Borate diffusion in wood from rods and liquid product. Application to laminated beams
1988 - IRG/WP 3482
In the aim to use borate preservatives (fused rods and boracol) in fields of building construction other than external joineries, tests of diffusion of borate rods and secondary boracol, were carried out on different species of woods exposed to different moisture conditions. Tests were also applied on laminated beams very often subjected to high moisture contents and thus decay of rot fungi. Diffu...
D Dirol
Tests with ammoniacal copper and alkyl ammonium compounds as wood preservatives
1984 - IRG/WP 3299
Formulations based on copper and alkyl ammonium compounds in ammonia solution have been tested in a fungus cellar on Pinus radiata and Fagus sylvatica. This type of products gives promising results as wood preservatives, especially on hardwood and are safe to destroy by e.g. combustion. The best results were achieved with a dialkyl ammonium compound, Cu/octyldecyl dimethyl ammonium chloride (NH3)....
C-E Sundman
Soluble nutrient influences on toxicity and permanence of CCA preservatives in wood
1980 - IRG/WP 3144
The influence of soluble carbohydrate and nitrogenous components concentrated at evaporative surfaces of wood on the toxicity and permanence of CCA preservatives has been examined using soil-burial techniques. Nutrient concentrations in lime (Tilia vulgaris Hayne) have been shown to be associated with reduction of toxic limits of preservatives to an extent in which a 100% increase in preservative ...
B King, G M Smith, A Bruce
Comparison of methods for monitoring CCA fixation
1994 - IRG/WP 94-40023
The CCA fixation status in the outer 12.5 mm of pole sections of southern pine (Pinus sp.), red pine (Pinus resinosa) and lodgepole pine (Pinus contorta var. latifolia) were followed during fixation at 21°C under non-drying conditions by the following procedures: - Qualitative CrVI indication by the chromotropic acid spot test. - Quantitative CrVI in the expressate by the diphenylcarbazide method...
P A Cooper, Y T Ung, G Zanjani
Effect of vapour boron treatment on mechanical properties of wood based board materials
1992 - IRG/WP 92-3727
The mechanical properties of Medium density fibre board, Chipboard and Oriented strand board were investigated after treatment to two retention levels of boric acid applied as a vapour phase system. A range of mechanical properties were investigated. The vapour boron treatment does not have any significant effect on most of the mechanical properties of the boards. The exception is a reduction in i...
R Hashim, D J Dickinson, R J Murphy, J Dinwoodie
A laboratory study on effect of coating materials on leaching of copper from CCA treated wood
2001 - IRG/WP 01-50176
Components of CCA preservatives can leach into surrounding soil and water and have some effect on germination and growth of some plants. In this report, the effect of coating materials in reducing chemical concentration in the leachate were evaluated. Rubber wood blocks (Hevea brasiliensis) treated with CCA were fixed at room temperature at high humidity. After air dried, they were painted with co...
A Veenin, T Veenin
Rainfall simulation to assess CCA permanence
1991 - IRG/WP 2373
During experimental work on accelerated fixation of chromium containing preservatives a method has been developed which compares the degree of preservative levels of contamination of simulated preservative fixation in timber with the levels of simulated rainfall. This method uses commercial sized wood sections wetted in a way that simulates actual rainfall and relates the associated run-off contam...
P Warburton, J A Cornfield
The effect of composition on the effectiveness and fixation of CCA and copper/chrome preservatives. Part 1: Effectiveness. Part 2: Selective absorption and fixation
1973 - IRG/WP 324
A preliminary study of a wide range of copper-chrome-arsenic formulations indicates that the most effective are in the region, CuSO4 · 5H2O - 35 to 45 per cent; K2Cr2O7 - 40 per cent and above; As2O5 · 2H2O - 25 to 15 per cent or less. Effectiveness appears to depend more on the copper content than the copper - arsenic. Observations on selective absorption and leaching suggest that the chromium ...
D N R Smith, A I Williams
New boron-based biocides for the protection of wood
2002 - IRG/WP 02-30283
Boric acid and other simple inorganic oxides of boron are amongst the oldest wood preservatives currently in use. Their relatively low toxicity and broad-spectrum activity are just some of their desirable characteristics. The primary disadvantage associated with conventional boron-based preservatives is their lack of permanence in exposed applications. A collaborative project between CSIRO and the...
D G Humphrey, P J Duggan, E M Tyndall, J M Carr, L J Cookson
The relationship between the electrical resistance and fixation of water-borne CCA salts and pressure-treated wood
1991 - IRG/WP 3657
Two investigations at 22°C and 30°C have been carried out. The electrical resistance in the treated wood and chemical analyses of the remaining amount of unfixed copper, chromium and arsenic were investigated. Samples impregnated with water were used as references. To hold the samples moist during the investigation, each sample was wrapped in a polyethylene plastic foil immediately after impregn...
F G Evans, B Nossen
Field evaluation determining the toxic effect and diffusion properties of Impel, Improsol and TBTO-capsules in L-joints (spruce) for pretreatment application
1991 - IRG/WP 3641
Bonded joints (L-joints and T-joints) are especially at risk from water absorption (rain, condensation) over bare, unprotected radial wood surfaces (joggle joints). It is therefore quite certain that lasting protection against fungi attack cannot be guaranteed in the long term if the surface of coating is damaged. Therefore, in a field investigation, using L-joints (spruce) over a total period of ...
R Gründlinger, K Messner, O Janotta
The emission of boron compounds from treated particleboard
2000 - IRG/WP 00-40179
The emission of chemical vapours can be harmful both during treatment and service of wood and wood products. Samples of Standard particleboard (for interior use) were treated with trimethylborate, and a number of modified organo-boron compounds. Treated samples were placed immediately under a desiccator lid and air was drawn across each samples to 3 water traps. Water samples were taken after 30, ...
K M Filcock, P Vinden
Emissions from the combusting of boron and fluoride containing wood
1995 - IRG/WP 95-50040-18
The combustion properties of waste wood and wood residues containing wood preservatives were investigated in several test series after having been blended with untreated wood at a ratio of 1:4. The results for CFB, SF and boric salt show that, provided an optimized combustion, the concentrations of the stack pollutants correspond approximately with those found for untreated wood. Only during the c...
T Salthammer, H Klipp, R-D Peek
Leachability of didecyldimethylammonium chloride (a quaternary ammonium compound) from four wood species
1982 - IRG/WP 3204
Sapwood blocks prepared from red pine, ponderosa pine, southern yellow pine and hem-fir (a commercial mixture of western hemlock and amabilis fir) were treated with didecyldimethylammonium chloride, (an alkylammonium compound, AAC). After oven drying the blocks were vacuum impregnated with distilled water and subjected to a static leach cycle for 48 hours. The leachate was analyzed and the amount ...
J N R Ruddick, A R H Sam
Preservative treatment of two bamboo species Borak (Bambusa balcooa Roxb) and Talla (Bambusa tulda Roxb) by Boucherie method
2003 - IRG/WP 03-40262
Bamboo is widely used as a construction material in rural and urban areas of Bangladesh. It is perishable in nature and highly susceptible to the attack of borer, termites and fungi. As a result, bamboo products do not last long. This short life of bamboo is increasing demand thereby increasing pressure on our homestead and natural reserve of bamboo. For this reason, it is needed to make the bambo...
M N Islam, A S M A Huda, A K Saha, S M Mithue
Borate-treated food affects survival, vitamin B12 content, and digestive processes of subterranean termites
1990 - IRG/WP 1448
Toxicity of boron compounds was studied by analyzing survival rates and vitamin B12 contents in Formosan subterranean termites, Coptotermes formosanus Shiraki, that were exposed to dietary treatments for 10 days. The dietary treatments applied in moistened cellulose were (a) 0.05% boric acid equivalent (BAE) of disodium octaborate tetrahydrate, (b) 0.05% BAE of anmonium pentaborate plus sodium sul...
L H Williams, S I Sallay, J A Breznak
Effect of water repellents on leaching of CCA from treated fence and deck units - An update
1997 - IRG/WP 97-50086
In an earlier study, it was shown that CCA leaching losses could be reduced over an accelerated leaching and short term natural weathering exposures by post treatment application of a commercial water repellent. In this report, the effects of this coating and two commercial CCA solution water repellent additives are evaluated after two years of natural weathering. Wood boards were pressure treated...
P A Cooper, Y T Ung, R M Vicar
Susceptibility of CCA treated North American hardwoods to Chaetomium globosum decay
1998 - IRG/WP 98-10278
Seven species of hardwood, Beech (Fagus grandifolia), Basswood (Tilia americana), Maple (Acer rubrum), Oak (Quercus rubra), Trembling Aspen (Populus tremuloides), White birch (Betula papyrifera) and Yellow poplar (Liriodendron tulipifera) were vacuum or pressure impregnated with CCA, at four retention levels. The CCA was allowed to fix in the wood at 35°C. Red pine (Pinus resinosa) was also inclu...
U Srinivasan, Y T Ung, P A Cooper
Waterborne preservative treatability of tamarack (Larix laricina (Du Roi) K.Koch)
1998 - IRG/WP 98-40112
Eastern larch or tamarack (Larix laricina (Du Roi) K.Koch) lumber from New Brunswick, Canada was evaluated for preservative treatability with chromated copper arsenate (CCA-C) and ammoniacal copper arsenate (ACA). The fixation and leaching characteristics of CCA-C treated tamarack sapwood and heartwood were also evaluated. CCA-C penetration into both sapwood and heartwood was poor. ACA fully penet...
A Taylor, Y T Ung, P A Cooper
Kinetics and mechanism of fixation of Cu-Cr-As wood preservatives. Part 6: The length of the primary precipitation period
1975 - IRG/WP 359
The end of the primary precipitation fixation period of CCA preservatives coincides with the first peak in pH versus time. This offers a simple way of estimating the duration of the period. The duration is determined by a number of factors and their interactions, the most important of which are: wood species (anatomy, natural pH, accessibility of reducing agents), preservative type, preservative c...
S-E Dahlgren
Chromium in wood preservation: Health and environmental aspects
1978 - IRG/WP 3120
The majority of water-borne salts in current use contain hexavalent chromium, usually as dichromate or chromium trioxide. In about 1913 it was suggested that chromates, phosphates or borates could be added to the sodium fluoride and dinitrophenol mixtures then in use in order to inhibit corrosion. Dichromates were found to be most suitable and the resulting mixture known as Thriolith and later Tri...
T R G Cox, B A Richardson
Heat transfer and wood moisture effects in moderate temperature fixation of CCA treated wood
1994 - IRG/WP 94-40022
Practical aspects of heat transfer and fixation of wood exposed to drying conditions after CCA treatment are considered. The rates of heat transfer and CCA fixation are substantially influenced by the cooling effect of water evaporating from the wood surface when drying occurs during fixation. At least in the early stages of fixation, the wood temperature approaches the wet bulb temperature, rathe...
J Chen, M Kaldas, Y T Ung, P A Cooper
Laboratory termite testing of copper boron tebuconazole
2000 - IRG/WP 00-20192
The American Wood Preservers' Association laboratory choice and no choice termite test (AWPA E1-97) was performed on a formulation of copper azole, which is comprised of copper, boric acid, and tebuconazole. The formulation tested has a ratio of copper:boric acid:tebuconazole of 25:25:1. So as to examine the impact of leaching, the southern yellow pine wafers were treated with and without...
R F Fox, E A Pasek, J Patel
Difference of CCA efficacy among coniferous wood species
1990 - IRG/WP 3601
Wood blocks of Cryptomeria japonica, Tsuga heterophylla, and Pinus radiata successively extracted with n-hexane, ether, and methanol were treated with various concentrations of CCA type 3, which were subjected to the decay by Tyromyces palustris. The weight loss were different among species and kinds of extraction. Cryptomeria japonica treated with CCA had higher fungal resistance than Tsuga heter...
K Yamamoto, M Inoue
A study of poplar LVL durability improvement:
1999 - IRG/WP 99-40148
The aim of this study was to optimise the durability of LVL panels by adding boron during the gluing process. Poplar veneers (2,6 mm thickness ) were selected by ISORY a French company . Two types of glue were tested : Phenol resorcine and Melamine Urea Formaldehyde. Each of them was mixed with various concentrations of borax (for the first one) and Boric acid(for the second one). Mechanical prope...
B Charrier, V Bridaux, N Fauroux, F Charrier