Diffusion of bifluorides and borates from preservative rods in laminated beams
1991 - IRG/WP 3644
Laminated beams from spruce, pine and larch were treated with two preservative rods, based on bifluorides and octaborate respectively. After 3 and 6 months placed in different climates (65% r.h., 100% r.h., water) the diffusion of the active ingredient was measured. After the 6 months period, the diffusion of the bifluorides was, in all species, ca. 5 times larger than the diffusion from octaborat...
H Militz
Fluoride woodpill
1987 - IRG/WP 3431
Decay problems of spruce joinery in the Netherlands in the 1960's and 1970's led to the introduction of preservative treatment. Because of the known penetration difficulties with Spruce, the results of the treatments were not always successful. The fact that the decay was found only in the joints led to development of the philosophy of "local preservation" of the joints in remedi...
J W P T Van der Drift, K J M Bonsen
Leaching results of shower test on L-joints with boric acid, bifluoride and TBTO rods
1995 - IRG/WP 95-50051
As part of the EC-project "Improvement of a local preservation process for wood products with reduced environmental impact", TNO has performed a leaching test on L-joints treated with pills with boric acid (Defence corner), bifluorides (Woodpil 55) and TBTO (Woodcap). The L-joints were exposed in an adapted shower test during 10 days, using 70 liters of water per day. The experiment is designed to...
P Esser, M J Boonstra, W L D Suitela, A J Pendlebury
Long term experiments for assessing the diffusion of boric acid and diluorides from local preservative pills in spruce and pine
1996 - IRG/WP 96-40065
For the experimental assessment of the diffusion of boric acid and difluorides over a three year period 2 tests were set up. In a test with large spruce blocks (150 x 150 x 300 mm³) 3 different pill types were exposed to 3 different climates: climate room (20°C, 65% r.h.), wet room (20°C, 95% r.h.), and to outside exposure. In a test with open L-joints without paint, with an alkyd paint and wit...
W J Homan, H Militz
Field evaluation determining the toxic effect and diffusion properties of Impel, Improsol and TBTO-capsules in L-joints (spruce) for pretreatment application
1991 - IRG/WP 3641
Bonded joints (L-joints and T-joints) are especially at risk from water absorption (rain, condensation) over bare, unprotected radial wood surfaces (joggle joints). It is therefore quite certain that lasting protection against fungi attack cannot be guaranteed in the long term if the surface of coating is damaged. Therefore, in a field investigation, using L-joints (spruce) over a total period of ...
R Gründlinger, K Messner, O Janotta