Your search resulted in 1687 documents. Displaying 25 entries per page.
Laboratory methods for assessing the resistance of wood plastic composites to fungal attack.
2006 - IRG/WP 06-20340
Wood plastic composites (WPC’s) have many attractive material features including dimensional stability and resistance to moisture, but the wood in these materials remains susceptible to fungal attack. Assessing WPC decay resistance in laboratory trials has proven difficult because the slow moisture sorption characteristics of this material do not allow for sufficient fungal attack over the trad...
J J Morrell
Testing durability of treated wood according to EN 252. Interpretation of data from Nordic test fields
2006 - IRG/WP 06-20341
To evaluate the effectiveness of new wood preservatives intended for treated wood in ground use there is a European standard, EN 252. The test shall run for five years before any formal interpretation of the results can be made.
Due to environmental concerns, the use of wood preservatives based on copper, chromium and arsenic (CCA) has been restricted in recent years. As a consequence of restrict...
M L Edlund, F G Evans, K Henriksen, T Nilsson
L-joint based testing for service life prediction of exterior plywood in out of ground contact conditions
2006 - IRG/WP 06-20342
Good biological performance of several plywood types in exterior conditions is most probably related to altered wood moisture behaviour compared to solid wood. Therefore a test set up was developed, using EN 330 L-joint testing methodology, to facilitate differentiation of plywood for exterior applications.
The proposed test set up is an adaptation of an accelerated L-joint method introduced by V...
J De Smet, I De Windt, J Van Acker
Performance of boron-treated radiata pine in above ground field tests in New Zealand
2006 - IRG/WP 06-30406
Boron treatment was approved for exterior, above ground use in New Zealand in 1958, provide treated commodities were painted with a three-coat paint system. Above ground tests of rail units and L-joints were established at the NZ Forest Research Institute (now Scion) between 1967 and 1980 to monitor performance of boron treatment in relation to that of untreated and CCA-treated timber.
Results sh...
M Hedley, D Page
Measuring Soil Respiration as a New Approach to Describe the Interaction Between Wood (Treated and Untreated) and Microbiologically Active Soil
2006 - IRG/WP 06-20344
Soil respirometry was employed to examine the relationship between both the performance of copper organic preservatives in contact with and the amount of carbon dioxide evolved from soil and the effect of wood treated with preservatives on carbon turnover in soil. Wood was treated with a range of copper organic preservatives intended for use in ground contact as well as an organic preservative in...
I Stephan, W Mierke
High-energy multiple impact (HEMI)-test – Part 1: A new tool for quality control of thermally modified timber
2006 - IRG/WP 06-20346
Thermal modification processes improve durability and dimensional stability of wood, but the strength properties, especially the dynamic ones, are compromised and need to be considered with respect to industrial quality control. Results from standard dynamic strength testing, such as impact bending tests, suffer from high variability, and therefore require a high number of replicates. To overcome ...
C Brischke, A O Rapp, C R Welzbacher
How to win friends and influence the market — Service Life Prediction and performance-based durability assessments of wood products in construction
2006 - IRG/WP 06-20348
Due to direct and implied demands from the market and from e.g. the EU Construction Products Directive, the need to supply service life estimates for building products is growing. For several years, a development of Service Life Prediction (SLP) methodologies has been going on, but the awareness of this development has hitherto reached only a very limited extent in the wood sector. For materials w...
F Englund
Standard Test Methods for Wood Preservatives by Laboratory Agar-Block Test
2006 - IRG/WP 06-20350
Wood is one of the most valuable and versatile resources for all sorts of constructional purposes. But timber in its various forms is subjected to several types of deterioration. This standard lays down the method for the laboratory determination of threshold value of wood preservatives against fungi. Most chemicals are initially tested for their ability to control decay fungi in agar-block tests....
P K Sarker, M A Rahman, M R Bulbul, T Das, G N M Ilias
Copper borate for the protection of engineered wood products
2006 - IRG/WP 06-40334
Copper borate was evaluated for use in protecting oriented strand board (OSB) from mould, decay, and termites. Aspen OSB bonded with either phenolic or isocyanate resin was treated with several formulations of copper borate at various loadings from 0.26 to 4 percent by weight. These panels were then tested to determine the impact of the preservative on mechanical properties as well as resistance ...
R Smart, W Wall
Tree crown architecture: a tool for decay resistance evaluation
2013 - IRG/WP 13-10793
The variability of natural durability contributes to the bad perception of some wood end-users. In our search, we need to adjust our methods and strategies to estimate natural durability and extract higher value from wood resources. Architectural analysis is essentially a detailed, multilevel, comprehensive and dynamic approach to plant development. Numerous biological process which impact some wo...
N Amusant, J-B Anouhé Say, A Amissa, J Beauchène, F Niamké, E Nicolinni
Further discussion of biological durability assessments of acetylated wood from several European institutes
2006 - IRG/WP 06-40340
In the last decade, interest in the development of wood modification systems has increased in Europe. Alongside several industrial initiatives for heat treatments, there have also been scaling up and pilot plant projects for chemical wood modification. Between 2000-03, the European Commission funded the "Thematic Network on Wood Modification". This paper features a re-evaluation of work undertaken...
D Jones, W Homan, F Bongers
Effect of fumigation with Sulfuryl Difluoride on wood inhabiting fungi, a laboratory test
2006 - IRG/WP 06-30410
Special methods are necessary for the control of wood destroying organisms in the preservation of monuments and historic buildings because of the conservation of their originality and uniqueness.
The control of wood destroying organisms can be realized with conventional liquid wood preservatives or alternative methods. One of these methods is the fumigation. One fumigant, which was in the past of...
A Pfeffer, W Unger, G Fröba, G Binker
Surface and system treatments of wood for outdoor use
2006 - IRG/WP 06-30412
The project “Surface and system treatment of wood for outdoor use” was initiated the summer 2001. The project evaluates environmentally friendly preservatives and water borne coating systems, to find the best protection for timber indented for outdoor use. The wood species selected as test material were pine and spruce. The different treatments were exposed in several outdoor accelerated tests...
B Jacobsen, F G Evans
Assessment of the Envelope Effect of Three Hot Oil Treatments: Resistance to Decay by Coniophora puteana and Postia placenta
2006 - IRG/WP 06-40344
Timber of Corsican pine (Pinus nigra var. maritima) and Norway spruce (Picea abies) was treated in hot linseed oil, rapeseed oil and a proprietary resin derived from linseed oil. The samples were immersed in oil or resin under reduced pressure at temperatures of 180°C and 200°C. Very high uptakes of the oils or resin were recorded for pine, while spruce showed lower weight percent gains, below...
M J Spear, C A S Hill, S F Curling, D Jones, M D C Hale
Furfurylated wood - An alternative to Preservative-treated wood
2006 - IRG/WP 06-40349
Chemically modified wood is currently being marketed as a non-toxic alternative to traditional preservative treated wood (wood impregnated with biocides). Over the last decade the authors have developed modernised processes for wood modified by furfurylation. These new systems do not add metals or halogens to the product, which is important for an environmentally acceptable product. This presentat...
S Lande, M H Schneider, M Westin, J Phillips
Wood-Plastic Composites and the Durability Dilemma: Observations from the Field
2006 - IRG/WP 06-40351
Wood-Plastic Composites (WPCs) used for decking, window & door moldings have experienced dramatic growth in North America over the last several years, with annual production increasing at rates greater than 20% per annum since 1998. A key factor contributing to this growth has been the successfully communicated message that they are "virtually maintenance free". The common perception being t...
M J Manning, F M Ascherl, M E Mankowski
Resistance of DMDHEU-treated pine wood against termite and fungi attack in field testing according to EN 252. Results after 30 months
2006 - IRG/WP 06-40354
The aim of this study was to determine the effectiveness against decay and termite attack of pine sapwood treated with pure and modified DMDHEU in a field test according to European Standard EN 252. Some of the treatments tested were able to increase, within the period of the test reported (30 months), the resistance of the wood both to micro-organisms and termites. The curing process seems to be ...
S Schaffert, L Nunes, A Krause, H Militz
Laboratory Leaching Tests to Study the Effects of Post-Treatment Storage Periods on CCA Leachability and Fixation in Treated Permeable and Refractory Malaysian Hardwoods
2006 - IRG/WP 06-50240
The biological resistance and environmental safety of CCA-treated wood relies on the extent of post-treatment storage fixation of CCA in wood prior to being utilized. A study on the comparative leachability (fixation) of CCA-treated refractory and permeable heartwoods of 3 Malaysian hardwoods subjected to different post-treatment storage (fixation) periods of up to 4 weeks, at 2 laboratory leachin...
A H H Wong, H C Lai, N P T Lim
Biological Protection of Composite Panel from Moulds and Decay
2007 - IRG/WP 07-10612
Composite panels, such as oriented strand board (OSB), are widely used in house construction in North America. These structural panels are normally made of non-durable wood species and are susceptible to moulds and decay when exposed to wet conditions. Building envelope failures due to moulds, decay or poor construction practices can negatively impact the image of wood. To ensure durability of com...
Dian-Qing Yang, Xiang-Ming Wang, Hui Wan
Phenol oxidase activity and one-electron oxidation activity in wood degradation by soft-rot deuteromycetes
2007 - IRG/WP 07-10615
Wood degradation, one-electron oxidation activity as assayed by ethylene generation from 2-keto-4-thiomethylbutyric acid (KTBA), and phenol oxidase activity were measured in cultures of six deuteromyce fungi, with glucose or wood as the carbon source. The four fungi that degraded Japanese beech wood had higher one-electron oxidation activities in wood-containing cultures than in glucose-containing...
H Tanaka, M Yamakawa, S Itakura, A Enoki
Current state of world standardization in the toxicometric methods for testing of wood preservatives
2007 - IRG/WP 07-20354
The paper presents an outline of the history of forming standardized toxicometric methods for testing of wood preservatives in the world during last 100 years. Numerous studies resulted in three main methods which are currently used for official and basis assessment of biocides:
- agar-block method in Europe (EN 113);
- soil-block method in the USA and Pacific countries (ASTM D 1413);
- modifi...
J Wazny
A New Decay Hazard Map for North America Using the Scheffer Index
2008 - IRG/WP 08-10672
Wood decay experts in the USA and Canada use the Scheffer Index for above-ground wood decay potential to decide among design and treatment options to ensure the durability of wood construction. This paper provides an updated North American decay hazard map and includes data on Central America. Index values calculated from recent climate data are higher than published values due to directional or c...
P I Morris, J Wang
Wood decay fungi from New Zealand ‘leaky’ buildings: PCR identification and laboratory decay tests of wood preservative-treated Pinus radiata (Part 1)
2007 - IRG/WP 07-10620
Fungi colonising Pinus radiata D. Don framing timber of ‘leaky’ New Zealand buildings were isolated to produce pure cultures. Mycelia from these cultures on agar media were collected to extract DNA. To identify the fungi to the species level, polymerase chain reaction (PCR) with primer pairs ITS1-F and ITS4 were performed followed by sequencing of the internal transcribed spacer (ITS) region. ...
D Stahlhut, R L Farrell, R Wakeling, M Hedley
Detecting fungal DNA in treated and non-treated wood
2007 - IRG/WP 07-10621
Isolating fungi from wood has long involved culturing on selective media followed by identification using various keys. This process can be cumbersome, costly, and, most importantly, not always capable of detecting all of the fungi present. The recent development of molecular methods for isolation and identification of fungi has created tremendous opportunities for expanding our knowledge of the...
C Freitag, M Freitag, J Morrell
The use of X-ray diffraction for analyzing biomodification of crystalline cellulose by wood decay fungi
2007 - IRG/WP 07-10622
X-ray diffraction (XRD) is based on the creation of an interference pattern by x-rays when they encounter a regularly spaced matrix. In wood, this process has been used to determine, among other things, the average width of the cellulose microcrystals, the percent of crystalline cellulose within the wood, and can be used to examine the changes in these parameters during degradation. Enhanced under...
C Howell, A C Steenkjær Hastrup, J Jellison