Your search resulted in 2591 documents. Displaying 25 entries per page.
Preliminary results of investigations on screening test of chemical compounds suitable for the preservation of lignocellulosic materials against biodeterioration
1976 - IRG/WP 262
This paper investigates the possibilities of reducing the time needed for the determination of the effectiveness of chemical compounds from the point of view of their eventual application to lignocellulosic materials for preservation against decay and soft-rot....
K Lutomski, S S Neyman
Iron promotes decay capacity of Serpula lacrymans
1993 - IRG/WP 93-10008
The influence of iron and iron compounds on the decay capacity of Serpula lacrymans was studied. Mass losses of pine wood caused by dry rot fungus were increased when FeSO4 was added into the culture medium or when there were iron nails or stone wool on the culture medium. This supports the hypothesis that iron in stone-based building materials is one reason for the increased decay capacity of Ser...
L Paajanen
Gloeophyllum trabeum and Gloeophyllum abietinum, the most frequent brown rot fungi in fir wood joinery
1999 - IRG/WP 99-10319
In Croatia the primary raw material for joinery production is silver fir wood (Abies alba Mill). L-joints made of home-grown fir sapwood and prepared according to EN 330: 1993 were used to establish the infection and colonisation of micro-organisms, particularly wood decay fungi, to compare the performance of untreated and 1% TnBTO treated L-joints. The L-joints were coated with two types of coat,...
R Despot, M Glavas
European standardization for wood preservation
1989 - IRG/WP 2335
G Castan
Collaborative soft rot tests: Proposals for a standardized soil burial test
1971 - IRG/WP 201
A F Bravery
Report on International Conference on Marine Biodeterioration, Goa, India, January 1986
1986 - IRG/WP 4127
At the International Conference on Marine Biodeterioration - Advanced Techniques Applicable to the Indian Ocean, there were a number of papers relevant to the aims of Working Group IV of IRG. Abstracts of these papers and a brief commentary on the conference are presented....
S M Cragg
Response of the Formosan Subterranean Termite (Coptotermes formosanus) to Cellulose Insulation Treated with Boric Acid in Choice and No-Choice Tests.
2004 - IRG/WP 04-10532
The tunneling ability of the Formosan subterranean termite Coptotermes formosanus Shiraki through a cellulose insulation material containing11.1% boric acid was tested in choice and no-choice bioassays. We examined tunneling behavior and mortality of termites exposed to treated and untreated insulation material in miniature simulated wall voids. In a choice test termites tunneled through untreat...
M E Mankowski, J K Grace
The influence of crystalline and amorphous cellulose on extracellular hydrogen peroxide production by brown-rot fungi
1991 - IRG/WP 1482
The production of hydrogen peroxide (H2O2) has been suggested to play a key role in the degradation of wood by wood-rotting fungi. The production of extracellular hydrogen peroxide was studied by a quantitative method which detects the oxidation of the 2,2-azinobis(3-ethylbenzthiazoline-6-sulphonic acid) (ABTS) by H2O2 and horseradish peroxidase (HRP) in liquid culture medium. The carbon sources u...
A-C Ritschkoff, L Viikari
Results of co-operative studies on determining toxic values against wood-destroying Basidiomycetes. Preliminary report to Sub-group members
1986 - IRG/WP 2271
A F Bravery, J K Carey
The leaching of copper, chrome and arsenate from CCA-impregnated poles stored for ten years in running water
1978 - IRG/WP 3122
There is no evidence to indicate that the chromium and copper components are leached from the outermost 5 mm of sapwood in poles impregnated with Boliden K33 and Tanalith C and stored in running water for ten years. The arsenic component, however, seems to be leached out during the first few months to an extent of about 20% of the initial amount. The leaching time is dependent on the preservative ...
F G Evans
Decay resistance of wood removed from poles treated with Trichoderma
1989 - IRG/WP 1386
Wood blocks removed from a distribution pole previously treated with a biological control product (Binab FYT pellets) were exposed in soil block tests to selected basidiomycetes. The blocks were removed from regions of poles where Trichoderma colonization had been confirmed by extensive sampling and computer mapping of microbial inhabitants. The results indicate that material from pole interiors c...
A Bruce, B King, T L Highley
Effects of a chitin synthesis inhibitor on spore germination of the decay fungi Gloeophyllum trabeum and Poria tenuis
1986 - IRG/WP 2253
This study sought to determine the effect of a chitin synthesis inhibitor - Polyoxin D, on spore germination and early hyphal development of a brown rot and a white rot fungus in-vitro. Polyoxin D is a competitive, substrate-analogue type of chitin synthtase inhibitor (2). The drawbacks to use of such a compound as a wood preservative tie. cost - $20,000/g, possible leaching or degradation) might ...
E L Schmidt
Reticulitermes lucifugus Rossi, and its damages in Turkey
1982 - IRG/WP 1152
The moist-wood termite, Reticulitermes lucifugus Rossi, is generally observed on the wood material which has a direct contact with the soil as trunks and fence stakes. It was reported to be found in some provinces in Turkey. The termite has been seen in these areas so far at the endemic level, but any considerable damage or epidemy has not yet been reported. Considerable damages were observed on t...
O A Sekendiz
Biological Durability of Laminated Veneer Lumber from Durable and Non-Durable Wood Species
2005 - IRG/WP 05-10567
Laminated Veneer Lumber (LVL) was laboratory manufactured using veneers from decay and non decay resistant species in order to evaluate changes in the durability as a result of the LVL manufacturing process, and to test if the mixing of decay resistant species and non decay resistant species can improve durability. Laboratory soil block test and field test were conducted. The durability of solid w...
P Nzokou, J Zyskowski, S Boury, D P Kamdem
Monographic card on Antrodia serialis
1984 - IRG/WP 1145
G Seehan
Test procedure to determine the effect of timber substrate on the effectiveness of different preservatives in sea-wate
1975 - IRG/WP 414
R A Eaton
Studies of the distribution and degradation of tributyltin naphthenate in double-vacuum treated wood
1983 - IRG/WP 3230
The effects of forced solvent evaporation by kilning redwood (Pinus sylvestris) that has been double-vacuum treated with tributyltin naphthenate (TBTN) have been investigated. Contrary to previous studies reported, it has been shown that forced evaporation can have a considerable influence on the losses of the fungicide. It has been found that, whether the solvent is allowed to evaporate slowly or...
J Jermer, M-L Edlund, W Hintze, S V Ohlsson
On site test for indicative determination of leaching of components of preservatives from treated timber. Part 2: New data on CCA-C, CC and CCB treated timber
1994 - IRG/WP 94-50025
The 'on site test' was published at the IRG meeting in Cannes in February 1993 (IRG/WP 93-50001/12). Since this publication many on site tests were performed parallel to so-called shower tests. The correlation between the test results of the on site tests and the shower test has been established more clearly. For chromium the correlation between both tests is indistinctive of pre...
W J Homan
Effectiveness and synergistic effects between copper and polymer betaine
1996 - IRG/WP 96-30097
Different formulations of "Copper Amine" and Polymer Betaine were studied. During laboratory tests a synergism between both active ingredients against soft rot and dry rot has been found. The efficacy against soft rot according to the "BAM method" and the European Standard ENV 807 depends only on the amount of copper. Long term tests in a fungus cellar for determining the relative protective effec...
H Härtner, V Barth
Decay fungi in Finnish houses on the basis of inspection samples from 1978 to 1988
1989 - IRG/WP 1401
A summary of the causes and sources of fungal damages was made on the basis of decay samples and sample information sent to the Forest Products Laboratory of the Technical Research Centre of Finland (VTT) between 1978 and 1988. About 50-130 decay cases in wood structures were studied annually. In almost 50% of all fungusdamage cases the cause was Serpula lacrymans. The proportion of Coniophora put...
L Paajanen, H Viitanen
Laboratory culturing and decay testing with Physisporinus vitreus and Donkioporia expansa orginating from identical cooling tower environments show major differences
1996 - IRG/WP 96-10184
Both Basidiomycete fungi Physisporinus vitreus (Pers.:Fr.) P. Karst. and Donkioporia expansa (Desm.) Kotl. & Pouz. were isolated from identical cooling tower environments. Azobé heartwood (Lophira alata), a very durable tropical wood species was totally deteriorated in cooling towers in a similar way by both fungi. First attempts to culture Physisporinus vitreus in laboratory circumstances sh...
J Van Acker, M Stevens
Efficacy of anhydrides as wood protection chemicals - II. Performance against soft rot fungi
1998 - IRG/WP 98-30174
Pine sapwood modified with various anhydrides and with butyl isocyanate was tested for its resistance to soft rot decay. Small stakes were exposed for 20 months in unsterile soil in a fungal cellar test.
Wood modified with butyl isocyanate performed better than any of the anhydrides tested, with a threshold level of protection (less than 3% weight loss) at 12% weight percent gain (WPG). Stakes ac...
S C Forster, M D C Hale, G R Williams
Collaborative field experiment. Questionnaire re site/soil
1980 - IRG/WP 3162
L E Leightley
Questionnaire pour la préparation de fiches monographiques pour les champignons lignivores
1972 - IRG/WP 103 F
C Jacquiot
Performance results of wood treated with CCA-PEG
1986 - IRG/WP 3363
The addition of polyethylene glycol (PEG) to the CCA system has been shown to reduce the surface hardness of poles and ease spur penetration during climbing. This paper addresses the results of tests dealing with preservative retention and penetration, permanence of CCA and PEG, strength, drying rate, and checking characteristics....
W P Trumble, E E Messina