed from the wood during the remediation. Thereby the concentration of copper in the wood is reduced from app. ...
I V Kristensen, L M Ottosen, A B Ribeiro, A Villumsen
The recycling of CCA treated wood
1999 - IRG/WP 99-50140
Efforts to recover CCA from CCA-treated wood have been focused on the extraction of small wood particles. This work describes a method capable of removing CCA from retired CCA treated pine boards without. The percent removal of copper varied from 82% to 94%, 72% to 90% for chromium, and 84% to 98% for arsenic. The mechanical properties of boards after the extraction of CCA was reduced to 30% compa...
D P Kamdem
Laboratory evaluation of the termiticidal effectiveness of TanalithÒ 3485
1995 - IRG/WP 95-10109
The termiticidal effectiveness of the copper azole TANALITH 3485 was evaluated with the benchmark preservative TANALITH C in a laboratory bioassay using two species of subterranean termites, Mastotermes darwiniensis Froggatt and Coptotermes acinaciformis (Froggatt). Retentions of TANALITH 3485 tested were 0.15, 0.24, 0.285 and 0.40% m/m Cu and for TANALITH C 0.025, 0.05, 0.08 and 0.095% m/m Cu. Un...
J W Creffield, J A Drysdale, N Chew, N-K Nguyen
Lab and field test results for wood treated with polymeric alkylphenol polysulfide
2001 - IRG/WP 01-30268
A new wood preservative based on polymeric alkyphenol polysulfide (PXTS-A) is being evaluated in a series of laboratory and field tests and the results continue to show promise. A modified formulation (PXTS-B), which contains additives to reduce the viscosity, is being evaluated along with the original formulation. Soil block decay tests comparing PXTS-B with CCA-C indicate that PXTS-B is equally ...
J Goswami, A Abramson, R Buff, D D Nicholas, T Schultz