Effects of Moisture Content and Species on Penetration of Liquid in Laser Incised Lumber by the Passive Impregnation Method
2008 - IRG/WP 08-40408
Penetration of liquid by passive impregnation method for Douglas-fir (Pseudotsuga menziesii Franco), sugi (Cryptomeria japonica D. Don) and Japanese larch (Larix leptolepis Gordon) were studied. Effects of initial moisture content of sugi (16, 43 and 70% moisture content) on liquid penetration by the method were also studied. Dried Douglas-fir and sugi, and green Japanese larch and sugi were treat...
N Hattori, M Nazrul Islam, K Ando, H Yamauchi
Comparison of laboratory and natural exposure leaching of copper from wood treated with three wood preservatives
2008 - IRG/WP 08-50258
Standard and non-standard laboratory and field leaching tests were used to compare copper leaching from wood treated to above ground and ground contact specified retentions for three wood preservative systems, CCA-C, ACQ-D and a micronized copper formulation with quat DDAC as co-biocide. Copper leaching was highest for the ACQ formulation. Percent leaching was lowest for the micronized copper sy...
P A Cooper, Y T Ung
Accelerated H3 above-ground decay trials in Australia
2009 - IRG/WP 09-20411
An above-ground H3 fungal field trial was installed at five sites (3 in Australia, 2 in New Zealand), with the aim of finding a method that would shorten the time required for evaluating new preservatives and protection systems. One-quarter of the H3 preservative retentions were mostly installed, as first results suitable for registration occur when these reach 70% soundness. Chemical analysis of ...
L J Cookson, J Carr
Analysis on dynamics of basidiomycetes in decayed wood by a method using non-specific amplification of DNA
2009 - IRG/WP 09-20426
A combination of non-specific amplification of DNA by Phi29 DNA polymerase and specific amplification of the internal transcribed spacer (ITS) region of ribosomal DNA (rDNA) by polymerase chain reaction (PCR) was applied to elucidate the ratio of basidiomycete species inhabiting decayed wood from an outdoor bench. After more than 8 hours incubation with Phi29 DNA polymerase, concentration of DNA ...
T Wada, K Igarashi, M Samejima
Laboratory and above ground exposure efficacy of silicon-boron treatments
2009 - IRG/WP 09-30510
The study deals with silicon compounds, namely tetraethoxysilane (TEOS), phenyltriethoxysilane (PhTES) and methyltriethoxysilane (MTES) at concentrations of 23, 16 and 10% in combination with 1.2-1.5% boric acid. The aim with the study was to combine the chemical approach with the necessary biological tests of the impregnated wood. The tested silicon-boron combinations ensured mass loss less than ...
N Terziev, D Panov, A Temiz, S Palanti, E Feci, G Daniel
A fast and economic method to produce grey wooden surfaces for decking and cladding: preliminary results
2009 - IRG/WP 09-40474
Uncoated wood is commonly used in France for cladding and decking to minimise maintenance. However wood surfaces progressively turn grey due to exposure to sunlight and water. This grey colour develops after several months depending on the wood species and the exposure: in the northern hemisphere surfaces facing south and west are most exposed and turn grey more rapidly than those facing north and...
L Podgorski, V Georges, I Garmendia, B Sánchez Sarachu
Natural Durability of Fence Poles from Fourteen Semi-Arid Land Species after Six-Month Exposition
2010 - IRG/WP 10-10724
A sample of thirty fence poles from each of fourteen tree native species from Northeast Mexico were tested in ground contact in a wood-cemetery area located in Linares, Nuevo Leon, Mexico. The samples were submitted to six treatments (control, debarked, chemical treated, used cooking oil, thermal and creosote) and randomly distributed in five blocks. The effectiveness of using a bark gauge tool â€...
A Carrillo, F Garza, V Bustamante, S Sandoval, H VillalĂłn
Decay Resistance of Maple (Acer Insigne) Wood Against White Rot
2010 - IRG/WP 10-10740
In this study, the decay resistance of maple (Acer insigne) in natural state and treated with ACC (Acid copper chromate) was investigated against the white rot fungus (Coriolus versicolor). ACC is a kind of water borne preservatives that was used in this study for treating specimens under vacuum and pressure (Bethell procedure) with 3 percent concentration. In conducting mentioned evaluation, koll...
V Tazakor Rezaei
Diagnosis of failures in wood beams from historical house in Banská Štiavnica – Relations between ultrasonic measurements and bending properties
2010 - IRG/WP 10-20437
Various degrees of rot and other damages in ceiling beams with dimensions of 6500-8800 x 160-200 x 240-310 mm (length x height x width) situated in one historical bourgeois house in the UNESCO town Banská Štiavnica, Slovakia were determined visually and by the PUNDIT-plus ultrasonic device. Subsequently, for seventeen of the most bio-damaged fir (Abies alba Mill.) beams chosen for exchange were ...
L Reinprecht, M Pánek
Development of microbiological test methods for the wooden packaging of foodstuffs
2010 - IRG/WP 10-20453
Whereas different sampling methods already exist for analysing contaminated surfaces or packaging made of plastic or paper, there is no methodology that enables the sampling and quantification of microorganisms in packaging made of wood. The objective of this study was to compare the most commonly used microbiological methods and to develop a reliable quality control test adapted to wooden packagi...
I Le Bayon, H Callot, M Kutnik, C Denis, A-M Revol-Junelles, J-B Millière, M Giraud, M Gabillé, N Passédat
Service life prediction for exterior timber cladding
2010 - IRG/WP 10-20460
This discussion paper considers service life prediction for timber and the work within the pan-European WoodExter project. The project aims to develop a model for service life prediction of exterior timber cladding, to enable better end use selection of material suitable for delivering the required service life of cladding and to provide information for professionals wanting to understand and use ...
E Suttie, F Englund
Mobility of Copper from MCQ in Shell-Treated Wood Exposed Above Ground
2010 - IRG/WP 10-30534
Most Canadian treated decking in service has been given just a thin shell of preservative treatment but it has still performed very well. This is because copper migrated into checks and prevented germination of basidiospores on the freshly exposed untreated wood. Unlike soluble copper systems, MCQ has its copper primarily in the form of small basic copper carbonate particles. For MCQ to be effecti...
R Stirling, P I Morris
Repairing of wooden elements by beta-method using carbon, steel or beech rods
2010 - IRG/WP 10-40488
Presented paper is focused on repairing of wooden elements by Beta joints reinforced with carbon, steel or beech rods, and on comparing the efficiency of these joints with traditional carpentry joints. In model laboratory experiments have been determined the bending strength (fm) and the modulus of elasticity (E) of control or original elements (fm-Control; Eo) from Norway spruce (Picea abies Kars...
L Reinprecht
Biological degradation of acetylated wood after 18 years in ground contact and 10 years in marine water
2010 - IRG/WP 10-40522
This paper addresses the resistance to biological degradation of acetylated wood.
Firstly, it presents results from an EN 252 test after 18 years’ exposure. The test is still running in Nordic NWPC test fields, Simlångsdalen in Sweden and Viikki in Finland. Results from this test were presented after 5 years’ exposure ( IRG/WP 97-30139), and showed that the resistance of acetylated wood wit...
P Larsson Brelid, M Westin
Quantitative design guideline for wood outdoors above ground applications
2011 - IRG/WP 11-20465
This paper describes the background and principles behind an engineering design guideline for wood in outdoor above ground applications, i.e. use class 3 according to EN 335. The guideline has been developed in the European research project WoodExter and can be seen as a first prototype for a quantitative design tool in the area of wood durability. It is based on a defined limit state for onset of...
S Thelandersson, T Isaksson, E Suttie, E FrĂĽhwald, T Toratti, G GrĂĽll, H Viitanen, J Jermer
A Method for Studying Boron Redistribution and Leaching in Timber Framing
2011 - IRG/WP 11-20476
In typical New Zealand timber framed house construction, the timber framing has a vapour permeable building wrap applied to the exterior and a cladding applied over 20 mm battens. An interior lining usually of gypsum plasterboard is then fixed once the timber framing has a moisture content of < 20%. Timber framing within the building envelope is not expected to be wet in-service or exposed to a le...
J A Drysdale, N Marston, M E Hedley
Slice - Cut and Analyze Laser Microdissection (LMD): A method to produce sample material from modified wood for chemical quality analysis
2011 - IRG/WP 11-20478
Wood modification with its various systems is an established way to enhance a wood products’ service life in outdoor applications. Per definition, selected material properties are enhanced by means of modification without producing toxic substances or residues during service life and combustion afterwards. The systems of impregnation modification include a physical and often chemical alteration ...
K Zimmer, E Larnøy, A Treu, M Fongen
Effect of P/F ratio, PF concentration and treating method on boron leaching from wood treated with PF modified boron compounds
2011 - IRG/WP 11-30559
In order to immobilize boron in wood, three kinds of resol-type phenol-formaldehyde (PF) resin with different P/F ratios were synthesized in laboratory and incorporated with three types of boron compounds to treat wood. The used boron compounds included boric acid (BA), borax (BX) and disodium octaborate tetrahydrate (DOT). The leaching test of boron from wood blocks was performed according to the...
Liping Yu, Jinzhen Cao
Comparison of rates of wood decay from four different field test protocols following 4-5 years exposure at a site in New Zealand
2011 - IRG/WP 11-30565
The rate of decay of Pinus radiata was evaluated using four different field test protocols at a site near New Plymouth, New Zealand. The average Scheffer index was 86 over the five year period of testing. The field tests were an in-ground stake test (AWPA Std E7-01) and three above ground tests – lap-joint (AWPA Std E16-98), decking (AWPC protocol) and ground proximity tests (AWPA Std E18-06) T...
P Lobb, K Day, A Siraa
Performance of Creosote/Chlorothalonil Preservatives
2011 - IRG/WP 11-30580
The addition of chlorothalonil to P2 creosote was found to increase the durability of southern pine in a series of ground contact stake tests. At retentions lower than those specified in the AWPA Standards, performance was increased when the creosote was amended with chlorothalonil. This indicates that lower creosote retentions may be required for as good or better ground contact when the amende...
H M Barnes, M G Sanders, G B Lindsey, T L Amburgey
Using an accelerated laboratory method to evaluate Aureobasidium pullulans colonization on painted surfaces and underlying wood substrate
2012 - IRG/WP 12-20480
Mold growth on painted surfaces can lead to premature paint film failure and is unsightly. Aureobasidium pullulans has been identified as a major cause of black stain on surfaces painted with acrylic or latex paints. In this study, an accelerated laboratory method developed by Zabel and Horner (1981) was used with modifications to the type of agar used and sample evaluation methods. A study was ...
C Schauwecker, L Burns, A Preston
Determination of Izod Impact Strength on Wood: A Suitable Method to Detect Fungal Decay in Protective Effectiveness-Screenings of Wood Preservatives
2012 - IRG/WP 12-20484
For testing a large number of different substances regarding fungicide properties, the reduction of the decay test duration is advantageous. In the present paper the suitability of a method for testing plastics using an impact testing machine was examined. The results clearly show that the fungal attack of European beech by the white-rot fungus Trametes versicolor leads to a decrease of izod imp...
H Delenk, M Zauer, A WagenfĂĽhr
Nano structural properties of La2O3-Beech Wood Flour With XRD technique
2012 - IRG/WP 12-40607
This research was considered to study various properties of the Lanthana mixed with beech wood flour (BWF), as a new structure. For this purpose, La2O3 powders in the BWF have been obtained by sol-gel method using simultaneous gelation of all cations. La2O3 - BW samples are analysed by X-ray diffraction .The obtained results showed the formation of nano crystalline La2O3 phases. The average crys...
M Ghorbani Kokandeh, I Bahamni, A Bahari
Development of a quality control assessment method to predict properties of heat treated wood
2012 - IRG/WP 12-40611
Heat treatment has been used to improve properties of non durable European species. Chemical modification of some of the wood components provides improved dimensional stability and biological performance against decay fungi while mechanical properties such as modulus of rupture are reduced. Quality control of commercially made thermally treated wood is one of the major challenges to allow its indu...
M Chaouch, K Candelier, S Dumarcay, A PĂ©trissans, M PĂ©trissans, P GĂ©rardin
A case study of investigating fungi that affect traditional Japanese shake roof with/without copper plates
2013 - IRG/WP 13-10810
A Japanese traditional shake roof is made from split logs. To keep the roof long, copper (Cu) plates are often inserted between the shakes. It has been thought that Cu elements from copper plates would flow out when a shake roof is exposed to rain and inhibit growth of wood rotting fungi. Actually there are some examples where the Cu plates seem to be effective in preventing fungal damage, but on ...
T Wada, Y Fujiwara, Y Fujii, R Kigawa