Your search resulted in 3693 documents. Displaying 25 entries per page.
Kiln drying of poles as a means of solving the problems of pre-treatment decay in poles
1985 - IRG/WP 1263
The concept that pre-treatment decay can cause wide variation in the treatability of wood and especially wood poles has caused much discussion and debate in wood preservation circles. Yet it seem only logical that if decay has effected the strength characteristics of the wood and caused a differential moisture content in the wood the treatment of the end product will be highly variable and the lon...
J A Taylor
Timber deterioration and its prevention in marine environment
2005 - IRG/WP 05-10559
Wood-borer activity is an established fact in Mumbai harbour that leads to severe deterioration of timber. In order to prevent the deterioration caused by wood borers three resin preservatives containing Zinc borate, Organo-copper polymer (4 wt% Cu) and Organo-Tin polymer Copoly(TBTM-MMA) were used for timber treatment. Test panels were treated using standard method and the...
B S Swami, M Udhayakumar, P Kumar, A B Samui
On the laboratory use of X-rays in timber decay evaluations
1981 - IRG/WP 2144
The paper reports the results of laboratory experiments on the X-raying of some Pinus radiata sapwood blocks infected with Serpula lacrymans to determine the effect of density and moisture content on the absorption of X-rays by wood. It is concluded that with increasing moisture content there is a very marked increase in time required to pass a constant quantity of X-rays through a test block and ...
J D Thornton, J W Creffield, O Collett
Water-storage for improving the permeability of sugi (Cryptomeria japonica D. Don)wood
1999 - IRG/WP 99-40129
The viable bacterial counts in sapwood and intermediate wood of sugi bolts increased immediately after floated in a fresh water pond. Bacterial invasion into the heartwood was not detected apparently during water-storage for 36 weeks, although a few bacterial species have inhabited in freshly-cut heartwood samples. The bacterial species isolated from the water-stored bolts were almost Gramnegative...
S Ohta, S Doi
Effect of vapour boron treatment on mechanical properties of wood based board materials
1992 - IRG/WP 92-3727
The mechanical properties of Medium density fibre board, Chipboard and Oriented strand board were investigated after treatment to two retention levels of boric acid applied as a vapour phase system. A range of mechanical properties were investigated. The vapour boron treatment does not have any significant effect on most of the mechanical properties of the boards. The exception is a reduction in i...
R Hashim, D J Dickinson, R J Murphy, J Dinwoodie
Black Stain of Western red-cedar by Aureobasidium pullulans and its Relationship with Tropolone Depletion
2005 - IRG/WP 05-10564
Western red-cedar is valued for its natural durability conferred by fungicidal tropolone chemicals. However, weathered surfaces of WRC products are still susceptible to ‘black stain’ caused by fungi such as Aureobasidium pullulans. The effect of weathering on the tropolone content of heartwood was characterized and correlated with the ability of this fungal species to colonize the same weather...
R Chedgy, R Daniels, P I Morris, C Breuil
The long road to understanding brown-rot decay. A view from the ditch
1995 - IRG/WP 95-10101
Interest in understanding how brown-rot fungi decay wood has received increasing interest in recent years because of a need to identify novel targets that can be inhibited for the next generation of antifungal wood preservatives. Brown-rot fungi are unique in that they can degrade holocellulose (cellulose and hemicellulose) in wood without first removing the lignin. Furthermore, they degrade holoc...
F Green III, T L Highley
A comparison of the migration behaviour in soil of different waterborne wood preservatives and their leachates
1997 - IRG/WP 97-50091
Lysimeter tests were carried out on water-soluble wood preservatives and on wood preservative components leached out of impregnated wood. The purpose of these tests was to determine the extent to which the migration behaviour of environmentally relevant ions in the soil is influenced under comparable conditions. The results clearly show that the groundwater is especially at risk when wood preserva...
E Melcher, R-D Peek
Acceleration of boric acid uptake into the subterranean termite, Coptotermes formosanus Shiraki using steamed larch wood
2000 - IRG/WP 00-10353
Laboratory tests were done to measure the efficacy of addition of steamed larch (Larix leptolepis (Sieb. et Zucc.) Gord.) heartwood extracts for the uptake of boric acid against the termite, Coptotermes formosanus Shiraki. Paper discs were treated with the water-soluble fraction obtained from hot-water extracts of steamed larch wood (S-Water) with or without 0.01-2.0% boric acid, followed by expos...
W Ohmura, S Doi, S Ohara
A laboratory study on effect of coating materials on leaching of copper from CCA treated wood
2001 - IRG/WP 01-50176
Components of CCA preservatives can leach into surrounding soil and water and have some effect on germination and growth of some plants. In this report, the effect of coating materials in reducing chemical concentration in the leachate were evaluated. Rubber wood blocks (Hevea brasiliensis) treated with CCA were fixed at room temperature at high humidity. After air dried, they were painted with co...
A Veenin, T Veenin
A review of incising as a means of improving treatment of sawnwood
1994 - IRG/WP 94-40019
The use of incising, perforation of the wood surface, is increased because of the need to treat refractory wood species. This paper reviews the development of incising and shows how the required incising patterns can be determined and specified. Most of the development has been in the area of toothed-roller incisors because of their rapid throughput. Needle, Laser, drill and water jet incisors hav...
P I Morris, J J Morrell, J N R Ruddick
Rapid loss of lignin at wood surfaces during natural weathering
1992 - IRG/WP 92-2390
Thin veneers of radiata pine (Pinus radiata D. Don) were exposed to natural weathering over a period of 30 days. Incident UV radiation was monitored at the test site. FTIR internal reflectance spectroscopy was used to study the chemical changes taking place at the veneer surface during weathering. Spectra obtained show that after only 3 days exposure there was substantial delignification at veneer...
P D Evans, K J Schmalzl, A J Michell
Is laboratory testing of decay resistance questionable as a single criterion for natural durability?
1996 - IRG/WP 96-20096
In a laboratory test set up over 20 hardwood species were evaluated according to the European Standard EN 350-1 including Basidiomycete and soft rot testing. Half of the species used were of a known natural durability. The Basidiomycete testing was carried out using Coriolus versicolor, Gloeophyllum trabeum and Coniophora puteana in a malt agar test similar to EN 113. From this test it was not pos...
J Van Acker, M Stevens, T Van Cauwenberghe, T Seynaeve
Moisture content development in lap-joints of different wood species in outside exposure trials
1998 - IRG/WP 98-20143
Lap-joint trails (following European Standard EN 12037) were set up with 11 different softwood and hardwood species. Half of the number of the lap-joint specimens were coated with an alkyd coating. The moisture development has been followed during a 19 months period. In this paper, the out comes of different moisture contents evaluations are presented. The results show, that the moisture content o...
H Militz, M Broertjes, C J Bloom
Mold and stain fungi associated with Radiata pine logs imported from New Zealand
2000 - IRG/WP 00-10346
The Korean sawmills have recently realized the importance of prevention of fungal discoloration due to increased losses in revenue. Before establishing integrated control strategies of fungal discoloration, more complete knowledge about causal organisms is needed. As a first step, we initiated a through survey of mold and stain fungi colonized commercially important softwood species (Pinus densifl...
Jae-Jin Kim, Gyu-Hyeok Kim
Evaluation of a utility pole inspection procedure
1996 - IRG/WP 96-20084
Methods were developed and are currently being utilized to appraise residual strength of utility poles based on visual assessment of increment cores. Strength tests, mycological descriptions and anatomical analyses were performed on eight utility poles taken out of service and one new (never in service) pole. Samples were obtained from increment cores removed from 6 levels in the pole: 2 feet, gro...
S E Anagnost, C J K Wang
Screening techniques for potential wood preservative chemicals. Proceedings of a special seminar held in association with the 10th Annual Meeting of the IRG, Peebles 1978. Report No 136, 1979
1980 - IRG/WP 2138
This paper continues following issues:
I. SCREENING INSECTICIDES
1) R W Berry (BRE/PRL, UK): Screen testing of insecticides for use in remedial wood preservatives.
2) D J Cross (FRI, New Zealand): Rapid screening of contact insecticides for use on forest products.
3) C R Coggins; A Forsyth; A E Glaser (Rentokil, UK): Experience in the use of indicative screening techniques for termiticides.
...
Anonymous
Proposing innovative technologies in the control of dry-wood insects
1985 - IRG/WP 1262
This paper discusses the social-economic problems involved in the biological evaluation of dry-wood insects with particular reference to Nigeria. It also discusses prospects of applying non-conventional methods of control against such insects, integrating these with the conventional preservatives as a control strategy. This discussion follows attempts made to identify the major dry-wood insects in...
M O Akanbi
New boron-based biocides for the protection of wood
2002 - IRG/WP 02-30283
Boric acid and other simple inorganic oxides of boron are amongst the oldest wood preservatives currently in use. Their relatively low toxicity and broad-spectrum activity are just some of their desirable characteristics. The primary disadvantage associated with conventional boron-based preservatives is their lack of permanence in exposed applications. A collaborative project between CSIRO and the...
D G Humphrey, P J Duggan, E M Tyndall, J M Carr, L J Cookson
Laboratory tests on the natural durability of timber methods and problems
1984 - IRG/WP 2217
In literature a large variety of test methods is mentioned to examine the natural resistance of timber against fungal attack. This concerns the kind of sampling as well as the test procedure, the test fungi, the duration of test, and the classification of the resistance according to the test results. These variations, however, are of great influence on the test result. Long term exposure will lead...
H Willeitner
The relationship between the electrical resistance and fixation of water-borne CCA salts and pressure-treated wood
1991 - IRG/WP 3657
Two investigations at 22°C and 30°C have been carried out. The electrical resistance in the treated wood and chemical analyses of the remaining amount of unfixed copper, chromium and arsenic were investigated. Samples impregnated with water were used as references. To hold the samples moist during the investigation, each sample was wrapped in a polyethylene plastic foil immediately after impregn...
F G Evans, B Nossen
Treatment of refractory timbers
1993 - IRG/WP 93-40001
Worldover crisis of wood is being felt due to the global environmental problems. Wood preservation technology plays a good role in curtailing the demands of wood for replacement by prolonging the service life of the timber and thus indirectly helps in saving the environment. Some species of timbers which could not be treated to the desired level by virtue of their refractory nature by any of the c...
I Dev, S Kumar
Corrosion of fasteners in treated wood
1971 - IRG/WP 303
Surveying tests for determining the corrosion rates of some metals and alloys in wood untreated as well as treated have been made. It is shown that ordinary steel corrodes faster than other common fastener metals such as copper, brass, aluminium and stainless steel do. Zinc coatings, however, will prevent the steel corrosion effectively provided that the coatings are thick sufficiently. Catalytic ...
T Wallin
Aspects of the fungal degradation of quaternary ammonium compounds in liquid culture
1997 - IRG/WP 97-30160
Didecyldimethylammonium chloride (DDAC) is a quaternary ammonium compound (QAC) that has found use as an anti-sapstain preservative for the transportation of softwood lumber from Canada to overseas markets. However, its use is limited by the knowledge that certain mould fungi seem capable of degrading it. The aim of this research was to gain knowledge about the fungal degradation of DDAC. The effe...
J W Dubois, J N R Ruddick
Emissions from the combusting of boron and fluoride containing wood
1995 - IRG/WP 95-50040-18
The combustion properties of waste wood and wood residues containing wood preservatives were investigated in several test series after having been blended with untreated wood at a ratio of 1:4. The results for CFB, SF and boric salt show that, provided an optimized combustion, the concentrations of the stack pollutants correspond approximately with those found for untreated wood. Only during the c...
T Salthammer, H Klipp, R-D Peek